CN108312661A - A kind of honeycomb ceramics composite liner and its manufacturing method - Google Patents
A kind of honeycomb ceramics composite liner and its manufacturing method Download PDFInfo
- Publication number
- CN108312661A CN108312661A CN201810101568.0A CN201810101568A CN108312661A CN 108312661 A CN108312661 A CN 108312661A CN 201810101568 A CN201810101568 A CN 201810101568A CN 108312661 A CN108312661 A CN 108312661A
- Authority
- CN
- China
- Prior art keywords
- honeycomb
- steel skeleton
- steel plate
- elastic adhesive
- composite liner
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of honeycomb ceramics composite liners, including steel plate, honeycomb steel skeleton, ceramic block and elastic adhesive.The honeycomb steel skeleton welds on the steel plate, and ceramic block is bonded in by elastic adhesive in the honeycomb that honeycomb steel skeleton is formed, and the honeycomb that the honeycomb steel skeleton is formed is triangle, quadrangle, hexagon or circular configuration.The present invention relates to liner plate technical field, the honeycomb composite liner and its manufacturing method：First; on the steel plate by the welding of honeycomb steel skeleton; and every ceramic block is bonded in by elastic adhesive in triangle, quadrangle, hexagon or the round honeycomb that honeycomb steel skeleton is formed; while keeping ceramic block not easily to fall off, and when by material impact ceramic block by elastic adhesive buffer protection；Secondly, using the shock resistance structure intensity that honeycomb steel skeleton is excellent, the integral strength of ceramic composite lining board is improved, overcomes the not shock proof disadvantage of conventional ceramic composite liner, improve the overall performance of ceramic composite lining board, expand products application range.
Description
Technical field
The present invention relates to composite liner technical field, specially a kind of honeycomb ceramics composite liner and its manufacturing method.
Background technology
Liner plate is to make direct impact and abrasion of the apparatus casing from material for protecting conveying and crushing plant shell,
To ensure the conveying and processing of material, it is ensured that production effectively carries out.Liner plate uses metal wear resistant material under normal circumstances,
But the wear-resisting property of metal wear resistant material is poor, of high cost, along with service life is short, frequently replaces, maintenance workload is big, shadow
Production is rung to be normally carried out.
Since there is ceramics very high hardness and lower manufacturing cost, the application prospect of present ceramic composite lining board to compare
Extensively.But because ceramics brittleness is big, the whole shock resistance of ceramic composite lining board is poor, limit ceramic composite lining board and replace
For extensive use of the conventional metals wear-resistant material in produce reality.
Invention content
For the deficiency of existing ceramic composite lining board, the present invention provides a kind of honeycomb ceramics composite liner and its manufactures
Method solves the problems, such as that raising ceramic composite lining board shock resistance is poor.
In order to achieve the above object, the present invention is achieved by the following technical programs：A kind of honeycomb ceramics composite liner,
Including steel plate, honeycomb steel skeleton, ceramic block and elastic adhesive；The honeycomb steel skeleton is welded on above steel plate,
And ceramic block is bonded in by elastic adhesive in the honeycomb that honeycomb steel skeleton surrounds.
As another optimal technical scheme of the present invention, it is triangle that the honeycomb steel skeleton, which is formed by honeycomb,
Shape, quadrangle, hexagon or round honeycomb structure, and honeycomb steel skeleton has certain thickness and impact strength, it can
To be made of forming methods such as welding, punching press, casting or mechanical processings.
As another optimal technical scheme of the present invention, the ceramic block is triangular prism, quadrangular, hexagonal prisms or cylinder
Shape, and the height of ceramic block is less than honeycomb steel skeleton.
As another optimal technical scheme of the present invention, the elastic adhesive be resinae with favorable elasticity,
Any elastic adhesive in polyurethanes, anaerobism class, esters of acrylic acid, hot melt adhesive class, rubber or silicone adhesive class.
As another optimal technical scheme of the present invention, a kind of honeycomb ceramics composite liner manufacturing method is specific to wrap
Include following steps：
Step 1 uses the forming methods such as welding, punching press, casting or mechanical processing to make honeycomb steel skeleton first
(2)；
The steel plate (1) of selection is placed on work top by step 2, is polished using sanding machine, polishes coarse rear cleaning extremely
Without greasy dirt；
After the completion of step 3, in step 2 steel plate (1) polishing cleaning, honeycomb steel skeleton (2) is placed into steel plate
(1) above, it and by welding machine will be welded between honeycomb steel skeleton (2) and steel plate (1)；
Step 4, in step 3 between honeycomb steel skeleton (2) and steel plate (1) weld after the completion of, by honeycomb steel
Elastic adhesive is filled in honeycomb on skeleton (2)；
In step 5, honeycomb in step 4 after filling elastic adhesive, several pieces of ceramic blocks (3) are put into honeycomb
Interior, several pieces of ceramic blocks (3) are bonded as one by elastic adhesive and honeycomb steel skeleton (2)；
Step 6, step 5 complete it is good after, by composite liner that bonding is completed by the fast rapid hardening of modes such as heating or humidifying
Gu completing the manufacturing process of entire honeycomb ceramics composite liner.
Advantageous effect
The present invention provides a kind of honeycomb ceramics composite liner and its manufacturing methods, have following advantageous effect：
The honeycomb ceramics composite liner and its manufacturing method, by the way that the honeycomb steel skeleton of high intensity is welded on steel
On plate, and ceramic block is bonded in by elastic adhesive in the honeycomb opened up on honeycomb steel skeleton, and honeycomb is taken full advantage of
The excellent shock resistance of shape steel skeleton and elastic adhesive play ceramic composite lining board to the buffer protection function of ceramic block
While high-wear resistance, the shock proof requirement of ceramic composite lining board is met, the integral strength of ceramic composite lining board is improved, prolongs
The service life of product is grown.
Description of the drawings
Fig. 1,3 are vertical view of the invention；
Fig. 2,4 are side view of the invention.
In figure：1- steel plates, 2- honeycomb steel skeleton, 3- ceramic blocks.
Specific implementation mode
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation describes, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
The present invention provides two kinds of embodiments：
Embodiment 1
Referring to Fig. 1,2, a kind of honeycomb ceramics composite liner, including steel plate, honeycomb steel skeleton, ceramic block and elasticity
Bonding agent；
The honeycomb steel skeleton is welded on above steel plate, and ceramic block is bonded in by elastic epoxy resin bonding agent
In the honeycomb that honeycomb steel skeleton surrounds.
It is quadrangle honeycomb structure that the honeycomb steel skeleton, which is formed by honeycomb, and honeycomb steel skeleton has one
Welding shaping method making may be used in fixed thickness and impact strength.
The ceramic block is quadrangular shape, and the height of ceramic block is less than honeycomb steel skeleton.
The elastic adhesive is the elastic epoxy resin bonding agent with excellent toughness.
A kind of honeycomb ceramics composite liner manufacturing method, specifically comprises the following steps：
The method that step 1, steel bar use welding fabrication first makes quadrangle honeycomb steel skeleton (2)；
The steel plate (1) of selection is placed on work top by step 2, is polished using sanding machine, polishes coarse rear cleaning extremely
Without greasy dirt；
After the completion of step 3, in step 2 steel plate (1) polishing cleaning, honeycomb steel skeleton (2) is placed into steel plate
(1) above, it and by welding machine will be welded between honeycomb steel skeleton (2) and steel plate (1)；
Step 4, in step 3 between honeycomb steel skeleton (2) and steel plate (1) weld after the completion of, by honeycomb steel
Elastic epoxy resin bonding agent is filled in honeycomb on skeleton (2)；
In step 5, honeycomb in step 4 after filling elastic epoxy resin bonding agent, several pieces of ceramic blocks (3) are put
Into honeycomb, several pieces of ceramic blocks (3) are bonded as one by elastic epoxy resin bonding agent and honeycomb steel skeleton (2)；
Step 6, step 5 complete it is good after, the composite liner that bonding is completed makes elastic epoxy resin by mode of heating
Quickly solidification, that is, complete the manufacturing process of entire honeycomb ceramics composite liner.
The honeycomb ceramics composite liner and its manufacturing method pass through the honeycomb steel skeleton for making high-intensity welding
On the steel plate, and quadrangular ceramic block is bonded in by elastic epoxy resin bonding agent and to be opened up on honeycomb steel skeleton for welding
In honeycomb, takes full advantage of the excellent shock resistance of honeycomb steel skeleton and elastic epoxy resin bonding agent delays ceramics
Protective effect is rushed, while playing ceramic composite lining board high-wear resistance, the shock proof requirement of ceramic composite lining board is met, carries
The integral strength of high ceramic composite lining board extends the service life of product.
Embodiment 2
Referring to Fig. 3,4, a kind of honeycomb ceramics composite liner, including steel plate, honeycomb steel skeleton, ceramic block and elasticity
Bonding agent；
The honeycomb steel skeleton is welded on above steel plate, and ceramic block is bonded in honeycomb steel by elastic adhesive
In the honeycomb that matter skeleton surrounds.
It is hexagon honeycomb structure that the honeycomb steel skeleton, which is formed by honeycomb, and honeycomb steel skeleton has one
Casting and molding method making may be used in fixed thickness and impact strength.
The ceramic block is hexagonal prism shape, and the height of ceramic block is less than honeycomb steel skeleton.
The elastic adhesive is the polyurethane adhesive with favorable elasticity.
A kind of honeycomb ceramics composite liner manufacturing method, specifically comprises the following steps：
Step 1, the method for using casting and forming first make hexagonal honeycomb steel skeleton (2)；
The steel plate (1) of selection is placed on work top by step 2, is polished using sanding machine, polishes coarse rear cleaning extremely
Without greasy dirt；
After the completion of step 3, in step 2 steel plate (1) polishing cleaning, honeycomb steel skeleton (2) is placed into steel plate
(1) above, it and by welding machine will be welded between honeycomb steel skeleton (2) and steel plate (1)；
Step 4, in step 3 between honeycomb steel skeleton (2) and steel plate (1) weld after the completion of, by honeycomb steel
Elastic polyurethane bonding agent is filled in honeycomb on skeleton (2)；
In step 5, honeycomb in step 4 after filling elastic polyurethane bonding agent, several pieces of ceramic blocks (3) are put
Into honeycomb, several pieces of ceramic blocks (3) are bonded as one by elastic polyurethane bonding agent and honeycomb steel skeleton (2)；
Step 6, step 5 complete it is good after, the composite liner that bonding is completed keeps elastic polyurethane fast by humidification method
Rapid hardening is solid, that is, completes the manufacturing process of entire honeycomb ceramics composite liner.
The honeycomb ceramics composite liner and its manufacturing method, by welding the honeycomb steel skeleton of high-strength casting
On the steel plate, and hexagonal prisms ceramic block is bonded in the honeycomb opened up on honeycomb steel skeleton by elastic polyurethane bonding agent
It is interior, take full advantage of the buffer protection of the excellent shock resistance of honeycomb steel skeleton and elastic polyurethane bonding agent to ceramics
Effect while playing ceramic composite lining board high-wear resistance, meets the shock proof requirement of ceramic composite lining board, improves ceramics
The integral strength of composite liner extends the service life of product.
It should be noted that herein, relational terms such as first and second and the like are used merely to a reality
Body or operation are distinguished with another entity or operation, are deposited without necessarily requiring or implying between these entities or operation
In any actual relationship or order or sequence.Moreover, the terms "include", "comprise" or its any other variant are intended to
Non-exclusive inclusion, so that the process, method, article or equipment including a series of elements is not only wanted including those
Element, but also include other elements that are not explicitly listed, or further include for this process, method, article or equipment
Intrinsic element.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of variations, modification, replace
And modification, the scope of the present invention is defined by the appended.
Claims (5)
1. a kind of honeycomb ceramics composite liner, which is characterized in that including steel plate (1), honeycomb steel skeleton (2) and ceramic block
(3)；The honeycomb steel skeleton (2) is welded on steel plate (1), and ceramic block (3) is bonded in honeycomb by elastic adhesive
In the honeycomb that shape steel skeleton (2) is formed.
2. a kind of honeycomb ceramics composite liner according to claim 1, it is characterised in that：The honeycomb steel skeleton
(2) honeycomb surrounded is triangle, quadrangle, hexagon or circular configuration, and honeycomb steel skeleton (2) has certain thickness
The making of the forming methods such as welding, punching press, casting or mechanical processing may be used in degree and impact strength.
3. a kind of honeycomb ceramics composite liner according to claim 1, it is characterised in that：The ceramic block (3) is three
Prism, quadrangular, hexagonal prisms or cylindrical shape, and can be embedded in triangle, quadrangle that honeycomb steel skeleton (2) surrounds,
In hexagon or round honeycomb, highly it is no more than honeycomb steel skeleton (2).
4. a kind of honeycomb ceramics composite liner according to claim 1, it is characterised in that：The elastic adhesive is tool
Have any in resinae, polyurethanes, anaerobism class, esters of acrylic acid, hot melt adhesive class, rubber or the silicone adhesive class of favorable elasticity
Kind elastic adhesive.
5. a kind of honeycomb ceramics composite liner manufacturing method, which is characterized in that specifically comprise the following steps：
Step 1 uses the forming methods such as welding, punching press, casting or mechanical processing to make honeycomb steel skeleton (2) first；
The steel plate (1) of selection is placed on work top by step 2, is polished using sanding machine, is cleaned to oil-free after polishing is coarse
It is dirty；
After the completion of step 3, in step 2 steel plate (1) polishing cleaning, honeycomb steel skeleton (2) is placed on steel plate (1)
Face, and will be welded between honeycomb steel skeleton (2) and steel plate (1) by welding machine；
Step 4, in step 3 between honeycomb steel skeleton (2) and steel plate (1) weld after the completion of, by honeycomb steel skeleton
(2) elastic adhesive is filled in the honeycomb on；
In step 5, honeycomb in step 4 after filling elastic adhesive, several pieces of ceramic blocks (3) are put in honeycomb, if
Dry block ceramic block (3) is bonded as one by elastic adhesive and honeycomb steel skeleton (2)；
Step 6, step 5 complete it is good after, composite liner that bonding is completed quickly is solidified by the modes such as heating or humidifying, i.e.,
Complete the manufacturing process of entire honeycomb ceramics composite liner.