CN108285627A - A kind of resin button and its production technology - Google Patents
A kind of resin button and its production technology Download PDFInfo
- Publication number
- CN108285627A CN108285627A CN201810156572.7A CN201810156572A CN108285627A CN 108285627 A CN108285627 A CN 108285627A CN 201810156572 A CN201810156572 A CN 201810156572A CN 108285627 A CN108285627 A CN 108285627A
- Authority
- CN
- China
- Prior art keywords
- resin
- button
- water
- raw material
- cooling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of resin button and its production technologies, including the selection of resin button raw material, raw material impurity processing, resin button production and processing processing, cooling and shaping processing, the examination and test of products, resin button is handled in accordance with the following steps during production：Step 1：Resin button raw material is chosen；Step 2：Raw material impurity processing；Step 3：Resin button production and processing is handled；Step 4：Cooling and shaping are handled；Step 5：The examination and test of products, by being equipped with raw material impurity processing step during resin button is processed, in such a way that hot water cleaning and cation and anion are into line replacement, impurity inside resin is handled, improve the degree of purity of resin, to improve the quality of resin button, gas-cooled mode is used for the molding type of cooling of resin button, the case where avoiding the pressure due to water by the way of water cooling that button is caused to deform upon occurs, so as to improve resin button finished product compliance rate.
Description
Technical field
The present invention relates to resin button technical field of producing, specially a kind of resin button and its production technology.
Background technology
Button is inserted in small shape sphere or tablet that the fastenings such as clothes are got up in button loop, with the development button of society
Material and type it is more and more diversified, there is resin button, since resin toughness is good and facilitates the various patterns of engraving, have
Good aesthetics gos deep into liking for consumer.
However the compliance rate for producing often finished product in traditional resin button process for button is very low, many knobs
Button specification is not achieved in standard and finished product there are many impurity, to influence the quality of resin button.
Invention content
The purpose of the present invention is to provide a kind of resin button and its production technologies, solve proposed in background technology
Problem.
To achieve the above object, the present invention provides the following technical solutions：A kind of resin button and its production technology, including tree
The selection of fat button raw material, raw material impurity processing, resin button production and processing processing, cooling and shaping processing, the examination and test of products, resin knob
It is handled in accordance with the following steps during being buckled in production：
Step 1：Resin button raw material is chosen；
Step 2：Raw material impurity processing；
Step 3：Resin button production and processing is handled；
Step 4：Cooling and shaping are handled；
Step 5：The examination and test of products.
As a kind of preferred embodiment of the present invention, the button uses resin material to be made and for cylindrical structure,
The thickness of the button is 0.5cm and a diameter of 4cm, and the button middle table is inlayed by four threading holes.
As a kind of preferred embodiment of the present invention, the resin button raw material is chosen, and the raw material for producing button is main
It is unsaturated polyester resin, curing agent and auxiliary material, 1) unsaturated polyester resin：Produce the resin requirement viscosity of button
For 10-20Pa.s, heat release is low when solidification, and gel time is short, and resin is easy colouring, cure stage hardness increase it is slower etc., 2)
Curing agent：Initiator uses methyl ethyl ketone peroxide, accelerating agent naphthoic acid cobalt, 3) auxiliary material：Including mill base, pearl powder, thixotroping
Agent etc., pearl powder are basic lead carbonate hexagon flake-like crystals, can be arranged in parallel in forming process, show pearly luster,
Thixotropic agent is active silica, is mainly used for preventing not having color to interpenetrate.
As a kind of preferred embodiment of the present invention, the raw material impurity processing, the new tree that preparation dress column is used
Fat first uses hot water（Clean tap water）It cleans repeatedly, cation exchange resin can use 70-80 DEG C of hot water, anion
The heat resistance of exchanger resin is more weaker, can use 50-60 DEG C of hot water.When starting to embathe, it is primary to change water every about 15 minutes, leaching
It to be stirred frequently when washing, after changing water 4-5 times, it is primary to change water every about 30 minutes, changes water in total 7-8 times, embathes to embathing water not
Band brown, when foam is seldom until, pay attention to：1）The requirement of cleaning solution water：Suggest using deionized water to doing analysis and testing, 2）.
Water temperature will determine according to the resin selected by you, and different resins has a maximum temperature, and 3）The resin being dehydrated centainly cannot
It directly washes with water, first to be impregnated with certain density saline solution, can be just washed with water after gradually diluting.
As a kind of preferred embodiment of the present invention, the resin button production and processing processing, using centrifugal casting formula
Bar casting produces, and resin solution is poured in button mold slots, pouring molding is carried out.
As a kind of preferred embodiment of the present invention, the cooling and shaping processing uses gas-cooled mode, passes through
Cooling blower carries out cooling treatment, and cooling gas is transported to by appendix in button mold slots, and cooling place is carried out to button
Reason finally carries out demoulding processing, is formed at flat.
As a kind of preferred embodiment of the present invention, the examination and test of products shape is consistent with sample, and 1）It is detained including thin side
Side size, face back of the body radian etc., 2）Test stone, finished product standard：1, color, decorative pattern, model and sample or the product requirement phase
Together；2, pin hole is rectified, is symmetrical, and needle gage and aperture size comply with standard；3, luminosity meets the requirements；4, the face back of the body is fried without vehicle, vehicle is broken, side
Gage distortion phenomenon；By style, color, decorative pattern, type classification packaging.
Compared with prior art, beneficial effects of the present invention are as follows：
1. by being equipped with raw material impurity processing step during resin button is processed, hot water cleaning and cation and the moon are utilized
Ion is handled the impurity inside resin into the mode of line replacement, improves the degree of purity of resin, to improve resin button
Quality.
2. for the molding type of cooling of resin button use gas-cooled mode, avoid by the way of water cooling by
Occur the case where the pressure of water causes button to deform upon, so as to improve resin button finished product compliance rate.
Description of the drawings
Fig. 1 is the schematic diagram of resin button in the present invention.
Specific implementation mode
Below in conjunction in the embodiment of the present invention, technical solution in the embodiment of the present invention is clearly and completely retouched
It states, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based on the present invention
In embodiment, every other implementation obtained by those of ordinary skill in the art without making creative efforts
Example, shall fall within the protection scope of the present invention.
The present invention provides a kind of technical solution：A kind of resin button and its production technology, including resin button raw material choose,
Raw material impurity processing, resin button production and processing processing, cooling and shaping processing, the examination and test of products, process of the resin button in production
In handled in accordance with the following steps：
Step 1：Resin button raw material is chosen；
Step 2：Raw material impurity processing；
Step 3：Resin button production and processing is handled；
Step 4：Cooling and shaping are handled；
Step 5：The examination and test of products.
The button uses resin material to be made and for cylindrical structure, and the thickness of the button is 0.5cm and a diameter of
4cm, the button middle table are inlayed by four threading holes.
The resin button raw material is chosen, and the raw material for producing button is mainly unsaturated polyester resin, curing agent and auxiliary
Material, 1) unsaturated polyester resin：The resin requirement viscosity of production button is 10-20Pa.s, and heat release is low when solidification, when gel
Between it is short, resin is easy colouring, cure stage hardness increase it is slower etc., 2) curing agent：Initiator uses methyl ethyl ketone peroxide, promotees
Into agent naphthoic acid cobalt, 3) auxiliary material：Including mill base, pearl powder, thixotropic agent etc., pearl powder is basic lead carbonate hexagon thin slice
Shape crystal, can be arranged in parallel in forming process, shows pearly luster, thixotropic agent is active silica, is mainly used for preventing
Do not have color to interpenetrate.
The raw material impurity processing, the new resin that preparation dress column is used, first uses hot water（Clean tap water）Instead
Multiple cleaning, cation exchange resin can use 70-80 DEG C of hot water, and the heat resistance of anion exchange resin is more weaker, can use
50-60 DEG C of hot water.When starting to embathe, it is primary to change water every about 15 minutes, to be stirred frequently when embathing, can be every after changing water 4-5 times
It is primary to change within about 30 minutes water, changes water in total 7-8 times, embathes to embathing water without brown, when foam is seldom until, pay attention to：1）Clear
The requirement of washing lotion water：Suggest using deionized water to doing analysis and testing, 2）Water temperature will determine according to the resin selected by you, different
Resin have a maximum temperature, 3）The resin being dehydrated centainly cannot be washed with water directly, be first with certain density food
Saline sook can just be washed with water after gradually diluting, by being equipped at raw material impurity during resin button is processed
Step is managed, in such a way that hot water cleaning and cation and anion are into line replacement, the impurity inside resin is handled, is carried
The degree of purity of high resin, to improve the quality of resin button.
The resin button production and processing processing, is produced using centrifugal casting formula bar casting, resin solution is poured
In in button mold slots, pouring molding is carried out.
The cooling and shaping processing uses gas-cooled mode, cooling treatment is carried out by cooling blower, by cooling air
Body is transported to by appendix in button mold slots, is carried out cooling treatment to button, is finally carried out demoulding processing, is formed at flat,
Gas-cooled mode is used for the molding type of cooling of resin button, avoids the pressure due to water by the way of water cooling
The case where causing button to deform upon, occurs, so as to improve resin button finished product compliance rate.
The examination and test of products shape is consistent with sample, and 1）Including the thin size in button, radian etc. is carried on the back in face, and 2）Test stone,
Finished product standard：1, color, decorative pattern, model are identical as sample or the product requirement；2, pin hole is rectified, is symmetrical, needle gage and pin hole
Size complies with standard；3, luminosity meets the requirements；4, the face back of the body is fried without vehicle, vehicle is broken, side gage distortion phenomenon；By style, color, flower
Line, type classification packaging.
Operation principle：It is chosen by resin button raw material, raw material impurity is handled, resin button production and processing is handled, cooling
Five steps such as forming processes, examination and test of products, by being equipped with raw material impurity processing step, profit during resin button is processed
It is cleaned with hot water and cationic and anion is into the mode of line replacement, the impurity inside resin is handled, resin is improved
Degree of purity uses gas-cooled mode for the molding type of cooling of resin button, keeps away to improve the quality of resin button
Exempting from the case where pressure due to water by the way of water cooling causes button to deform upon occurs, so as to improve resin button
Finished product compliance rate.
Finally it should be noted that：The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention,
Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art, still may be used
With technical scheme described in the above embodiments is modified or equivalent replacement of some of the technical features.
All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in the present invention's
Within protection domain.
Claims (8)
1. a kind of resin button and its production technology, including resin button raw material is chosen, raw material impurity is handled, resin button production
Working process, cooling and shaping processing, the examination and test of products, it is characterised in that：Resin button during production in accordance with the following steps
It is handled：
Step 1：Resin button raw material is chosen；
Step 2：Raw material impurity processing；
Step 3：Resin button production and processing is handled；
Step 4：Cooling and shaping are handled；
Step 5：The examination and test of products.
2. a kind of resin button according to claim 1, it is characterised in that：The button use resin material be made and for
The thickness of cylindrical structure, the button is 0.5cm and a diameter of 4cm, and the button middle table is inlayed by four threading holes.
3. a kind of resin button according to claim 1 and its production technology, it is characterised in that：The resin button raw material
It chooses, the raw material for producing button is mainly unsaturated polyester resin, curing agent and auxiliary material, and 1) unsaturated polyester resin：It is raw
The resin requirement viscosity of production button is 10-20Pa.s, and heat release is low when solidification, and gel time is short, and resin is easy colouring, cures rank
Section hardness increase it is slower etc., 2) curing agent：Initiator uses methyl ethyl ketone peroxide, accelerating agent naphthoic acid cobalt, 3) auxiliary material：
Including mill base, pearl powder, thixotropic agent etc., pearl powder is basic lead carbonate hexagon flake-like crystals, can be put down in forming process
Row arrangement, shows pearly luster, thixotropic agent is active silica, is mainly used for preventing not having color to interpenetrate.
4. a kind of resin button according to claim 1 and its production technology, it is characterised in that：At the raw material impurity
Reason, the new resin that preparation dress column is used, first uses hot water（Clean tap water）It cleans repeatedly, cation exchange resin
70-80 DEG C of hot water can be used, the heat resistance of anion exchange resin is more weaker, can use 50-60 DEG C of hot water.
5. start to embathe, it is primary to change water every about 15 minutes, to be stirred frequently when embathing, can be every about 30 points after changing water 4-5 times
Zhong Huanshui is primary, changes water in total 7-8 times, embathes to embathing water without brown, when foam is seldom until, pay attention to：1）Cleaning solution water
Requirement：Suggest using deionized water to doing analysis and testing, 2）Water temperature will determine according to the resin selected by you, different resins
There is a maximum temperature, 3）The resin being dehydrated centainly cannot be washed with water directly, be first with certain density salt water logging
Bubble, can just be washed with water after gradually diluting.
6. a kind of resin button according to claim 1 and its production technology, it is characterised in that：The resin button production
Working process is produced using centrifugal casting formula bar casting, and resin solution is poured in button mold slots, pour building up
Type.
7. a kind of resin button according to claim 1 and its production technology, it is characterised in that：The cooling and shaping processing
Using gas-cooled mode, cooling treatment is carried out by cooling blower, cooling gas is transported to button mould by appendix
Have in slot, cooling treatment is carried out to button, finally carries out demoulding processing, is formed at flat.
8. a kind of resin button according to claim 1 and its production technology, it is characterised in that：The examination and test of products shape
It is consistent with sample, 1）Including the thin size in button, radian etc. is carried on the back in face, and 2）Test stone, finished product standard：1, color, decorative pattern,
Model is identical as sample or the product requirement；2, pin hole is rectified, is symmetrical, and needle gage and aperture size comply with standard；3, luminosity meets
It is required that；4, the face back of the body is fried without vehicle, vehicle is broken, side gage distortion phenomenon；By style, color, decorative pattern, type classification packaging.