CN108329824A - A kind of aqueous light UV solidification aluminium paint, preparation method and its application method - Google Patents

A kind of aqueous light UV solidification aluminium paint, preparation method and its application method Download PDF

Info

Publication number
CN108329824A
CN108329824A CN201711452847.3A CN201711452847A CN108329824A CN 108329824 A CN108329824 A CN 108329824A CN 201711452847 A CN201711452847 A CN 201711452847A CN 108329824 A CN108329824 A CN 108329824A
Authority
CN
China
Prior art keywords
parts
aluminium
paint
aqueous
agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201711452847.3A
Other languages
Chinese (zh)
Inventor
王景泉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chuzhou Jinqiao Deke New Material Co Ltd
Original Assignee
Chuzhou Jinqiao Deke New Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chuzhou Jinqiao Deke New Material Co Ltd filed Critical Chuzhou Jinqiao Deke New Material Co Ltd
Priority to CN201711452847.3A priority Critical patent/CN108329824A/en
Publication of CN108329824A publication Critical patent/CN108329824A/en
Withdrawn legal-status Critical Current

Abstract

The present invention relates to a kind of aqueous light UV solidifications aluminium paint, preparation method and its application methods, and the workpiece surface that can solve plating is rough, and gloss is low, and the bad problem such as poor adhesive force, not wear-resisting belongs to environmentally friendly aluminium paint field.The aluminium paint of the present invention includes mainly that the component of following mass parts is made:65 ~ 95 parts of aqueous UV urethane acrylates, 0.05 ~ 0.5 part of wetting agent, 0.05 ~ 0.5 part of levelling agent, 2 ~ 10 parts of thickener, 0.5 ~ 3.5 part of photoinitiator, 0.05 ~ 0.5 part of antifoaming agent, 0.1 ~ 3.0 part of dimethylethanolamine, 1 ~ 6 part of water, 2 ~ 14 parts of aluminium paste.The aluminium paint of the present invention can be used in the application of household electrical appliances plastic part surface, and paint film has the characteristics that good aluminium powder arrangement effect, high glaze, high rigidity, high abrasion.

Description

A kind of aqueous light UV solidification aluminium paint, preparation method and its application method
Technical field
The invention belongs to environmentally friendly aluminium paint fields, and in particular to a kind of aqueous light UV solidifications aluminium paint;In addition, this hair The bright preparation method and application method for also relating to the aqueous light UV solidifications aluminium paint.
Background technology
Aluminium paint is a kind of paint containing aluminium powder, because the good ductility of aluminium can form continuously aluminium in film Film can cover pin hole, reduce permeability.
Traditional aluminium paint application usually produces the paint vehicle of aluminium paint by alkyd tree usually based on solvent based coating Fat, solvent and aluminum paste composition, and alkyd resin be with polyacid, unit acid and the raw materials such as polyalcohol in resin reaction kettle into What row esterification generated.Solvent for use is gasoline, dimethylbenzene, turpentine oil etc., and aromatic solvent is not belonging to film forming matter, used Solvent can be discharged into air, not only waste resource, but also polluted environment, certain harm can also be caused to human body.
Coating material solidified ultraviolet light (UV) is the liquid oligomer and list caused using ultraviolet initiator in coating system Free radical polymerization occurs for body to realize that crosslinking curing forms a kind of coating of film, because less or have without using solvent There are green, environmental protection;Moreover, because using ultraviolet light as energy source is caused, without additional heating, therefore in coating Energy expenditure can be reduced in solidification process and obtains faster curing rate;Because of these features, UV is coating material solidified in each row Extensive use is just gradually obtained in industry, especially in consumer electronics product such as laptop, mobile phone industry just gradually The polyurethane coating of high energy consumption, high VOC emission is replaced to be applied as the principal item of external coating.
Compared with traditional solvent based coating, water paint has price low, safe to use, saves resource and the energy, subtracts The advantages that few environmental pollution and public hazards, thus have become the Main way of current development coatings industry.Water-base resin system at present Have water alcohol acid, water soluble acrylic acid, water-base epoxy, waterborne polyurethane resin, aqueous inorganic silicate, water-based fluororesin and it Modified resin.Acrylic acid(PA)There are wearability, the defect of water resistance and chemical-resistant difference, single polyurethane for lotion (PU)There is also some shortcomings for lotion, and the gloss retention such as stability, white thickening property and film is poor, and solid content is high, and application range is not wide Deng.PU and PA has complementation in nature.The advantages of PUA complex emulsions have had both the two, has wear-resisting, corrosion-resistant and light Bright, soft flexible, water resistance and mechanical mechanics property are good, and weatherability is good etc., and characteristics, a development for becoming current coating become Gesture.
Invention content
The purpose of the present invention is on the basis of existing technology, providing a kind of aqueous light UV solidifications aluminium paint, can solve The workpiece surface being certainly electroplated is rough, and gloss is low, the bad problem such as poor adhesive force, not wear-resisting.
Another mesh of the present invention is to provide a kind of preparation method of above-mentioned aqueous light UV solidifications aluminium paint.
The present invention also provides the application methods that a kind of aqueous light UV cures aluminium paint.
Technical scheme is as follows:
A kind of aqueous light UV solidifications aluminium paint, mainly the component including following mass parts is made for it:Aqueous UV polyurethane propylene 7,655 65 ~ 95 parts of acid esters UCECOAT, 0.05 ~ 0.5 part of wetting agent, 0.05 ~ 0.5 part of levelling agent, 2 ~ 10 parts of thickener, light 0.5 ~ 3.5 part of initiator, 0.05 ~ 0.5 part of antifoaming agent, 0.1 ~ 3.0 part of dimethylethanolamine, 1 ~ 6 part of water, 2 ~ 14 parts of aluminium paste.
In a kind of preferred embodiment, aluminium paint of the invention includes mainly that the component of following mass parts is made:The aqueous poly- ammonia of UV 7,655 70 ~ 90 parts of ester acrylate UCECOAT, 0.1 ~ 0.3 part of wetting agent, 0.1 ~ 0.3 part of levelling agent, 3 ~ 9 parts of thickener, 1.0 ~ 3.0 parts of photoinitiator, 0.1 ~ 0.3 part of antifoaming agent, 0.2 ~ 2.5 part of dimethylethanolamine, 2 ~ 5 parts of water, 4 ~ 12 parts of aluminium paste.
In a kind of more preferable scheme, aluminium paint of the invention includes mainly that the component of following mass parts is made:Aqueous UV is poly- 7,655 75 ~ 85 parts of urethane acrylate UCECOAT, 0.15 ~ 0.25 part of wetting agent, 0.15 ~ 0.25 part of levelling agent, thickener 5 ~ 7 parts, 1.5 ~ 2.5 parts of photoinitiator, 0.15 ~ 0.25 part of antifoaming agent, 0.4 ~ 1.0 part of dimethylethanolamine, 3 ~ 4 parts of water, aluminium paste 6 ~ 10 parts.
In a kind of scheme, the aluminium paste mainly includes the component of following mass parts:50 ~ 70 parts of Japan FZ-F-290, water 5 ~ 15 parts, 15 ~ 35 parts of propylene glycol methyl ether acetate, 2 ~ 10 parts of dispersant, 0.03 ~ 0.2 part of dimethylethanolamine.
In a kind of preferred embodiment, the aluminium paste mainly includes the component of following mass parts:Japan FZ-F-290 55 ~ 65 Part, 7.5 ~ 12.5 parts of water, 20 ~ 30 parts of propylene glycol methyl ether acetate, 4 ~ 8 parts of dispersant, 0.06 ~ 0.12 part of dimethylethanolamine.
In a kind of scheme, the dispersant can be selected from BYK190, BYK194, BYK184, TEGO 651, TEGO 656 or One or more of TEGO 685.
In a kind of preferred embodiment, the dispersant can be in BYK190, BYK194, TEGO 656 or TEGO 685 It is one or more of.
In a kind of more preferable scheme, the dispersant can selected from BYK190, BYK194 or TEGO 685 one kind or It is several.
In a kind of scheme, the wetting agent can be selected from BYK346, BYK377, TEGO Wet 270, TEGO Wet 245 Or one or more of TEGO Wet 280.
In a kind of preferred embodiment, the wetting agent can be selected from BYK346, BYK377, TEGO Wet 270 or TEGO Wet One or more of 280.
In a kind of more preferable scheme, the wetting agent can be selected from BYK346, TEGO Wet 270 or TEGO Wet 280 One or more of.
In a kind of scheme, the levelling agent can be selected from BYK333, BYK307, BYK345, TEGO Rad 2200N or One or more of TEGO Rad 2100N.
In a kind of preferred embodiment, the levelling agent can be selected from BYK333, BYK345, TEGO Rad 2200N or TEGO One or more of Rad 2100N.
In a kind of more preferable scheme, the levelling agent can be selected from BYK333 or TEGO Rad 2100N.
In a kind of scheme, the thickener can be selected from ten thousand magnificent chemistry Vesmody U300, ten thousand China chemistry Vesmody One or more of U902, UH 450, UH 752 or UH 420.
In a kind of preferred embodiment, the thickener can be selected from ten thousand magnificent chemistry Vesmody U300,450 UH, UH 752 or One or more of UH 420.
In a kind of more preferable scheme, the thickener can be selected from ten thousand magnificent chemistry Vesmody U300,450 UH or UH One or more of 420.
In a kind of scheme, the photoinitiator can be selected from 2,4,6- trimethylbenzoyl phosphinic acid ethyl esters, 2- hydroxyls -2- Methyl-1-phenyl-1- acetone, 1- hydroxycyclohexyl phenyl ketones, 2- hydroxy-2-methyls-1- [4- (2- hydroxyl-oxethyls) benzene Base] one or more of -1- acetone or bis- (2.4.6- trimethylbenzoyls) phosphine oxides of phenyl.
In a kind of preferred embodiment, the photoinitiator can be selected from 2,4,6- trimethylbenzoyl phosphinic acid ethyl esters, 2- hydroxyls Base -2- methyl-1s-phenyl -1- acetone, 1- hydroxycyclohexyl phenyl ketones or bis- (2.4.6- trimethylbenzoyls) oxygen of phenyl Change one or more of phosphine.
In a kind of more preferable scheme, the photoinitiator can be selected from 2,4,6- trimethylbenzoyl phosphinic acid ethyl esters or benzene Bis- (2.4.6- trimethylbenzoyls) phosphine oxides of base.
In a kind of scheme, the antifoaming agent can be selected from BYK024, BYK019, BYK088, TEGO Foamex 1488 or One or more of TEGO Foamex 1495.
In a kind of preferred embodiment, the antifoaming agent can be selected from BYK024, BYK019, TEGO Foamex 1488 or TEGO One or more of Foamex 1495.
In a kind of more preferable scheme, the antifoaming agent can be selected from BYK024, TEGO Foamex 1488 or TEGO One or more of Foamex 1495.
A kind of preparation method of aqueous light UV solidifications aluminium paint, it includes the following steps:
(1)Prepare aluminium paste:Japan FZ-F-290 is added in container a, set mixing speed as 600 ~ 800r/min, stir 5 ~ 10 min;Water, propylene glycol methyl ether acetate, dispersant and dimethylethanolamine are added, 5 ~ 15min of stirring is continued;
(2)Resin material mixes:Aqueous UV urethane acrylates are added in container b, setting speed is 600 ~ 800r/ Min stirs water, wetting agent, levelling agent and the dimethylethanolamine of addition formula ratio after 5 ~ 10 min, continues stirring 5 ~ 10 min;The thickener of photoinitiator, antifoaming agent and half formula ratio is added, raising rotating speed is 1400 ~ 1600r/min, continues to stir 10~20 min;
(3)Aluminium paste is mixed with resin:The rotating speed of container b is reduced to 400 ~ 600r/min, the aluminium paste that container a is prepared by with Side's amount is added in container b, after stirring 10 ~ 20 min, adds remaining thickener, continues 5 ~ 15min of stirring.
A kind of application method of aqueous light UV solidifications aluminium paint, it includes the following steps:
(1)Aluminium paint pre-processes:20 ~ 30 parts of deionized water dilutions are added in aluminium paint;
(2)Spraying:By ground alcohol wipe, oil stain and dust on ground are removed, spraying air pressure is 2.0 ~ 3.0kg/ cm2, spray gun is 12 ~ 15cm at a distance from coat side, according to requiring suitably to adjust film thickness;
(3)55 ~ 65 DEG C of baking, 8 ~ 15min;1500 ~ 2000mj/cm of ultraviolet curing energy2
Technical solution using the present invention, advantage are as follows:
Aluminium paint provided by the invention, the workpiece surface that can solve plating is rough, and gloss is low, poor adhesive force, not wear-resisting etc. Bad problem.
Aluminium paint provided by the invention, can be used in the application of household electrical appliances plastic part surface, and paint film has high glaze, height hard The characteristics of degree, high abrasion, and paint film adhesion is good, glossiness is high, and also the aluminium powder arrangement effect of indirect proof paint film is good.
Specific implementation mode
Cure aluminium paint and preparation method thereof to a kind of aqueous light UV of the present invention by following embodiment to make further Explanation, but these embodiments do not form any restrictions to the present invention.
The preparation method of aqueous light UV solidifications aluminium paint provided by the invention, it includes the following steps:
(1)Prepare aluminium paste:Japan FZ-F-290 is added in container a, set mixing speed as 600 ~ 800r/min, stir 5 ~ 10 min;Water, propylene glycol methyl ether acetate, dispersant and dimethylethanolamine are added, 5 ~ 15min of stirring is continued;
(2)Resin material mixes:Aqueous UV urethane acrylates are added in container b, setting speed is 600 ~ 800r/ Min stirs water, wetting agent, levelling agent and the dimethylethanolamine of addition formula ratio after 5 ~ 10 min, continues stirring 5 ~ 10 min;The thickener of photoinitiator, antifoaming agent and half formula ratio is added, raising rotating speed is 1400 ~ 1600r/min, continues to stir 10~20 min;
(3)Aluminium paste is mixed with resin:The rotating speed of container b is reduced to 400 ~ 600r/min, the aluminium paste that container a is prepared by with Side's amount is added in container b, after stirring 10 ~ 20 min, adds remaining thickener, continues 5 ~ 15min of stirring.
The application method of aqueous light UV solidifications aluminium paint provided by the invention, it includes the following steps:
(1)Aluminium paint pre-processes:20 ~ 30 parts of deionized water dilutions are added in aluminium paint;
(2)Spraying:By ground alcohol wipe, oil stain and dust on ground are removed, spraying air pressure is 2.0 ~ 3.0kg/ cm2, spray gun is 12 ~ 15cm at a distance from coat side, according to requiring suitably to adjust film thickness;
(3)55 ~ 65 DEG C of baking, 8 ~ 15min;1500 ~ 2000mj/cm of ultraviolet curing energy2
Embodiment 1
Aluminium paste includes following component and mass fraction:54 parts of Japan FZ-F-290,7.0 parts of water, propylene glycol methyl ether acetate 18 parts, 3 parts of dispersant, 0.05 part of dimethylethanolamine.
A kind of aqueous light UV solidifications aluminium paint, it includes following component and mass fraction:
Aqueous 7,655 68 parts of UV urethane acrylates UCECOAT;
Wetting agent(TEGO Wet 270)0.08 part;
Levelling agent(TEGO Rad 2100N)0.02 part;
Levelling agent(BYK333)0.05 part;
1.5 parts of water;
0.15 part of dimethylethanolamine;
Photoinitiator(2- hydroxy-2-methyl -1- phenyl -1- acetone)0.9 part;
Antifoaming agent(BYK088)0.09 part;
Thickener(Ten thousand China chemistry Vesmody U300)1.4 part;
Thickener(UH 450)1.4 part;
3 parts of aluminium paste.
The preparation method of this aluminium paint includes the following steps:
(1)Prepare aluminium paste:Japan FZ-F-290 is added in container a, sets mixing speed as 640 r/min, stirs 7 min; Water, propylene glycol methyl ether acetate, dispersant and dimethylethanolamine are added, continues to stir 12 min;
(2)Resin material mixes:Aqueous UV urethane acrylates are added in container b, setting speed is 660 r/min, Water, wetting agent, levelling agent and the dimethylethanolamine that formula ratio is added after 6 min are stirred, continues to stir 8 min;Light is added to draw Send out agent, antifoaming agent and half formula ratio thickener, raisings rotating speed be 1440 r/min, continue stirring 12 min;
(3)Aluminium paste is mixed with resin:The rotating speed of container b is reduced to 450 r/min, the aluminium paste that container a is prepared is by formula Amount is added in container b, after stirring 14 min, adds remaining thickener, continues to stir 9 min.
Embodiment 2
Aluminium paste includes following component and mass fraction:58 parts of Japan FZ-F-290,13 parts of water, propylene glycol methyl ether acetate 26.8 parts, 5.2 parts of dispersant, 0.08 part of dimethylethanolamine.
A kind of aqueous light UV solidifications aluminium paint, it includes following component and mass fraction:
Aqueous 7,655 74 parts of UV urethane acrylates UCECOAT;
Wetting agent(BYK346)0.14 part;
Levelling agent(TEGO Rad 2100N)0.16 part;
2.8 parts of water;
0.25 part of dimethylethanolamine;
Photoinitiator(2- hydroxy-2-methyl -1- phenyl -1- acetone)1.8 part;
Photoinitiator(2,4,6- trimethylbenzoyl phosphinic acid ethyl esters)0.8 part;
Antifoaming agent(BYK088)0.13 part;
Antifoaming agent(BYK024)0.08 part;
Thickener(U450)2.1 part;
Thickener(UH 420)2.1 part;
10 parts of aluminium paste.
The preparation method of this aluminium paint includes the following steps:
(1)Prepare aluminium paste:Japan FZ-F-290 is added in container a, sets mixing speed as 740 r/min, stirs 8 min; Water, propylene glycol methyl ether acetate, dispersant and dimethylethanolamine are added, continues to stir 8 min;
(2)Resin material mixes:Aqueous UV urethane acrylates are added in container b, setting speed is 760 r/min, Water, wetting agent, levelling agent and the dimethylethanolamine that formula ratio is added after 7 min are stirred, continues to stir 9 min;Light is added to draw Send out agent, antifoaming agent and half formula ratio thickener, raisings rotating speed be 1540 r/min, continue stirring 14 min;
(3)Aluminium paste is mixed with resin:The rotating speed of container b is reduced to 480 r/min, the aluminium paste that container a is prepared is by formula Amount is added in container b, after stirring 7 min, adds remaining thickener, continues to stir 6 min.
Embodiment 3
Aluminium paste includes following component and mass fraction:60 parts of Japan FZ-F-290,10 parts of water, propylene glycol methyl ether acetate 23.9 parts, 6.0 parts of dispersant, 0.1 part of dimethylethanolamine.
A kind of aqueous light UV solidifications aluminium paint, it includes following component and mass fraction:
Aqueous 7,655 80 parts of UV urethane acrylates UCECOAT;
Wetting agent(BYK346)0.2 part;
Levelling agent(TEGO Rad 2100N)0.2 part;
3.3 parts of water;
0.5 part of dimethylethanolamine;
Photoinitiator(2,4,6- trimethylbenzoyl phosphinic acid ethyl esters)2.0 part;
Antifoaming agent(BYK024)0.2 part;
Thickener(Ten thousand China chemistry Vesmody U300)1.5 part;
Thickener(UH 450)1.5 part;
8 parts of aluminium paste.
The preparation method of this aluminium paint includes the following steps:
(1)Prepare aluminium paste:Japan FZ-F-290 is added in container a, sets mixing speed as 700 r/min, stirs 8 min; Water, propylene glycol methyl ether acetate, dispersant and dimethylethanolamine are added, continues to stir 6 min;
(2)Resin material mixes:Aqueous UV urethane acrylates are added in container b, setting speed is 720 r/min, Water, wetting agent, levelling agent and the dimethylethanolamine that formula ratio is added after 8 min are stirred, continues to stir 7 min;Light is added to draw Send out agent, antifoaming agent and half formula ratio thickener, raisings rotating speed be 1560 r/min, continue stirring 12 min;
(3)Aluminium paste is mixed with resin:The rotating speed of container b is reduced to 500 r/min, the aluminium paste that container a is prepared is by formula Amount is added in container b, after stirring 6 min, adds remaining thickener, continues to stir 8 min.
The application method of aqueous light UV solidifications aluminium paint provided by the invention, it includes the following steps:
(1)Aluminium paint pre-processes:20 ~ 30 parts of deionized water dilutions are added in aluminium paint;
(2)Spraying:By ground alcohol wipe, oil stain and dust on ground are removed, spraying air pressure is 2.0 ~ 3.0kg/ cm2, spray gun is 12 ~ 15cm at a distance from coat side, according to requiring suitably to adjust film thickness;
(3)55 ~ 65 DEG C of baking, 8 ~ 15min;1500 ~ 2000mj/cm of ultraviolet curing energy2
Comparative example 1
Aluminium paste includes following component and mass fraction:54 parts of Japan FZ-F-290,7.0 parts of water, propylene glycol methyl ether acetate 18 parts, 3 parts of dispersant, 0.05 part of dimethylethanolamine.
A kind of aqueous light UV solidifications aluminium paint, it includes following component and mass fraction:
Aqueous 7,655 68 parts of UV urethane acrylates UCECOAT;
Levelling agent(TEGO Rad 2100N)0.02 part;
Levelling agent(BYK333)0.05 part;
1.5 parts of water;
0.15 part of dimethylethanolamine;
Photoinitiator(2- hydroxy-2-methyl -1- phenyl -1- acetone)0.9 part;
Antifoaming agent(BYK088)0.09 part;
Thickener(Ten thousand China chemistry Vesmody U300)1.4 part;
Thickener(UH 450)1.4 part;
3 parts of aluminium paste.
The preparation method of this aluminium paint is with reference to embodiment 1.
Comparative example 2
Aluminium paste includes following component and mass fraction:58 parts of Japan FZ-F-290,13 parts of water, propylene glycol methyl ether acetate 26.8 parts, 5.2 parts of dispersant, 0.08 part of dimethylethanolamine.
A kind of aqueous light UV solidifications aluminium paint, it includes following component and mass fraction:
Aqueous 7,655 74 parts of UV urethane acrylates UCECOAT;
Wetting agent(BYK346)0.14 part;
Levelling agent(TEGO Rad 2100N)0.16 part;
2.8 parts of water;
Photoinitiator(2- hydroxy-2-methyl -1- phenyl -1- acetone)1.8 part;
Photoinitiator(2,4,6- trimethylbenzoyl phosphinic acid ethyl esters)0.8 part;
Antifoaming agent(BYK088)0.13 part;
Antifoaming agent(BYK024)0.08 part;
Thickener(U450)2.1 part;
Thickener(UH 420)2.1 part;
10 parts of aluminium paste.
The preparation method of this aluminium paint is with reference to embodiment 2.
Comparative example 3
Aluminium paste includes following component and mass fraction:60 parts of Japan FZ-F-290,10 parts of water, propylene glycol methyl ether acetate 23.9 parts, 6.0 parts of dispersant, 0.1 part of dimethylethanolamine.
A kind of aqueous light UV solidifications aluminium paint, it includes following component and mass fraction:
Aqueous 7,655 80 parts of UV urethane acrylates UCECOAT;
Wetting agent(BYK346)0.2 part;
Levelling agent(TEGO Rad 2100N)0.2 part;
2.9 parts of water;
0.5 part of dimethylethanolamine;
Photoinitiator(2,4,6- trimethylbenzoyl phosphinic acid ethyl esters)2.0 part;
Antifoaming agent(BYK024)0.6 part;
Thickener(Ten thousand China chemistry Vesmody U300)1.5 part;
Thickener(UH 450)1.5 part;
8 parts of aluminium paste.
The preparation method of this aluminium paint is with reference to embodiment 3.
Embodiment 4
The aluminium paint performance test of the present invention is as follows:
The performance of 1 aluminium paint of table
Sample Hardness Adhesive force Film RCA Glossiness(Degree) Resistance to hand perspiration test Bin stability
Embodiment 1 2H 5B 410 92 It is unchanged It is unchanged
Embodiment 2 2H 5B 480 96 It is unchanged It is unchanged
Embodiment 3 2H 5B 460 98 It is unchanged It is unchanged
Comparative example 1 H 3B 310 73 There is paint There is paint
Comparative example 2 H 3B 320 76 There is paint There is paint
Comparative example 3 H 3B 360 78 There is paint There is paint
The test method of the present invention is as follows:
Pencil hardness:GB/T 6739-2006.
Adhesive force:3M adhesive tapes, the test of hundred lattice, GB/T 5210-2006.
Bin stability:60 DEG C, relative humidity 95%, seven days.
Film RCA:Wearability, load 175g.
Glossiness:ASTM D523-2014, single angle measurement.
Hand perspiration is tested:PH4.7 ~ pH10.2, room temperature 24 hours.
Although above having used general explanation, specific implementation mode and experiment, the present invention is made to retouch in detail It states, but on the basis of the present invention, it can be made some modifications or improvements, this is apparent to those skilled in the art 's.Therefore, these modifications or improvements without departing from theon the basis of the spirit of the present invention, belong to claimed Range.

Claims (10)

1. a kind of aqueous light UV cures aluminium paint, which is characterized in that mainly the component including following mass parts is made for it:It is aqueous 7,655 65 ~ 95 parts of UV urethane acrylates UCECOAT, 0.05 ~ 0.5 part of wetting agent, 0.05 ~ 0.5 part of levelling agent, thickening 2 ~ 10 parts of agent, 0.5 ~ 3.5 part of photoinitiator, 0.05 ~ 0.5 part of antifoaming agent, 0.1 ~ 3.0 part of dimethylethanolamine, 1 ~ 6 part of water, 2 ~ 14 parts of aluminium paste.
2. aqueous light UV according to claim 1 cures aluminium paint, which is characterized in that it includes mainly following mass parts Component be made:Aqueous 7,655 70 ~ 90 parts of UV urethane acrylates UCECOAT, 0.1 ~ 0.3 part of wetting agent, levelling agent 0.1 ~ 0.3 part, 3 ~ 9 parts of thickener, 1.0 ~ 3.0 parts of photoinitiator, 0.1 ~ 0.3 part of antifoaming agent, dimethylethanolamine 0.2 ~ 2.5 Part, 2 ~ 5 parts of water, 4 ~ 12 parts of aluminium paste.
3. aqueous light UV according to claim 1 cures aluminium paint, which is characterized in that it includes mainly following mass parts Component be made:Aqueous 7,655 75 ~ 85 parts of UV urethane acrylates UCECOAT, 0.15 ~ 0.25 part of wetting agent, levelling 0.15 ~ 0.25 part of agent, 5 ~ 7 parts of thickener, 1.5 ~ 2.5 parts of photoinitiator, 0.15 ~ 0.25 part of antifoaming agent, dimethylethanolamine 0.4 ~ 1.0 part, 3 ~ 4 parts of water, 6 ~ 10 parts of aluminium paste.
4. aqueous light UV according to claim 1,2 or 3 cures aluminium paint, which is characterized in that the aluminium paste mainly wraps Include the component of following mass parts:50 ~ 70 parts of Japan FZ-F-290,5 ~ 15 parts of water, 15 ~ 35 parts of propylene glycol methyl ether acetate, point 2 ~ 10 parts of powder, 0.03 ~ 0.2 part of dimethylethanolamine.
5. aqueous light UV according to claim 4 cures aluminium paint, which is characterized in that the aluminium paste includes mainly following The component of mass parts:55 ~ 65 parts of Japan FZ-F-290,7.5 ~ 12.5 parts of water, 20 ~ 30 parts of propylene glycol methyl ether acetate, dispersion 4 ~ 8 parts of agent, 0.06 ~ 0.12 part of dimethylethanolamine.
6. aqueous light UV according to claim 4 cures aluminium paint, which is characterized in that the dispersant can be selected from One or more of BYK190, BYK194, BYK184, TEGO 651, TEGO 656 or TEGO 685.
7. aqueous light UV according to claim 1 cures aluminium paint, which is characterized in that the wetting agent can be selected from One or more of BYK346, BYK377, TEGO Wet 270, TEGO Wet 245 or TEGO Wet 280;The levelling Agent can be selected from one or more of BYK333, BYK307, BYK345, TEGO Rad 2200N or TEGO Rad 2100N.
8. aqueous light UV according to claim 1 cures aluminium paint, which is characterized in that the thickener can be selected from ten thousand One or more of magnificent chemistry Vesmody U300, ten thousand magnificent chemistry Vesmody U902,450 UH, UH 752 or UH 420; The photoinitiator can be selected from 2,4,6- trimethylbenzoyls phosphinic acid ethyl ester, 2- hydroxy-2-methyl -1- phenyl -1- acetone, 1- hydroxycyclohexyl phenyl ketones, 2- hydroxy-2-methyls -1- [4- (2- hydroxyl-oxethyls) phenyl] -1- acetone or phenyl are double One or more of (2.4.6- trimethylbenzoyls) phosphine oxide;The antifoaming agent can be selected from BYK024, BYK019, One or more of BYK088, TEGO Foamex 1488 or TEGO Foamex 1495.
9. a kind of preparation method of aqueous light UV solidifications aluminium paint as described in claim 1, which is characterized in that it include with Lower step:
(1)Prepare aluminium paste:Japan FZ-F-290 is added in container a, set mixing speed as 600 ~ 800r/min, stir 5 ~ 10 min;Water, propylene glycol methyl ether acetate, dispersant and dimethylethanolamine are added, 5 ~ 15min of stirring is continued;
(2)Resin material mixes:Aqueous UV urethane acrylates are added in container b, setting speed is 600 ~ 800r/ Min stirs water, wetting agent, levelling agent and the dimethylethanolamine of addition formula ratio after 5 ~ 10 min, continues stirring 5 ~ 10 min;The thickener of photoinitiator, antifoaming agent and half formula ratio is added, raising rotating speed is 1400 ~ 1600r/min, continues to stir 10~20 min;
(3)Aluminium paste is mixed with resin:The rotating speed of container b is reduced to 400 ~ 600r/min, the aluminium paste that container a is prepared by with Side's amount is added in container b, after stirring 10 ~ 20 min, adds remaining thickener, continues 5 ~ 15min of stirring.
10. a kind of application method of aqueous light UV solidifications aluminium paint as described in claim 1, which is characterized in that it includes Following steps:
(1)Aluminium paint pre-processes:20 ~ 30 parts of deionized water dilutions are added in aluminium paint;
(2)Spraying:By ground alcohol wipe, oil stain and dust on ground are removed, spraying air pressure is 2.0 ~ 3.0kg/ cm2, Spray gun is 12 ~ 15cm at a distance from coat side, according to requiring suitably to adjust film thickness;
(3)55 ~ 65 DEG C of baking, 8 ~ 15min;1500 ~ 2000mj/cm of ultraviolet curing energy2
CN201711452847.3A 2017-12-28 2017-12-28 A kind of aqueous light UV solidification aluminium paint, preparation method and its application method Withdrawn CN108329824A (en)