CN108265369A - A kind of radiation protection antibacterial fabric and preparation method thereof - Google Patents
A kind of radiation protection antibacterial fabric and preparation method thereof Download PDFInfo
- Publication number
- CN108265369A CN108265369A CN201810252039.0A CN201810252039A CN108265369A CN 108265369 A CN108265369 A CN 108265369A CN 201810252039 A CN201810252039 A CN 201810252039A CN 108265369 A CN108265369 A CN 108265369A
- Authority
- CN
- China
- Prior art keywords
- parts
- radiation protection
- warp
- stalk
- weft
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
This case provides a kind of radiation protection antibacterial fabric and preparation method thereof, which is woven by warp and weft, and warp is formed by radioresistance fiber through spinning, and the composition of each component of radioresistance fiber by weight is:30 45 parts of 5 25 parts of red copper ultrafine wire, 25 40 parts of textile fabric, 20 45 parts of aqueous UV resins, 15 parts of light curing agent and water, weft is formed by anti-bacterial fibre through spinning, anti-bacterial fibre includes the composite fibre extracted by the pulp of garlic stalk, wormwood stalk, juniper, cotton mixing, wherein, garlic stalk, wormwood stalk, juniper, cotton mass ratio be(2‑3):(2‑3):(1‑2):(4‑5).The fabric that this case is provided not only has radiation proof function, and also with antibacterial functions, pregnant mother can clean the clothes made by the fabric in period of gestation, avoids by peculiar smell worry;In addition, the clothes made by the fabric personal can be worn, need to wear feeling of oppression and heat caused by an ordinary coat in the case of avoiding day heat more.
Description
Technical field
The present invention relates to textile manufacturing manufacture field, more particularly to a kind of radiation protection antibacterial fabric and preparation method thereof.
Background technology
The shielding property of silver is a long time ago just by it is found that and utilize, wide-spread silver fiber currently on the market
Exposure suit approves that such clothes should not clean by vast pregnant mother, and worn for long periods can grow many bacteriums, even if carrying out
Cleaning can not rub to avoid silver fiber is destroyed as ordinary coat and influence using effect, but simple clear water cleaning side
Formula is unable to reach effective degerming purpose, influences the health of pregnant woman.
Therefore, a kind of energy anti-radiation and antibacterial how is provided, fabric capable of washing becomes industry technology hardly possible urgently to be resolved hurrily
Topic.
Invention content
The purpose of the present invention is to provide a kind of radiation protection antibacterial fabric and preparation method thereof, to overcome the prior art not
Foot.
In order to achieve the above objectives, technical scheme is as follows:
The embodiment of the invention discloses a kind of radiation protection antibacterial fabrics, are woven by warp and weft, and the warp is by anti-spoke
It penetrates fiber to be formed through spinning, the composition of each component of the radioresistance fiber by weight is:5-25 parts of red copper ultrafine wire, weaving
30-45 parts of 25-40 parts of fiber, 20-45 parts of aqueous UV resins, 1-5 parts of light curing agent and water, the weft is passed through by anti-bacterial fibre
Spinning is formed, and the anti-bacterial fibre includes the mixing extracted by the pulp of garlic stalk, wormwood stalk, juniper, cotton mixing
Fiber, wherein, the garlic stalk, wormwood stalk, juniper, cotton mass ratio be(2-3):(2-3):(1-2):(4-5).Institute
State red copper ultrafine wire a diameter of 50-80 microns, length are 250-600 microns.
One of preferred embodiment as the present invention, the component of the red copper ultrafine wire is yellow gold.
One of preferred embodiment as the present invention, the textile fabric are polyester fiber.
One of preferred embodiment as the present invention, the aqueous UV resins are aqueous polyurethane acrylate, water-base epoxy
At least one of acrylate and waterborne polyester acrylate.
The embodiment of the invention also discloses a kind of production methods of radiation protection antibacterial fabric, include the following steps:
1)Weft makes:Pulp is respectively extracted from garlic stalk, wormwood stalk, juniper, cotton, wherein, the garlic straw
Stalk, wormwood stalk, juniper, cotton mass ratio be(2-3):(2-3):(1-2):(4-5), after various pulps are mixed, with super
Mixed pulp is promoted to generate concussion for acoustic wave device so that various pulps are uniformly mixed, with caustic soda and carbon disulfide processing slurry
The dregs of rice form antibacterial weft so as to form spinning solution, with spinning solution spinning;
2)Warp makes:By 5-25 parts of red copper ultrafine wire, 25-40 parts of textile fabric, 20-45 parts of aqueous UV resins, light curing agent
1-5 parts and 30-45 parts of water are uniformly mixed, and so as to obtain meridional fibers slurry, then, the meridional fibers slurry are carried out UV
Curing, so as to obtain radioresistance fiber, finally, radiation protection warp is made by spinning process by radioresistance fiber;
3)Above-mentioned warp and weft are knitted to form radiation protection antibacterial fabric.
One of preferred embodiment as the present invention after various pulp mixing, is ultrasonically treated with ultrasonic unit at room temperature
1-2 hours.
One of preferred embodiment as the present invention, to step 1)Obtained radiation protection warp sprays clear water to moistening, so
The radiation protection warp of moistening is fumigated with the aqueous solution of cactus and aloe afterwards;When the moisture in the aqueous solution of cactus and aloe is received
When being reduced to 50-100 times of the juice for being cactus and aloe, bleeding agent is added in thereto, and be uniformly mixed;Radiation protection is passed through again
Cactus that line input moisture is shunk and carry out immersion treatment 18-30 hour in the aqueous solution of aloe, finally will be after immersion prevent
Processing is dried in radiation warp.
One of preferred embodiment as the present invention, a diameter of 50-80 microns of the red copper ultrafine wire, length 250-
600 microns;And/or the component of the red copper ultrafine wire is yellow gold;And/or the textile fabric is polyester fiber;With/
Or, the aqueous UV resins is in aqueous polyurethane acrylate, waterborne epoxy acrylate and waterborne polyester acrylate
It is at least one.
Compared with prior art, the advantage of the invention is that:
1)Fabric provided by the present invention not only has radiation proof function, and also with antibacterial functions, pregnant mother can be in period of pregnancy
Between the clothes made by the fabric is cleaned, avoid by peculiar smell worry;In addition, the clothes made by the fabric can paste
It wears, needs to wear feeling of oppression and heat caused by an ordinary coat more in the case of avoiding day heat.2)Face provided by the present invention
The materials of material are relatively broad, cheap, saved manufacture cost, can be widely popularized.
Specific embodiment
Below in conjunction with the embodiment of the present invention, the technical solution in the embodiment of the present invention is clearly and completely described.
The embodiment of the invention discloses a kind of radiation protection antibacterial fabrics, are woven by warp and weft, the warp by
Radioresistance fiber is formed through spinning, and the composition of each component of the radioresistance fiber by weight is:5-25 parts of red copper ultrafine wire,
30-45 parts of 25-40 parts of textile fabric, 20-45 parts of aqueous UV resins, 1-5 parts of light curing agent and water, the weft is by antibacterial fibre
Dimension is formed through spinning, and the anti-bacterial fibre includes what is extracted by the pulp of garlic stalk, wormwood stalk, juniper, cotton mixing
Composite fibre, wherein, the garlic stalk, wormwood stalk, juniper, cotton mass ratio be(2-3):(2-3):(1-2):(4-
5).A diameter of 50-80 microns of the red copper ultrafine wire, length are 250-600 microns.
One of preferred embodiment as the present invention, the component of the red copper ultrafine wire is yellow gold,(Silver-bearing copper is red copper
It is a kind of)
As one of preferred embodiment of the present invention, the textile fabric is polyester fiber, but and be limited to polyester fiber, can also be
Other chemical fibres or natural fiber.
One of preferred embodiment as the present invention, the aqueous UV resins are aqueous polyurethane acrylate, water-base epoxy
At least one of acrylate and waterborne polyester acrylate.
The embodiment of the invention also discloses the production methods of above-mentioned radiation protection antibacterial fabric, include the following steps:
1)Weft makes:Pulp is respectively extracted from garlic stalk, wormwood stalk, juniper, cotton, wherein, the garlic straw
Stalk, wormwood stalk, juniper, cotton mass ratio be(2-3):(2-3):(1-2):(4-5), after various pulps are mixed, with super
Mixed pulp is promoted to generate concussion for acoustic wave device so that various pulps are uniformly mixed, with caustic soda and carbon disulfide processing slurry
The dregs of rice form antibacterial weft so as to form spinning solution, with spinning solution spinning;Various pulps can be caused using ultrasonic oscillation
Between movement occur be uniformly mixed so as to various pulps, avoid more violent mechanical stirring and cause the broken of fibr tissue
It is bad;
2)Warp makes:By 5-25 parts of red copper ultrafine wire, 25-40 parts of textile fabric, 20-45 parts of aqueous UV resins, light curing agent
1-5 parts and 30-45 parts of water are uniformly mixed, and so as to obtain meridional fibers slurry, then, the meridional fibers slurry are carried out UV
Curing, so as to obtain radioresistance fiber, finally, radiation protection warp is made by spinning process by radioresistance fiber;
3)Above-mentioned warp and weft are knitted to form radiation protection antibacterial fabric.
Garlic stalk, wormwood stalk, juniper, cotton materials are extensive, and cheap, garlic stalk, wormwood stalk, juniper
It is respectively provided with preferably sterilization and fungistatic effect, thus the weft using garlic stalk, wormwood stalk, juniper with reference to made by cotton
Can have good sterilization and fungistatic effect.Using the red copper with radiation-resisting functional as warp made of one of raw material with
Radiation-resisting functional, and can be cleaned.
One of preferred embodiment as the present invention after various pulp mixing, is ultrasonically treated with ultrasonic unit at room temperature
1-2 hours.One of preferred embodiment as the present invention, to step 1)Obtained radiation protection warp sprays clear water to moistening, so
The radiation protection warp of moistening is fumigated with the aqueous solution of cactus and aloe afterwards;When the moisture in the aqueous solution of cactus and aloe is received
When being reduced to 50-100 times of the juice for being cactus and aloe, bleeding agent is added in thereto, and be uniformly mixed;Radiation protection is passed through again
Cactus that line input moisture is shunk and carry out immersion treatment 18-30 hour in the aqueous solution of aloe, finally will be after immersion prevent
Processing is dried in radiation warp.Now radiation protection warp, which is fumigated, with the aqueous solution of cactus and aloe can cause anti-spoke
The fabric penetrated made by warp is more soft, is unlikely to deform, then the cactus and aloe that radiation protection warp input moisture is shunk
Aqueous solution carry out immersion treatment, can cause cactus and aloe is penetrated into going inside radiation protection warp, so as to further carry
The radiation-proof effect of high antibacterial warp.
By above technical scheme, fabric provided by the present invention not only has radiation proof function, also with antibacterial functions,
Pregnant mother can clean the clothes made by the fabric in period of gestation, avoid by peculiar smell worry;The fabric is made
Into clothes personal can wear, need to wear feeling of oppression and heat caused by an ordinary coat in the case of avoiding day heat more;In addition,
The materials of fabric provided by the present invention are relatively broad, cheap, saved manufacture cost, can be widely popularized.
Below in conjunction with specific embodiment, further explanation and description of the technical solution of the present invention are carried out.
Embodiment 1:
The present invention implements 1 and discloses a kind of radiation protection antibacterial fabric, is woven by warp and weft, warp is by radioresistance fiber
It is formed through spinning, the composition of each component of radioresistance fiber by weight is:It is 5 parts of red copper ultrafine wire, 25 parts of textile fabric, aqueous
30 parts of 20 parts of UV resins, 2 parts of light curing agent and water, weft are formed by anti-bacterial fibre through spinning, and anti-bacterial fibre is included by garlic
The composite fibre that the pulp that stalk, wormwood stalk, juniper, cotton mix is extracted, wherein, garlic stalk, wormwood stalk, Chinese juniper
Cypress, cotton mass ratio be 2:2:1:4.
Wherein, a diameter of 50 microns of red copper ultrafine wire, length are 250 microns, and the component of red copper ultrafine wire is closed for silver-bearing copper
Gold, textile fabric are polyester fiber, and aqueous UV resins are aqueous polyurethane acrylate, waterborne epoxy acrylate and aqueous poly-
At least one of ester acrylate.
The production method that the embodiment of the present invention 1 also discloses above-mentioned radiation protection antibacterial fabric, includes the following steps:
1)Weft makes:Pulp is respectively extracted from garlic stalk, wormwood stalk, juniper, cotton, wherein, garlic stalk, Chinese mugwort
Careless stalk, juniper, cotton mass ratio be 2:2:1:4, after various pulps are mixed, after being ultrasonically treated mixing with ultrasonic unit
Pulp 1 hour so that various pulps are uniformly mixed, pulp is handled so as to form spinning solution with caustic soda and carbon disulfide,
Antibacterial weft is formed with spinning solution spinning;
Clear water is sprayed to moistening to radiation protection warp, and the radiation protection that moistening is then fumigated with the aqueous solution of cactus and aloe passes through
Line;When the moisture in the aqueous solution of cactus and aloe is contracted to 100 times of the juice for being cactus and aloe, add thereto
Enter bleeding agent, and be uniformly mixed;It will be soaked in the aqueous solution of the cactus of radiation protection warp input moisture contraction and aloe again
Bubble processing 18 hours, is finally dried processing by the radiation protection warp after immersion;
2)Warp makes:5 parts of red copper ultrafine wire, 25 parts of textile fabric, 20 parts of aqueous UV resins, 2 parts of light curing agent and water 30
Part is uniformly mixed, and so as to obtain meridional fibers slurry, then, meridional fibers slurry is carried out UV curings, so as to obtain radioresistance
Finally, radiation protection warp is made by spinning process in radioresistance fiber by fiber;
3)Above-mentioned warp and weft are knitted to form radiation protection antibacterial fabric.
Embodiment 2:
The present invention implements 2 and discloses a kind of radiation protection antibacterial fabric, is woven by warp and weft, warp is by radioresistance fiber
It is formed through spinning, the composition of each component of radioresistance fiber by weight is:10 parts of red copper ultrafine wire, 30 parts of textile fabric, water
Property 35 parts of 25 parts of UV resins, 3 parts of light curing agent and water, weft formed by anti-bacterial fibre through spinning, and anti-bacterial fibre is including by big
The composite fibre that the pulp that garlic stalk, wormwood stalk, juniper, cotton mix is extracted, wherein, garlic stalk, wormwood stalk, Chinese juniper
Cypress, cotton mass ratio be 2:2:1:4.
Wherein, a diameter of 60 microns of red copper ultrafine wire, length are 300 microns, and the component of red copper ultrafine wire is closed for silver-bearing copper
Gold, textile fabric are polyester fiber, and aqueous UV resins are aqueous polyurethane acrylate, waterborne epoxy acrylate and aqueous poly-
At least one of ester acrylate.
The production method that the embodiment of the present invention 2 also discloses above-mentioned radiation protection antibacterial fabric, includes the following steps:
2)Weft makes:Pulp is respectively extracted from garlic stalk, wormwood stalk, juniper, cotton, wherein, garlic stalk, Chinese mugwort
Careless stalk, juniper, cotton mass ratio be 2:2:1:4, after various pulps are mixed, after being ultrasonically treated mixing with ultrasonic unit
Pulp 1 hour so that various pulps are uniformly mixed, pulp is handled so as to form spinning solution with caustic soda and carbon disulfide,
Antibacterial weft is formed with spinning solution spinning;
Clear water is sprayed to moistening to radiation protection warp, and the radiation protection that moistening is then fumigated with the aqueous solution of cactus and aloe passes through
Line;When the moisture in the aqueous solution of cactus and aloe is contracted to 90 times of the juice for being cactus and aloe, add thereto
Enter bleeding agent, and be uniformly mixed;It will be soaked in the aqueous solution of the cactus of radiation protection warp input moisture contraction and aloe again
Bubble processing 20 hours, is finally dried processing by the radiation protection warp after immersion;
2)Warp makes:10 parts of red copper ultrafine wire, 30 parts of textile fabric, 25 parts of aqueous UV resins, 3 parts of light curing agent and water 35
Part is uniformly mixed, and so as to obtain meridional fibers slurry, then, meridional fibers slurry is carried out UV curings, so as to obtain radioresistance
Finally, radiation protection warp is made by spinning process in radioresistance fiber by fiber;
3)Above-mentioned warp and weft are knitted to form radiation protection antibacterial fabric.
Embodiment 3:
The present invention implements 3 and discloses a kind of radiation protection antibacterial fabric, is woven by warp and weft, warp is by radioresistance fiber
It is formed through spinning, the composition of each component of radioresistance fiber by weight is:15 parts of red copper ultrafine wire, 35 parts of textile fabric, water
Property 40 parts of 30 parts of UV resins, 4 parts of light curing agent and water, weft formed by anti-bacterial fibre through spinning, and anti-bacterial fibre is including by big
The composite fibre that the pulp that garlic stalk, wormwood stalk, juniper, cotton mix is extracted, wherein, garlic stalk, wormwood stalk, Chinese juniper
Cypress, cotton mass ratio be 2.5:2.5:1.5:4.5.
Wherein, a diameter of 70 microns of red copper ultrafine wire, length are 350 microns, and the component of red copper ultrafine wire is closed for silver-bearing copper
Gold, textile fabric are polyester fiber, and aqueous UV resins are aqueous polyurethane acrylate, waterborne epoxy acrylate and aqueous poly-
At least one of ester acrylate.
The production method that the embodiment of the present invention 3 also discloses above-mentioned radiation protection antibacterial fabric, includes the following steps:
3)Weft makes:Pulp is respectively extracted from garlic stalk, wormwood stalk, juniper, cotton, wherein, garlic stalk, Chinese mugwort
Careless stalk, juniper, cotton mass ratio be 2.5:2.5:1.5:4.5, after various pulps are mixed, at ultrasonic unit ultrasound
It manages mixed pulp 1 hour, so that various pulps are uniformly mixed, is spun with caustic soda and carbon disulfide processing pulp so as to be formed
Silk stock solution forms antibacterial weft with spinning solution spinning;
Clear water is sprayed to moistening to radiation protection warp, and the radiation protection that moistening is then fumigated with the aqueous solution of cactus and aloe passes through
Line;When the moisture in the aqueous solution of cactus and aloe is contracted to 80 times of the juice for being cactus and aloe, add thereto
Enter bleeding agent, and be uniformly mixed;It will be soaked in the aqueous solution of the cactus of radiation protection warp input moisture contraction and aloe again
Bubble processing 25 hours, is finally dried processing by the radiation protection warp after immersion;
2)Warp makes:15 parts of red copper ultrafine wire, 35 parts of textile fabric, 30 parts of aqueous UV resins, 4 parts of light curing agent and water 40
Part is uniformly mixed, and so as to obtain meridional fibers slurry, then, meridional fibers slurry is carried out UV curings, so as to obtain radioresistance
Finally, radiation protection warp is made by spinning process in radioresistance fiber by fiber;
3)Above-mentioned warp and weft are knitted to form radiation protection antibacterial fabric.
Embodiment 4:
The present invention implements 4 and discloses a kind of radiation protection antibacterial fabric, is woven by warp and weft, warp is by radioresistance fiber
It is formed through spinning, the composition of each component of radioresistance fiber by weight is:20 parts of red copper ultrafine wire, 40 parts of textile fabric, water
Property 40 parts of 35 parts of UV resins, 4.5 parts of light curing agent and water, weft formed by anti-bacterial fibre through spinning, anti-bacterial fibre including by
Garlic stalk, wormwood stalk, juniper, cotton mixing the composite fibre extracted of pulp, wherein, garlic stalk, wormwood stalk,
Juniper, cotton mass ratio be 2.5:2.5:1.5:4.5.
Wherein, a diameter of 75 microns of red copper ultrafine wire, length are 500 microns, and the component of red copper ultrafine wire is closed for silver-bearing copper
Gold, textile fabric are polyester fiber, and aqueous UV resins are aqueous polyurethane acrylate, waterborne epoxy acrylate and aqueous poly-
At least one of ester acrylate.
The production method that the embodiment of the present invention 4 also discloses above-mentioned radiation protection antibacterial fabric, includes the following steps:
4)Weft makes:Pulp is respectively extracted from garlic stalk, wormwood stalk, juniper, cotton, wherein, garlic stalk, Chinese mugwort
Careless stalk, juniper, cotton mass ratio be 2.5:2.5:1.5:4.5, after various pulps are mixed, at ultrasonic unit ultrasound
It manages mixed pulp 1 hour, so that various pulps are uniformly mixed, is spun with caustic soda and carbon disulfide processing pulp so as to be formed
Silk stock solution forms antibacterial weft with spinning solution spinning;
Clear water is sprayed to moistening to radiation protection warp, and the radiation protection that moistening is then fumigated with the aqueous solution of cactus and aloe passes through
Line;When the moisture in the aqueous solution of cactus and aloe is contracted to 70 times of the juice for being cactus and aloe, add thereto
Enter bleeding agent, and be uniformly mixed;It will be soaked in the aqueous solution of the cactus of radiation protection warp input moisture contraction and aloe again
Bubble processing 30 hours, is finally dried processing by the radiation protection warp after immersion;
2)Warp makes:20 parts of red copper ultrafine wire, 40 parts of textile fabric, 35 parts of aqueous UV resins, 4.5 parts of light curing agent and water
40 parts are uniformly mixed, and so as to obtain meridional fibers slurry, then, meridional fibers slurry are carried out UV curings, so as to obtain anti-spoke
Fiber is penetrated, finally, radioresistance fiber is made by radiation protection warp by spinning process;
3)Above-mentioned warp and weft are knitted to form radiation protection antibacterial fabric.
Embodiment 5:
The present invention implements 5 and discloses a kind of radiation protection antibacterial fabric, is woven by warp and weft, warp is by radioresistance fiber
It is formed through spinning, the composition of each component of radioresistance fiber by weight is:25 parts of red copper ultrafine wire, 40 parts of textile fabric, water
Property 45 parts of 45 parts of UV resins, 5 parts of light curing agent and water, weft formed by anti-bacterial fibre through spinning, and anti-bacterial fibre is including by big
The composite fibre that the pulp that garlic stalk, wormwood stalk, juniper, cotton mix is extracted, wherein, garlic stalk, wormwood stalk, Chinese juniper
Cypress, cotton mass ratio be 3:3:2:5.
Wherein, a diameter of 80 microns of red copper ultrafine wire, length are 600 microns, and the component of red copper ultrafine wire is closed for silver-bearing copper
Gold, textile fabric are polyester fiber, and aqueous UV resins are aqueous polyurethane acrylate, waterborne epoxy acrylate and aqueous poly-
At least one of ester acrylate.
The production method that the embodiment of the present invention 5 also discloses above-mentioned radiation protection antibacterial fabric, includes the following steps:
5)Weft makes:Pulp is respectively extracted from garlic stalk, wormwood stalk, juniper, cotton, wherein, garlic stalk, Chinese mugwort
Careless stalk, juniper, cotton mass ratio be 3:3:2:5, after various pulps are mixed, after being ultrasonically treated mixing with ultrasonic unit
Pulp 1 hour so that various pulps are uniformly mixed, pulp is handled so as to form spinning solution with caustic soda and carbon disulfide,
Antibacterial weft is formed with spinning solution spinning;
Clear water is sprayed to moistening to radiation protection warp, and the radiation protection that moistening is then fumigated with the aqueous solution of cactus and aloe passes through
Line;When the moisture in the aqueous solution of cactus and aloe is contracted to 50 times of the juice for being cactus and aloe, add thereto
Enter bleeding agent, and be uniformly mixed;It will be soaked in the aqueous solution of the cactus of radiation protection warp input moisture contraction and aloe again
Bubble processing 30 hours, is finally dried processing by the radiation protection warp after immersion;
2)Warp makes:25 parts of red copper ultrafine wire, 40 parts of textile fabric, 45 parts of aqueous UV resins, 5 parts of light curing agent and water 45
Part is uniformly mixed, and so as to obtain meridional fibers slurry, then, meridional fibers slurry is carried out UV curings, so as to obtain radioresistance
Finally, radiation protection warp is made by spinning process in radioresistance fiber by fiber;
3)Above-mentioned warp and weft are knitted to form radiation protection antibacterial fabric.
The shielding property evaluation of the fabric improved of 1-5 of the embodiment of the present invention:
It is below the fabric shield effectiveness in embodiment 1-5(Shield effectiveness refer under the same level of drive by shielding material with
The ratio between received power or voltage during no shielding material)Test result, effect experiment explanation:The detection method of shield effectiveness
Using the prior art, test result is shown in Table 1.
Table 1
Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 |
99.99915% | 99.99917% | 99.99921% | 99.99925% | 99.99928% |
A variety of modifications of these embodiments will be apparent for those skilled in the art, determine herein
The General Principle of justice can be realized in other embodiments without departing from the spirit or scope of the present invention.Therefore, originally
Invention is not intended to be limited to the embodiments shown herein, and is to fit to and the principles and novel features disclosed herein
Consistent most wide range.
Claims (9)
1. a kind of radiation protection antibacterial fabric, it is characterised in that:It is woven by warp and weft, the warp is by radioresistance fiber
It is formed through spinning, the composition of each component of the radioresistance fiber by weight is:5-25 parts of red copper ultrafine wire, textile fabric
30-45 parts of 25-40 parts, 20-45 parts of aqueous UV resins, 1-5 parts of light curing agent and water, the weft is by anti-bacterial fibre through spinning
It being formed, the anti-bacterial fibre includes the composite fibre extracted by the pulp of garlic stalk, wormwood stalk, juniper, cotton mixing,
Wherein, the garlic stalk, wormwood stalk, juniper, cotton mass ratio be(2-3):(2-3):(1-2):(4-5).
2. a kind of radiation protection antibacterial fabric according to claim 1, it is characterised in that:The red copper ultrafine wire it is a diameter of
50-80 microns, length is 250-600 microns.
3. a kind of radiation protection antibacterial fabric according to claim 1, it is characterised in that:The component of the red copper ultrafine wire is
Yellow gold.
4. a kind of radiation protection antibacterial fabric according to claim 1, it is characterised in that:The textile fabric is fine for polyester
Dimension.
5. a kind of radiation protection antibacterial fabric according to claim 1, it is characterised in that:The aqueous UV resins are aqueous poly-
At least one of urethane acrylate, waterborne epoxy acrylate and waterborne polyester acrylate.
6. a kind of production method of radiation protection antibacterial fabric, it is characterised in that:Include the following steps:
1)Weft makes:Pulp is respectively extracted from garlic stalk, wormwood stalk, juniper, cotton, wherein, the garlic straw
Stalk, wormwood stalk, juniper, cotton mass ratio be(2-3):(2-3):(1-2):(4-5), after various pulps are mixed, with super
Mixed pulp is promoted to generate concussion for acoustic wave device so that various pulps are uniformly mixed, with caustic soda and carbon disulfide processing slurry
The dregs of rice form antibacterial weft so as to form spinning solution, with spinning solution spinning;
2)Warp makes:By 5-25 parts of red copper ultrafine wire, 25-40 parts of textile fabric, 20-45 parts of aqueous UV resins, light curing agent
1-5 parts and 30-45 parts of water are uniformly mixed, and so as to obtain meridional fibers slurry, then, the meridional fibers slurry are carried out UV
Curing, so as to obtain radioresistance fiber, finally, radiation protection warp is made by spinning process by radioresistance fiber;
3)Above-mentioned warp and weft are knitted to form radiation protection antibacterial fabric.
7. the production method of radiation protection antibacterial fabric according to claim 6, it is characterised in that:After various pulp mixing,
It is ultrasonically treated 1-2 hours with ultrasonic unit at room temperature.
8. the production method of radiation protection antibacterial fabric according to claim 6, it is characterised in that:To step 1)Obtained
Radiation protection warp sprays clear water to moistening, and the radiation protection warp of moistening is then fumigated with the aqueous solution of cactus and aloe;
When the moisture in the aqueous solution of cactus and aloe is contracted to 50-100 times of the juice for being cactus and aloe, Xiang Qi
Middle addition bleeding agent, and be uniformly mixed;
Immersion treatment will be carried out 18-30 hours in the aqueous solution of the cactus of radiation protection warp input moisture contraction and aloe again,
Processing finally is dried in the radiation protection warp after immersion.
9. the production method of radiation protection antibacterial fabric according to claim 6, it is characterised in that:The red copper ultrafine wire
50-80 microns a diameter of, length is 250-600 microns;And/or the component of the red copper ultrafine wire is yellow gold;And/or
The textile fabric is polyester fiber;And/or the aqueous UV resins are aqueous polyurethane acrylate, water-base epoxy propylene
At least one of acid esters and waterborne polyester acrylate.