CN108315108A - 一种环保型高效钢铁件挂灰去除剂 - Google Patents

一种环保型高效钢铁件挂灰去除剂 Download PDF

Info

Publication number
CN108315108A
CN108315108A CN201810312705.5A CN201810312705A CN108315108A CN 108315108 A CN108315108 A CN 108315108A CN 201810312705 A CN201810312705 A CN 201810312705A CN 108315108 A CN108315108 A CN 108315108A
Authority
CN
China
Prior art keywords
environment
highly efficient
dust remover
iron parts
efficient steel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810312705.5A
Other languages
English (en)
Inventor
姜宏毅
刘翻
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenzhen Colman Environmental Protection Technology Co Ltd
Original Assignee
Shenzhen Colman Environmental Protection Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenzhen Colman Environmental Protection Technology Co Ltd filed Critical Shenzhen Colman Environmental Protection Technology Co Ltd
Priority to CN201810312705.5A priority Critical patent/CN108315108A/zh
Publication of CN108315108A publication Critical patent/CN108315108A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种环保型高效钢铁件挂灰去除剂。该环保型高效钢铁件挂灰去除剂由以下重量份的原料制成：有机酸0.7％‑3.5％，有机酸聚合物0.3％‑2.0％，非离子表面活性剂0.3％‑2.0％，阴离子表面活性剂0.1％‑0.7％，其余为水。本发明使用范围广，适用于钢铁、不锈钢、锌合金、铝合金等多种基材；摒弃了传统的强酸体系，大大减低了对于环境的污染；使用了易于生物降解的表面活性剂，大大降低了体系的COD，符合情节生产要求。

Description

一种环保型高效钢铁件挂灰去除剂
技术领域
本发明涉及化学产品领域，尤其涉及一种环保型高效钢铁件挂灰去除剂。
背景技术
随着工业化的不断发展，环境污染问题越来越严重，对于保护环境，清洁、环保、节能的生产越来越受行业的重视。
钢铁件表面的挂灰是附着在其表面的直径极小(一般在0.01um以下) 的粉垢，是在经过除蜡、化学除油和电解除油工序之后残留在基体表面的不完整薄膜。这层挂灰一般来说用水是清洗不掉的，但是用手或者抹布轻轻一抹就能除掉.目前去除挂灰的方法有化学方法、电解方法和人工擦洗。化学方法使用强酸、强氧化剂等，对于生产环境造成很大污染，同时也严重影响人员健康。人工擦洗方法生产效率低，而且对于形状复杂的零件很难擦洗到位。严重影响电镀产品的质量。
钢铁件表面挂灰主要是材料中的惰性元素、碳粒、硅粒、金属化合物的质点与难容物。其产生的主要原因有以下几种情况：
材质本身含碳量较高，一部分铁被融解了，剩下的碳组分形成挂灰。
零件在机加工过程中使用的润滑油、防锈油含有碳微粒，当吸附在工件表面的油污被除掉后，由于碳微粒的表面能比较大，碳微粒仍然吸附在零件表面形成挂灰。
零件加工完在较长的存放过程中吸附了空气中的尘埃，尘埃被零件表面的油膜吸附住，当油膜被除掉时，尘埃仅仅吸附在零件表面形成挂灰。
综上所述，现在市面上亟需一种简单、方便而且安全的高效钢铁挂灰去除剂。
发明内容
本发明为了解决去除钢铁挂灰时容易造成生产环境很大污染，同时也严重影响人员健康，且人工擦洗方法生产效率低，而且对于形状复杂的零件很难擦洗到位，严重影响电镀产品的质量的问题，提出一种环保型高效钢铁件挂灰去除剂。
为达上述目的，本发明采用的技术方案如下：
一种环保型高效钢铁件挂灰去除剂，其特征在于，所述环保型高效钢铁件挂灰去除剂由以下重量份的原料制成：有机酸0.7％-3.5％，有机酸聚合物0.3％-2.0％，非离子表面活性剂0.3％-2.0％，阴离子表面活性剂0.1％-0.7％，其余为水。
在一些实施例中，所述环保型高效钢铁件挂灰去除剂由以下重量份的原料制成：有机酸1.0％-3.0％，有机酸聚合物0.4％-1.5％，非离子表面活性剂0.35％-1.7％，阴离子表面活性剂0.12％-0.55％，其余为水。
在一些实施例中，所述环保型高效钢铁件挂灰去除剂由以下重量份的原料制成：有机酸1.25％-2.5％，有机酸聚合物0.5％-1.25％，非离子表面活性剂0.5％-1.5％，阴离子表面活性剂0.15％-0.5％，其余为水。
在一些实施例中，所述有机酸为乳酸、氨基酸、马来酸、酒石酸、草酸、醋酸中的一种或者多种。
在一些实施例中，所述有机酸聚合物为马来酸均聚物、丙烯酸均聚物、马来酸-丙酸共聚物、磺化苯乙烯聚合物中的一种或者多种。
在一些实施例中，所述马来酸均聚物、丙烯酸均聚物、马来酸-丙酸共聚物、磺化苯乙烯聚合物的分子量5000-10000。
在一些实施例中，所述非离子表面活性剂为脂肪醇烷氧基化物。
在一些实施例中，所述脂肪醇烷氧基化物含有6-18个碳原子。
在一些实施例中，所述非离子表面活性剂分子间增加了聚环氧丙烷嵌段链的多支链化烷基聚氧乙烯。
在一些实施例中，所述阴离子表面活性剂为烷基苯磺酸盐、烷基萘磺酸盐、烷基磺酸盐、烯烃磺酸盐中的一种或者多种。
与现有技术相比，本发明至少具有以下有益效果：本发明使用范围广，适用于钢铁、不锈钢、锌合金、铝合金等多种基材；摒弃了传统的强酸体系，大大减低了对于环境的污染；使用了易于生物降解的表面活性剂，大大降低了体系的COD，符合情节生产要求。
具体实施方式
下面对本发明做进一步说明。
本实施例提出了一种环保型高效钢铁件挂灰去除剂，所述环保型高效钢铁件挂灰去除剂由以下重量份的原料制成：有机酸0.7％-3.5％，有机酸聚合物0.3％-2.0％，非离子表面活性剂0.3％-2.0％，阴离子表面活性剂0.1％-0.7％，其余为水。
有机酸是指一些具有酸性的有机化合物。最常见的有机酸是羧酸，其酸性源于羧基(-COOH)。磺酸(-SO3H)、亚磺酸(RSOOH)、硫羧酸 (RCOSH)等也属于有机酸。有机酸可与醇反应生成酯。
在一些实施例中，所述环保型高效钢铁件挂灰去除剂由以下重量份的原料制成：有机酸1.0％-3.0％，有机酸聚合物0.4％-1.5％，非离子表面活性剂0.35％-1.7％，阴离子表面活性剂0.12％-0.55％，其余为水。
在一些实施例中，所述环保型高效钢铁件挂灰去除剂由以下重量份的原料制成：有机酸1.25％-2.5％，有机酸聚合物0.5％-1.25％，非离子表面活性剂0.5％-1.5％，阴离子表面活性剂0.15％-0.5％，其余为水。
在一些实施例中，所述有机酸为乳酸、氨基酸、马来酸、酒石酸、草酸、醋酸中的一种或者多种。
在一些实施例中，所述有机酸聚合物为马来酸均聚物、丙烯酸均聚物、马来酸-丙酸共聚物、磺化苯乙烯聚合物中的一种或者多种。
在一些实施例中，所述马来酸均聚物、丙烯酸均聚物、马来酸-丙酸共聚物、磺化苯乙烯聚合物的分子量5000-10000。
在一些实施例中，所述非离子表面活性剂为脂肪醇烷氧基化物。
在一些实施例中，所述脂肪醇烷氧基化物含有6-18个碳原子。
在一些实施例中，所述非离子表面活性剂分子间增加了聚环氧丙烷嵌段链的多支链化烷基聚氧乙烯。
具体的，非离子表面活性剂的引入，使得体系的乳化、润湿分散性能进一步提高。
在一些实施例中，所述阴离子表面活性剂为烷基苯磺酸盐、烷基萘磺酸盐、烷基磺酸盐、烯烃磺酸盐中的一种或者多种。
具体的，阴离子表面活性剂的引入增强了体系的渗透、抗静电能力。
综上所述，本发明使用范围广，适用于钢铁、不锈钢、锌合金、铝合金等多种基材；摒弃了传统的强酸体系，大大减低了对于环境的污染；使用了易于生物降解的表面活性剂，大大降低了体系的COD，符合情节生产要求。
实施例一
一种环保型高效钢铁件挂灰去除剂，所述环保型高效钢铁件挂灰去除剂由以下重量份的原料制成：乳酸1.25％，氨基磺酸0.60％，丙烯酸 0.50％，丙烯酸均聚物0.75％，非离子表面活性剂0.50％，阴离子表面活性剂0.15％，水96.25％。
上述成分组成的环保型高效钢铁件挂灰去除剂其PH为5.35，呈弱酸性。
下表为本实施例的主要项目检测报告，及检测试验方法依据的标准：
实施例二
一种环保型高效钢铁件挂灰去除剂，所述环保型高效钢铁件挂灰去除剂由以下重量份的原料制成：酒石酸2.50％，丙烯酸均聚物1.25％，非离子表面活性剂1.50％，阴离子表面活性剂0.5％，水94.25％。
上述成分组成的环保型高效钢铁件挂灰去除剂其PH为6.05，呈弱酸性。
下表为本实施例的主要项目检测报告，及检测试验方法依据的标准：
实施例三
一种环保型高效钢铁件挂灰去除剂，所述环保型高效钢铁件挂灰去除剂由以下重量份的原料制成：醋酸1.88％，磺化苯乙烯聚合物0.88％，非离子表面活性剂1.0％，阴离子表面活性剂0.38％，水95.86％。
上述成分组成的环保型高效钢铁件挂灰去除剂其PH为5.78，呈弱酸性。
下表为本实施例的主要项目检测报告，及检测试验方法依据的标准：
实施例四
一种环保型高效钢铁件挂灰去除剂，所述环保型高效钢铁件挂灰去除剂由以下重量份的原料制成：乳酸1.25％，草酸0.60％，马来酸-丙酸共聚物0.50％，磺化苯乙烯聚合物0.50％，非离子表面活性剂0.50％，阴离子表面活性剂0.15％，水96.5％。
上述成分组成的环保型高效钢铁件挂灰去除剂其PH为6.25，呈弱酸性。
下表为本实施例的主要项目检测报告，及检测试验方法依据的标准：
实施例五
一种环保型高效钢铁件挂灰去除剂，所述环保型高效钢铁件挂灰去除剂由以下重量份的原料制成：酒石酸0..98％，醋酸0.50％，丙烯酸均聚物0.45％，磺化苯乙烯聚合物0.88％，非离子表面活性剂1.0％，阴离子表面活性剂0.38％，水95.81％。
上述成分组成的环保型高效钢铁件挂灰去除剂其PH为5.85，呈弱酸性。
下表为本实施例的主要项目检测报告，及检测试验方法依据的标准：
上述通过具体实施例对本发明进行了详细的说明，这些详细的说明仅仅限于帮助本领域技术人员理解本发明的内容，并不能理解为对本发明保护范围的限制。本领域技术人员在本发明构思下对上述方案进行的各种润饰、等效变换等均应包含在本发明的保护范围内。

Claims (10)

1.一种环保型高效钢铁件挂灰去除剂，其特征在于，所述环保型高效钢铁件挂灰去除剂由以下重量份的原料制成：有机酸0.7％-3.5％，有机酸聚合物0.3％-2.0％，非离子表面活性剂0.3％-2.0％，阴离子表面活性剂0.1％-0.7％，其余为水。
2.根据权利要求1所述的环保型高效钢铁件挂灰去除剂，其特征在于，所述环保型高效钢铁件挂灰去除剂由以下重量份的原料制成：有机酸1.0％-3.0％，有机酸聚合物0.4％-1.5％，非离子表面活性剂0.35％-1.7％，阴离子表面活性剂0.12％-0.55％，其余为水。
3.根据权利要求2所述的环保型高效钢铁件挂灰去除剂，其特征在于，所述环保型高效钢铁件挂灰去除剂由以下重量份的原料制成：有机酸1.25％-2.5％，有机酸聚合物0.5％-1.25％，非离子表面活性剂0.5％-1.5％，阴离子表面活性剂0.15％-0.5％，其余为水。
4.根据权利要求1-3中任意一项所述的环保型高效钢铁件挂灰去除剂，其特征在于，所述有机酸为乳酸、氨基酸、马来酸、酒石酸、草酸、醋酸中的一种或者多种。
5.根据权利要求4所述的环保型高效钢铁件挂灰去除剂，其特征在于，所述有机酸聚合物为马来酸均聚物、丙烯酸均聚物、马来酸-丙酸共聚物、磺化苯乙烯聚合物中的一种或者多种。
6.根据权利要求5所述的环保型高效钢铁件挂灰去除剂，其特征在于，所述马来酸均聚物、丙烯酸均聚物、马来酸-丙酸共聚物、磺化苯乙烯聚合物的分子量5000-10000。
7.根据权利要求1-3中任意一项所述的环保型高效钢铁件挂灰去除剂，其特征在于，所述非离子表面活性剂为脂肪醇烷氧基化物。
8.根据权利要求7所述的环保型高效钢铁件挂灰去除剂，其特征在于，所述脂肪醇烷氧基化物含有6-18个碳原子。
9.根据权利要求8所述的环保型高效钢铁件挂灰去除剂，其特征在于，所述非离子表面活性剂分子间增加了聚环氧丙烷嵌段链的多支链化烷基聚氧乙烯。
10.根据权利要求1-3中任意一项所述的环保型高效钢铁件挂灰去除剂，其特征在于，所述阴离子表面活性剂为烷基苯磺酸盐、烷基萘磺酸盐、烷基磺酸盐、烯烃磺酸盐中的一种或者多种。
CN201810312705.5A 2018-04-09 2018-04-09 一种环保型高效钢铁件挂灰去除剂 Pending CN108315108A (zh)