CN101967726B - Knitted fabric comprising platinum light quanta and preparation method thereof - Google Patents
Knitted fabric comprising platinum light quanta and preparation method thereof Download PDFInfo
- Publication number
- CN101967726B CN101967726B CN 201010295701 CN201010295701A CN101967726B CN 101967726 B CN101967726 B CN 101967726B CN 201010295701 CN201010295701 CN 201010295701 CN 201010295701 A CN201010295701 A CN 201010295701A CN 101967726 B CN101967726 B CN 101967726B
- Authority
- CN
- China
- Prior art keywords
- platinum
- lycra
- dyeing
- preparation
- percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a knitted fabric comprising platinum light quanta and a preparation method thereof. The knitted fabric is prepared from the following raw materials in percentage by weight: 95 percent of platinum fiber blended fibers, and 5 percent of lycra, wherein the platinum fiber blended fibers comprise the following components in percentage by weight: 55 to 80 percent of platinum fibers, and 20 to 45 percent of long stapled cotton. The knitted fabric is scientifically blended by adopting the platinum fibers and the high-quality long stapled cotton, and then is knitted through perfect combination with the lycra. The platinum fibers comprise nano-scale ultra-microns namely photoion powder of which the content is more than or equal to 0.5 percent; and the photoion powder can absorb light quanta with various wavelengths to ensure that the photoion powder is amplified by over 10 times, and is radiated out to act on a human body and generate a positive effect.
Description
Technical field
The present invention relates to a kind of weaving face fabric, especially relate to a kind of knit fabric that contains the platinum light quantum and preparation method thereof.
Background technology
" platinum fiber " be Jilin Chemical Fibre Co., Ltd with natural plant raw material and platinum light quantum, adopt the patent of Japanese photoelectricity medical treatment goods, materials and equipments Co., Ltd. invention, utilize special process, the functional fiber of joint development.
Contain ultramicron through experiment confirm " platinum fiber ", have the human activin large biological molecule activity, the molecule of organism can be excited and be in higher vibrational state, make these trace elements can absorb and resonate from the trace fertility light (4-14 μ m) of the person, radiate again the fertility light of the new model with far infrared effect, and stably launch and be equivalent to the light quantum of existing light quantum more than 4 times in the air.
The ultramicron releasing mechanism: the ultramicron semiconductor powder absorbs the light of all wavelengths, and amplification also radiates light, as the far infrared effect of wavelength effect with as the photocatalyst effect of graininess effect.
" platinum fiber " that contains ultramicron has the microcirculation in human body of improvement, suction, the specific function such as antistatic, antibiotic.But the trace element in the platinum fiber forms luminous energy, electric energy and heat energy in the thing absorbing environmental, discharge the energy as photocatalyst, reach the function of sterilization, contained trace element forms the light quantum that thing discharges in " platinum fiber " except sterilization, all right activating cell, stimulating circulation increases self resistance, improves the effect of immunity.Its employed platinum photoion powder can absorb the light quantum of various wavelength, make it amplification, and radiate, the light quantum quantitative determination of carrying out through northeastern Japan electronic industry Co., Ltd., amplification can reach 10 times, it not only has the far infrared effect as wavelength, has simultaneously the photocatalyst effect as graininess.Promote and improve blood circulation, strengthen metabolism, improve immune function of human body and have anti-inflammatory, detumescence, analgesic effect.
Table 1 platinum fiber and other fibre property contrast tables
| Cotton | Model | Terylene | Platinum fiber | Long-staple cotton | |
| Line density (dtex) | 1.65-1.95 | 1.7 | 1.7 | 1.11-5.56 | 1.43-1.67 |
| Do strong (CN/tex) | 20-24 | 34-36 | 40-52 | ≥21 | 29-34 |
| Wet strong (CN/tex) | 26-30 | 19-21 | 40-52 | ≥12 | 35-40 |
As can be seen from the above table, platinum fiber wet lower by force, only strong by about 50% for doing.
In theory, that platinum fiber has is antibiotic, promote and improve sanguimotor effect, can be applicable to underwear, bed necessaries, household and health treatment series, but because after platinum fiber absorbs moisture, the diameter chap, Length Contraction, and become heavily hardening, brute force be drop by half almost also, therefore should not under hygrometric state, process, give knitting weave, dyeing and finishing brought very large difficulty, and the wearability of its fabric is had a greatly reduced quality, and affected its application in knitting field.
Summary of the invention
First technical problem that the present invention will solve provides a kind of knit fabric that contains the platinum light quantum, and this fabric adopts platinum fiber and the blending of high-quality long-staple cotton science, forms with Lycra perfect adaptation braiding.Containing the nanoscale ultramicron in the platinum fiber---the photoion powder, its content 〉=0.5% can absorb the light quantum of various wavelength, makes it amplification more than 10 times and radiate to act on human body, produces positive effect.
Second technical problem that the present invention will solve provides a kind of preparation method who contains the knit fabric of platinum light quantum.
For solving above-mentioned first technical problem, technical scheme provided by the present invention is: a kind of knit fabric that contains the platinum light quantum, and it is to be made by the raw material of following percentage by weight: the platinum fiber blended yarn is 95%, Lycra is 5%; Wherein, contain the composition of following percentage by weight in the described platinum fiber blended yarn: platinum fiber 55%～80%, long-staple cotton 20%～45%.
For solving above-mentioned second technical problem, the above-mentioned preparation method who contains the knit fabric of platinum light quantum comprises the steps:
(1) select the raw material of following percentage by weight:
The platinum fiber blended yarn is 95%, and Lycra is 5%; The composition that contains following percentage by weight in the described platinum fiber blended yarn: platinum fiber 55%～80%, long-staple cotton 20%～45%, the number of this platinum fiber blended yarn are 30～80s;
(2) spinning
Described spinning process comprises: opener, comb and parallel cotton fibers prior to spinning, in the lump, two also, rove and spun yarn;
(3) weave
Above-mentioned platinum fiber blended yarn and Lycra yarn are interweaved apart from loom at fine needle, be made into knitting blank cloth, wherein, the production temperature is 28～30 ℃, and relative humidity is 65%～68%, and the loom speed of a motor vehicle is 17～19r/min; The platinum fiber yarn is very sensitive to weaving workshop moisture temperature, when relative humidity is low, and yarn powerful good, good springiness, ABRASION RESISTANCE is good, easily weaves; But too small, broken end increases, and fabric defect increases.Hello yarn tension should guarantee stable nothing sudden change when weaving in addition, and yarn tension is controlled at 3～6g.
(3) dyeing and finishing
Described dyeing and finishing process comprises: blank breaks volume, pre-setting, closes rib, floats the end, dyeing, frivolous water, torn edges and typing.
Further, described long-staple cotton is that length is 38～40mm, and short fiber content is at the long-staple cotton below 0.9%; The long-staple cotton fiber length that adopts is long, and regularity is good, and short flannel is few, and the blended yarn brute force is high behind the resultant yarn, and bar is done evenly, and yam surface is bright and clean, and filoplume is few, and the wearability of fabric improves.
Further, use airflow dyeing machine in the described dyeing and finishing process, to reduce the infringement to fiber.Platinum fiber belongs to responsive fiber, because airflow dyeing machine is dye liquor through atomizing again by soft the taking on the fabric of air, can not damage platinum fiber; And common overflow dyeing machine is the dye liquor brute force to be injected in could promote fabric on the fabric, very easily damages platinum fiber.
Described platinum fiber physical index such as following table 1:
Table 1
| Project | Unit | Data |
| Do strong | CN/dtex | ≥2.1 |
| Wet strong | CN/dtex | ≥1.2 |
| Dried stretching | ％ | ≥17 |
| Platinum photoion effective content | ％ | ≥0.5 |
The invention has the beneficial effects as follows:
1, strengthens the clotting time value
Detect impact such as following table 2 that tested material was worth the rat clotting time through Beijing Disease Prevention and Control Centre:
Table 2 tested material is on the impact of TT, APTT (s) changing value degree
| Group | Number of animals (only) | The TT time (s) | The P value | The APTT time (s) | The P value |
| Control group | 11 | 21.94±0.56 | 14.91±1.24 |
| 70% fibrous type group | 10 | 22.81±0.92 | 0.010 | 16.06±1.14 | 0.033 |
Control group fabric: sticking cotton Lycra single jersey: 95% J40
SThe 20D Lycra of viscose glue 70%/cotton 30%+5%;
70% fibrous type group fabric: platinum Lycra single jersey: 95% J40
SThe 20D Lycra of platinum fiber 70%/long-staple cotton 30%+5%.
By as seen from Table 2, rat contact in 4 hours 70% platinum fiber fabric is compared with contrast cloth group, thrombin time test value (TT) and activated partial thrombin time test value (APTT) are apparently higher than control group, and significant difference (P＜0.05) is arranged, can judge that 70% platinum fiber fabric has the effect that strengthens the clotting time.
2, reduce blood viscosity
Detect through Beijing Disease Prevention and Control Centre, tested material is on impact such as the following table 3 of rat blood rheology:
Table 3 tested material is on the impact of rat blood rheology
| Group | Number of animals (only) | 1s | The P value | 30s | The P value | 180s | The P value |
| Control group | 11 | 20.07±3.45 | 6.86±0.81 | 4.33±0.38 | |||
| 70% fibrous type group | 10 | 31.08±5.85 | 0.000 | 8.62±1.12 | 0.000 | 5.15±0.97 | 0.000 |
Control group fabric: sticking cotton Lycra single jersey: 95% J40
SThe 20D Lycra of viscose glue 70%/cotton 30%+5%;
70% fibrous type group fabric: platinum Lycra single jersey: 95% J40
SThe 20D Lycra of platinum fiber 70%/long-staple cotton 30%+5%.
By as seen from Table 3, behind rat contact in the 4 hours 70% platinum fiber fabric, all apparently higher than contrast cloth contact group, and its difference had conspicuousness (P＜0.01) to its blood flow variate, can judge that 70% platinum fiber fabric has the effect that reduces blood viscosity 1 second, 30 seconds and 180 seconds.
3, antibiotic, biocidal property
After testing, the described bacteriostasis rate that contains the light quantum knit fabric reaches 99%, has extremely strong antibiotic and bacteriostasis.
The specific embodiment
Embodiment 1
A kind of manufacture method of knit fabric of platiniferous light quantum comprises the steps:
1) spinning
Be that 55% platinum fiber, 45% long-staple cotton spun yarn number are the platinum fiber blended yarn of 40s with percentage by weight; The length of described long-staple cotton is 40mm, and short fiber content is 0.8%; Its spinning technological process is: opener-comb and parallel cotton fibers prior to spinning-in the lump-two also-rove-spun yarn.
2) weave
Above-mentioned platinum fiber blended yarn is interweaved with the 20D Lycra on the knitting single-side machine of 28G, be woven into knitting blank cloth; The weight ratio of described platinum fiber blended yarn and Lycra is 95%: 5%; The loom speed of a motor vehicle is 17r/min, and yarn tension is 3g; The production temperature is 28 ℃, and relative humidity is 65%.
3) dyeing and finishing
With above-mentioned knitting blank cloth process: blank break volume-pre-setting-close rib-the float end-dyeing-frivolous water-torn edges-shaping process to carry out the dyeing and finishing processing, forms the described knit fabric that contains the platinum light quantum; Dyeing process uses airflow dyeing machine in dyeing and finishing process.
Embodiment 2
A kind of manufacture method of knit fabric of platiniferous light quantum comprises the steps:
1) spinning
Be that 80% platinum fiber, 20% long-staple cotton spun yarn number are the platinum fiber blended yarn of 40s with percentage by weight; The length of described long-staple cotton is 38mm, and short fiber content is 0.8%; Its spinning technological process is: opener-comb and parallel cotton fibers prior to spinning-in the lump-two also-rove-spun yarn.
2) weave
Above-mentioned platinum fiber blended yarn is interweaved with the 20D Lycra on the knitting single-side machine of 28G, be woven into knitting blank cloth; The weight ratio of described platinum fiber blended yarn and Lycra is 95%: 5%, and the loom speed of a motor vehicle is 19r/min, and yarn tension is 6g; The production temperature is 30 ℃, and relative humidity is 68%.
3) dyeing and finishing
With above-mentioned knitting blank cloth process: blank break volume-pre-setting-close rib-the float end-dyeing-frivolous water-torn edges-shaping process to carry out the dyeing and finishing processing, forms the described knit fabric that contains the platinum light quantum; Dyeing process uses airflow dyeing machine in dyeing and finishing process.
Obviously, the above embodiment of the present invention only is for example of the present invention clearly is described, and is not to be restriction to embodiments of the present invention.For those of ordinary skill in the field, can also make other changes in different forms on the basis of the above description.Here can't give all embodiments exhaustive.Everyly belong to the row that apparent variation that technical scheme of the present invention extends out or change still are in protection scope of the present invention.
Claims (3)
1. a preparation method who contains the knit fabric of platinum light quantum is characterized in that, comprises the steps:
(1) select the raw material of following percentage by weight:
The platinum fiber blended yarn is 95%, and Lycra is 5%; The composition that contains following percentage by weight in the described platinum fiber blended yarn: platinum fiber 55%～80%, long-staple cotton 20%～45%, the number of this platinum fiber blended yarn are 30～80s;
(2) spinning;
(3) weave
Above-mentioned platinum fiber blended yarn and Lycra yarn are interweaved apart from loom at fine needle, be made into knitting blank cloth, wherein, the production temperature is 28～30 ℃, and relative humidity is 65%～68%, and the loom speed of a motor vehicle is 17～19r/min, and yarn tension is 3～6g;
(4) dyeing and finishing.
2. the preparation method who contains the knit fabric of platinum light quantum according to claim 1 is characterized in that, described long-staple cotton is that length is 38～40mm, and short fiber content is at the long-staple cotton below 0.9%.
3. the preparation method who contains the knit fabric of platinum light quantum according to claim 1 is characterized in that, dyeing process uses airflow dyeing machine in the described dyeing and finishing process.