KR101818135B1 - Antifouling coating composition - Google Patents
Antifouling coating composition Download PDFInfo
- Publication number
- KR101818135B1 KR101818135B1 KR1020170034606A KR20170034606A KR101818135B1 KR 101818135 B1 KR101818135 B1 KR 101818135B1 KR 1020170034606 A KR1020170034606 A KR 1020170034606A KR 20170034606 A KR20170034606 A KR 20170034606A KR 101818135 B1 KR101818135 B1 KR 101818135B1
- Authority
- KR
- South Korea
- Prior art keywords
- coating composition
- minutes
- polyalkoxysiloxane
- mixture
- crosslinking agent
- Prior art date
Abstract
Description
본 발명은 표면코팅으로 표면에 오염된 오염물질을 용이하게 제거할 수 있는 비점착성 코팅제 조성물에 관한 것으로, 보다 상세하게는 벽지 또는 벽면의 표면이 유성펜이나 수성펜, 크레파스, 볼펜, 락카 등에 의한 낙서로 오염되는 경우 낙서물질이 벽지나 벽면에 침투되지 않도록 하여 젖은 헝겊으로 닦아주면 깨끗하게 낙서를 제거할 수 있도록 하고, 벽지나 벽면에 곰팡이가 발생되지 않도록 하는 코팅제 조성물에 관한 것이다. The present invention relates to a non-tacky coating composition capable of easily removing contaminants contaminating a surface by a surface coating, and more particularly, to a non-tacky coating composition capable of easily removing contaminants contaminated on a surface by a surface coating, The present invention relates to a coating composition for preventing graffiti from being scratched when wiped with a damp cloth so as to prevent graffiti material from penetrating into wall paper or a wall surface in case of contamination, and to prevent molds from forming on wall paper or wall surface.
도심의 거리를 보면 배전함, 전신주, 가로등, 각종 홍보물 간판, 이정표, 버스정류장에 불법 광고 부착물 등이 붙어있어 거리 환경미화에 악영향을 끼치고 있는 것을 쉽게 발견할 수 있다. 이러한 반복적인 불법부착물 제거과정에서 광고 부착물을 막기 위한 대상(피도체)이 외부 물리적, 화학적인 요인에 의해 직접적으로 노출되어 피도체의 변형 및 손상을 가져올 수가 있다. If you look at the streets of the city center, you can easily find out that it has adverse effects on street environment beautification because it is attached with distribution boxes, telephone poles, street lights, various promotional signs, milestones, and illegal advertising attachments in bus stops. In the process of eliminating the repeated illegal adhering materials, objects (objects to be adhered) for blocking ad attachments may be directly exposed to external physical and chemical factors, resulting in deformation and damage of the objects.
또한, 불법부착물 이외에 펜 등을 이용하여 낙서를 하게 되면, 미관상 악영향을 끼칠 뿐만 아니라, 피착제가 오염되면서 번지게 되어 2차적 오염물이 되는 문제점이 있다.In addition, if graffiti is performed using a pen or the like in addition to the illegal adherence, not only adverse effects on the appearance are caused but also the adherend becomes contaminated and becomes a secondary contaminant.
이러한 문제점을 해결하기 위해 피도체에 부착 방지용 코팅액 조성물을 직접 코팅하는 방식이 선호되고 있다. In order to solve such a problem, a method of directly coating a coating liquid composition for preventing adhesion to a conductor is preferred.
이와 같은 방식으로 폴리에틸렌계 수지나, 실리콘 오일, 불소계 수지, 계면 활성제, 실란계 유기결합제, 도료용 첨가제 등을 사용한 벽보물 부착 방지용 코팅제 조성물이 개시되어 있는데, 이러한 기술들은 시간의 경과에 따른 광변색이나 미세먼지와 분진에 대한 방지기능이 떨어지는 문제점을 갖고 있을 뿐만 아니라 자체 세정기능이 없는 문제점이 있다. A coating composition for preventing adhesion of wall treasures using polyethylene resin, silicone oil, fluorine resin, surfactant, silane-based organic binder, paint additive and the like is disclosed in this manner. These techniques are applied to photochromic And has a problem that the function to prevent fine dust and dust is inferior, but also has a problem that it has no self-cleaning function.
또한, 상기 코팅제 조성물을 제조하여 스티커 방지제로 사용하였으나 이 코팅제도 오염성은 개선되었지만 오일류가 표면층으로 도출되어 끈적임이 증가되어 스티커가 달라붙는 문제점이 있다.In addition, although the coating composition was prepared and used as an anti-sticking agent, the coating agent was also improved in staining property, but the oil flow was led to the surface layer, and the stickiness was increased to stick the sticker.
본 발명은 이와 같은 종래의 문제점을 해결하기 위한 것으로서, 각종 오염물질에 의한 표면 오염 방지를 위해 상기 벽면의 표면을 코팅하는 경우, 상기 코팅을 위해 폴리 알콕시 실록산 수지와 가교제, 에틸 실리케이트, 실리콘 폴리머, 촉매제, 용제를 일정 비율로 섞어 제조됨으로써, 내마모성, 내오염성, 세척용이성, 자외서차단, 표면경도 및 비점착성이 우수하고, 내열성이 우수한 코팅제 조성물을 제공하는 것을 목적으로 한다. SUMMARY OF THE INVENTION The present invention has been made in view of the above problems, and it is an object of the present invention to provide a method for coating a surface of a wall surface of a polyolefin- A coating agent composition having excellent abrasion resistance, stain resistance, ease of washing, external blocking, surface hardness and non-stickiness, and excellent heat resistance by being produced by mixing a catalyst and a solvent in a certain ratio.
그러나 본 발명의 목적은 상기에 언급된 목적으로 제한되지 않으며, 언급되지 않은 또 다른 목적은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다. However, the object of the present invention is not limited to the above-mentioned object, and another object which is not mentioned can be understood by those skilled in the art from the following description.
상기 목적을 달성하기 위하여, 본 발명은 각종 오염물질에 의한 표면 오염 방지를 위해 제조되는 코팅제 조성물에 있어서, 상기 코팅제 조성물은 폴리 알콕시 실록산 수지와 가교제, 에틸 실리케이트, 실리콘 폴리머, 촉매제, 용제가 함유되어 제조된다.In order to achieve the above object, the present invention provides a coating composition for preventing surface contamination by various contaminants, wherein the coating composition contains a polyalkoxysiloxane resin, a crosslinking agent, an ethyl silicate, a silicone polymer, a catalyst, and a solvent .
이때, 상기 코팅제 조성물은 상기 폴리 알콜시 실록산 수지 100 중량부에 대해, 가교제 0.1 내지 5 중량부, 에틸 실리케이트 1 내지 10 중량부, 실리콘 폴리머 5 내지 20 중량부, 촉매제 1 내지 25 중량부, 용제 5 내지 20 중량부가 함유되어 제조된다.The coating composition may contain 0.1 to 5 parts by weight of a crosslinking agent, 1 to 10 parts by weight of ethyl silicate, 5 to 20 parts by weight of a silicone polymer, 1 to 25 parts by weight of a catalyst, 5 parts by weight of a
상기 가교제는 부착력 증진성능을 갖는 것으로 비닐실란, 메틸트리메톡시실란, 알콕시실란 중 하나이고, 상기 실리콘 폴리머는 비점착성 및 오염방지 성능을 갖는 상온습기경화형 실리콘 수지이며, 상기 촉매제는 백금, 지르코늄, 티타네이트, 틴 중 하나이고, 상기 용제는 작업성 및 점도조절에 효과를 갖는 것으로, 카보네이트 종류나 알코올 종류 중 하나가 사용된다. The crosslinking agent is one of vinylsilane, methyltrimethoxysilane and alkoxysilane which has adhesion promoting ability, and the silicone polymer is a room temperature moisture curing type silicone resin having non-tackiness and stain-proofing capability, and the catalyst is platinum, zirconium, Titanate, and tin, and the solvent has an effect on workability and viscosity control, and one of carbonate type and alcohol type is used.
상기 코팅제 조성물의 제조방법은 상기 폴리 알콕시 실록산에 상기 가교제를 첨가하여 200 - 400rpm으로 상온에서 30분 - 120분간 혼합하여 교반하는 단계(S100), 상기 교반된 상기 폴리 알콕시 실록산, 상기 가교제에 에틸실리케이트를 첨가하여 200 - 400rpm으로 상온에서 30분 - 120분간 혼합하여 교반하는 단계(S110), 상기 교반된 상기 폴리 알콕시 실록산, 상기 가교제, 상기 에틸실리케이트에 실리콘 폴리머를 첨가하여 200 - 400rpm으로 상온에서 30분 - 120분간 혼합하여 교반하는 단계(S120), 상기 교반된 상기 폴리 알콕시 실록산, 상기 가교제, 상기 에틸실리케이트, 실리콘 폴리머에 촉매제를 첨가하여 200 - 400rpm으로 상온에서 30분 - 120분간 혼합하여 교반하는 단계(S130), 상기 교반된 상기 교반된 상기 폴리 알콕시 실록산, 상기 가교제, 상기 에틸실리케이트, 실리콘 폴리머, 상기 촉매제에 카보네이트 또는 알코올을 첨가하여 200 - 400rpm으로 상온에서 25분 - 35분간 혼합하여 교반하는 단계(S140)를 거쳐 저온용 코팅제 조성물이 제조된다.The coating composition may be prepared by adding the cross-linking agent to the polyalkoxysiloxane, stirring the mixture at a temperature of 200 to 400 rpm for 30 to 120 minutes at room temperature (S100), adding the stirred polyalkoxysiloxane, (S110). The silicone polymer is added to the agitated polyalkoxysiloxane, the crosslinking agent, and the ethyl silicate, and the mixture is stirred at 200 - 400 rpm at room temperature for 30 minutes at room temperature. (S120). The catalyst is added to the stirred polyalkoxysiloxane, the crosslinking agent, the ethyl silicate, and the silicone polymer, and the mixture is stirred at 200 - 400 rpm at room temperature for 30 minutes to 120 minutes and stirred. (S130), stirring the stirred polyalkoxysiloxane, the crosslinking agent, the ethyl silicate, the silicone Polymer or a catalyst or a carbonate or an alcohol is added to the catalyst, and the mixture is stirred at 200 to 400 rpm at room temperature for 25 minutes to 35 minutes and stirred (S140).
또한, 상기 저온용 코팅제 조성물의 온도를 섭씨 20℃ 내지 40℃로 유지하는 단계를 거쳐 고온용 코팅제 조성물이 제조된다. Also, the temperature of the low temperature coating composition is maintained at 20 to 40 캜 to prepare a high temperature coating composition.
본 발명의 특징 및 이점들은 첨부도면에 의거한 다음의 상세한 설명으로 더욱 명백해질 것이다.The features and advantages of the present invention will become more apparent from the following detailed description based on the accompanying drawings.
이에 앞서 본 명세서 및 청구범위에 사용된 용어나 단어는 통상적이고 사전적인 의미로 해석되어서는 아니 되며, 발명자가 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합되는 의미와 개념으로 해석되어야 한다.Prior to that, terms and words used in the present specification and claims should not be construed in a conventional and dictionary sense, and the inventor may properly define the concept of the term in order to best explain its invention It should be construed as meaning and concept consistent with the technical idea of the present invention.
상기와 같이 구성된 본 발명은 상기 코팅제 조성물이 건출물의 실내 벽면이나 벽지 또는 코팅 가능한 모든 기재 등에 도포되는 경우, 낙서의 도구로 사용된 유성펜이나 수성펜, 볼펜, 잉크나 크레파스 등의 물질이 벽지나 벽면에 오염되지 않고, 내장재의 내부로 침투되지 않아 표면에만 묻어 있는 상태가 되기 때문에 젖은 헝겊으로 가볍에 닦아주어도 낙서가 깔끔하게 지워진다는 효과가 있다. When the coating composition is applied to the interior wall of a dried article, wallpaper, or any substrate that can be coated, a material such as a stationary pen, a water pen, a ballpoint pen, an ink or a c Since it is not contaminated and does not penetrate into the interior of the interior, it is only on the surface. Therefore, even if it is wiped with a wet cloth, graffiti is cleanly removed.
또한, 상기 코팅제 조성물에 비점착성 성능을 갖는 상온습기경화형 실리콘 수지가 혼합되어 상기 벽면이나 벽지에 끈적임을 갖는 테이프나, 스티커 등이 부착되지 않아 상기 테이프나 스티커로 인한 끈적임이 남지 않아 깔끔한 상태를 유지하는 것이 가능한 장점이 있다. Also, since the silicone resin of room temperature and moisture hardening type having a non-sticking property is mixed with the coating composition, a tape or sticker having stickiness to the wall surface or wallpaper is not adhered, and the stickiness due to the tape or sticker is not left, There is an advantage that it is possible to do.
도 1은 본 발명의 실시예에 따른 저온용 코팅제 조성물의 제조방법을 나타낸 순서도이다.
도 2는 본 발명의 실시예에 따른 고온용 코팅제 조성물의 제조방법을 나타낸 순서도이다.
도 3은 본 발명의 실시예에 따른 코팅제 조성물의 실험결과가 나타난 표이다.
도 4는 본 발명의 실시예에 따른 코팅제 조성물의 실험결과가 나타난 표이다.
도 5는 본 발명의 실시예에 따른 코팅제 조성물의 실험결과가 나타난 표이다.
도 6은 본 발명의 실시예에 따른 코팅제 조성물의 실험결과가 나타난 표이다.1 is a flowchart illustrating a method of manufacturing a coating composition for low temperature according to an embodiment of the present invention.
2 shows a process for producing a high temperature coating composition according to an embodiment of the present invention It is a flowchart.
3 is a table showing experimental results of a coating composition according to an embodiment of the present invention.
4 is a table showing experimental results of a coating composition according to an embodiment of the present invention.
5 is a table showing experimental results of a coating composition according to an embodiment of the present invention.
6 is a table showing experimental results of a coating composition according to an embodiment of the present invention.
이하, 본 발명의 바람직한 실시예를 첨부된 도면을 참조하여 설명하기로 한다. 이 과정에서 도면에 도시된 선들의 두께나 구성요소의 크기 등은 설명의 명료성과 편의상 과장되게 도시되어 있을 수 있다.Hereinafter, preferred embodiments of the present invention will be described with reference to the accompanying drawings. In this process, the thicknesses of the lines and the sizes of the components shown in the drawings may be exaggerated for clarity and convenience of explanation.
또한, 후술되는 용어들은 본 발명에서의 기능을 고려하여 정의된 용어들로서 이는 사용자, 운용자의 의도 또는 관례에 따라 달라질 수 있다. 그러므로 이러한 용어들에 대한 정의는 본 명세서 전반에 걸친 내용을 토대로 하여 내려져야 할 것이다.In addition, the terms described below are defined in consideration of the functions of the present invention, which may vary depending on the intention or custom of the user, the operator. Therefore, definitions of these terms should be made based on the contents throughout this specification.
아울러, 아래의 실시예는 본 발명의 권리범위를 한정하는 것이 아니라 본 발명의 청구범위에 제시된 구성요소의 예시적인 사항에 불과하며, 본 발명의 명세서 전반에 걸친 기술사상에 포함되고 청구범위의 구성요소에서 균등물로서 치환 가능한 구성요소를 포함하는 실시예는 본 발명의 권리범위에 포함될 수 있다.In addition, the following embodiments are not intended to limit the scope of the present invention, but merely as exemplifications of the constituent elements set forth in the claims of the present invention, and are included in technical ideas throughout the specification of the present invention, Embodiments that include components replaceable as equivalents in the elements may be included within the scope of the present invention.
이하 첨부된 도면들을 참조하여 본 발명의 바람직한 실시예에 따른 코팅제 조성물에 대하여 상세하게 설명하지만, 본 발명이 하기 실시예에 의해 제한되거나 한정되는 것은 아니다. BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, a coating composition according to a preferred embodiment of the present invention will be described in detail with reference to the accompanying drawings, but the present invention is not limited or limited by the following examples.
도 1은 본 발명의 실시예에 따른 저온용 코팅제 조성물의 제조방법을 나타낸 순서도이고, 도 2는 본 발명의 실시예에 따른 고온용 코팅제 조성물의 제조방법을 나타낸 순서도이며, 도 3 내지 도 6은 본 발명의 실시예에 따른 코팅제 조성물의 실험결과 나타낸 표이다.FIG. 1 is a flow chart showing a method of manufacturing a coating composition for low temperature according to an embodiment of the present invention, FIG. 2 is a flowchart showing a method for manufacturing a coating composition for high temperature according to an embodiment of the present invention, 1 is a table showing experimental results of a coating composition according to an embodiment of the present invention.
도 1을 참조하면, 본 발명은 각종 오염물질에 의한 표면 오염 방지를 위해 제조되는 코팅제 조성물에 있어서, 상기 코팅제는 폴리 알콕시 실록산 수지와 가교제, 에틸 실리케이트, 실리콘 폴리머, 촉매제, 용제 중 하나 이상이 함유되어 제조된다.Referring to FIG. 1, the present invention provides a coating composition for preventing surface contamination by various pollutants, wherein the coating agent comprises at least one of a polyalkoxysiloxane resin and a crosslinking agent, an ethyl silicate, a silicone polymer, a catalyst, .
이때, 상기 코팅제는 상기 폴리 알콜시 실록산 수지 100 중량부에 대해, 가교제 0.1 내지 5 중량부, 에틸 실리케이트 1 내지 10 중량부, 실리콘 폴리머 5 내지 20 중량부, 촉매제 1 내지 25 중량부, 용제 5 내지 20 중량부가 함유되어 제조된다.The coating agent may contain 0.1 to 5 parts by weight of a crosslinking agent, 1 to 10 parts by weight of ethyl silicate, 5 to 20 parts by weight of a silicone polymer, 1 to 25 parts by weight of a catalyst, 5 to 5 parts by weight of a catalyst, 20 parts by weight.
상기 가교제는 부착력 증진효과를 갖는 것으로 비닐실란, 메틸트리메톡시실란, 알콕시실란 중 하나를 사용한다. The crosslinking agent has an adhesion-promoting effect, and one of vinylsilane, methyltrimethoxysilane, and alkoxysilane is used.
또한, 상기 실리콘 폴리머는 비점착성, 낙서방지 및 세척용이성 등의 성능 개선을 위해 알콜 촉매로 가수분해된 실리콘 축합물로써, 비점착성 및 오염방지 성능을 갖는 상온습기경화형 실리콘 수지이다.The silicone polymer is a silicon condensation product hydrolyzed with an alcohol catalyst to improve performance such as non-tackiness, graffiti prevention and ease of washing, and is a room temperature moisture curable silicone resin having non-tackiness and stain-proofing performance.
더불어, 상기 촉매제는 경화 촉진을 위한 것으로, 백금이나 지르코늄이나 티타네이트나 틴 중 하나로써, 상기 촉매제중 하나가 사용된다.In addition, the catalyst is used for accelerating curing, and one of the catalysts is used as one of platinum, zirconium and titanate natine.
상기 용제는 작업성 및 점도조절에 효과를 갖는 것으로, 카보네이트 종류나 알코올 종류 중 하나가 사용된다. The solvent has an effect on workability and viscosity control, and one of a carbonate type and an alcohol type is used.
이때, 상기 실리콘 폴리머의 첨가량의 투입 범위를 벗어나는 경우, 투명성과 접착서잉 떨어지거나 비점착성 성능이 결여되고, 상기 에틸실리케이트의 첨가량이 투입 범위를 벗어나는 경우에는 표면경도가 약해지거나, 경화시간이 길어진다.If the added amount of the silicone polymer is outside the range of application, the transparency and adhesive sealant deteriorate or the non-adhesive performance is lacked. If the addition amount of the ethyl silicate is out of the range of application, the surface hardness becomes weak or the curing time becomes long .
따라서, 상기 에틸실리케이트의 중량에 따라 상기 표면경도가 약해지거나 강해지고, 상기 실리콘 폴리머가 함유되는 중량에 따라 상기 비점착성의 강도가 약해지거나 강해진다.Therefore, the surface hardness becomes weaker or stronger depending on the weight of the ethyl silicate, and the non-adhesive strength becomes weaker or stronger depending on the weight of the silicone polymer contained therein.
상기 코팅제 조성물의 제조방법은 상기 폴리 알콕시 실록산에 상기 가교제를 첨가하여 200 - 400rpm으로 상온에서 30분 - 120분간 혼합하여 교반하는 단계(S100), 상기 교반된 상기 폴리 알콕시 실록산, 상기 가교제에 에틸실리케이트를 첨가하여 200 - 400rpm으로 상온에서 30분 - 120분간 혼합하여 교반하는 단계(S110), 상기 교반된 상기 폴리 알콕시 실록산, 상기 가교제, 상기 에틸실리케이트에 실리콘 폴리머를 첨가하여 200 - 400rpm으로 상온에서 30분 - 120분간 혼합하여 교반하는 단계(S120), 상기 교반된 상기 폴리 알콕시 실록산, 상기 가교제, 상기 에틸실리케이트, 실리콘 폴리머에 촉매제를 첨가하여 200 - 400rpm으로 상온에서 30분 - 120분간 혼합하여 교반하는 단계(S130), 상기 교반된 상기 교반된 상기 폴리 알콕시 실록산, 상기 가교제, 상기 에틸실리케이트, 실리콘 폴리머, 상기 촉매제에 카보네이트 또는 알코올을 첨가하여 200 - 400rpm으로 상온에서 25분 - 35분간 혼합하여 교반하는 단계(S140)를 거쳐 저온용 코팅제 조성물이 제조된다. The coating composition may be prepared by adding the cross-linking agent to the polyalkoxysiloxane, stirring the mixture at a temperature of 200 to 400 rpm for 30 to 120 minutes at room temperature (S100), adding the stirred polyalkoxysiloxane, (S110). The silicone polymer is added to the agitated polyalkoxysiloxane, the crosslinking agent, and the ethyl silicate, and the mixture is stirred at 200 - 400 rpm at room temperature for 30 minutes at room temperature. (S120). The catalyst is added to the stirred polyalkoxysiloxane, the crosslinking agent, the ethyl silicate, and the silicone polymer, and the mixture is stirred at 200 - 400 rpm at room temperature for 30 minutes to 120 minutes and stirred. (S130), stirring the stirred polyalkoxysiloxane, the crosslinking agent, the ethyl silicate, the silicone Polymer or a catalyst or a carbonate or an alcohol is added to the catalyst, and the mixture is stirred at 200 to 400 rpm at room temperature for 25 minutes to 35 minutes and stirred (S140).
이때, 상기 저온용 코팅제 조성물은 200℃내에서 사용 가능하다.At this time, the low temperature coating composition can be used at 200 ° C.
또한, 도 2를 참조하면, 상기 저온용 코팅제 조성물의 온도를 섭씨 20℃ 내지 40℃로 유지하는 단계(S200)를 거쳐 고온용 코팅제 조성물이 제조되는 것이 가능하다.Also, referring to FIG. 2, it is possible to prepare the coating composition for high temperature by maintaining the temperature of the coating composition for low temperature at 20 to 40 캜 (S200).
이때, 상기 온도를 유지하면서, ph농도를 6 내지 9로 유지해야한다.At this time, the pH should be maintained at 6 to 9 while maintaining the temperature.
또한, 상기 ph수치를 측정하여 상기 ph수치가 6 보다 낮으면 알칼리 성분을 첨가시키고, ph수치가 높으면 산성을 첨가시켜 ph수치를 범위 내에 존재하도록 조절한다.Further, the pH value is measured. When the pH value is lower than 6, an alkali component is added. When the pH value is high, acidity is added to adjust the pH value to be within the range.
또한, 상기 고온용 코팅제 조성물은 800℃까지 견딜 수 있어, 저온용 코팅제 조성물보다 내열성이 뛰어나다.In addition, the coating composition for high temperature can withstand up to 800 占 폚, which is superior in heat resistance to the coating composition for low temperature.
본 발명의 특징 및 이점들은 첨부도면에 의거한 다음의 상세한 설명으로 더욱 명백해질 것이다.The features and advantages of the present invention will become more apparent from the following detailed description based on the accompanying drawings.
이하에서는 실시예를 통하여 본 발명을 보다 상세히 설명한다.Hereinafter, the present invention will be described in more detail with reference to Examples.
이하의 실시예는 실시를 통하여 본 발명을 설명하고자 하는 것이지 이들로 본 발명을 한정하고자 하는 것은 아니다. The following examples are intended to illustrate the invention through practice and are not intended to limit the invention.
도 3 내지 도 6을 참조하여 본 발명의 실시예 1에 따른 코팅제 조성물을 사용해 한국화학융합시험연구원으로부터 한전표준규격(ES-9905-0015) 시험방법을 통해 실험된 시험결과를 설명한다.3 to 6, the test results of the coating composition according to Example 1 of the present invention and the results of the test conducted by the Korean Chemical Fusion Test Institute through the ES-9905-0015 test method will be described.
본 발명의 일 실시예에 따른 코팅제 조성물을 한전표준규격(ES-9905-0015) 시험방법을 통해 실험한 결과, 본 발명에 따른 코팅제 조성물은 습도시험, 충돌시험, 내후성 시험에 의한 균열 및 부풀음 유무, 내열성 시험, 내염수성과 내산성 후 부식여부의 결과가 이상없음으로 나타났고, 내후성 시험에 따른 밀착성에서 0등급을 받았고, 도장막 두께는 51㎛로 정상수치를 받았으며, 내오염성에 따른 색차의 수치도 각각 5.2와 0.3으로 정상범위에 존재하는 것을 알 수 있다. The coating composition according to one embodiment of the present invention was tested through the ES-9905-0015 test method. As a result, the coating composition according to the present invention was evaluated for the presence of cracks and swelling , Heat resistance test, corrosion resistance, and corrosion resistance after corrosion resistance showed no abnormality, and the adhesion according to the weathering test was rated as 0, the coating film thickness was 51 μm, and the color difference according to the stain resistance Are in the normal range of 5.2 and 0.3, respectively.
이때, 상기 밀착성은 테이프나 풀과 같은 접착력이 있는 물질이 붙지 않는 정도를 뜻하며, 상기 색차는 탈색되는 정도를 의미한다.In this case, the adhesion means a degree to which an adhesive substance such as a tape or a glue does not adhere, and the color difference means a degree of discoloration.
또한, ASTM D4060-14 시험방법에 따른 마모시험의 결과 165㎎으로 정상범위내에 존재하고, ASTM D2794-09 시험방법에 따른 충격시험에서도 이상없음으로 나타났음으로 문제가 없음을 알 수 있으며, KS S IEC 60093 시험방법에 따른 표면고유저항(250V)에서도 상기 결과치가 6 x 104 ㏁으로 나타나 문제가 없는 것으로 판단된다.In addition, as a result of the abrasion test according to the ASTM D4060-14 test method, it is found that there is no problem because it is within the normal range of 165 mg and the impact test according to the test method according to ASTM D2794-09 shows no abnormality. The result of the surface resistivity (250 V) according to the 60093 test method is 6 × 10 4 ㏁, which is considered to be no problem.
더불어, 상기 도 3에 도시된 시험결과에서 테이프가 시험면에 붙지 않음이 기재된 것으로 보아, 비점착성이 우수한 것을 확인할 수 있다. In addition, in the test results shown in FIG. 3, it is described that the tape does not adhere to the test surface, so that it can be confirmed that the tape has excellent non-stickiness.
따라서, 본 발명의 일 실시예에 따른 코팅제 조성물은 내마모성, 내오염성, 세척용이성 및 내열성이 우수하고, 표면경도와 비점착성도 기존에 사용되는 다른 코팅제 조성물보다 현저히 우수한 것을 확인할 수 있다. Accordingly, it can be seen that the coating composition according to an embodiment of the present invention is excellent in abrasion resistance, stain resistance, ease of washing and heat resistance, and surface hardness and non-stickiness are remarkably superior to other coating compositions used in the past.
이때, 상기 내후성 시험조건과 한전표준규격에 따른 시험방법, ASTM D4060-14,ASTM D2794-09, KS S IEC 60093에 따른 시험방법은 이미 규정화된 시험방법으로써 상기 시험 방법에 대해 별도로 서술하지 않는다. At this time, the test methods according to the weathering test conditions and the test methods according to KEPCO Standard, ASTM D4060-14, ASTM D2794-09, and
이상 본 발명을 구체적인 실시예를 통하여 상세히 설명하였으나, 이는 본 발명을 구체적으로 설명하기 위한 것으로, 본 발명은 이에 한정되지 않으며, 본 발명의 기술적 사상 내에서 당 분야의 통상의 지식을 가진 자에 의해 그 변형이나 개량이 가능함이 명백하다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the same is by way of illustration and example only and is not to be construed as limiting the present invention. It is obvious that the modification or improvement is possible.
본 발명의 단순한 변형 내지 변경은 모두 본 발명의 범주에 속하는 것으로 본 발명의 구체적인 보호 범위는 첨부된 특허청구범위에 의해 명확해질 것이다.It is intended that the present invention cover the modifications and variations of this invention provided they come within the scope of the appended claims and their equivalents.
Claims (7)
상기 코팅제 조성물은,
폴리 알콕시 실록산 수지와 가교제, 에틸 실리케이트, 실리콘 폴리머, 촉매제, 용제가 포함되도록 제조되되,
상기 폴리 알콕시 실록산 수지 100 중량부에 대해,
가교제 0.1 내지 5 중량부, 에틸 실리케이트 1 내지 10 중량부, 실리콘 폴리머 5 내지 20 중량부, 촉매제 1 내지 25 중량부, 용제 5 내지 20 중량부가 함유되어 제조되고,
상기 실리콘 폴리머는, 비점착성 및 오염방지 성능을 갖는 상온습기경화형 실리콘 수지이고,
상기 용제는 작업성 및 점도조절의 기능을 갖는, 카보네이트 종류나 알코올 종류 중 하나 이상을 사용하며,
상기 가교제는, 부착력 증진성능을 갖는, 비닐실란, 메틸트리메톡시실란, 알콕시실란 중 하나 이상을 사용하는 것을 특징으로 하는 표면 오염 방지용 코팅제 조성물.A coating composition for preventing surface contamination by various contaminants,
The coating composition may comprise,
A polyalkoxysiloxane resin and a crosslinking agent, an ethyl silicate, a silicone polymer, a catalyst, and a solvent,
With respect to 100 parts by weight of the polyalkoxysiloxane resin,
0.1 to 5 parts by weight of a crosslinking agent, 1 to 10 parts by weight of ethyl silicate, 5 to 20 parts by weight of a silicone polymer, 1 to 25 parts by weight of a catalyst and 5 to 20 parts by weight of a solvent,
The silicone polymer is a room temperature moisture curable silicone resin having non-tackiness and stain-proofing performance,
The solvent may be at least one of a carbonate type and an alcohol type having a function of workability and viscosity control,
Wherein the cross-linking agent is one or more of vinyl silane, methyltrimethoxysilane, and alkoxysilane having an adhesion-improving ability.
상기 촉매제는,
백금, 지르코늄, 티타네이트, 틴 중 하나 이상을 사용하는 것을 특징으로 하는 표면 오염 방지용 코팅제 조성물.The method according to claim 1,
In the catalyst,
Wherein at least one of platinum, zirconium, titanate, and tin is used.
상기 코팅제 조성물의 제조방법은,
상기 폴리 알콕시 실록산에 상기 가교제를 첨가하여 200 - 400rpm으로 상온에서 30분 - 120분간 혼합하여 교반하는 단계;
상기 교반된 상기 폴리 알콕시 실록산, 상기 가교제에 에틸실리케이트를 첨가하여 200 - 400rpm으로 상온에서 30분 - 120분간 혼합하여 교반하는 단계;
상기 교반된 상기 폴리 알콕시 실록산, 상기 가교제, 상기 에틸실리케이트에 실리콘 폴리머를 첨가하여 200 - 400rpm으로 상온에서 30분 - 120분간 혼합하여 교반하는 단계;
상기 교반된 상기 폴리 알콕시 실록산, 상기 가교제, 상기 에틸실리케이트, 실리콘 폴리머에 촉매제를 첨가하여 200 - 400rpm으로 상온에서 30분 - 120분간 혼합하여 교반하는 단계;
상기 교반된 상기 교반된 상기 폴리 알콕시 실록산, 상기 가교제, 상기 에틸실리케이트, 실리콘 폴리머, 상기 촉매제에 카보네이트 또는 알코올을 첨가하여 200 - 400rpm으로 상온에서 25분 - 35분간 혼합하여 교반하는 단계; 를 거쳐 저온용 코팅제 조성물이 제조되는 것을 특징으로 하는 표면 오염 방지용 코팅제 조성물 제조방법. 6. A method for preparing a coating composition according to any one of claims 1 to 5,
The method for producing the coating composition comprises:
Adding the crosslinking agent to the polyalkoxysiloxane, mixing the mixture at 200 - 400 rpm at room temperature for 30 minutes to 120 minutes, and stirring the mixture;
Adding ethyl silicate to the agitated polyalkoxysiloxane, crosslinking agent, mixing at 200 - 400 rpm at room temperature for 30 minutes to 120 minutes, and stirring;
Adding the silicone polymer to the agitated polyalkoxysiloxane, the crosslinking agent, and the ethyl silicate, mixing the mixture at a temperature of 200 to 400 rpm at room temperature for 30 minutes to 120 minutes, and stirring the mixture;
Adding a catalyst to the agitated polyalkoxysiloxane, the crosslinking agent, the ethyl silicate, and the silicone polymer, mixing the mixture at a temperature of 200 to 400 rpm for 30 minutes to 120 minutes, and stirring the mixture;
Adding the carbonate or alcohol to the agitated polyalkoxysiloxane, the crosslinking agent, the ethyl silicate, the silicone polymer, and the catalyst, mixing the mixture at 200 to 400 rpm at room temperature for 25 to 35 minutes and stirring the mixture; Wherein the low-temperature coating composition is prepared through the steps of: