CN108300015A - A kind of environment-friendly type television set method of producing waterproof coating material - Google Patents
A kind of environment-friendly type television set method of producing waterproof coating material Download PDFInfo
- Publication number
- CN108300015A CN108300015A CN201710911487.2A CN201710911487A CN108300015A CN 108300015 A CN108300015 A CN 108300015A CN 201710911487 A CN201710911487 A CN 201710911487A CN 108300015 A CN108300015 A CN 108300015A
- Authority
- CN
- China
- Prior art keywords
- parts
- temperature
- environment
- coating material
- television set
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of environment-friendly type television set method of producing waterproof coating material provided by the invention includes following components, 50 70 parts of polyvinyl acetate resin by weight, 15 25 parts of butyl glycidyl ether, 5 15 parts of ammonium hydroxide, 39 parts of graphene, 48 parts of kaolin, 24 parts of coalescents, 13 parts of emulsifier, 58 parts of conditioning agent, composition is simple, and configuration is convenient, cost is relatively low, non-hazardous, and water resistance is good, whole service life is effectively extended, can more meet the needs of producer.
Description
Technical field
The present invention relates to technical field of coatings more particularly to a kind of environment-friendly type television set method of producing waterproof coating material.
Background technology
Coating, in the entitled paint of Chinese tradition.So-called coating be coated in the body surface being protected or decorated, and
The continuous film of firm attachment can be formed with coated article, typically based on resin or oil or lotion, add or do not add face
Material, filler add corresponding additive, the thick liquid being formulated with organic solvent or water.However existing television set is for a long time
After use, due to being placed on for a long time in air, the influence of steam in air is often will receive, generates the phenomenon that surface falls off,
It can not meet the needs of user.
Invention content
The object of the present invention is to provide a kind of environment-friendly type television set method of producing waterproof coating material, solve existing TV captain
After time use, due to being placed on for a long time in air, the influence of steam in air is often will receive, what generation surface fell off shows
As can not meet the needs of user.
The purpose of the present invention can be achieved through the following technical solutions；
A kind of environment-friendly type television set method of producing waterproof coating material, preparation method are as follows：
（1）Following components, 50-70 parts of polyvinyl acetate resin, 15-25 parts of butyl glycidyl ether, ammonia are weighed by weight
5-15 parts of water, 3-9 parts of graphene, 4-8 parts of kaolin, 2-4 parts of coalescents, 1-3 parts of emulsifier, 5-8 parts of conditioning agent；
（2）Ethylene glycol phenyl ether and propylene glycol are put into reaction kettle, temperature is 35 DEG C -65 DEG C, and uniform stirring 10-30min is obtained
Coalescents；
（3）Sodium alkyl sulfate and polyvinyl alcohol are put into reaction kettle, temperature is 65 DEG C -85 DEG C, and uniform stirring 15-30min is obtained
To emulsifier；
（4）Sodium hydroxide and potassium hydroxide are put into reaction kettle, temperature is 55 DEG C -75 DEG C, and uniform stirring 10-20min is obtained
At conditioning agent；
（5）Polyvinyl acetate resin, butyl glycidyl ether and ammonium hydroxide are put into reaction kettle, 10-30min is stirred, temperature is
45℃-55℃；After temperature is promoted to 60 DEG C -70 DEG C, it is separately added into graphene and conditioning agent, continues to stir 5-15min, works as temperature
After degree is promoted to 75 DEG C -85 DEG C, emulsifier is added, stirring 20-30min is put into kaolinite after temperature is promoted to 90 DEG C -100 DEG C
Soil and coalescents continue after stirring 30-50min, you can.
Above-mentioned a kind of environment-friendly type television set method of producing waterproof coating material, wherein the coalescents are ethylene glycol phenyl
Ether is stirred with mixed with propylene glycol, portion rate 3:1.
Above-mentioned a kind of environment-friendly type television set method of producing waterproof coating material, wherein the emulsifier is sodium alkyl sulfate
It is stirred with polyvinyl alcohol, portion rate 3:2.
A kind of above-mentioned environment-friendly type television set method of producing waterproof coating material, wherein the conditioning agent be sodium hydroxide with
Potassium hydroxide mixes together, portion rate 2:1.
The advantageous effect of this programme：
A kind of environment-friendly type television set method of producing waterproof coating material provided by the invention, composition is simple, and configuration is convenient, and cost is relatively low,
Non-hazardous, water resistance is good, effectively extends whole service life, can more meet the needs of producer.
Specific implementation mode
Embodiment 1：A kind of environment-friendly type television set method of producing waterproof coating material, preparation method are as follows：
（1）Weigh following components by weight, 50 parts of polyvinyl acetate resin, 15 parts of butyl glycidyl ether, 5 parts of ammonium hydroxide,
3 parts of graphene, 4 parts of kaolin, 2 parts of coalescents, 1 part of emulsifier, 5 parts of conditioning agent；
（2）Ethylene glycol phenyl ether and propylene glycol are put into reaction kettle, temperature is 35 DEG C, uniform stirring 10min, obtains film forming and helps
Agent；
（3）Sodium alkyl sulfate and polyvinyl alcohol are put into reaction kettle, temperature is 65 DEG C, and uniform stirring 15min is emulsified
Agent；
（4）Sodium hydroxide and potassium hydroxide are put into reaction kettle, temperature is 55 DEG C, and uniform stirring 10min obtains into adjusting
Agent；
（5）Polyvinyl acetate resin, butyl glycidyl ether and ammonium hydroxide are put into reaction kettle, 10min, temperature 45 are stirred
℃；After temperature is promoted to 60 DEG C, it is separately added into graphene and conditioning agent, continues to stir 5min, after temperature is promoted to 75 DEG C,
Emulsifier is added, stirring 20min is put into kaolin and coalescents after temperature is promoted to 90 DEG C, continues after stirring 30min,
.
Embodiment 2：A kind of environment-friendly type television set method of producing waterproof coating material, preparation method are as follows：
A kind of environment-friendly type television set method of producing waterproof coating material, preparation method are as follows：
（1）Following components, 60 parts of polyvinyl acetate resin, 20 parts of butyl glycidyl ether, ammonium hydroxide 10 are weighed by weight
Part, 6 parts of graphene, 6 parts of kaolin, 3 parts of coalescents, 2 parts of emulsifier, 7 parts of conditioning agent；
（2）Ethylene glycol phenyl ether and propylene glycol are put into reaction kettle, temperature is 55 DEG C, uniform stirring 20min, obtains film forming and helps
Agent；
（3）Sodium alkyl sulfate and polyvinyl alcohol are put into reaction kettle, temperature is 75 DEG C, and uniform stirring 25min is emulsified
Agent；
（4）Sodium hydroxide and potassium hydroxide are put into reaction kettle, temperature is 60 DEG C, and uniform stirring 15min obtains into adjusting
Agent；
（5）Polyvinyl acetate resin, butyl glycidyl ether and ammonium hydroxide are put into reaction kettle, 20min, temperature 50 are stirred
℃；After temperature is promoted to 65 DEG C, it is separately added into graphene and conditioning agent, continues to stir 10min, when temperature is promoted to 80 DEG C
Afterwards, emulsifier is added, stirring 25min is put into kaolin and coalescents after temperature is promoted to 95 DEG C, continues to stir 40min
Afterwards, you can.
Embodiment 3：A kind of environment-friendly type television set method of producing waterproof coating material, preparation method are as follows：
（1）Following components, 70 parts of polyvinyl acetate resin, 25 parts of butyl glycidyl ether, ammonium hydroxide 15 are weighed by weight
Part, 9 parts of graphene, 8 parts of kaolin, 4 parts of coalescents, 3 parts of emulsifier, 8 parts of conditioning agent；
（2）Ethylene glycol phenyl ether and propylene glycol are put into reaction kettle, temperature is 65 DEG C, uniform stirring 30min, obtains film forming and helps
Agent；
（3）Sodium alkyl sulfate and polyvinyl alcohol are put into reaction kettle, temperature is 85 DEG C, and uniform stirring 30min is emulsified
Agent；
（4）Sodium hydroxide and potassium hydroxide are put into reaction kettle, temperature is 75 DEG C, and uniform stirring 20min obtains into adjusting
Agent；
（5）Polyvinyl acetate resin, butyl glycidyl ether and ammonium hydroxide are put into reaction kettle, 30min, temperature 55 are stirred
℃；After temperature is promoted to 70 DEG C, it is separately added into graphene and conditioning agent, continues to stir 15min, when temperature is promoted to 85 DEG C
Afterwards, emulsifier is added, stirring 30min is put into kaolin and coalescents after temperature is promoted to 100 DEG C, continues to stir
After 50min, you can.
A kind of environment-friendly type television set method of producing waterproof coating material provided by the invention, composition is simple, and configuration is convenient, cost compared with
Low, non-hazardous, water resistance is good, effectively extends whole service life, can more meet the needs of producer.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, the change or replacement that can be readily occurred in,
Should all it cover within the scope of the present invention.Therefore, protection scope of the present invention should be with the protection domain of claims
Subject to.
Claims (4)
1. a kind of environment-friendly type television set method of producing waterproof coating material, it is characterized in that, preparation method is as follows：
（1）Following components, 50-70 parts of polyvinyl acetate resin, 15-25 parts of butyl glycidyl ether, ammonia are weighed by weight
5-15 parts of water, 3-9 parts of graphene, 4-8 parts of kaolin, 2-4 parts of coalescents, 1-3 parts of emulsifier, 5-8 parts of conditioning agent；
（2）Ethylene glycol phenyl ether and propylene glycol are put into reaction kettle, temperature is 35 DEG C -65 DEG C, and uniform stirring 10-30min is obtained
Coalescents；
（3）Sodium alkyl sulfate and polyvinyl alcohol are put into reaction kettle, temperature is 65 DEG C -85 DEG C, and uniform stirring 15-30min is obtained
To emulsifier；
（4）Sodium hydroxide and potassium hydroxide are put into reaction kettle, temperature is 55 DEG C -75 DEG C, and uniform stirring 10-20min is obtained
At conditioning agent；
（5）Polyvinyl acetate resin, butyl glycidyl ether and ammonium hydroxide are put into reaction kettle, 10-30min is stirred, temperature is
45℃-55℃；After temperature is promoted to 60 DEG C -70 DEG C, it is separately added into graphene and conditioning agent, continues to stir 5-15min, works as temperature
After degree is promoted to 75 DEG C -85 DEG C, emulsifier is added, stirring 20-30min is put into kaolinite after temperature is promoted to 90 DEG C -100 DEG C
Soil and coalescents continue after stirring 30-50min, you can.
2. a kind of environment-friendly type television set method of producing waterproof coating material as described in claim 1, it is characterized in that, the film forming helps
Agent is that ethylene glycol phenyl ether is stirred with mixed with propylene glycol, portion rate 3:1.
3. a kind of environment-friendly type television set method of producing waterproof coating material as described in claim 1, it is characterized in that, the emulsifier
It is stirred for sodium alkyl sulfate and polyvinyl alcohol, portion rate 3:2.
4. a kind of environment-friendly type television set method of producing waterproof coating material as described in claim 1, it is characterized in that, the conditioning agent
It is mixed together for sodium hydroxide and potassium hydroxide, portion rate 2:1.