CN108329503A - A kind of antistatic ebonite set - Google Patents
A kind of antistatic ebonite set Download PDFInfo
- Publication number
- CN108329503A CN108329503A CN201810134871.0A CN201810134871A CN108329503A CN 108329503 A CN108329503 A CN 108329503A CN 201810134871 A CN201810134871 A CN 201810134871A CN 108329503 A CN108329503 A CN 108329503A
- Authority
- CN
- China
- Prior art keywords
- titanium dioxide
- ebonite
- antistatic
- coating
- ebonite set
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to cutting ferrule fields, specifically disclose a kind of antistatic ebonite set, and the ebonite set is made of rubber material, and the surface of rubber material is equipped with titanium dioxide coating, and anti-static coating is coated on the surface of titanium dioxide coating.The ebonite set is by being kneaded and vulcanizing after mixing raw material, then injection molding, prepares titanium dioxide coating by magnetron sputtering method in ebonite set outer surface, finally coats anti-static coating on the surface of titanium dioxide coating.A kind of antistatic ebonite set of the present invention, which solves the problems, such as that ebonite set easy tos produce electrostatic in the prior art, is easy aging, to be influenced to use, to improve the coefficient safe to use and service life of ebonite set.
Description
Technical field
The present invention relates to cutting ferrule fields, specifically disclose a kind of antistatic ebonite set.
Background technology
Ebonite set is commonly used in installation file, card and other items.With the development of intelligent cards, card is as modern society
In essential authentication article, it will usually carry and frequently use, and mounted in ebonite set in card, can because
Electrostatic is generated with objects frictions such as clothings, contacting card to user brings certain trouble or even larger electrostatic that can make card
Piece damages.On the other hand, ebonite set of rubber material due to being made, and regular contacted with air can be easy aging, after aging
Ebonite set can make to be difficult to recognize mounted in internal card or file and pollute file or card, influence because character changes
It uses.
Invention content
In order to overcome shortcoming and defect existing in the prior art, the purpose of the present invention is to provide a kind of antistatic ebonites
Set, solving the problems, such as that the easy ebonite set of ebonite is easy to produce static electricity in the prior art, aging occurs influences to use.
To achieve the above object, the present invention uses following scheme.
A kind of antistatic ebonite set, is made of rubber material, it is characterised in that:The surface of rubber material is equipped with titanium dioxide
Titanium coating, titanium dioxide coating are equipped with anti-static coating.Titanium dioxide coating can improve the anti-aging of rubber material surface
Intensity, moreover it is possible to prevent the rubber that ebonite covers from being contacted with air, prevent the extraneous factor for causing ageing of rubber.
On the one hand, rubber material is by silicon rubber, chlorinated paraffin, titanium dioxide, methyl phenyl silicone oil, tert butyl phenolic resin
Composition.
On the other hand, the anti-static coating is by hexamethylene diisocyanate, acrylic styrene copolymer, second
Oxygroup cocoalkyl amines, surfactant composition.
Further, anti-static coating further includes cumarin.Chlorinated paraffin is added in rubber material has fluorescence
Effect, can shine when night, convenient for find, prevent ebonite set lose.And cumarin is as a kind of organic
After ebonite set is added in luminescent material, its luminous intensity at night is further improved, ebonite is made to be sleeved on the situation for not having light to lack light
Under it is more obvious.
In one embodiment, card set can be by preparation method, by silicon rubber, chlorinated paraffin, titanium dioxide, methylbenzene
It is kneaded and vulcanizes after base silicone oil, tert butyl phenolic resin mixing, then injection molding is ebonite set, is passed through in ebonite set outer surface
Magnetron sputtering method prepares titanium dioxide coating, finally coats anti-static coating on the surface of titanium dioxide coating.
Beneficial effects of the present invention:Efficiently solve the problems, such as that ebonite covers easy to produce static electricity, easy to aging in the prior art, from
And improve the coefficient safe to use and service life of ebonite set.
Specific implementation mode
For the ease of the understanding of those skilled in the art, with reference to embodiment, the present invention is further illustrated, real
The content that the mode of applying refers to not is limitation of the invention.
Ebonite set can be prepared by the following method, by silicon rubber, chlorinated paraffin, titanium dioxide, methyl phenyl silicone oil, uncle
Butyl phenolic resin is according to 12:1:3:1:After 0.5 mass ratio mixing, it is added in kneading machine and is kneaded, be then added to vulcanization
Vulcanize in machine, injection molding is ebonite set in preset die later;Ebonite is sleeved in magnetron sputtering coater, with titanium dioxide
Titanium is target, and TiO 2 coating film layer is formed on ebonite set surface;Then by hexamethylene diisocyanate, acrylate-benzene
Ethylene copolymer, ethyoxyl cocoalkyl amines, surfactant are according to 3:1:6:0.5:0.2 mass ratio mixing after, be added with
Mixture quality ratio is 1:1 ethyl alcohol and the adhesive of mixture gross mass 1/10, coating materials are formed after stirring
Material forms anti-static coating later by being screen printed onto coating slurry on the superficial layer of card set after dry.
The above content is only presently preferred embodiments of the present invention, for those of ordinary skill in the art, according to the present invention
Thought, there will be changes in the specific implementation manner and application range, and the content of the present specification should not be construed as to the present invention
Limitation.
Claims (5)
1. a kind of antistatic ebonite set, is made of rubber material, it is characterised in that:The surface of rubber material is equipped with titanium dioxide
Coating, titanium dioxide coating are equipped with anti-static coating.
2. antistatic ebonite set according to claim 1, it is characterised in that:The rubber material is by silicon rubber, chlorination stone
Wax, titanium dioxide, methyl phenyl silicone oil, tert butyl phenolic resin composition.
3. antistatic ebonite set according to claim 1, it is characterised in that:The anti-static coating is different by hexa-methylene two
Cyanate, acrylic styrene copolymer, ethyoxyl cocoalkyl amines, surfactant composition.
4. antistatic ebonite set according to claim 1, it is characterised in that:Anti-static coating further includes cumarin.
5. a kind of preparation method of any antistatic ebonite sets of claim 1-4, it is characterised in that:By silicon rubber, chlorine
It is kneaded and vulcanizes after fossil waxes, titanium dioxide, methyl phenyl silicone oil, tert butyl phenolic resin mixing, then injection molding is hard
Gum cover prepares titanium dioxide coating, finally on the surface of titanium dioxide coating in ebonite set outer surface by magnetron sputtering method
Coat anti-static coating.