CN107877404B - A kind of preparation process of environment-friendly type flexible polishing grinding tool - Google Patents
A kind of preparation process of environment-friendly type flexible polishing grinding tool Download PDFInfo
- Publication number
- CN107877404B CN107877404B CN201711137763.0A CN201711137763A CN107877404B CN 107877404 B CN107877404 B CN 107877404B CN 201711137763 A CN201711137763 A CN 201711137763A CN 107877404 B CN107877404 B CN 107877404B
- Authority
- CN
- China
- Prior art keywords
- environment
- friendly type
- grinding tool
- heat drying
- type flexible
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to grinding tool technical fields, and in particular to a kind of preparation process of environment-friendly type flexible polishing grinding tool.The preparation process includes: step Step 1: selection substrate；Step 2: applying primer；Step 3: electrostatic sand-planting；Step 4: heat drying；Step 5: applying re-glue；Step 6: coating blocking preventing coating；Step 7: heat drying；Step 8: adhesive fabric base；Step 9: heat drying.A kind of preparation process of environment-friendly type flexible polishing grinding tool of the invention, obtained environment-friendly type flexible polishing grinding tool has excellent flexibility, and then make the environment-friendly type flexible polishing grinding tool that there is excellent sticking nature, there is unique advantage to the polishing of irregular surface and curved surface, and falling off for abrasive material can be prevented, and can be reduced scratch.And environment-friendly type flexible polishing grinding tool obtained by the technique can substitute existing water mill polishing mode, and then do not generate waste water with the polishing mode of dustfree dry grinding, not pollute working environment compared with existing water-proof abrasive paper.
Description
Technical field
The present invention relates to grinding tool technical fields, and in particular to a kind of preparation process of environment-friendly type flexible polishing grinding tool.
Background technique
Currently, auto repair, automobile after sale and in 3C electronics industry, are needed to car body and vehicle paint, 3C electronic product
It polishes on surface.In the prior art, auto repair, automobile after sale and the technique for grinding in 3C electronics industry, mostly use water-fast
Sand paper carries out plus the mode of water polishing carries out grinding process, however, this meeting in such a way that water-proof abrasive paper carries out plus water is polished
A large amount of waste water is generated, and is manual grinding, the working environment of operative employee is very severe.
In addition, flexible abrasive product is often referred to grinding tool abrasive material being adhered to organic binder on deflection matrix, binder
There are hide glue, gelatine, cheese cement and synthetic resin gum etc., matrix has cloth, paper and cloth paper composites etc., and abrasive material and matrix rely on
Binder mechanical bond.However, that there are abrasive materials is low with substrate bond strength for flexible abrasive product in the prior art, abrasive material is easy to fall off,
The defect of scratch is easy to appear when polishing surface.
Summary of the invention
In view of the above-mentioned deficiencies in the prior art, it is an object of the present invention to provide a kind of preparation work of environment-friendly type flexible polishing grinding tool
Skill, environment-friendly type flexible polishing grinding tool made from the preparation process can substitute water mill polishing mode, not generate waste water, do not pollute work
Environment, and abrasive material is good with substrate bond strength, abrasive material is not easily to fall off, polish surface when no marking.
To achieve the goals above, the present invention adopts the following technical scheme:
A kind of preparation process of environment-friendly type flexible polishing grinding tool is provided, it the following steps are included:
Step 1: selecting substrate: selecting high polymer elastic glue film as basis material；
Step 2: applying primer: primer being applied on the high polymer elastic glue film for investing step 1；
Step 3: electrostatic sand-planting: being adsorbed onto abrasive material on the high polymer elastic glue film that primer is coated by high-pressure electrostatic；
Step 4: heat drying: being thermally dried after completing the electrostatic sand-planting of step 3；
Step 5: apply re-glue: abrasive surface again uniformly coated one layer of re-glue；
Step 6: coating blocking preventing coating: blocking preventing coating is coated on abrasive material；
Step 7: heat drying: be thermally dried after completing the coating blocking preventing coating of step 6, obtain sand film half at
Product；
Step 8: adhesive fabric base: with hot-melt adhesive membrane by the bottom surface of Bu Ji and the high polymer elastic glue film of sand film semi-finished product
It is bonded together, and is firmly bonded the two by hot pressing；
Step 9: heat drying: being thermally dried after completing the adhesive fabric base of step 8, it is soft to obtain the environment-friendly type
Property polishing abrasive tool.
In above-mentioned technical proposal, in the step 1, the high polymer elastic glue film is set as thermoplastic polyurethane elastic
Body rubber film.
In above-mentioned technical proposal, in the step 1, the thickness of the high polymer elastic glue film be set as 0.05mm~
0.15mm。
In above-mentioned technical proposal, the re-glue of the primer of the step 2 and the step 5 by following parts by weight group
Part composition:
In above-mentioned technical proposal, in the step 6, the blocking preventing coating is made of the component of following parts by weight:
In above-mentioned technical proposal, the stearate is one of zinc stearate, calcium stearate or magnesium stearate or appoints
Composition more than the two of anticipating.
In above-mentioned technical proposal, the adhesive is one or both of polyurethane adhesive or cellulose family adhesive
Composition.
In above-mentioned technical proposal, the antistatic agent be one of the cruel amine of ethyoxyl laurel or monostearin or
Two kinds of composition.
It is described Step 4: the temperature of the heat drying of step 7 and step 9 is disposed as 80 DEG C in above-mentioned technical proposal
~110 DEG C, the time of heat drying is disposed as 3min~10min.
In above-mentioned technical proposal, in the step 8, the cloth base is set as flannelette.
Compared with prior art, beneficial effect is the present invention:
(1) preparation process of a kind of environment-friendly type flexible polishing grinding tool provided by the invention, due to high polymer elastic glue film
As basis material and as the supporting body of abrasive material, and then make obtained environment-friendly type flexible polishing grinding tool that there is excellent softness
Property, and then make the environment-friendly type flexible polishing grinding tool that there is excellent sticking nature, have to the polishing of irregular surface and curved surface only
Special advantage.
(2) preparation process of a kind of environment-friendly type flexible polishing grinding tool provided by the invention, obtained environment-friendly type flexibility are thrown
Tarry matter tool can substitute existing water mill polishing mode compared with existing water-proof abrasive paper with the polishing mode of dustfree dry grinding,
And then waste water is not generated, do not pollute working environment.
(3) preparation process of a kind of environment-friendly type flexible polishing grinding tool provided by the invention, due to uniform again in abrasive surface
Coated one layer of re-glue, can increase the adhesion strength of abrasive material and substrate, and then can prevent obtained grinding tool abrasive material in polishing
The phenomenon that falling off.
(4) preparation process of a kind of environment-friendly type flexible polishing grinding tool provided by the invention, it is anti-due to being coated on abrasive material
Stifled coating, which has the function of lubrication well and eliminates electrostatic, can make obtained environment-friendly type flexible polishing
The grindstone dust energy rapid dispersion that grinding tool generates when in use has good anti-blockage function without coalescing, and can improve polishing
Surface quality, and reduce scratch, prolong the service life.
(5) preparation process of a kind of environment-friendly type flexible polishing grinding tool provided by the invention, production simple with technical process
It is at low cost, and the characteristics of industrializing large-scale application can be suitable for.
Specific embodiment
In order to which the technical problems, technical solutions and beneficial effects solved by the present invention is more clearly understood, below in conjunction with
Embodiment, the present invention will be described in further detail.It should be appreciated that specific embodiment described herein is only used to explain
The present invention is not intended to limit the present invention.
Embodiment 1.
A kind of preparation process of environment-friendly type flexible polishing grinding tool, it the following steps are included:
Step 1: selecting substrate: selecting high polymer elastic glue film as basis material；Wherein, in the present embodiment, macromolecule
Elastic glue film is preferably thermoplastic polyurethane elastomer rubber membrane；In the present embodiment, the thickness of high polymer elastic glue film is set as
0.10mm；
Step 2: applying primer: primer being applied on the high polymer elastic glue film for investing step 1；
Step 3: electrostatic sand-planting: being adsorbed onto abrasive material on the high polymer elastic glue film that primer is coated by high-pressure electrostatic；
Step 4: heat drying: being thermally dried after completing the electrostatic sand-planting of step 3；In the present embodiment, heating is dry
Dry temperature is disposed as 100 DEG C, and the time of heat drying is disposed as 6min；
Step 5: apply re-glue: abrasive surface again uniformly coated one layer of re-glue；
Step 6: coating blocking preventing coating: blocking preventing coating is coated on abrasive material；
Step 7: heat drying: be thermally dried after completing the coating blocking preventing coating of step 6, obtain sand film half at
Product；In the present embodiment, the temperature of heat drying is disposed as 100 DEG C, and the time of heat drying is disposed as 6min；
In the present embodiment, blocking preventing coating is made of the component of following parts by weight:
In the present embodiment, stearate is zinc stearate；
In the present embodiment, adhesive is polyurethane adhesive；
In the present embodiment, antistatic agent is the cruel amine of ethyoxyl laurel；
In the present embodiment, organic solvent is dimethylbenzene；
Step 8: adhesive fabric base: with hot-melt adhesive membrane by the bottom surface of Bu Ji and the high polymer elastic glue film of sand film semi-finished product
It is bonded together, and is firmly bonded the two by hot pressing；Wherein, in the present embodiment, cloth base is preferably flannelette, and flannelette is preferably
Woollen goods hasp flannelette, woollen goods hasp flannelette have the function of Self-adhesive, and then can be with high polymer elastic glue film secure bond；
Step 9: heat drying: being thermally dried after completing the adhesive fabric base of step 8, it is soft to obtain the environment-friendly type
Property polishing abrasive tool；In the present embodiment, the temperature of heat drying is disposed as 100 DEG C, and the time of heat drying is disposed as 6min；
In the present embodiment, the primer of step 2 and the re-glue of step 5 are made of the component of following parts by weight:
In the present embodiment, organic solvent is dimethylbenzene.
Embodiment 2.
A kind of preparation process of environment-friendly type flexible polishing grinding tool, it the following steps are included:
Step 1: selecting substrate: selecting high polymer elastic glue film as basis material；Wherein, in the present embodiment, macromolecule
Elastic glue film is preferably thermoplastic polyurethane elastomer rubber membrane；In the present embodiment, the thickness of high polymer elastic glue film is set as
0.05mm；
Step 2: applying primer: primer being applied on the high polymer elastic glue film for investing step 1；
Step 3: electrostatic sand-planting: being adsorbed onto abrasive material on the high polymer elastic glue film that primer is coated by high-pressure electrostatic；
Step 4: heat drying: being thermally dried after completing the electrostatic sand-planting of step 3；In the present embodiment, heating is dry
Dry temperature is disposed as 80 DEG C, and the time of heat drying is disposed as 10min；
Step 5: apply re-glue: abrasive surface again uniformly coated one layer of re-glue；
Step 6: coating blocking preventing coating: blocking preventing coating is coated on abrasive material；
Step 7: heat drying: be thermally dried after completing the coating blocking preventing coating of step 6, obtain sand film half at
Product；In the present embodiment, the temperature of heat drying is disposed as 80 DEG C, and the time of heat drying is disposed as 10min；
In the present embodiment, blocking preventing coating is made of the component of following parts by weight:
In the present embodiment, stearate is calcium stearate；
In the present embodiment, adhesive is cellulose family adhesive；
In the present embodiment, antistatic agent is monostearin；
In the present embodiment, organic solvent is toluene；
Step 8: adhesive fabric base: with hot-melt adhesive membrane by the bottom surface of Bu Ji and the high polymer elastic glue film of sand film semi-finished product
It is bonded together, and is firmly bonded the two by hot pressing；Wherein, in the present embodiment, cloth base is preferably flannelette；
Step 9: heat drying: being thermally dried after completing the adhesive fabric base of step 8, it is soft to obtain the environment-friendly type
Property polishing abrasive tool；In the present embodiment, the temperature of heat drying is disposed as 80 DEG C, and the time of heat drying is disposed as 10min；
In the present embodiment, the primer of step 2 and the re-glue of step 5 are made of the component of following parts by weight:
In the present embodiment, organic solvent is toluene.
Embodiment 3.
A kind of preparation process of environment-friendly type flexible polishing grinding tool, it the following steps are included:
Step 1: selecting substrate: selecting high polymer elastic glue film as basis material；Wherein, in the present embodiment, macromolecule
Elastic glue film is preferably thermoplastic polyurethane elastomer rubber membrane；In the present embodiment, the thickness of high polymer elastic glue film is set as
0.15mm；
Step 2: applying primer: primer being applied on the high polymer elastic glue film for investing step 1；
Step 3: electrostatic sand-planting: being adsorbed onto abrasive material on the high polymer elastic glue film that primer is coated by high-pressure electrostatic；
Step 4: heat drying: being thermally dried after completing the electrostatic sand-planting of step 3；In the present embodiment, heating is dry
Dry temperature is disposed as 110 DEG C, and the time of heat drying is disposed as 3min；
Step 5: apply re-glue: abrasive surface again uniformly coated one layer of re-glue；
Step 6: coating blocking preventing coating: blocking preventing coating is coated on abrasive material；
Step 7: heat drying: be thermally dried after completing the coating blocking preventing coating of step 6, obtain sand film half at
Product；In the present embodiment, the temperature of heat drying is disposed as 110 DEG C, and the time of heat drying is disposed as 3min；
In the present embodiment, blocking preventing coating is made of the component of following parts by weight:
In the present embodiment, stearate is magnesium stearate；
In the present embodiment, adhesive is the composition of polyurethane adhesive and cellulose family adhesive；
In the present embodiment, antistatic agent is the composition of ethyoxyl laurel cruel amine and monostearin；
In the present embodiment, organic solvent is dimethylbenzene；
Step 8: adhesive fabric base: with hot-melt adhesive membrane by the bottom surface of Bu Ji and the high polymer elastic glue film of sand film semi-finished product
It is bonded together, and is firmly bonded the two by hot pressing；Wherein, in the present embodiment, cloth base is preferably flannelette；
Step 9: heat drying: being thermally dried after completing the adhesive fabric base of step 8, it is soft to obtain the environment-friendly type
Property polishing abrasive tool；In the present embodiment, the temperature of heat drying is disposed as 110 DEG C, and the time of heat drying is disposed as 3min；
In the present embodiment, the primer of step 2 and the re-glue of step 5 are made of the component of following parts by weight:
In the present embodiment, organic solvent is dimethylbenzene.
Embodiment 4.
A kind of preparation process of environment-friendly type flexible polishing grinding tool, it the following steps are included:
Step 1: selecting substrate: selecting high polymer elastic glue film as basis material；Wherein, in the present embodiment, macromolecule
Elastic glue film is preferably thermoplastic polyurethane elastomer rubber membrane；In the present embodiment, the thickness of high polymer elastic glue film is set as
0.08mm；
Step 2: applying primer: primer being applied on the high polymer elastic glue film for investing step 1；
Step 3: electrostatic sand-planting: being adsorbed onto abrasive material on the high polymer elastic glue film that primer is coated by high-pressure electrostatic；
Step 4: heat drying: being thermally dried after completing the electrostatic sand-planting of step 3；In the present embodiment, heating is dry
Dry temperature is disposed as 90 DEG C, and the time of heat drying is disposed as 8min；
Step 5: apply re-glue: abrasive surface again uniformly coated one layer of re-glue；
Step 6: coating blocking preventing coating: blocking preventing coating is coated on abrasive material；
Step 7: heat drying: be thermally dried after completing the coating blocking preventing coating of step 6, obtain sand film half at
Product；In the present embodiment, the temperature of heat drying is disposed as 90 DEG C, and the time of heat drying is disposed as 8min；
In the present embodiment, blocking preventing coating is made of the component of following parts by weight:
In the present embodiment, stearate is the composition of zinc stearate, calcium stearate and magnesium stearate；
In the present embodiment, adhesive is polyurethane adhesive；
In the present embodiment, antistatic agent is the cruel amine of ethyoxyl laurel；
In the present embodiment, organic solvent is dimethylbenzene.
Step 8: adhesive fabric base: with hot-melt adhesive membrane by the bottom surface of Bu Ji and the high polymer elastic glue film of sand film semi-finished product
It is bonded together, and is firmly bonded the two by hot pressing；Wherein, in the present embodiment, cloth base is preferably flannelette；
Step 9: heat drying: being thermally dried after completing the adhesive fabric base of step 8, it is soft to obtain the environment-friendly type
Property polishing abrasive tool；In the present embodiment, the temperature of heat drying is disposed as 90 DEG C, and the time of heat drying is disposed as 8min；
In the present embodiment, the primer of step 2 and the re-glue of step 5 are made of the component of following parts by weight:
Embodiment 5.
A kind of preparation process of environment-friendly type flexible polishing grinding tool, it the following steps are included:
Step 1: selecting substrate: selecting high polymer elastic glue film as basis material；Wherein, in the present embodiment, macromolecule
Elastic glue film is preferably thermoplastic polyurethane elastomer rubber membrane；In the present embodiment, the thickness of high polymer elastic glue film is set as
0.12mm；
Step 2: applying primer: primer being applied on the high polymer elastic glue film for investing step 1；
Step 3: electrostatic sand-planting: being adsorbed onto abrasive material on the high polymer elastic glue film that primer is coated by high-pressure electrostatic；
Step 4: heat drying: being thermally dried after completing the electrostatic sand-planting of step 3；In the present embodiment, heating is dry
Dry temperature is disposed as 105 DEG C, and the time of heat drying is disposed as 4min；
Step 5: apply re-glue: abrasive surface again uniformly coated one layer of re-glue；
Step 6: coating blocking preventing coating: blocking preventing coating is coated on abrasive material；
Step 7: heat drying: be thermally dried after completing the coating blocking preventing coating of step 6, obtain sand film half at
Product；In the present embodiment, the temperature of heat drying is disposed as 105 DEG C, and the time of heat drying is disposed as 4min；
In the present embodiment, blocking preventing coating is made of the component of following parts by weight:
In the present embodiment, stearate is zinc stearate；
In the present embodiment, adhesive is polyurethane adhesive；
In the present embodiment, antistatic agent is monostearin；
In the present embodiment, organic solvent is dimethylbenzene；
Step 8: adhesive fabric base: with hot-melt adhesive membrane by the bottom surface of Bu Ji and the high polymer elastic glue film of sand film semi-finished product
It is bonded together, and is firmly bonded the two by hot pressing；Wherein, in the present embodiment, cloth base is preferably flannelette；
Step 9: heat drying: being thermally dried after completing the adhesive fabric base of step 8, it is soft to obtain the environment-friendly type
Property polishing abrasive tool；In the present embodiment, the temperature of heat drying is disposed as 105 DEG C, and the time of heat drying is disposed as 4min；
In the present embodiment, the primer of step 2 and the re-glue of step 5 are made of the component of following parts by weight:
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than limiting the scope of the invention, although
The present invention is explained in detail referring to preferred embodiment, those skilled in the art should understand that, it can be to this hair
Bright technical solution is modified or replaced equivalently, without departing from the spirit and scope of technical solution of the present invention.
Claims (5)
1. a kind of preparation process of environment-friendly type flexible polishing grinding tool, it is characterised in that: it the following steps are included:
Step 1: selecting substrate: selecting high polymer elastic glue film as basis material；
Step 2: applying primer: primer being applied on the high polymer elastic glue film for investing step 1；
Step 3: electrostatic sand-planting: being adsorbed onto abrasive material on the high polymer elastic glue film that primer is coated by high-pressure electrostatic；
Step 4: heat drying: being thermally dried after completing the electrostatic sand-planting of step 3；
Step 5: apply re-glue: abrasive surface again uniformly coated one layer of re-glue；
Step 6: coating blocking preventing coating: blocking preventing coating is coated on abrasive material；
Step 7: heat drying: being thermally dried after completing the coating blocking preventing coating of step 6, obtain sand film semi-finished product；
Step 8: adhesive fabric base: being bonded the bottom surface of Bu Ji and the high polymer elastic glue film of sand film semi-finished product with hot-melt adhesive membrane
Together, and by hot pressing it is firmly bonded the two；
Step 9: heat drying: being thermally dried after completing the adhesive fabric base of step 8, obtain the environment-friendly type flexibility and throw
Tarry matter tool；
The re-glue of the primer of the step 2 and the step 5 is made of the component of following parts by weight:
In the step 6, the blocking preventing coating is made of the component of following parts by weight:
In the step 1, the high polymer elastic glue film is set as thermoplastic polyurethane elastomer rubber membrane；
In the step 1, the thickness of the high polymer elastic glue film is set as 0.05mm~0.15mm；
In the step 8, the cloth base is set as flannelette.
2. a kind of preparation process of environment-friendly type flexible polishing grinding tool according to claim 1, it is characterised in that: the tristearin
Hydrochlorate is the composition of one of zinc stearate, calcium stearate or magnesium stearate or any the two or more.
3. a kind of preparation process of environment-friendly type flexible polishing grinding tool according to claim 1, it is characterised in that: the gluing
Agent is the composition of one or both of polyurethane adhesive or cellulose family adhesive.
4. a kind of preparation process of environment-friendly type flexible polishing grinding tool according to claim 1, it is characterised in that: it is described resist it is quiet
Electric agent is the composition of one or both of the cruel amine of ethyoxyl laurel or monostearin.
5. a kind of preparation process of environment-friendly type flexible polishing grinding tool according to claim 1, it is characterised in that: the step
Four, the temperature of the heat drying of step 7 and step 9 is disposed as 80 DEG C~110 DEG C, and the time of heat drying is disposed as
3min~10min.