CN108358540B - 一种用于多彩混凝土装饰板材料及其制备方法 - Google Patents
一种用于多彩混凝土装饰板材料及其制备方法 Download PDFInfo
- Publication number
- CN108358540B CN108358540B CN201810078878.5A CN201810078878A CN108358540B CN 108358540 B CN108358540 B CN 108358540B CN 201810078878 A CN201810078878 A CN 201810078878A CN 108358540 B CN108358540 B CN 108358540B
- Authority
- CN
- China
- Prior art keywords
- fiber
- decorative plate
- parts
- colorful
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供一种用于多彩混凝土装饰板材料及制备方法；所述材料由以下重量份数的各组分组成：彩色骨料20～80份，胶凝材料10～50份，掺合料2～40份，颜料0.01～2份，外加剂0.1～5份，纤维0.01～2份。本发明的混合料由多彩混凝土装饰板材料组成或彩色混凝土填充彩色骨料组成，将其浇筑试模中，养护到一定龄期后切割、抛光，涂覆保护剂，即形成色彩缤纷的艺术装饰板，可以大幅降低生产成本，有效节约资源；本发明涉及的多彩混凝土装饰板是在工厂预制，可集保温与装饰为一体，现场组装方便，施工快捷，装饰效果好。
Description
技术领域
本发明涉及建筑技术领域，具体涉及一种用于多彩混凝土装饰板材料及其制备方法。
背景技术
目前我国建筑节能相关产业蓬勃发展，国家大力推进装配式建筑发展，积极倡导固体废弃物资源化综合利用。本发明提出的多彩混凝土装饰板，具有质量轻、强度高、保温隔热防火、成本低廉等优点。装饰板的制备采用预制方法，通过在混凝土中填充不同粒径的彩色骨料，经过养护、切割、打磨、抛光等工序，制成集保温与装饰为一体的墙板材料，本发明对彩色骨料的品质要求较低，可选择范围大，如可利用建筑垃圾、工业废渣等，从而实现较高的经济效益，具有良好的推广价值。
发明内容
本发明的目的是提供一种用于多彩混凝土装饰板材料及制备方法；该装饰板通过彩色骨料与彩色混凝土(或砂浆)配制而成，将其浇筑试模中，养护到一定龄期后切割、抛光，涂覆保护剂，即形成色彩缤纷的艺术装饰板。该多彩混凝土装饰板可制成装饰板材、装配式墙板、轻质隔墙板等，以适应不同工程设计需求。
第一方面，本发明提供一种用于多彩混凝土装饰板材料，由以下重量份数的各组分组成：
优选地，所述彩色骨料由建筑垃圾、工业废渣中的一种或几种组成。
优选地，所述胶凝材料由普通硅酸盐水泥、白水泥、铝酸盐水泥、石膏、石灰中的一种或几种组成。
优选地，所述掺合料由粉煤灰、矿粉、硅灰、石粉、稻壳灰中的一种或几种组成。
优选地，所述颜料由氧化铁、氧化铬、氧化钛、氧化钴、炭黑、立德粉、镉红、铬黄、钡铬黄、群青、钴蓝中的一种或几种组成。
优选地，所述外加剂由减水剂、引气剂、膨胀剂、发泡剂、早强剂、激发剂中的一种或几种组成。
优选地，所述纤维由钢纤维、聚丙烯纤维、聚乙烯纤维、聚乙烯醇纤维、尼龙纤维、玻璃纤维、碳纤维、氧化铝纤维、碳化硅纤维中的一种或几种组成。
第二方面，本发明还涉及前述的用于多彩混凝土装饰板材料制备装饰板的方法，包括以下步骤：
步骤1：在模具中先浇一层由所述多彩混凝土装饰板材料组成的混合料或彩色混凝土填充彩色骨料组成的混合料，厚度控制在10mm～200mm，所述彩色骨料与所述多彩混凝土体积比为10％-60％；
步骤2：在浇筑面上布加强筋，所述加强筋为钢筋、钢丝网、网格布、三维网、土工格栅的任意一种或任意几种的组合；
步骤3：重复步骤1和步骤2，至浇筑到设计高度；
步骤4：混合料硬化后拆模，保湿养护；
步骤5：养护到一定龄期后，按模块切割试件，所述模块尺寸：长300mm～4000mm、宽150mm～12000mm、厚10mm～400mm；
步骤6：对切割装饰面分级打磨抛光；
步骤7：对抛光面涂覆保护剂，即可制得装饰板，所述保护剂为蜡、丙烯酸树脂、有机硅树脂、氟碳聚合物的任意一种或任意几种的组合。
优选地，将所述装饰板制成薄型装饰板材，用于室内、外装饰装修。
优选地，将所述装饰板预制成装配式墙板，用于装配式建筑；将所述装饰板制成轻质隔墙板，用于建筑室内隔墙。
与现有技术相比，本发明具有如下的有益效果：
(1)本发明的混合料由多彩混凝土装饰板材料组成或彩色混凝土填充彩色骨料组成，可以大幅降低生产成本，有效节约资源；
(2)本发明涉及的彩色骨料可选范围广，材料方面可以使用建筑垃圾、工业废渣；尺寸方面可以应用经过粗加工的彩色骨料，能够有效节约能源资源；
(3)本发明涉及的彩色骨料和加强筋的使用可增加混凝土的抗拉、抗折强度，改善混凝土的干缩开裂性能；
(4)本发明涉及的多彩混凝土装饰板是在工厂预制，可集保温与装饰为一体，现场组装方便，施工快捷，装饰效果好。
具体实施方式
下面结合具体实施例对本发明进行详细说明。以下实施例将有助于本领域的技术人员进一步理解本发明，但不以任何形式限制本发明。应当指出的是，对本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进。这些都属于本发明的保护范围。
实施例1
本实施例涉及一种用于多彩混凝土装饰板材料，按以下重量份数称取原材料：彩色骨料65，胶凝材料15，掺合料5，颜料2，外加剂3，纤维0.5，水10。
其中，所述彩色骨料为废装饰石材。
其中，所述胶凝材料为硫铝酸盐水泥。
其中，所述掺合料为石粉。
其中，所述颜料为氧化铁。
其中，所述外加剂按以下重量份数称取原材料：减水剂0.4、引气剂0.02、膨胀剂2、早强剂0.4、激发剂0.1。
其中，所述纤维为碳纤维。
本实施例中提供一种用于多彩混凝土装饰板材料制备多彩混凝土装饰板的方法，包括如下步骤：
步骤1：在模具中先浇一层由上述多彩混凝土装饰板材料组成的混合料，厚度控制在20mm；
步骤2：在浇筑面上布置加强筋，所述加强筋为三维网；
步骤3：重复步骤1和步骤2，直至浇筑到设计高度；
步骤4：混合料硬化后拆模，保湿养护；
步骤5：养护到一定龄期后，按模块切割试件，所述模块尺寸：长600mm、宽300mm、厚15mm；
步骤6：对切割装饰面分级打磨抛光；
步骤7：对抛光面涂覆保护剂，所述保护剂为氟碳聚合物。
实施例2
本实施例涉及一种多彩混凝土装饰板材料，按以下重量份数称取原材料：彩色骨料60，胶凝材料20，掺合料5，颜料2，外加剂3，纤维0.8，水10。
其中，所述彩色骨料为废铜尾矿石。
其中，所述胶凝材料为普通硅酸盐水泥。
其中，所述掺合料为矿粉。
其中，所述颜料为钴蓝。
其中，所述外加剂按以下重量份数称取原材料：减水剂0.5、膨胀剂2.5。
其中，所述纤维为聚乙烯纤维。
本实施例中提供一种用于多彩混凝土装饰板材料制备多彩混凝土装饰板的方法，包括如下步骤：
步骤1：在模具中先浇一层由上述多彩混凝土装饰板材料组成的混合料，厚度控制在200mm；
步骤2：在浇筑面上布置加强筋，所述加强筋为钢筋；
步骤3：重复步骤1和步骤2，直至浇筑到设计高度；
步骤4：混合料硬化后拆模，保湿养护；
步骤5：养护到一定龄期后，按模块切割试件，所述模块尺寸：长2400mm、宽600mm、厚200mm；
步骤6：对切割装饰面分级打磨抛光；
步骤7：对抛光面涂覆保护剂，所述保护剂为有机硅树脂。
实施例3
本实施例涉及一种多彩混凝土装饰板材料，按以下重量份数称取原材料：彩色骨料50，胶凝材料25，掺合料5，颜料0.5，外加剂3.5，纤维0.5，水15。
其中，所述彩色骨料为废红石。
其中，所述胶凝材料为普通硅酸盐水泥。
其中，所述掺合料为粉煤灰。
其中，所述颜料为群青。
其中，所述外加剂按以下重量份数称取原材料：减水剂0.2、膨胀剂2.5、发泡剂0.3、早强剂0.5。
其中，所述纤维为聚丙烯纤维。
本实施例中提供一种多彩混凝土装饰板的制备方法，包括如下步骤：
步骤1：在模具中先浇一层由上述彩色泡沫混凝土，厚度控制在150mm，填抛彩色骨料；
步骤2：在浇筑面上布置加强筋，所述加强筋为钢筋和钢丝网；
步骤3：重复步骤1和步骤2，直至浇筑到设计高度；
步骤4：混合料硬化后拆模，保湿养护；
步骤5：养护到一定龄期后，按模块切割试件，所述模块尺寸：长2500mm、宽600mm、厚150mm；
步骤6：对切割装饰面分级打磨抛光；
步骤7：对抛光面涂覆保护剂，所述保护剂为丙烯酸树脂。
以上对本发明的具体实施例进行了描述。需要理解的是，本发明并不局限于上述特定实施方式，本领域技术人员可以在权利要求的范围内做出各种变形或修改，这并不影响本发明的实质内容。
Claims (3)
1.一种用于多彩混凝土装饰板材料制备装饰板的方法，其特征在于，包括以下步骤：
步骤1：在模具中先浇一层由所述用于多彩混凝土装饰板材料组成的混合料，厚度控制在10mm～200mm；
步骤2：在浇筑面上布加强筋，所述加强筋为钢筋、钢丝网、网格布、土工格栅的任意一种或任意几种的组合；
步骤3：重复步骤1和步骤2，至浇筑到设计高度；
步骤4：混合料硬化后拆模，保湿养护；
步骤5：养护到一定龄期后，按模块切割试件，所述模块尺寸：长300mm～4000mm、宽150mm～1200mm、厚10mm～400mm；
步骤6：对切割装饰面分级打磨抛光；
步骤7：对抛光面涂覆保护剂，即可制得装饰板，所述保护剂为蜡、丙烯酸树脂、有机硅树脂、氟碳聚合物的任意一种或任意几种的组合，
所述用于多彩混凝土装饰板材料，由以下重量份数的各组分组成：
所述彩色骨料由建筑垃圾、工业废渣中的一种或几种组成，所述胶凝材料由普通硅酸盐水泥、白水泥、铝酸盐水泥、石膏、石灰中的一种或几种组成，所述掺合料由粉煤灰、矿粉、硅灰、石粉、稻壳灰中的一种或几种组成，所述颜料由氧化铁、氧化铬、氧化钛、氧化钴、炭黑、立德粉、镉红、铬黄、钡铬黄、群青、钴蓝中的一种或几种组成，所述外加剂由减水剂、引气剂、膨胀剂、发泡剂、早强剂、激发剂中的一种或几种组成，所述纤维由钢纤维、聚丙烯纤维、聚乙烯纤维、聚乙烯醇纤维、尼龙纤维、玻璃纤维、碳纤维、氧化铝纤维、碳化硅纤维中的一种或几种组成。
2.根据权利要求1所述的用于多彩混凝土装饰板材料制备装饰板的方法，其特征在于，将所述装饰板制成薄型装饰板材，用于室内、外装饰装修。
3.根据权利要求1所述的用于多彩混凝土装饰板材料制备装饰板的方法，其特征在于，将所述装饰板预制成装配式墙板，用于装配式建筑；将所述装饰板制成轻质隔墙板，用于建筑室内隔墙。