CN107722813A - A kind of environment-friendly type television set preparation method of anticorrosion paint - Google Patents
A kind of environment-friendly type television set preparation method of anticorrosion paint Download PDFInfo
- Publication number
- CN107722813A CN107722813A CN201710911489.1A CN201710911489A CN107722813A CN 107722813 A CN107722813 A CN 107722813A CN 201710911489 A CN201710911489 A CN 201710911489A CN 107722813 A CN107722813 A CN 107722813A
- Authority
- CN
- China
- Prior art keywords
- parts
- temperature
- television set
- environment
- friendly type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of environment-friendly type television set preparation method of anticorrosion paint provided by the invention, by weight including following components, 30 50 parts of EU epoxy resin, 5 30 parts of silica 1,39 parts of filler, 26 parts of graphite powder, 58 parts of antimony oxide, 28 parts of diluent, 15 parts of defoamer, composition is simple, and configuration is convenient, and cost is relatively low, non-hazardous, antiseptic property is good, effectively extends overall service life, can more meet the needs of producer.
Description
Technical field
The present invention relates to technical field of coatings, more particularly to a kind of environment-friendly type television set preparation method of anticorrosion paint.
Background technology
Coating, in the entitled paint of Chinese tradition.So-called coating is to be coated in the body surface protected or decorated, and
The continuous film of firm attachment can be formed with coated article, typically based on resin or oil or emulsion, adds or does not add face
Material, filler, add corresponding additive, the thick liquid being formulated with organic solvent or water.But existing television set is for a long time
After use, due to being placed on for a long time in atmosphere, the influence of steam in air is often received, produces the phenomenon that surface comes off,
It can not meet the needs of user.
The content of the invention
It is an object of the invention to provide a kind of environment-friendly type television set preparation method of anticorrosion paint, solves existing TV captain
After time use, due to being placed on for a long time in atmosphere, the influence of steam in air is often received, what generation surface came off shows
As can not meet the needs of user.
The purpose of the present invention can be achieved through the following technical solutions；
A kind of environment-friendly type television set preparation method of anticorrosion paint, its preparation method are as follows：
（1）Following components is weighed by weight, EU epoxy resin 30-50 parts, silica 1 5-30 parts, is filled out
Expect 3-9 parts, graphite powder 2-6 parts, antimony oxide 5-8 parts, diluent 2-8 parts, defoamer 1-5 parts；
（2）Mica powder and talcum powder are put into reactor, temperature is 55 DEG C -65 DEG C, uniform stirring 20-30min, is filled out
Material；
（3）Propylene glycol monomethyl ether and propandiol butyl ether are put into reactor, temperature is 35 DEG C -55 DEG C, uniform stirring 15-25min,
Obtain into diluent；
（4）Organic siloxane and mineral oil are put into reactor, temperature is 25 DEG C -35 DEG C, uniform stirring 10-20min, is obtained into
Defoamer；
（5）EU epoxy resin and silica are put into reactor, stir 10-15min, temperature is 35 DEG C-
55℃；After temperature is promoted to 60 DEG C -75 DEG C, graphite powder and antimony oxide are separately added into, continues to stir 5-15min, works as temperature
After degree is promoted to 80 DEG C -90 DEG C, diluent and defoamer are added, stirs 15-30min, after temperature is promoted to 95 DEG C -105 DEG C,
Filler is put into, is continued after stirring 30-50min, you can.
A kind of above-mentioned environment-friendly type television set preparation method of anticorrosion paint, wherein, described filler is mica powder and talcum
Powder mixes together, and its portion rate is 2:1.
A kind of above-mentioned environment-friendly type television set preparation method of anticorrosion paint, wherein, described diluent is propylene glycol monomethyl ether
Mixed together with propandiol butyl ether, its portion rate is 3:2.
A kind of above-mentioned environment-friendly type television set preparation method of anticorrosion paint, wherein, described defoamer be organic siloxane and
Mineral oil stirring forms, and its portion rate is 2:5.
The beneficial effect of this programme：
A kind of environment-friendly type television set preparation method of anticorrosion paint provided by the invention, composition is simple, and configuration is convenient, and cost is relatively low,
Non-hazardous, antiseptic property is good, effectively extends overall service life, can more meet the needs of producer.
Embodiment
Embodiment 1：A kind of environment-friendly type television set preparation method of anticorrosion paint, its preparation method are as follows：
（1）Weigh following components by weight, 30 parts of EU epoxy resin, 5 parts of silica 1,3 parts of filler,
2 parts of graphite powder, 5 parts of antimony oxide, 2 parts of diluent, 1 part of defoamer；
（2）Mica powder and talcum powder are put into reactor, temperature is 55 DEG C, uniform stirring 20min, obtains filler；
（3）Propylene glycol monomethyl ether and propandiol butyl ether are put into reactor, temperature is 35 DEG C, uniform stirring 15min, is obtained into dilute
Release agent；
（4）Organic siloxane and mineral oil are put into reactor, temperature is 25 DEG C, uniform stirring 10min, obtains into defoamer；
（5）EU epoxy resin and silica are put into reactor, stir 10min, temperature is 35 DEG C；Work as temperature
After degree is promoted to 60 DEG C, graphite powder and antimony oxide are separately added into, continues to stir 5min, after temperature is promoted to 80 DEG C, adds
Enter diluent and defoamer, stir 15min, after temperature is promoted to 95 DEG C -105 DEG C, be put into filler, continue after stirring 30min,
.
Embodiment 2：A kind of environment-friendly type television set preparation method of anticorrosion paint, its preparation method are as follows：
A kind of environment-friendly type television set preparation method of anticorrosion paint, its preparation method are as follows：
（1）Weigh following components by weight, 40 parts of EU epoxy resin, 20 parts of silica, 6 parts of filler,
4 parts of graphite powder, 7 parts of antimony oxide, 6 parts of diluent, 4 parts of defoamer；
（2）Mica powder and talcum powder are put into reactor, temperature is 60 DEG C, uniform stirring 25min, obtains filler；
（3）Propylene glycol monomethyl ether and propandiol butyl ether are put into reactor, temperature is 45 DEG C, uniform stirring 20min, is obtained into dilute
Release agent；
（4）Organic siloxane and mineral oil are put into reactor, temperature is 30 DEG C, uniform stirring 15min, obtains into defoamer；
（5）EU epoxy resin and silica are put into reactor, stir 12min, temperature is 45 DEG C；Work as temperature
After degree is promoted to 70 DEG C, graphite powder and antimony oxide are separately added into, continues to stir 10min, after temperature is promoted to 85 DEG C, adds
Enter diluent and defoamer, stir 20min, after temperature is promoted to 100 DEG C, be put into filler, continue after stirring 40min, you can.
Embodiment 3：A kind of environment-friendly type television set preparation method of anticorrosion paint, its preparation method are as follows：
（1）Weigh following components by weight, 50 parts of EU epoxy resin, 30 parts of silica, 9 parts of filler,
6 parts of graphite powder, 8 parts of antimony oxide, 8 parts of diluent, 5 parts of defoamer；
（2）Mica powder and talcum powder are put into reactor, temperature is 65 DEG C, uniform stirring 30min, obtains filler；
（3）Propylene glycol monomethyl ether and propandiol butyl ether are put into reactor, temperature is 55 DEG C, uniform stirring 25min, is obtained into dilute
Release agent；
（4）Organic siloxane and mineral oil are put into reactor, temperature is 35 DEG C, uniform stirring 20min, obtains into defoamer；
（5）EU epoxy resin and silica are put into reactor, stir 15min, temperature is 55 DEG C；Work as temperature
After degree is promoted to 75 DEG C, graphite powder and antimony oxide are separately added into, continues to stir 15min, after temperature is promoted to 90 DEG C, adds
Enter diluent and defoamer, stir 30min, after temperature is promoted to 105 DEG C, be put into filler, continue after stirring 50min, you can.
A kind of environment-friendly type television set preparation method of anticorrosion paint provided by the invention, composition is simple, and configuration is convenient, cost compared with
Low, non-hazardous, antiseptic property is good, effectively extends overall service life, can more meet the needs of producer.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, the change or replacement that can readily occur in,
It should all cover within the scope of the present invention.Therefore, protection scope of the present invention should be with the protection domain of claims
It is defined.
Claims (4)
1. a kind of environment-friendly type television set preparation method of anticorrosion paint, it is characterized in that, its preparation method is as follows：
（1）Following components is weighed by weight, EU epoxy resin 30-50 parts, silica 1 5-30 parts, is filled out
Expect 3-9 parts, graphite powder 2-6 parts, antimony oxide 5-8 parts, diluent 2-8 parts, defoamer 1-5 parts；
（2）Mica powder and talcum powder are put into reactor, temperature is 55 DEG C -65 DEG C, uniform stirring 20-30min, is filled out
Material；
（3）Propylene glycol monomethyl ether and propandiol butyl ether are put into reactor, temperature is 35 DEG C -55 DEG C, uniform stirring 15-25min,
Obtain into diluent；
（4）Organic siloxane and mineral oil are put into reactor, temperature is 25 DEG C -35 DEG C, uniform stirring 10-20min, is obtained into
Defoamer；
（5）EU epoxy resin and silica are put into reactor, stir 10-15min, temperature is 35 DEG C-
55℃；After temperature is promoted to 60 DEG C -75 DEG C, graphite powder and antimony oxide are separately added into, continues to stir 5-15min, works as temperature
After degree is promoted to 80 DEG C -90 DEG C, diluent and defoamer are added, stirs 15-30min, after temperature is promoted to 95 DEG C -105 DEG C,
Filler is put into, is continued after stirring 30-50min, you can.
2. a kind of environment-friendly type television set preparation method of anticorrosion paint as claimed in claim 1, it is characterized in that, described filler is
Mica powder mixes together with talcum powder, and its portion rate is 2:1.
3. a kind of environment-friendly type television set preparation method of anticorrosion paint as claimed in claim 1, it is characterized in that, described diluent
Mixed together for propylene glycol monomethyl ether and propandiol butyl ether, its portion rate is 3:2.
4. a kind of environment-friendly type television set preparation method of anticorrosion paint as claimed in claim 1, it is characterized in that, described defoamer
Formed for organic siloxane and mineral oil stirring, its portion rate is 2:5.