CN108301613A - A method of manufacture clear-water concrete plank sheathing - Google Patents
A method of manufacture clear-water concrete plank sheathing Download PDFInfo
- Publication number
- CN108301613A CN108301613A CN201711178299.XA CN201711178299A CN108301613A CN 108301613 A CN108301613 A CN 108301613A CN 201711178299 A CN201711178299 A CN 201711178299A CN 108301613 A CN108301613 A CN 108301613A
- Authority
- CN
- China
- Prior art keywords
- putty
- ply board
- plank sheathing
- water concrete
- clear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A method of manufacture clear-water concrete plank sheathing is related to a kind of multi-face structure facing template for building, including step A：Plywood form is manufactured by the shape of pour mass；Step B：Several pieces of three-ply boards are fixed by way of white glue or rifle nail or the two unification and are tightly attached on plywood form face；Step C：The piece between three-ply board is subjected to joint filling processing by putty, grinding process then is carried out to three-ply board so that three-ply board rough surface；Step D：In three-ply board surface smear putty, grinding process is carried out to putty after putty is fully hardened so that putty surfacing is coarse；Step E：In putty external coating varnish, smooth bubble-free is wanted on varnish surface.This invention ensures that the globality of plank sheathing system, solves the technical barrier that concrete surface seam influences its exterior aesthetics.The uniformity that ensure that template surface properties solves the problems, such as that faced concrete surface appearance uniformity is poor.
Description
Technical field
The present invention relates to a kind of multi-face structure facing template for building, especially a kind of multi-face structure clear-water concrete
Plank sheathing.
Background technology
With the raising of the integral level of Building Trade in China, the rise of green building theory and people's environmental consciousness
It is promoted, clear-water concrete is increasingly valued by people, and more and more architectural designs use clear-water concrete.Clear water is mixed
Solidifying soil directly using the natural texture after concrete formation as finishing effect, with concrete it is inherent it is simple and unadorned,
Naturally sedate appearance charm, and clear-water concrete one-pass molding are not necessarily to secondary facing, reduce the secondary facing of concrete surface
The a large amount of building wastes brought.
For the clear-water concrete structure of regular shape, existing technical merit generally ensures that the appearance of clear-water concrete
Forming Quality.And for the more curved surface clear-water concrete structures in complex-shaped space, existing technical merit can't ensure it
Appearance Forming Quality.Under normal conditions, for more curved surface clear-water concrete structures, since steel form deformation performance is preferable, and table
Face is relatively smooth, and customization all-steel mold plate is typically preference.However the cost for customizing all-steel mold plate is usually higher, for shape list
One special structure, if it cannot be guaranteed that customization all-steel mold plate is used in turn rate, the construction cost of steel form will be very high.
Compared to steel form, the cost of plank sheathing wants much lower.However such as according to plank sheathing, template and concrete mortar when due to construction
It is in direct contact, plank is easy water suction and generates bulking, since the wooden spongiosa and the wooden compact substance degrees of expansion are different, can exist after template removing
Faced concrete surface leaves wood grain, influences the beauty of clear-water concrete.
Further for more curved surface clear-water concrete structures, either steel form or plank sheathing, it is required for splicing to complete more
Circular formwork, the piece between more circular formworks will form seam in faced concrete surface, and leave trace, eventually affect clear
The appearance Forming Quality of water coagulation soil.After ensureing concreting, in the unlikely stickup concrete of template surface and unsuitable
Form removal is needed under normal conditions in template surface brushing releasing agent, and currently used releasing agent is the releasing agent of liquid and powdery,
But releasing agent usually occurs leakage brush in painting process and brushes non-uniform phenomenon, the uneven or leakage of releasing agent brushing
Brush can cause the inhomogeneities of faced concrete surface Forming Quality, influence the aesthetics of its appearance.Due to clear-water concrete one
Secondary molding is not necessarily to secondary facing, therefore liquid or powdered releasing agent should not be as the releasing agents of clear-water concrete.
Invention content
This method is directed to deficiency in the prior art, provides a kind of method of manufacture clear-water concrete plank sheathing, this hair
It is bright to lead to brushing putty and varnish on plank sheathing, it ensure that the globality of plank sheathing system, solve concrete surface seam shadow
Ring the technical barrier of its exterior aesthetics.Simultaneously using the varnish after solidification as releasing agent, instead of traditional liquid or powdery
Releasing agent, ensure that the uniformity of template surface properties, solve the problems, such as that faced concrete surface appearance uniformity is poor, and is clear
Faced concrete surface will not be pasted and be polluted to paint, ensure that the appearance Forming Quality of clear-water concrete.This last plank sheathing is torn open
Mould is convenient, and cheap, solving previous steel template construction cost will be very high, shifts difficult problem.
In order to solve the above-mentioned technical problem, this method is addressed by following technical proposals：A kind of manufacture clear water coagulation
The method of building template, it is characterized in that including following steps, step A：Plywood form is manufactured by the shape of pour mass；
Step B：Several pieces of three-ply boards are fixed by way of white glue or rifle nail or the two unification and are tightly attached on plywood form face；
Step C：The piece between three-ply board is subjected to joint filling processing by putty, grinding process then is carried out to three-ply board so that three
Cleat surface is coarse；Step D：In three-ply board surface smear putty, grinding process is carried out to putty after putty is fully hardened, is made
It is coarse to obtain putty surfacing；Step E：In putty external coating varnish, smooth bubble-free is wanted on varnish surface.
In above-mentioned technical proposal, it is preferred that in stepb, plywood form external coating has white glue, three-ply board to stick white
It is followed closely by rifle after on glue and is fixed with plywood form again, wherein without hollowing between plywood form and three-ply board.
In above-mentioned technical proposal, it is preferred that in step C, before edge joint position carries out joint filling processing, it is necessary first to pass through sand
Paper carries out polishing to edge joint position and ensures the fastness pasted between putty and three-ply board.
In above-mentioned technical proposal, it is preferred that after the completion of edge joint position carries out joint filling, need to beat edge joint position by sand paper
Mill ensures that the flatness at joint filling is consistent with three-ply board.
In above-mentioned technical proposal, it is preferred that in step D, putty should be brushed uniformly, brushing thickness 0.3 mm ~
Between 0.5mm.
In above-mentioned technical proposal, it is preferred that in step E, the brushing parameter of varnish is two to three times.
In above-mentioned technical proposal, it is preferred that the varnish is novolaks.
In above-mentioned technical proposal, it is preferred that the putty is automobile putty.
The invention discloses a kind of clear-water concrete plank sheathing, three-ply board is followed closely by rifle and white glue is fixed and is tightly attached to glue
On plywood template face, by the paving three-ply board on plywood form face, the flatness of template system entirety and submissive is improved
Degree.Joint filling processing is carried out by piece of the automobile putty between three-ply board, further ensures the smooth of template system
Degree carries out grinding process to the three-ply board after having handled, keeps three-ply board face coarse, leads to brush vapour to three-ply board face by automobile putty
Vehicle putty, in its external coating varnish after automobile putty is fully hardened, varnish is as the isolation between plank sheathing and concrete
Layer.Varnish brushing pass is two to three times, and varnish should be brushed uniformly, and surface is answered smooth.Clear-water concrete is to template surface
Requirement it is very high, varnish is a kind of oily material, and varnish will not melt in water, has good water resistance, therefore clear
Paint plays protective effect to plank sheathing, can prevent plank sheathing from meeting water and deform.Varnish surface is very smooth, while varnish
After fully hardened, chemical stability is relatively good, will not be chemically reacted with concrete, also can avoid wooden model plate face and gets on the car
The pollution of putty and plank sheathing to concrete.The finish and flatness on last varnish surface ensure that the outer of clear-water concrete
See Forming Quality.
The present invention leads to brushing putty and varnish on plank sheathing, ensure that the globality of plank sheathing system, solves coagulation
Native face joint influences the technical barrier of its exterior aesthetics.Simultaneously using the varnish after solidification as releasing agent, instead of traditional
The releasing agent of liquid or powdery ensure that the uniformity of template surface properties, solve faced concrete surface appearance uniformity
The problem of difference, and faced concrete surface will not be pasted and be polluted to varnish, ensure that the appearance Forming Quality of clear-water concrete.Most
The form removal of this plank sheathing is convenient afterwards, and cheap, solving previous steel template construction cost will be very high, shifts difficult ask
Topic.
Description of the drawings
Fig. 1 is this method schematic diagram.
Specific implementation mode
This method is described in further detail with specific implementation mode below in conjunction with the accompanying drawings.
Embodiment one：As shown in Figure 1, a kind of method of manufacture clear-water concrete plank sheathing, including following steps, step
Rapid A：Plywood form 1 is manufactured by the shape of pour mass.Step B：Several pieces of three-ply boards 2 are fixed and are tightly attached to glued template die
On 1 face of plate.1 external coating of plywood form is followed closely and plywood form 1 by rifle again after having white glue, three-ply board 2 to stick on white glue
It is fixed, wherein without hollowing between plywood form 1 and three-ply board 2.
Step C：The piece between three-ply board 2 is subjected to joint filling processing by putty 3, is then polished three-ply board 2
Processing so that 2 rough surface of three-ply board.Before edge joint position carries out joint filling processing, it is necessary first to be carried out to edge joint position by sand paper
Polishing ensures the fastness pasted between putty 3 and three-ply board 2.After the completion of edge joint position carries out joint filling, need through sand paper to spelling
It polishes at seam, ensures that the flatness at joint filling is consistent with three-ply board.
Step D：In 2 surface smear putty 3 of three-ply board, grinding process is carried out to putty 3 after putty 3 is fully hardened, is made
It is coarse to obtain 3 surfacing of putty；Putty should be brushed uniformly, and brushing thickness is between 0.3 mm ~ 0.5mm.The putty 3 is
Automobile putty.
Step E：In 3 external coating varnish 4 of putty, smooth bubble-free is wanted on 4 surface of varnish.The brushing parameter of varnish 4 is two
To three times.The varnish 4 is novolaks.Varnish 4 should check the flatness and bubble on 4 surface of varnish after the completion of brushing,
If there is local defect, it should be handled,
A kind of clear-water concrete plank sheathing, including plywood form 1 are glued with three-ply board 2, institute on the plywood form 1
It is coated with putty 3 on the three-ply board 2 stated, varnish 4 is painted on the putty 3.
Claims (8)
1. a kind of method of manufacture clear-water concrete plank sheathing, it is characterized in that include following steps,
Step A：Plywood form is manufactured by the shape of pour mass；
Step B：Several pieces of three-ply boards are fixed by way of white glue or rifle nail or the two unification and are tightly attached to plywood form
On face；
Step C：The piece between three-ply board is subjected to joint filling processing by putty, grinding process then is carried out to three-ply board, is made
Obtain three-ply board rough surface；
Step D：In three-ply board surface smear putty, grinding process is carried out to putty after putty is fully hardened so that putty table
Face is smooth coarse；
Step E：In putty external coating varnish, smooth bubble-free is wanted on varnish surface.
2. a kind of method of manufacture clear-water concrete plank sheathing according to claim 1, it is characterized in that, in stepb, glue
Plywood template surface is painted with white glue, and three-ply board is followed closely again by rifle after sticking on white glue and fixed with plywood form, wherein glued
Without hollowing between template die plate and three-ply board.
3. a kind of method of manufacture clear-water concrete plank sheathing according to claim 1, it is characterized in that, in step C,
Before edge joint position carries out joint filling processing, it is necessary first to carry out polishing to edge joint position by sand paper and ensure to paste between putty and three-ply board
Fastness.
4. a kind of method of manufacture clear-water concrete plank sheathing according to claim 3, it is characterized in that, edge joint position is filled out
It after the completion of seam, needs to polish to edge joint position by sand paper, ensures that the flatness at joint filling is consistent with three-ply board.
5. a kind of method of manufacture clear-water concrete plank sheathing according to claim 1, it is characterized in that, it is in step D, greasy
Son should be brushed uniformly, and brushing thickness is between 0.3 mm ~ 0.5mm.
6. a kind of method of manufacture clear-water concrete plank sheathing according to claim 1, it is characterized in that, in step E, clearly
The brushing parameter of paint is two to three times.
7. a kind of method of manufacture clear-water concrete plank sheathing according to claim 1, it is characterized in that, the varnish is
Novolaks.
8. a kind of method of manufacture clear-water concrete plank sheathing according to claim 1, it is characterized in that, the putty is
Automobile putty.