CN107629529A - A kind of weaving anti-static coatings and its preparation technology - Google Patents
A kind of weaving anti-static coatings and its preparation technology Download PDFInfo
- Publication number
- CN107629529A CN107629529A CN201710825275.2A CN201710825275A CN107629529A CN 107629529 A CN107629529 A CN 107629529A CN 201710825275 A CN201710825275 A CN 201710825275A CN 107629529 A CN107629529 A CN 107629529A
- Authority
- CN
- China
- Prior art keywords
- parts
- static coatings
- curing agent
- stabilizer
- weaving anti
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of weaving anti-static coatings, it is characterised in that：Include following component according to weight fraction meter：30 45 parts of epoxy resin, 5 10 parts of titanium dioxide, 8 12 parts of antistatic additive, 24 parts of coupling agent, 0.5 1.5 parts of curing agent, 35 parts of silicon powder, 0.8 1.2 parts of stabilizer, 40 60 parts of ionized water；Wherein, the antistatic additive is anionic antistatic agents, and the curing agent is one or more mixtures in acid anhydrides, amino resins, dicyandiamide.The invention also discloses a kind of preparation technology of weaving anti-static coatings.
Description
Technical field
The present invention relates to a kind of weaving anti-static coatings and its preparation technology, belong to textile technology field.
Background technology
Traditional fabric is usually single layer structure, and function is more single.In recent years with the development of textile industry, occur
Double-layer fabric, double-layer fabric are three-dimensional structure, have solid layer feeling, abundant degree and intensity are all relatively good, but do not possess anti-quiet
Electricity Functional.At present, antistatic fabric smears one layer of antistatic backing, but existing antistatic backing typically by web surface
Performance it is not firm enough, after a long time use, will gradually lose electrostatic-proof function.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of weaving anti-static coatings and its preparation technology, by
Add curing agent and stabilizer in component, anti-static coatings stability made of guarantee more preferably, can ensure fabric when long
Between still there is antistatic performance after use.
In order to solve the above-mentioned technical problem, the technical solution adopted in the present invention is：
A kind of weaving anti-static coatings, it is characterised in that：Include following component according to weight fraction meter：
Epoxy resin 30-45 parts
Titanium dioxide 5-10 parts
Antistatic additive 8-12 parts
Coupling agent 2-4 parts
Curing agent 0.5-1.5 parts
Silicon powder 3-5 parts
Stabilizer 0.8-1.2 parts
Ionized water 40-60 parts；
Wherein, the antistatic additive is anionic antistatic agents, and the curing agent is one in acid anhydrides, amino resins, dicyandiamide
Kind or a variety of mixtures.
A kind of foregoing weaving anti-static coatings, it is characterised in that：The coupling agent be di-tert-butyl peroxide or
The mixture of one or both of di-isopropylbenzene hydroperoxide.
A kind of foregoing weaving anti-static coatings, it is characterised in that：The stabilizer is organotin.
A kind of foregoing weaving anti-static coatings, it is characterised in that：Include following component according to weight fraction meter：Epoxy
35 parts of resin, 8 parts of titanium dioxide, 10 parts of antistatic additive, 3 parts of coupling agent, 1 part of curing agent, 3 parts of silicon powder, 1 part of stabilizer, ion
50 parts of water.
A kind of preparation technology of weaving anti-static coatings as the aforementioned, it is characterised in that：Comprise the following steps：
（1）Component proportion：Include following component according to weight fraction meter：It is epoxy resin 30-45 parts, titanium dioxide 5-10 parts, anti-quiet
Electric agent 8-12 parts, coupling agent 2-4 parts, curing agent 0.5-1.5 parts, silicon powder 3-5 parts, stabilizer 0.8-1.2 parts, ionized water 40-
60 parts；
（2）By step（1）The middle epoxy resin matched, titanium dioxide, silicon powder are poured into agitating device and mixed,
Antistatic additive, coupling agent and ionized water are sequentially added during stirring；
（3）By step（2）In the material that stirs pour into reactor, the temperature of reactor is increased to 140 DEG C -155 DEG C
Between, stir 20-25min；
（4）By step（3）Material after middle heating stirring naturally cools to room temperature, sequentially adds curing agent, stabilizer, again will
The temperature of reactor is increased to 50 DEG C -65 DEG C, stirs 10-15min；
（5）Room temperature is naturally cooled to, water-repellent paint is made.
A kind of preparation technology of foregoing weaving anti-static coatings, it is characterised in that：The step（3）Middle reactor
Temperature is increased to 155 DEG C.
A kind of preparation technology of foregoing weaving anti-static coatings, it is characterised in that：The step（4）Middle reactor
Temperature is increased to 55 DEG C.
The beneficial effects of the invention are as follows：By adding curing agent and stabilizer in component, antistatic made of guarantee applies
Expect stability more preferably, can ensure that fabric still has antistatic performance after a long time use.
Embodiment
Below in conjunction with specific embodiment, the present invention is further illustrated.
A kind of weaving anti-static coatings, it is characterised in that：Include following component according to weight fraction meter：
Epoxy resin 30-45 parts
Titanium dioxide 5-10 parts
Antistatic additive 8-12 parts
Coupling agent 2-4 parts
Curing agent 0.5-1.5 parts
Silicon powder 3-5 parts
Stabilizer 0.8-1.2 parts
Ionized water 40-60 parts；
Wherein, the antistatic additive is anionic antistatic agents, and the curing agent is one in acid anhydrides, amino resins, dicyandiamide
Kind or a variety of mixtures.By adding curing agent and stabilizer, anti-static coatings stability made of guarantee in component
More preferably, it can ensure that fabric still has antistatic performance after a long time use.
The coupling agent is the mixture of one or both of di-tert-butyl peroxide or di-isopropylbenzene hydroperoxide,
The stabilizer is organotin, and organic tin stabilizer biggest advantage is with the remarkable transparency, uses organic tin stabilizer
Coating formula, can be crystallized as product.
It is a kind of weaving anti-static coatings, to include according to weight fraction meter as follows that one of the present invention, which hands over good embodiment,
Component：35 parts of epoxy resin, 8 parts of titanium dioxide, 10 parts of antistatic additive, 3 parts of coupling agent, 1 part of curing agent, 3 parts of silicon powder, stabilizer
1 part, 50 parts of ionized water.
Present invention also offers a kind of preparation technology of weaving anti-static coatings as the aforementioned, it is characterised in that：Including
Following steps：（1）Component proportion：Include following component according to weight fraction meter：Epoxy resin 30-45 parts, titanium dioxide 5-10 parts,
Antistatic additive 8-12 parts, coupling agent 2-4 parts, curing agent 0.5-1.5 parts, silicon powder 3-5 parts, stabilizer 0.8-1.2 parts, ion
Water 40-60 parts；（2）By step（1）The middle epoxy resin matched, titanium dioxide, silicon powder are poured into agitating device and mixed
Stirring, sequentially adds antistatic additive, coupling agent and ionized water during stirring；（3）By step（2）In the material that stirs
Material is poured into reactor, between the temperature of reactor is increased into 140 DEG C -155 DEG C, stirs 20-25min；（4）By step（3）
Material after middle heating stirring naturally cools to room temperature, sequentially adds curing agent, stabilizer, again raises the temperature of reactor
To 50 DEG C -65 DEG C, 10-15min is stirred；（5）Room temperature is naturally cooled to, water-repellent paint is made.
In the present embodiment, the step（3）The temperature of middle reactor is increased to 155 DEG C, the step（4）Middle reactor
Temperature is increased to 55 DEG C.
In summary, a kind of weaving anti-static coatings provided by the invention and its preparation technology, by adding in component
Enter curing agent and stabilizer, anti-static coatings stability made of guarantee more preferably, can ensure fabric after a long time use
Still there is antistatic performance.
General principle, the main features and advantages of the present invention have been shown and described above.The technical staff of the industry should
Understand, the present invention is not limited to the above embodiments, the original for simply illustrating the present invention described in above-described embodiment and specification
Reason, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes and improvements
It all fall within the protetion scope of the claimed invention.The claimed scope of the invention is by appended claims and its equivalent
Boundary.
Claims (7)
- A kind of 1. weaving anti-static coatings, it is characterised in that：Include following component according to weight fraction meter：Epoxy resin 30-45 partsTitanium dioxide 5-10 partsAntistatic additive 8-12 partsCoupling agent 2-4 partsCuring agent 0.5-1.5 partsSilicon powder 3-5 partsStabilizer 0.8-1.2 partsIonized water 40-60 parts；Wherein, the antistatic additive is anionic antistatic agents, and the curing agent is one in acid anhydrides, amino resins, dicyandiamide Kind or a variety of mixtures.
- 2. one kind weaving anti-static coatings according to claim 1, it is characterised in that：The coupling agent is di-t-butyl The mixture of one or both of peroxide or di-isopropylbenzene hydroperoxide.
- 3. one kind weaving anti-static coatings according to claim 1, it is characterised in that：The stabilizer is organotin.
- 4. one kind weaving anti-static coatings according to claim 1, it is characterised in that：Include such as according to weight fraction meter Lower component：35 parts of epoxy resin, 8 parts of titanium dioxide, 10 parts of antistatic additive, 3 parts of coupling agent, 1 part of curing agent, 3 parts of silicon powder, stably 1 part of agent, 50 parts of ionized water.
- A kind of 5. preparation technology of the weaving anti-static coatings in 1-4 such as claim as described in any one, it is characterised in that： Comprise the following steps：（1）Component proportion：Include following component according to weight fraction meter：It is epoxy resin 30-45 parts, titanium dioxide 5-10 parts, anti-quiet Electric agent 8-12 parts, coupling agent 2-4 parts, curing agent 0.5-1.5 parts, silicon powder 3-5 parts, stabilizer 0.8-1.2 parts, ionized water 40- 60 parts；（2）By step（1）The middle epoxy resin matched, titanium dioxide, silicon powder are poured into agitating device and mixed, Antistatic additive, coupling agent and ionized water are sequentially added during stirring；（3）By step（2）In the material that stirs pour into reactor, the temperature of reactor is increased to 140 DEG C -155 DEG C Between, stir 20-25min；（4）By step（3）Material after middle heating stirring naturally cools to room temperature, sequentially adds curing agent, stabilizer, again will The temperature of reactor is increased to 50 DEG C -65 DEG C, stirs 10-15min；（5）Room temperature is naturally cooled to, water-repellent paint is made.
- A kind of 6. preparation technology of weaving anti-static coatings according to claim 5, it is characterised in that：The step （3）The temperature of middle reactor is increased to 155 DEG C.
- A kind of 7. preparation technology of weaving anti-static coatings according to claim 1, it is characterised in that：The step （4）The temperature of middle reactor is increased to 55 DEG C.