KR102476749B1 - Cement-based composites and manufacturing the same - Google Patents
Cement-based composites and manufacturing the same Download PDFInfo
- Publication number
- KR102476749B1 KR102476749B1 KR1020220066889A KR20220066889A KR102476749B1 KR 102476749 B1 KR102476749 B1 KR 102476749B1 KR 1020220066889 A KR1020220066889 A KR 1020220066889A KR 20220066889 A KR20220066889 A KR 20220066889A KR 102476749 B1 KR102476749 B1 KR 102476749B1
- Authority
- KR
- South Korea
- Prior art keywords
- cement
- forming
- based material
- mortar
- different
- Prior art date
Abstract
Description
본 발명은 시멘트계 복합재에 관한 것으로서, 더욱 상세하게는, 시멘트계 모르타르 또는 콘크리트와 이종 재료를 포함하는 시멘트계 복합재 및 그 제조 방법에 관한 것이다.The present invention relates to a cement-based composite, and more particularly, to a cement-based composite including a cement-based mortar or concrete and a heterogeneous material, and a manufacturing method thereof.
토목, 건축의 각 공사에는 일반적인 시멘트로 포틀랜드 시멘트가 널리 사용되고 있다. 포틀랜드 시멘트는 물, 모래 등과 혼합되어 모르타르로 형성되거나, 또는 물, 모래, 자갈 등과 혼합되어 콘크리트로 형성될 수 있다. Portland cement is widely used as a general cement for civil engineering and construction works. Portland cement may be mixed with water, sand, etc. to form mortar, or mixed with water, sand, gravel, etc. to form concrete.
모르타르 또는 콘크리트는 제조 비용이 저렴하고 내구성과 표면 강도가 높다. 그러나, 건물 표면 등에 모르타르 또는 콘크리트가 단독으로 사용되는 경우에 색상과 질감이 단조롭고 특유의 유독성과 분진발생등의 문제 때문에 다양성과 친환경을 중시하는 현대의 건축에는 이와 같은 모르타르 또는 콘크리트 마감이 사용자들을 충분히 만족시키지 못하고 있다. Mortar or concrete is inexpensive to manufacture and has high durability and surface strength. However, when mortar or concrete is used alone on the surface of a building, the color and texture are monotonous, and because of problems such as toxicity and dust generation, such mortar or concrete finishes are sufficient for modern architecture that values diversity and eco-friendliness. not satisfying
본 발명은 상술한 종래 기술의 문제점을 해결하기 위한 것으로, 시멘트계 재료 표면이 다양한 패턴과 자연특유의 색상 및 질감을 나타낼 수 있는 시멘트계 복합재의 제조, 시공 방법 및 그 제조 방법에 의해 제조된 시멘트계 복합재를 제공하는 것을 목적으로 한다.The present invention is to solve the problems of the prior art described above, and to provide a method for manufacturing and constructing a cement-based composite material in which the surface of the cement-based material can exhibit various patterns and unique colors and textures, and a cement-based composite material manufactured by the manufacturing method. intended to provide
상술한 과제를 해결하기 위한 수단으로서, 본 발명의 일 실시예에 따른 시멘트계 복합재의 제조 방법은, 콘크리트 또는 모르타르를 포함하는 시멘트계 재료를 형성하는 시멘트계 재료 형성 단계; 및 상기 시멘트계 재료 상에 상기 시멘트계 재료와 상이한 이종 재료를 포함하는 이종 재료층을 형성하는 이종 재료층 형성 단계를 포함할 수 있다. As a means for solving the above problems, a method for manufacturing a cement-based composite material according to an embodiment of the present invention includes a cement-based material forming step of forming a cement-based material including concrete or mortar; and forming a different material layer comprising a different material different from the cement-based material on the cement-based material.
일 실시예에서, 상기 이종 재료층이 형성된 표면에 대하여 폴리싱 처리를 수행하는 단계를 더 포함할 수 있다. 상기 이종 재료는 자개, 패각, 대모, 상아 및 나무 중 하나 이상을 포함할 수 있다. In one embodiment, the method may further include performing a polishing process on the surface on which the different material layer is formed. The heterogeneous material may include one or more of mother-of-pearl, shell, tortoiseshell, ivory, and wood.
일 실시예에서, 옻 또는 투명 도장 재료를 포함하는 도장층을 형성하는 도장층 형성 단계를 더 포함할 수 있다. In one embodiment, a coating layer forming step of forming a coating layer including lacquer or a transparent coating material may be further included.
일 실시예에서, 상기 이종 재료층 형성 단계는, 상기 시멘트계 재료의 표면을 폴리싱 처리하여 평활한 상태로 조성하는 단계; 상기 이종 재료를 도안에 따라 접착제를 이용하여 상기 시멘트계 재료에 부착하는 단계; 및 부착된 상기 이종 재료가 묻히도록 시멘트 모르타르를 타설하는 단계를 포함할 수 있다. In one embodiment, the forming of the heterogeneous material layer may include polishing a surface of the cement-based material to make it smooth; attaching the dissimilar material to the cement-based material using an adhesive according to the pattern; and pouring cement mortar so that the attached heterogeneous materials are buried.
일 실시예에서, 상기 이종 재료층 형성 단계는, 상기 이종 재료를 상기 시멘트계 재료의 성형을 위하여 제작된 성형틀의 바닥에 도안에 따라 접착제를 이용하여 부착하는 단계를 포함하고, 상기 시멘트계 재료 형성 단계는, 상기 이종 재료가 부착된 성형틀에 상기 시멘트계 재료를 타설하고, 상기 시멘트게 재료의 양생후에 성형틀을 제거하는 단계를 포함할 수 있다. In one embodiment, the step of forming the heterogeneous material layer includes attaching the heterogeneous material to the bottom of a molding mold manufactured for molding the cement-based material using an adhesive according to a pattern, and the step of forming the cement-based material The step of pouring the cement-based material into the mold to which the heterogeneous material is attached, and removing the mold after curing the cement material.
일 실시예에서, 상기 이종 재료층 형성 단계는, 도안에 따라 상기 시멘트계 재료의 표면을 음각하는 단계; 상기 이종 재료를 모르타르 또는 투명 유기 수지 도료와 혼합 및 교반하여 충진 재료를 생성하는 단계; 및 상기 충진 재료를 상기 시멘트계 재료의 표면의 음각부에 충진하는 단계를 포함할 수 있다. In one embodiment, the forming of the heterogeneous material layer may include engraving the surface of the cement-based material according to a pattern; mixing and stirring the heterogeneous material with mortar or a transparent organic resin paint to create a filling material; and filling the concave portion of the surface of the cement-based material with the filling material.
일 실시예에서, 상기 이종 재료층 형성 단계는, 수용성 수지를 모르타르 분말과 섞은 바탕 고름용 모르타르를 기준 마감 레벨에 맞춰서 소정 두께로 시공면에 형성하는 단계; 및 상기 이종 재료를 상기 바탕 고름용 모르타르의 형성면에 고정시키는 단계를 포함하고, 상기 시멘트계 재료 형성 단계는, 기준 레벨에 맞춰서 상기 시멘트계 재료를 시공면에 타설하고, 미장마감하는 단계를 포함할 수 있다. In one embodiment, the step of forming the heterogeneous material layer may include forming a mortar for ground filling in which a water-soluble resin is mixed with mortar powder to a predetermined thickness according to a standard finish level on the construction surface; and a step of fixing the different material to the surface on which the mortar for the base mortar is formed, wherein the step of forming the cement-based material may include a step of pouring the cement-based material on the construction surface according to a standard level and finishing with plastering. have.
상술한 과제를 해결하기 위한 다른 수단으로서, 본 발명의 일 실시예에 따른 시멘트계 복합재는, 상기 시멘트계 복합재의 제조 방법에 의해 제조된 시멘트계 복합재로서, 콘크리트 또는 모르타르를 포함하는 시멘트계 재료층; 및 상기 시멘트계 재료층 상에 형성되고, 콘크리트 또는 모르타르와 상이한 이종 재료를 포함하는 이종 재료층을 구비할 수 있다. As another means for solving the above problems, a cement-based composite material according to an embodiment of the present invention is a cement-based composite material prepared by the method for manufacturing a cement-based composite material, comprising: a cement-based material layer including concrete or mortar; and a heterogeneous material layer formed on the cement-based material layer and including a heterogeneous material different from concrete or mortar.
본 발명의 실시예에 따르면, 콘크리트 또는 모르타르를 포함하는 시멘트계 재료를 형성하고, 시멘트계 재료 상에 시멘트계 재료와 상이한 이종 재료를 포함하는 이종 재료층을 형성함으로써, 시멘트계 재료 표면이 다양한 색상 및 질감을 나타낼 수 있는 시멘트계 복합재의 제조 방법 및 그 제조 방법에 의해 제조된 시멘트계 복합재가 제공될 수 있다.According to an embodiment of the present invention, by forming a cement-based material including concrete or mortar and forming a heterogeneous material layer including a different material different from the cement-based material on the cement-based material, the surface of the cement-based material may exhibit various colors and textures. A method for manufacturing a cement-based composite material that can be manufactured and a cement-based composite material manufactured by the manufacturing method may be provided.
도 1은 본 발명의 일 실시예에 따른 시멘트계 복합재의 제조 방법의 흐름도이다.
도 2는 본 발명의 일 실시예에 따른 시멘트계 복합재의 제조 방법(함침법)의 흐름을 나타내는 도면이다.
도 3은 도 2의 시멘트계 복합재의 제조 방법(함침법)에 의해 제조된 시멘트계 복합재의 시제품 사진을 나타내는 도면이다.
도 4은 본 발명의 일 실시예에 따른 시멘트계 복합재의 제조 방법(타설법)의 흐름을 나타내는 도면이다.
도 5는 도 4의 시멘트계 복합재의 제조 방법(타설법)에 의해 제조된 시멘트계 복합재의 시제품 사진을 나타내는 도면이다.
도 6는 본 발명의 일 실시예에 따른 시멘트계 복합재의 제조 방법(상감법)의 흐름을 나타내는 도면이다.
도 7은 도 6의 시멘트계 복합재의 제조 방법(상감법)에 의해 제조된 시멘트계 복합재의 시제품 사진(벽면부)을 나타내는 도면이다.
도 8는 본 발명의 일 실시예에 따른 시멘트계 복합재의 제조 방법(고정법)의 흐름을 나타내는 도면이다.
도 9은 도 8의 시멘트계 복합재의 제조 방법(고정법)에 의해 제조된 시멘트계 복합재의 렌더링 이미지을 나타내는 도면이다.
도 10은 본 발명의 일 실시예에 따른 흑화 형상 방지를 위한 전처리의 효과를 나타내는 사진이다.1 is a flowchart of a method for manufacturing a cement-based composite material according to an embodiment of the present invention.
2 is a view showing the flow of a method (impregnation method) for manufacturing a cement-based composite material according to an embodiment of the present invention.
FIG. 3 is a view showing a photograph of a prototype of a cement-based composite material manufactured by the manufacturing method (impregnation method) of the cement-based composite material of FIG. 2 .
4 is a view showing the flow of a manufacturing method (placing method) of a cement-based composite material according to an embodiment of the present invention.
5 is a view showing a photograph of a prototype of a cement-based composite material manufactured by the manufacturing method (placing method) of the cement-based composite material of FIG. 4 .
6 is a view showing the flow of a method (damascene method) for manufacturing a cement-based composite material according to an embodiment of the present invention.
FIG. 7 is a view showing a photograph (wall surface portion) of a cement-based composite material manufactured by the manufacturing method (damascene method) of the cement-based composite material of FIG. 6 .
8 is a view showing the flow of a method (fixation method) for manufacturing a cement-based composite according to an embodiment of the present invention.
FIG. 9 is a view showing a rendered image of a cement-based composite material manufactured by the manufacturing method (fixation method) of FIG. 8 .
10 is a photograph showing the effect of pretreatment for preventing blackening according to an embodiment of the present invention.
이하, 첨부된 도면을 참조하여 본 발명의 바람직한 실시예를 상세히 설명하기로 한다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.
본 발명에서 사용되는 용어는 본 발명에서의 기능을 고려하면서 가능한 현재 널리 사용되는 일반적인 용어들을 선택하였으나, 이는 당 분야에 종사하는 기술자의 의도 또는 판례, 새로운 기술의 출현 등에 따라 달라질 수 있다. 또한, 특정한 경우는 출원인이 임의로 선정한 용어도 있으며, 이 경우 해당되는 발명의 설명 부분에서 상세히 그 의미를 기재할 것이다. 따라서 본 발명에서 사용되는 용어는 단순한 용어의 명칭이 아닌, 그 용어가 가지는 의미와 본 발명의 전반에 걸친 내용을 토대로 정의되어야 한다The terms used in the present invention have been selected from general terms that are currently widely used as much as possible while considering the functions in the present invention, but these may vary depending on the intention of a person skilled in the art or precedent, the emergence of new technologies, and the like. In addition, in a specific case, there is also a term arbitrarily selected by the applicant, and in this case, the meaning will be described in detail in the description of the invention. Therefore, the term used in the present invention should be defined based on the meaning of the term and the overall content of the present invention, not simply the name of the term.
명세서 전체에서 어떤 부분이 어떤 구성요소를 "포함"한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성요소를 제외하는 것이 아니라 다른 구성요소를 더 포함할 수 있음을 의미한다. When it is said that a certain part "includes" a certain component throughout the specification, it means that it may further include other components without excluding other components unless otherwise stated.
아래에서는 첨부한 도면을 참고하여 본 발명의 실시예에 대하여 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다. Hereinafter, with reference to the accompanying drawings, embodiments of the present invention will be described in detail so that those skilled in the art can easily carry out the present invention. However, the present invention may be embodied in many different forms and is not limited to the embodiments described herein.
도 1은 본 발명의 일 실시예에 따른 시멘트계 복합재의 제조 방법의 흐름도이다.1 is a flowchart of a method for manufacturing a cement-based composite material according to an embodiment of the present invention.
도 1을 참조하면, 시멘트계 복합재의 제조 방법은 시멘트계 재료 형성 단계(S110), 이종 재료층 형성 단계(S120), 폴리싱(연마광택) 단계(S130) 및 도장층 형성 단계(S140)를 포함할 수 있다. Referring to FIG. 1 , the method for manufacturing a cement-based composite material may include forming a cement-based material (S110), forming a heterogeneous material layer (S120), polishing (polishing) step (S130), and forming a paint layer (S140). have.
시멘트계 재료 형성 단계(S110)에서는 콘크리트 또는 모르타르를 포함하는 시멘트계 재료를 형성할 수 있다. 이종 재료층 형성 단계(S120)에서는 시멘트계 재료 상에 이종 재료를 포함하는 이종 재료층을 형성할 수 있다. 이종 재료는 자개, 패각, 대모(바다거북과의 동물인 대모의 등과 배를 싸고 있는 껍데기), 상아 및 나무 중 하나 이상을 포함할 수 있다.In the cement-based material forming step ( S110 ), a cement-based material including concrete or mortar may be formed. In the step of forming the different material layer ( S120 ), a different material layer including a different material may be formed on the cement-based material. The heterogeneous material may include one or more of mother-of-pearl, shell, hawksbill (a shell covering the back and belly of a hawksbill, an animal of the sea turtle family), ivory, and wood.
시멘트계 재료 형성 단계(S110)가 이종 재료층 형성 단계(S120) 보다 먼저 수행될 수도 있고, 이종 재료층 형성 단계(S120)가 시멘트계 재료 형성 단계(S110) 보다 먼저 수행될 수도 있다. The step of forming the cement-based material (S110) may be performed before the step of forming the different material layer (S120), or the step of forming the different material layer (S120) may be performed before the step of forming the cement-based material (S110).
폴리싱 단계(S130)에서는 이종 재료층이 형성된 표면에 대하여 폴리싱 처리를 수행할 수 있다. 폴리싱 처리는 콘크리트 또는 시멘트 모르타르가 완전히 양생된 후에 이종 재료층이 형성된 표면에 대하여 수행될 수 있다. In the polishing step ( S130 ), a polishing process may be performed on the surface on which the different material layer is formed. The polishing treatment may be performed on the surface on which the heterogeneous material layer is formed after the concrete or cement mortar has completely cured.
도장층 형성 단계(S140)는 옻 또는 투명 도장 재료(상도 도장재)를 1회 이상 폴리싱 후의 이종 재료층 표면에 도포할 수 있다. 도장 재료는 붓, 롤러, 에어스프레이 또는 에어리스스프레이 등의 도구를 이용하여 도장면에 도포될 수 있다. In the coating layer forming step (S140), lacquer or a transparent coating material (top coating material) may be applied to the surface of the different material layer after polishing one or more times. The painting material may be applied to the painted surface using a tool such as a brush, roller, air spray or airless spray.
일 실시예에서, 도장층 형성 단계(S140)는 시멘트계 재료의 표면을 전처리한 후에 옻칠 마감을 수행할 수 있다. 표면 전처리는 옻칠의 흑화 현상을 방지하도록 알칼리 규산염을 포함하는 조성물을 시멘트계 재료에 도포하는 처리를 포함할 수 있다. In one embodiment, the coating layer forming step (S140) may perform a lacquer finish after pre-treating the surface of the cement-based material. The surface pretreatment may include a treatment of applying a composition containing an alkali silicate to the cement-based material to prevent blackening of the lacquer.
통상적인 콘크리트, 모르타르의 양생 후에 원 상태의 표면에 옻칠을 하는 경우에 시멘트 내부의 잔여 수분과 옻이 반응하여 옻칠이 검게 타는 흑화 현상이 나타날 수 있다. 이러한 흑화 현상을 방지하기 위하여, 본 발명에서는 콘크리트와 모르타르의 표면에 알칼리 규산염이 주성분인 액상을 시멘트 표면에 도포하여 수산화칼슘과 반응시켜 공극내에 불용성염인 칼슘실리케이트를 생성하여 옻칠로 인한 흑화 현상을 방지하며, 옻칠 특유의 투명한 담황색 마감을 구현할 수 있다. When lacquer is applied to the original surface after normal concrete and mortar curing, a blackening phenomenon in which the lacquer is burned black may occur due to the reaction of the lacquer with the remaining moisture inside the cement. In order to prevent this blackening phenomenon, in the present invention, a liquid phase containing alkali silicate as the main component is applied to the surface of concrete and mortar on the surface of cement and reacts with calcium hydroxide to form calcium silicate, an insoluble salt in the pores. Prevents blackening caused by lacquer It can realize the unique transparent pale yellow finish of lacquer.
[화학식][chemical formula]
알칼리 규산염을 이용하여 표면 전처리는 이하에서 설명하는 순서로 수행될 수 있다. 먼저, 양생이 충분히 경과된 콘크리트, 모르타르의 표면(바닥, 벽체)을 고르게 연삭하여 평활도를 높인다. 이 때, 방수 합판 등으로 매끄럽게 마감된 표면은 세라믹, 메탈 패드 등을 이용하여 폴리싱한다. 마감 패드 연삭 전 알칼리 규사염액을 충분히 도포하여 표면에 고이지 않도록 뿌린다. 충분히 경화후, 남아 있는 생성물을 긁어내거나 갈아낸다. Surface pretreatment using an alkali silicate may be performed in the order described below. First, evenly grind the surface (floor, wall) of concrete and mortar where curing has sufficiently elapsed to increase smoothness. At this time, the surface finished smoothly with waterproof plywood or the like is polished using ceramic or metal pads. Before grinding the finishing pad, apply enough alkali silicate solution and spray it so that it does not pool on the surface. After sufficient curing, the remaining product is scraped off or ground.
세라믹 패드 기준 #400~#1200 정도로 폴리싱한다. 설계 내용에 따라서는 폴리싱을 수행하지 않고 그대로 마감할 수 있다. 패드 작업 후 정제된 옻칠을 그 용도와 사양에 따라 3회 이상(예를 들면, 9회) 도포한다. 옻칠 도장 후 재도장시에는 표면을 사포질한 후에 제작하고, 마지막으로 광택 작업을 수행한다. Polish to #400~#1200 based on ceramic pad. Depending on the design content, it may be finished as is without performing polishing. After the pad work, the refined lacquer is applied three or more times (for example, nine times) depending on the purpose and specifications. When re-coating after lacquer painting, the surface is sanded, and finally polished.
본 발명의 시멘트계 재료의 표면 전처리에 의하면, 옻칠의 특성 중 수분과 반응하면 검게 변하는 흑화 현상을 방지하여, 그 특유의 미려한 투명의 담황색의 마감을 만들 수 있으며, 기존의 유기계 투명 도료와는 전혀 다른 친환경적이며 위생적인 마감이 가능하다. According to the surface pretreatment of the cement-based material of the present invention, the blackening phenomenon, which turns black when reacted with moisture, among the characteristics of lacquer, can be prevented to create a unique and beautiful transparent pale yellow finish, completely different from conventional organic transparent paints. An eco-friendly and hygienic finish is possible.
도 2는 본 발명의 일 실시예에 따른 시멘트계 복합재의 제조 방법(함침법)의 흐름을 나타내는 도면이다.2 is a view showing the flow of a method (impregnation method) for manufacturing a cement-based composite material according to an embodiment of the present invention.
콘크리트 또는 모르타르를 포함하는 시멘트계 재료를 이용하여 시멘트계 재료층을 형성하고, 양생후에 시멘트계 재료층의 표면을 연마처리하여 평활한 상태로 조성한다. 준비된 자개, 패각, 대모, 상아 등의 이종 재료를 사전에 준비된 도안에 따라 접착제를 이용하여 부착한다. 일 실시예에서, 자개, 패각, 대모, 상아 등의 이종 재료는 2 mm ~ 3 mm 범위의 두께를 가질 수 있다. A cement-based material layer is formed using a cement-based material including concrete or mortar, and after curing, the surface of the cement-based material layer is polished to make it smooth. Prepared mother-of-pearl, shell, godmother, ivory, etc., are attached using adhesive according to a previously prepared pattern. In one embodiment, the heterogeneous material such as mother-of-pearl, shell, mother-of-pearl, ivory, etc. may have a thickness ranging from 2 mm to 3 mm.
자개, 패각, 대모, 상아 등의 이종 재료는 그대로 사용할 수도 있고, 부착후에 고무 망치 등으로 두드려 깨트려서 사용할 수도 있다. Dissimilar materials such as mother-of-pearl, shell, tortoiseshell, and ivory may be used as they are, or may be used after being attached and then broken by beating with a rubber mallet or the like.
부착물이 충분히 경화된 후, 시멘트계 모르타르로 부착물을 2 mm 내외가 함침되도록 타설 마감한다. 시멘트 모르타르가 완전히 양생된 후, 폴리싱 처리를 수행한다. 폴리싱 처리시에는 기존 부착물의 손상에 주의한다. After the attachment is sufficiently hardened, pour and finish the attachment with cement-based mortar so that the attachment is impregnated around 2 mm. After the cement mortar is fully cured, a polishing treatment is performed. When polishing, pay attention to damage to existing attachments.
설계된 명도의 광택 작업이 끝난 후에 보완 작업을 수행한다. 보완 작업은 탈락부, 광택 부족 부위 등에 대하여 수행될 수 있다. 그 후, 옻칠 또는 지정된 상도 도장재를 1회 이상(2~3회) 도포한다. 도 2의 시멘트계 복합재의 제조 방법(함침법)은 바닥 또는 벽체에 사용하기 적합한 방식이다. Complementary work is performed after the polishing of the designed brightness is finished. Complementary work may be performed on a missing part, a part lacking luster, and the like. After that, apply lacquer or a designated top coat one or more times (2 to 3 times). The manufacturing method (impregnation method) of the cement-based composite of FIG. 2 is suitable for use in floors or walls.
도 3은 도 2의 시멘트계 복합재의 제조 방법(함침법)에 의해 제조된 시멘트계 복합재의 시제품 사진을 나타내는 도면이다.FIG. 3 is a view showing a photograph of a prototype of a cement-based composite material manufactured by the manufacturing method (impregnation method) of the cement-based composite material of FIG. 2 .
도 3의 (a)는 시멘트계 재료의 표면을 나타낸다. 도 3의 (b)는 시멘트계 재료의 표면에 자개 등의 이종 재료를 도안에 맞춰 부착한 것이다. 도 3의 (c)는 이종 재료가 묻히도록 시멘트 모르타르를 타설하고, 폴리싱 처리를 수행한 사진이다. 도 3의 (d)는 폴리싱 처리를 수행한 표면에 옻칠을 1회 수행한 사진이고, 도 3의 (e)는 옻칠을 2회 수행한 사진이며, 도 3의 (f)는 옻칠을 3회 수행한 사진이다. Figure 3 (a) shows the surface of the cement-based material. 3(b) shows that different materials such as mother-of-pearl are attached to the surface of the cement-based material according to the pattern. (c) of FIG. 3 is a photograph of cement mortar being poured so that different materials are buried and polishing treatment performed. Figure 3 (d) is a photograph of performing lacquer once on the polished surface, Figure 3 (e) is a photograph of performing lacquer twice, Figure 3 (f) is a photograph of lacquer three times This is a photo done.
도 4은 본 발명의 일 실시예에 따른 시멘트계 복합재의 제조 방법(타설법)의 흐름을 나타내는 도면이다.4 is a view showing the flow of a manufacturing method (placing method) of a cement-based composite material according to an embodiment of the present invention.
콘크리트, 모르타르를 성형하기 위한 성형틀을 제작하고(이형제 도포 및 실링 작업), 준비된 2~3mm 두께의 자개, 패각, 대모, 상아 등을 사전에 준비된 도안에 따라 접착제를 이용하여 성형틀의 바닥에 단단히 부착한다. 자개, 패각 등을 그대로 사용할 수도 있고, 분쇄된 자개 또는 패각을 접착제가 부착된 표면에 부리는 방식으로 사용될 수도 있다. A mold for molding concrete and mortar is manufactured (release agent application and sealing work), and prepared mother-of-pearl, shell, tortoiseshell, ivory, etc. with a thickness of 2 to 3 mm are attached to the bottom of the mold using an adhesive according to a previously prepared pattern. Attach firmly. Mother-of-pearl, shells, etc. may be used as they are, or may be used in a manner in which pulverized mother-of-pearl or shells are applied to the surface to which the adhesive is attached.
부착물이 충분히 경화된 후에 콘크리트 또는 시멘트계 모르타르를 설계 두께로 타설 마감한다. 시멘트 모르타르가 완전히 양생된 후, 성형틀을 제거한 후에 표면을 폴리싱 마감한다. 그 후에, 설계된 명도의 광택 작업이 끝난 후 보완 작업을 실시한다. 보완 작업 후에 옻칠 또는 지정된 상도 도장재를 순서에 따라 2~3회 도포한다. 도 4의 시멘트계 복합재의 제조 방법(타설법)은 식탁의 상판 등과 같이 상판 제작에 적합한 방식이다. After the attachment is sufficiently hardened, concrete or cement-based mortar is poured and finished to the design thickness. After the cement mortar is completely cured, the mold is removed and the surface is polished. After that, a supplementary work is performed after the polishing work of the designed brightness is finished. After supplementary work, apply lacquer or designated top coat 2-3 times in order. The manufacturing method (casting method) of the cement-based composite of FIG. 4 is suitable for manufacturing a top plate, such as a table top plate.
도 5는 도 4의 시멘트계 복합재의 제조 방법(타설법)에 의해 제조된 시멘트계 복합재의 시제품 사진을 나타내는 도면이다. 욕조의 성형틀에 고래 모양의 자개 조각을 접착제를 이용하여 부착시킨 후, 시멘트 모르타르를 타설한 후에, 폴리싱 및 옷칠을 수행하면 도 5에 도시된 품위있고 예술적인 욕조를 제조할 수 있다. 5 is a view showing a photograph of a prototype of a cement-based composite material manufactured by the manufacturing method (placing method) of the cement-based composite material of FIG. 4 . An elegant and artistic bathtub shown in FIG. 5 can be manufactured by attaching the whale-shaped mother-of-pearl pieces to the mold of the bathtub using an adhesive, pouring cement mortar, and then performing polishing and lacquering.
도 6는 본 발명의 일 실시예에 따른 시멘트계 복합재의 제조 방법(상감법)의 흐름을 나타내는 도면이다.6 is a view showing the flow of a method (damascene method) for manufacturing a cement-based composite material according to an embodiment of the present invention.
상감법은 기존의 사용중인 슬라브에 적용이 가능한 방식이다. 기존의 마감재를 제거한 후, 바닥과 벽체의 오염 물질을 제거하고, 평탄 작업을 수행한다. 사전에 정해진 도안과 패턴에 따라 5mm 이상 음각을 형성한다. 이때 도안의 공동부(넓은 부분)는 평삭 작업을 수행한다. The inlaid method is a method that can be applied to existing slabs in use. After removing the existing finishing materials, remove contaminants from the floor and walls, and perform leveling work. Form an intaglio of 5 mm or more according to a pre-determined design and pattern. At this time, the cavity (wide part) of the pattern is planarized.
시멘트 모르타르(또는 투명 유기수지도료)와 칩 상태의 자개(또는 패각 등)와 일정한 비율로 충분히 섞이도록 교반하여 충진 재료를 제조한다. 음각과 평삭으로 제거된 부분에 충진 재료를 이용하여 충진 또는 미장 미감한다. 충진 재료가 완전히 양생된 후 폴리싱 작업을 수행한다. 설계된 명도의 광택 작업이 끝난 후에 보완 작업을 수행하고, 옻칠 또는 지정된 상도 도장재를 순서에 따라 2~3회 도포한다. Filling material is prepared by mixing cement mortar (or transparent organic resin paint) and chipped mother-of-pearl (or shell, etc.) in a constant ratio. Fill or plaster the parts removed by intaglio and planing using filling materials. The polishing operation is performed after the filling material is completely cured. After finishing the polishing of the designed brightness, perform supplementary work, and apply lacquer or designated top coat 2-3 times in order.
도 7은 도 6의 시멘트계 복합재의 제조 방법(상감법)에 의해 제조된 시멘트계 복합재의 시제품 사진(벽면부)을 나타내는 도면이다. 벽체에 상감법에 의해 시멘트계 복합재를 형성하면 도 7에 도시된 바와 같이 미감이 뛰어난 벽체를 얻을 수 있다.FIG. 7 is a view showing a photograph (wall surface portion) of a cement-based composite material manufactured by the manufacturing method (damascene method) of the cement-based composite material of FIG. 6 . When a cement-based composite is formed on a wall by the inlaid method, a wall with excellent aesthetics can be obtained as shown in FIG. 7 .
도 8는 본 발명의 일 실시예에 따른 시멘트계 복합재의 제조 방법(고정법)의 흐름을 나타내는 도면이다.8 is a view showing the flow of a manufacturing method (fixing method) of a cement-based composite material according to an embodiment of the present invention.
고정법은 패각을 이용한 마감 기법에 적합한 방식이다. 50mm 이상의 바닥 마감 공사시에 적용 가능한 기법이며, 바탕 고름 모르타르 공법을 적용한다.The fixation method is suitable for the finishing technique using shells. This is a technique that can be applied in the case of floor finishing work of 50mm or more, and the base solid mortar method is applied.
패각이나 두꺼운 자개판을 에폭시 등의 수지를 모르타르 분말과 섞은 바탕 고름용 모르타르를 이용하여 기준 마감 레벨에 맞춰 바닥이나 벽에 고정시킨다. 그 후, 기준 레벨에 맞춰 콘크리트 또는 모르타르를 타설하고 미장 마감한다. The shells or thick mother-of-pearl plates are fixed to the floor or wall according to the standard finish level using mortar for base filling, which is a mixture of resin such as epoxy and mortar powder. After that, concrete or mortar is poured according to the standard level and plastering is finished.
충분히 양생된 상태의 바닥 표면을 연마기를 사용하여 패각이나 자재의 원형(링) 모습이 나오도록 연마하고 단계에 따라 폴리싱 작업으로 마무리한다. 그 후, 설계된 명도의 광택 작업이 끝난 후 보완 작업을 수행하고, 옻칠 또는 지정된 상도 도장재를 순서에 따라 2~3회 도포한다. The floor surface in a sufficiently cured state is polished using a grinder to form a circular (ring) shape of shell or material, and is finished with polishing according to the steps. Then, after the polishing of the designed brightness is completed, supplementary work is performed, and lacquer or designated top coat is applied 2 to 3 times in order.
도 9은 도 8의 시멘트계 복합재의 제조 방법(고정법)에 의해 제조된 시멘트계 복합재의 렌더링 이미지을 나타내는 도면이다. 바닥에 고정법에 의해 시멘트계 복합재를 형성하면 도 9에 도시된 바와 같이 예술성과 미감이 뛰어난 바닥을 얻을 수 있다.FIG. 9 is a view showing a rendered image of a cement-based composite material manufactured by the manufacturing method (fixation method) of FIG. 8 . When the cement-based composite is formed by the fixing method on the floor, as shown in FIG. 9, a floor with excellent artistry and aesthetics can be obtained.
도 10은 본 발명의 일 실시예에 따른 흑화 형상 방지를 위한 전처리의 효과를 나타내는 사진이다. 10 is a photograph showing the effect of pretreatment for preventing blackening according to an embodiment of the present invention.
도 10의 (a)는 시멘트계 재료층의 타설 및 양생 완료후의 사진이다. 도 10의 (b)는 시멘트계 재료층에 전처리를 수행하지 않고 옻칠을 3회 도포한 후의 사진이다. 도 10의 (b)에서는 시멘트 내부의 잔여 수분과 옻칠이 반응하여 흑화 현상이 나타나는 것을 알 수 있다. Figure 10 (a) is a photograph after completion of casting and curing of the cement-based material layer. Figure 10 (b) is a photograph after applying lacquer three times without performing pretreatment on the cement-based material layer. In (b) of FIG. 10, it can be seen that the remaining moisture inside the cement reacts with the lacquer, resulting in blackening.
도 10의 (c)는 시멘트계 재료층에 흑화 현상 방지를 위한 전처리를 수행한 후에 옻칠을 3회 도포한 후의 사진이다. 도 10의 (d)는 옻칠 특유의 담황색 마감 색상이 나타나는 시멘트계 복합재의 표면의 사진이다. 도 10의 (c) 및 (d)에서는 전처리에 의해 흑화 현상이 나타나지 않고, 옻칠 특유의 담황색 마감 색상이 나타나는 것을 파악할 수 있다.10(c) is a photograph after applying lacquer three times after performing a pretreatment for preventing blackening on a cement-based material layer. 10 (d) is a photograph of the surface of a cement-based composite material showing a light yellow finish color unique to lacquer. In (c) and (d) of FIG. 10 , it can be seen that the pretreatment does not cause blackening, and a light yellow finish color peculiar to lacquer appears.
Claims (9)
상기 시멘트계 재료 상에 상기 시멘트계 재료와 상이한 이종 재료를 포함하는 이종 재료층을 형성하는 이종 재료층 형성 단계; 및
상기 이종 재료층이 형성된 상기 시멘트계 재료의 표면에 대하여 알칼리 규산염을 포함하는 조성물을 이용하여 표면 전처리를 수행하는 표면 전처리 단계; 및
표면 전처리가 수행된 상기 시멘트계 재료의 표면에 옻을 포함하는 도장 재료를 1회 또는 복수회 도포하는 도장층 형성 단계
를 포함하고,
상기 이종 재료층 형성 단계는,
상기 시멘트계 재료의 표면을 폴리싱 처리하여 평활한 상태로 조성하는 단계;
상기 이종 재료를 도안에 따라 접착제를 이용하여 상기 시멘트계 재료에 부착하는 단계; 및
부착된 상기 이종 재료가 묻히도록 시멘트 모르타르를 타설하는 단계
를 포함하는 시멘트계 복합재의 제조 방법.A cement-based material forming step of forming a cement-based material including concrete or mortar;
forming a different material layer comprising a different material different from the cement-based material on the cement-based material; and
a surface pretreatment step of performing surface pretreatment using a composition containing an alkali silicate on the surface of the cement-based material on which the heterogeneous material layer is formed; and
A coating layer forming step of applying a coating material containing lacquer once or multiple times to the surface of the cement-based material on which the surface pretreatment has been performed
including,
In the step of forming the heterogeneous material layer,
Polishing the surface of the cement-based material to make it smooth;
attaching the dissimilar material to the cement-based material using an adhesive according to the pattern; and
Placing cement mortar so that the attached heterogeneous material is buried
Method for producing a cement-based composite comprising a.
상기 이종 재료층 상에 콘크리트 또는 모르타르를 포함하는 시멘트계 재료를 형성하는 시멘트계 재료 형성 단계; 및
상기 이종 재료층이 형성된 상기 시멘트계 재료의 표면에 대하여 알칼리 규산염을 포함하는 조성물을 이용하여 표면 전처리를 수행하는 표면 전처리 단계; 및
표면 전처리가 수행된 상기 시멘트계 재료의 표면에 옻을 포함하는 도장 재료를 1회 또는 복수회 도포하는 도장층 형성 단계
를 포함하고,
상기 이종 재료층 형성 단계는, 상기 이종 재료를 상기 시멘트계 재료의 성형을 위하여 제작된 성형틀의 바닥에 도안에 따라 접착제를 이용하여 부착하는 단계를 포함하고,
상기 시멘트계 재료 형성 단계는, 상기 이종 재료가 부착된 성형틀에 상기 시멘트계 재료를 타설하고, 상기 시멘트계 재료의 양생후에 성형틀을 제거하는 단계를 포함하는 시멘트계 복합재의 제조 방법.a different material layer forming step of forming a different material layer comprising a different material different from the cement-based material;
a cement-based material forming step of forming a cement-based material including concrete or mortar on the heterogeneous material layer; and
a surface pretreatment step of performing surface pretreatment using a composition containing an alkali silicate on the surface of the cement-based material on which the heterogeneous material layer is formed; and
A coating layer forming step of applying a coating material containing lacquer once or multiple times to the surface of the cement-based material on which the surface pretreatment has been performed
including,
The step of forming the heterogeneous material layer includes attaching the heterogeneous material to the bottom of a mold manufactured for molding the cement-based material using an adhesive according to a pattern,
The step of forming the cement-based material comprises pouring the cement-based material into a mold to which the heterogeneous material is attached, and removing the mold after curing the cement-based material.
상기 시멘트계 재료 상에 상기 시멘트계 재료와 상이한 이종 재료를 포함하는 이종 재료층을 형성하는 이종 재료층 형성 단계; 및
상기 이종 재료층이 형성된 상기 시멘트계 재료의 표면에 대하여 알칼리 규산염을 포함하는 조성물을 이용하여 표면 전처리를 수행하는 표면 전처리 단계; 및
표면 전처리가 수행된 상기 시멘트계 재료의 표면에 옻을 포함하는 도장 재료를 1회 또는 복수회 도포하는 도장층 형성 단계
를 포함하고,
상기 이종 재료층 형성 단계는,
수용성 수지를 모르타르 분말과 섞은 바탕 고름용 모르타르를 기준 마감 레벨에 맞춰서 소정 두께로 시공면에 형성하는 단계; 및
상기 이종 재료를 상기 바탕 고름용 모르타르의 형성면에 고정시키는 단계
를 포함하고,
상기 시멘트계 재료 형성 단계는, 기준 레벨에 맞춰서 상기 시멘트계 재료를 시공면에 타설하고, 미장마감하는 단계를 포함하는 시멘트계 복합재의 제조 방법.A cement-based material forming step of forming a cement-based material including concrete or mortar;
forming a different material layer comprising a different material different from the cement-based material on the cement-based material; and
a surface pretreatment step of performing surface pretreatment using a composition containing an alkali silicate on the surface of the cement-based material on which the heterogeneous material layer is formed; and
A coating layer forming step of applying a coating material containing lacquer once or multiple times to the surface of the cement-based material on which the surface pretreatment has been performed
including,
In the step of forming the heterogeneous material layer,
Forming a mortar for ground filling in which a water-soluble resin is mixed with mortar powder to a predetermined thickness on a construction surface according to a standard finish level; and
fixing the dissimilar material to the forming surface of the mortar for filling the background
including,
The step of forming the cement-based material comprises the step of pouring the cement-based material on the construction surface according to a reference level and finishing the plaster.
상기 이종 재료층 형성 단계와 상기 표면 전처리 단계 사이에, 상기 이종 재료층이 형성된 표면에 대하여 폴리싱 처리를 수행하는 단계를 더 포함하는 시멘트계 복합재의 제조 방법.According to any one of claims 1 to 3,
The manufacturing method of the cement-based composite material further comprising the step of performing a polishing treatment on the surface on which the different material layer is formed between the step of forming the different material layer and the step of pre-treating the surface.
상기 이종 재료는 자개, 패각, 대모, 상아 및 나무 중 하나 이상을 포함하는 시멘트계 복합재의 제조 방법.According to any one of claims 1 to 3,
The heterogeneous material is a method for producing a cement-based composite comprising at least one of mother-of-pearl, shell, mother-of-pearl, ivory, and wood.
콘크리트 또는 모르타르를 포함하는 시멘트계 재료층; 및
상기 시멘트계 재료층 상에 형성되고, 콘크리트 또는 모르타르와 상이한 이종 재료를 포함하는 이종 재료층
을 구비하는 시멘트계 복합재.A cement-based composite produced by the method for producing a cement-based composite according to any one of claims 1 to 3,
a cement-based material layer including concrete or mortar; and
A heterogeneous material layer formed on the cement-based material layer and including a heterogeneous material different from concrete or mortar.
A cement-based composite comprising a.