CN102068090A - Method for manufacturing jewelry mold - Google Patents
Method for manufacturing jewelry mold Download PDFInfo
- Publication number
- CN102068090A CN102068090A CN2009101128143A CN200910112814A CN102068090A CN 102068090 A CN102068090 A CN 102068090A CN 2009101128143 A CN2009101128143 A CN 2009101128143A CN 200910112814 A CN200910112814 A CN 200910112814A CN 102068090 A CN102068090 A CN 102068090A
- Authority
- CN
- China
- Prior art keywords
- wax
- mould
- jewellery
- pattern
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for manufacturing a jewelry mold. The manufacturing method comprises manufacturing a rubber mold, a wax mold and a seed mold, pouring the molds, and roasting. Compared with the prior art, the method has the characteristics of short manufacturing time, good color formation and the like, and is easy to operate. The method greatly improves the processing efficiency of jewelry, and brings new flyby to the jewelry manufacturing industry.
Description
Technical field
The invention belongs to ornament craft product field, relate in particular to a kind of preparation method of jewellery mould.
Background technology
At present a lot of jewellery need be with traditional, make by hand, the trouble of doing manual work, common jewellery moulding needs 1-2 hour, weld, can reduce quality, numerous and diverse jewellery take 1-2 days, and want old artist to make, general apprentice is sayed that acknowledging sb. as one's master learns a craft or trade generally wanted for 1 year could graduate, and because technology is coarse, and solder joint is many, reasons such as brightness difference cause the finished product sense organ very poor because of this hand-built jewellery.
Summary of the invention
The preparation method that the objective of the invention is to overcome above-mentioned weak point of the prior art and a kind of jewellery mould is provided becomes simple efficient so that jewellery are made.
The present invention realizes in the following way:
Preparation method flow process of the present invention is:
One, rubber pattern
The jewellery specimen holder that to make by manual mode is between two blocks of rubber earlier; the pressurization that heats up on molding press is dissolved rubber and tightly is contained within outside the jewellery sample, after the cooling under pressure; with instrument rubber is cut the jewellery sample that will contain in it and take out, form rubber pattern.
Two, wax-pattern
Wax injector is added wax, regulates temperature and pressure and wax is injected rubber pattern form wax-pattern, behind the wax-pattern cooling forming, it is taken out from rubber pattern, again with instrument with the blank equating mouth of a river.
Three, plant wax
Utilize electric iron, wax spare according to different materials, is planted into a wax kind, reinstall one and have in the container of metal shell, form a mould, prepare reverse mould.
Four, reverse mould
Pour the mould for the treatment of reverse mould into gypsum, gypsum is vacuumized again, back seal model word seal is done in moulding then naturally, prepares roasting.
Five, roasting
To treat that the roasting mould puts into 800 degrees centigrade high-temperature roasting stove mould is dried, can form the jewellery mould after the wax evaporation in mould.
According to the requirement of unlike material,, materials such as gold, silver can form needed jewellery style as long as being dissolved the back above-mentioned jewellery mould of injection.
In sum, the present invention compares with existing traditional handicraft, has: characteristics such as Production Time is short, of good quality, easy to operate.Common jewellery one-shot forming needed only 15 minutes, and numerous and diverse jewellery also needed only 15 minutes, and as long as the ordinary people just can operate, for the apprentice, understood operation at a glance, and 7 days just can be skilled, the technology exquisiteness, and no solder joint, brightness is good, and innovation ability is strong.The present invention has improved the working (machining) efficiency of jewellery greatly, the jewellery manufacturing industry is sayed brought new leaping.
The specific embodiment
The specific embodiment of the invention now is described in detail in detail, and preparation method flow process of the present invention is:
One, rubber pattern
The jewellery specimen holder that to make by manual mode is between two blocks of rubber earlier; the pressurization that heats up on molding press is dissolved rubber and tightly is contained within outside the jewellery sample, after the cooling under pressure; with instrument rubber is cut the jewellery sample that will contain in it and take out, form rubber pattern.
Two, wax-pattern
Wax injector is added wax, regulates temperature and pressure and wax is injected rubber pattern form wax-pattern, behind the wax-pattern cooling forming, it is taken out from rubber pattern, again with instrument with the mould mould blank equating mouth of a river.
Three, plant wax
Utilize electric iron, wax-pattern spare according to different materials, is planted into a wax kind, reinstall one and have metal shell and the bottom is provided with in the container of wax-pattern bearing, wax-pattern and metal shell keep certain clearance, prepare reverse mould after forming a mould.
Four, reverse mould
Pour the mould for the treatment of reverse mould into gypsum, gypsum is vacuumized through modes such as vibrating, bleed by equipment, moulding is then at one end printed model word seal after doing naturally, prepares roasting.
Five, roasting
To treat that the roasting mould puts into 800 degrees centigrade high-temperature roasting stove mould is dried, treat to form the jewellery mould after the wax evaporation in the mould.
According to the requirement of unlike material,, materials such as gold, silver can form needed jewellery style as long as being dissolved the back above-mentioned jewellery mould of injection.
Claims (1)
1. the preparation method of a jewellery mould is characterized in that:
Preparation method flow process of the present invention is:
One, rubber pattern
The jewellery specimen holder that to make by manual mode is between two blocks of rubber earlier, the pressurization that heats up on molding press is dissolved rubber and tightly is contained within outside the jewellery sample, after the cooling under pressure, with instrument rubber is cut the jewellery sample that will contain in it and take out, form rubber pattern;
Two, wax-pattern
Wax injector is added wax, regulates temperature and pressure and wax is injected rubber pattern form wax-pattern, behind the wax-pattern cooling forming, it is taken out from rubber pattern, again with instrument with the blank equating mouth of a river;
Three, plant wax
Utilize electric iron, wax spare according to different materials, is planted into a wax kind, reinstall one and have in the container of metal shell, form a mould, prepare reverse mould;
Four, reverse mould
Pour the mould for the treatment of reverse mould into gypsum, gypsum is vacuumized again, back seal model word seal is done in moulding then naturally, prepares roasting;
Five, roasting
To treat that the roasting mould puts into 800 degrees centigrade high-temperature roasting stove mould is dried, can form the jewellery mould after the wax evaporation in mould.