CN108330681A - 一种医用棉纱布制备工艺及方法 - Google Patents
一种医用棉纱布制备工艺及方法 Download PDFInfo
- Publication number
- CN108330681A CN108330681A CN201711418920.5A CN201711418920A CN108330681A CN 108330681 A CN108330681 A CN 108330681A CN 201711418920 A CN201711418920 A CN 201711418920A CN 108330681 A CN108330681 A CN 108330681A
- Authority
- CN
- China
- Prior art keywords
- cotton gauze
- degreasing
- water
- degreasing cotton
- impregnated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种医用棉纱布制备工艺及方法，脱脂棉纱布首先需要进行消毒预处理，采用无水乙醇对棉纱布进行消毒灭菌处理，进行预处理结束后，脱水处理，将脱脂棉纱布投入一定浓度的烧碱水进行浸泡处理，脱脂棉纱布经过烧碱水浸泡后，脱水处理，再使用热水进行浸泡，对使用热水浸泡后的脱脂棉纱布进行脱水处理，然后投入一定浓度的弱酸水进行浸泡，使用弱酸水进行浸泡后。本发明首先通过无水乙醇对棉纱布进行消毒处理，保障棉纱布在无菌的环境下进行后续加工处理，然后使用烧碱水对棉纱布进行膨化处理，弱酸水对碱性物质进行中和，使用抗菌整体剂对棉纱布的蓬松结构进行抗菌处理，使得医用棉纱布在使用时具有良好的抗菌性。
Description
技术领域
本发明涉及医用棉纱布技术领域，具体为一种医用棉纱布制备工艺及方法。
背景技术
随着社会的发展，科技的不断进步，越来越多设备的使用大大降低了人们生产生活的劳动强度，同时越来越多新产品的生产对人们的生产生活也起到积极的作用，改善了人们的生产生活的方式，其中棉纱布在医疗使用者起到了重要的作用，棉制品作为一种天然纤维素纤维，棉制品不仅以其优良的服用性能深受人们喜爱，而且以其与人体极好的亲和性，成为广泛应用的医用基材之一，医用棉纱布是国内外广泛使用的产品，供清洁皮肤或创面、吸收手术过程中的体内渗出液、与创面护理常用药物一起使用及手术过程中支撑器官、组织等，国内企业生产的医用棉纱布在临床上已得到广泛应用，社会效益和经济效益明显。
但现有的医用棉纱布在使用时存在抗菌性不好的问题，使得医用棉纱布在对患者伤口进行接触时，易产生细菌，延缓患者伤口的恢复，严重是还会引发感染等问题。
发明内容
（一）解决的技术问题
针对现有技术的不足，本发明提供了一种医用棉纱布制备工艺及方法，具备防止细菌滋长保护患者伤口皮肤等优点，解决了现有的医用棉纱布在使用时易产生细菌延缓患者伤口恢复的问题。
（二）技术方案
为实现上述防止细菌滋长保护患者伤口皮肤的目的，本发明提供如下技术方案：
一种医用棉纱布制备工艺及方法，脱脂棉纱布首先需要进行消毒预处理，采用无水乙醇对棉纱布进行消毒灭菌处理，进行预处理结束后，脱水处理，将脱脂棉纱布投入一定浓度的烧碱水进行浸泡处理，脱脂棉纱布经过烧碱水浸泡后，脱水处理，再使用热水进行浸泡，对使用热水浸泡后的脱脂棉纱布进行脱水处理，然后投入一定浓度的弱酸水进行浸泡，使用弱酸水进行浸泡后，使用热水对脱脂棉纱布进行浸泡和洗涤，然后进行抗菌处理，抗菌处理过后进行脱水烘干。
优选的，所述无水乙醇的溶液浓度为95%-98%，无水乙醇对棉纱布进行完全浸泡处理。
优选的，所述烧碱水内主要含有氢氧化钠，氢氧化钠的含量为30% -35%，烧碱水的温度为30-40摄氏度。
优选的，所述弱酸水内主要含有氯化氢和醋酸，氯化氢的含量为5%-10%，醋酸的含量为2%-7%。
优选的，所述抗菌处理主要采用抗菌剂对脱脂棉纱布进行处理，抗菌剂主要采用抗菌整理剂。
本发明提供一种医用棉纱布制备工艺及方法，包括以下步骤：
S1、消毒预处理：将脱脂棉纱布放置在盛有无水乙醇的浸泡池内，进行浸泡，对脱脂棉纱布进行消毒灭菌处理，浸泡时间为80-100分钟，浸泡过后的脱脂棉纱布使用脱水设备进行脱水，去除脱脂棉纱布上残留的大量无水乙醇。
S2、烧碱水浸泡处理：将脱水过后的脱脂棉纱布使用氢氧化钠浓度为30% -35%烧碱水进行浸泡，烧碱水的温度为30-40摄氏度，浸泡时间为40-60分钟，浸泡过后的脱脂棉纱布再使用脱水设备进行脱水处理，去除脱脂棉纱布上残留的大量烧碱水。
S3、经过烧碱水浸泡过后的脱脂棉纱布脱水过后，投入热水中进行浸泡洗涤，热水的温度为45-50摄氏度，浸泡洗涤的时间为20-30分钟，去除脱脂棉纱布上残留的碱性残留物，然后使用脱水设备进行脱水处理。
S4、将脱水过后的脱脂棉纱布投入盛有弱酸水的浸泡浸泡池中，进行浸泡，弱酸水内主要含有氯化氢和醋酸，氯化氢的含量为5%-10%，醋酸的含量为2%-7%，弱酸水对脱脂棉纱布中的碱性物进行中和，直至酸碱中和完成，PH=7，然后使用脱水设备对脱脂剂棉纱布进行脱水处理。
S5、脱水过后的脱脂棉纱布使用热水进行浸泡和洗涤，热水的温度为40-50摄氏度，浸泡洗涤的时间为30-50分钟，然后使用抗菌整体剂在60-80摄氏度的环境温度下对脱脂棉纱布进行抗菌处理，处理时间为60-80分钟。
S6、脱脂棉纱布进行抗菌处理过后，使用脱水设备对脱脂棉纱布进行脱水处理，然后使用烘干器将脱脂棉纱布在70摄氏度的环境温度下进行烘干处理。
（三）有益效果
与现有技术相比，本发明提供了一种医用棉纱布制备工艺及方法，具备以下有益效果：
1、该医用棉纱布的制备工艺和方法，首先通过无水乙醇对棉纱布进行消毒处理，保障棉纱布在无菌的环境下进行后续加工处理，然后使用烧碱水对棉纱布进行膨化处理，弱酸水对碱性物质进行中和，有效的保障棉纱布结构的膨化疏松，有利于后续棉纱布的抗菌处理，提高有效的提高棉纱布的抗菌性。
2、该医用棉纱布的的制备工艺和方法，当棉纱布酸碱中和进行清洗过后，使用抗菌整体剂对棉纱布的蓬松结构进行抗菌处理，有利于抗菌整体剂与棉纱布整体的融合，然后将脱脂棉纱布进行脱水烘干即可。
具体实施方式
下面将结合本发明的实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
一种医用棉纱布制备工艺及方法，脱脂棉纱布首先需要进行消毒预处理，采用无水乙醇对棉纱布进行消毒灭菌处理，无水乙醇的溶液浓度为95%-98%，无水乙醇对棉纱布进行完全浸泡处理，进行预处理结束后，脱水处理，将脱脂棉纱布投入一定浓度的烧碱水进行浸泡处理，烧碱水内主要含有氢氧化钠，氢氧化钠的含量为30% -35%，烧碱水的温度为30-40摄氏度，脱脂棉纱布经过烧碱水浸泡后，脱水处理，再使用热水进行浸泡，对使用热水浸泡后的脱脂棉纱布进行脱水处理，然后投入一定浓度的弱酸水进行浸泡，弱酸水内主要含有氯化氢和醋酸，氯化氢的含量为5%-10%，醋酸的含量为2%-7%，使用弱酸水进行浸泡后，使用热水对脱脂棉纱布进行浸泡和洗涤，然后进行抗菌处理，抗菌处理主要采用抗菌剂对脱脂棉纱布进行处理，抗菌剂主要采用抗菌整理剂，抗菌处理过后进行脱水烘干。
实施例一：
S1、消毒预处理：将脱脂棉纱布放置在盛有无水乙醇的浸泡池内，进行浸泡，对脱脂棉纱布进行消毒灭菌处理，浸泡时间为80分钟，浸泡过后的脱脂棉纱布使用脱水设备进行脱水，去除脱脂棉纱布上残留的大量无水乙醇。
S2、烧碱水浸泡处理：将脱水过后的脱脂棉纱布使用氢氧化钠浓度为30% 烧碱水进行浸泡，烧碱水的温度为30摄氏度，浸泡时间为40分钟，浸泡过后的脱脂棉纱布再使用脱水设备进行脱水处理，去除脱脂棉纱布上残留的大量烧碱水。
S3、经过烧碱水浸泡过后的脱脂棉纱布脱水过后，投入热水中进行浸泡洗涤，热水的温度为45摄氏度，浸泡洗涤的时间为20分钟，去除脱脂棉纱布上残留的碱性残留物，然后使用脱水设备进行脱水处理。
S4、将脱水过后的脱脂棉纱布投入盛有弱酸水的浸泡浸泡池中，进行浸泡，弱酸水内主要含有氯化氢和醋酸，氯化氢的含量为5%，醋酸的含量为2%，弱酸水对脱脂棉纱布中的碱性物进行中和，直至酸碱中和完成，PH=7，然后使用脱水设备对脱脂剂棉纱布进行脱水处理。
S5、脱水过后的脱脂棉纱布使用热水进行浸泡和洗涤，热水的温度为40摄氏度，浸泡洗涤的时间为30分钟，然后使用抗菌整体剂在60摄氏度的环境温度下对脱脂棉纱布进行抗菌处理，处理时间为60分钟。
S6、脱脂棉纱布进行抗菌处理过后，使用脱水设备对脱脂棉纱布进行脱水处理，然后使用烘干器将脱脂棉纱布在70摄氏度的环境温度下进行烘干处理。
实施例二：
S1、消毒预处理：将脱脂棉纱布放置在盛有无水乙醇的浸泡池内，进行浸泡，对脱脂棉纱布进行消毒灭菌处理，浸泡时间为90分钟，浸泡过后的脱脂棉纱布使用脱水设备进行脱水，去除脱脂棉纱布上残留的大量无水乙醇。
S2、烧碱水浸泡处理：将脱水过后的脱脂棉纱布使用氢氧化钠浓度为33% 烧碱水进行浸泡，烧碱水的温度为35摄氏度，浸泡时间为50分钟，浸泡过后的脱脂棉纱布再使用脱水设备进行脱水处理，去除脱脂棉纱布上残留的大量烧碱水。
S3、经过烧碱水浸泡过后的脱脂棉纱布脱水过后，投入热水中进行浸泡洗涤，热水的温度为48摄氏度，浸泡洗涤的时间为25分钟，去除脱脂棉纱布上残留的碱性残留物，然后使用脱水设备进行脱水处理。
S4、将脱水过后的脱脂棉纱布投入盛有弱酸水的浸泡浸泡池中，进行浸泡，弱酸水内主要含有氯化氢和醋酸，氯化氢的含量为7%，醋酸的含量为5%，弱酸水对脱脂棉纱布中的碱性物进行中和，直至酸碱中和完成，PH=7，然后使用脱水设备对脱脂剂棉纱布进行脱水处理。
S5、脱水过后的脱脂棉纱布使用热水进行浸泡和洗涤，热水的温度为45摄氏度，浸泡洗涤的时间为40分钟，然后使用抗菌整体剂在70摄氏度的环境温度下对脱脂棉纱布进行抗菌处理，处理时间为70分钟。
S6、脱脂棉纱布进行抗菌处理过后，使用脱水设备对脱脂棉纱布进行脱水处理，然后使用烘干器将脱脂棉纱布在70摄氏度的环境温度下进行烘干处理。
实施例三：
S1、消毒预处理：将脱脂棉纱布放置在盛有无水乙醇的浸泡池内，进行浸泡，对脱脂棉纱布进行消毒灭菌处理，浸泡时间为100分钟，浸泡过后的脱脂棉纱布使用脱水设备进行脱水，去除脱脂棉纱布上残留的大量无水乙醇。
S2、烧碱水浸泡处理：将脱水过后的脱脂棉纱布使用氢氧化钠浓度为35% 烧碱水进行浸泡，烧碱水的温度为40摄氏度，浸泡时间为60分钟，浸泡过后的脱脂棉纱布再使用脱水设备进行脱水处理，去除脱脂棉纱布上残留的大量烧碱水。
S3、经过烧碱水浸泡过后的脱脂棉纱布脱水过后，投入热水中进行浸泡洗涤，热水的温度为50摄氏度，浸泡洗涤的时间为30分钟，去除脱脂棉纱布上残留的碱性残留物，然后使用脱水设备进行脱水处理。
S4、将脱水过后的脱脂棉纱布投入盛有弱酸水的浸泡浸泡池中，进行浸泡，弱酸水内主要含有氯化氢和醋酸，氯化氢的含量为10%，醋酸的含量为7%，弱酸水对脱脂棉纱布中的碱性物进行中和，直至酸碱中和完成，PH=7，然后使用脱水设备对脱脂剂棉纱布进行脱水处理。
S5、脱水过后的脱脂棉纱布使用热水进行浸泡和洗涤，热水的温度为50摄氏度，浸泡洗涤的时间为50分钟，然后使用抗菌整体剂在80摄氏度的环境温度下对脱脂棉纱布进行抗菌处理，处理时间为80分钟。
S6、脱脂棉纱布进行抗菌处理过后，使用脱水设备对脱脂棉纱布进行脱水处理，然后使用烘干器将脱脂棉纱布在70摄氏度的环境温度下进行烘干处理。
本发明的有益效果是：首先通过无水乙醇对棉纱布进行消毒处理，保障棉纱布在无菌的环境下进行后续加工处理，然后使用烧碱水对棉纱布进行膨化处理，弱酸水对碱性物质进行中和，有效的保障棉纱布结构的膨化疏松，有利于后续棉纱布的抗菌处理，提高有效的提高棉纱布的抗菌性，当棉纱布酸碱中和进行清洗过后，使用抗菌整体剂对棉纱布的蓬松结构进行抗菌处理，有利于抗菌整体剂与棉纱布整体的融合，使得医用棉纱布在使用时具有良好的抗菌性。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (6)
1.一种医用棉纱布制备工艺及方法，其特征在于，脱脂棉纱布首先需要进行消毒预处理，采用无水乙醇对棉纱布进行消毒灭菌处理，进行预处理结束后，脱水处理，将脱脂棉纱布投入一定浓度的烧碱水进行浸泡处理，脱脂棉纱布经过烧碱水浸泡后，脱水处理，再使用热水进行浸泡，对使用热水浸泡后的脱脂棉纱布进行脱水处理，然后投入一定浓度的弱酸水进行浸泡，使用弱酸水进行浸泡后，使用热水对脱脂棉纱布进行浸泡和洗涤，然后进行抗菌处理，抗菌处理过后进行脱水烘干。
2.根据权利要求1所述的一种医用棉纱布制备工艺及方法，其特征在于，所述无水乙醇的溶液浓度为95%-98%，无水乙醇对棉纱布进行完全浸泡处理。
3.根据权利要求1所述的一种医用棉纱布制备工艺及方法，其特征在于，所述烧碱水内主要含有氢氧化钠，氢氧化钠的含量为30% -35%，烧碱水的温度为30-40摄氏度。
4.根据权利要求1所述的一种医用棉纱布制备工艺及方法，其特征在于，所述弱酸水内主要含有氯化氢和醋酸，氯化氢的含量为5%-10%，醋酸的含量为2%-7%。
5.根据权利要求1所述的一种医用棉纱布制备工艺及方法，其特征在于，所述抗菌处理主要采用抗菌剂对脱脂棉纱布进行处理，抗菌剂主要采用抗菌整理剂。
6.一种医用棉纱布制备工艺及方法，其特征在于，包括以下步骤：
S1、消毒预处理：将脱脂棉纱布放置在盛有无水乙醇的浸泡池内，进行浸泡，对脱脂棉纱布进行消毒灭菌处理，浸泡时间为80-100分钟，浸泡过后的脱脂棉纱布使用脱水设备进行脱水，去除脱脂棉纱布上残留的大量无水乙醇；
S2、烧碱水浸泡处理：将脱水过后的脱脂棉纱布使用氢氧化钠浓度为30% -35%烧碱水进行浸泡，烧碱水的温度为30-40摄氏度，浸泡时间为40-60分钟，浸泡过后的脱脂棉纱布再使用脱水设备进行脱水处理，去除脱脂棉纱布上残留的大量烧碱水；
S3、经过烧碱水浸泡过后的脱脂棉纱布脱水过后，投入热水中进行浸泡洗涤，热水的温度为45-50摄氏度，浸泡洗涤的时间为20-30分钟，去除脱脂棉纱布上残留的碱性残留物，然后使用脱水设备进行脱水处理；
S4、将脱水过后的脱脂棉纱布投入盛有弱酸水的浸泡浸泡池中，进行浸泡，弱酸水内主要含有氯化氢和醋酸，氯化氢的含量为5%-10%，醋酸的含量为2%-7%，弱酸水对脱脂棉纱布中的碱性物进行中和，直至酸碱中和完成，PH=7，然后使用脱水设备对脱脂剂棉纱布进行脱水处理；
S5、脱水过后的脱脂棉纱布使用热水进行浸泡和洗涤，热水的温度为40-50摄氏度，浸泡洗涤的时间为30-50分钟，然后使用抗菌整体剂在60-80摄氏度的环境温度下对脱脂棉纱布进行抗菌处理，处理时间为60-80分钟；
S6、脱脂棉纱布进行抗菌处理过后，使用脱水设备对脱脂棉纱布进行脱水处理，然后使用烘干器将脱脂棉纱布在70摄氏度的环境温度下进行烘干处理。