CN105483936B - A kind of production method of spunlace non-woven cloth - Google Patents
A kind of production method of spunlace non-woven cloth Download PDFInfo
- Publication number
- CN105483936B CN105483936B CN201610055655.8A CN201610055655A CN105483936B CN 105483936 B CN105483936 B CN 105483936B CN 201610055655 A CN201610055655 A CN 201610055655A CN 105483936 B CN105483936 B CN 105483936B
- Authority
- CN
- China
- Prior art keywords
- woven cloth
- spunlace non
- obtains
- production method
- thing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of production method of spunlace non-woven cloth, comprise the following steps：(1) root of cotton piece is won；(2) the cotton piece root thing that step (1) obtains is smashed；(3) thing of smashing for obtaining step (2) is heated to 70 75 DEG C, and keeps 40 60min at such a temperature, obtains slurry；(4) slurry that step (3) obtains is stirred into 20 25min at 70 75 DEG C, obtains the ultra-fine cotton fiber for producing spunlace non-woven cloth；(5) viscose rayon is added in the ultra-fine cotton fiber obtained to step (4), obtain spunlace non-woven cloth, the spunlace non-woven cloth obtained using the production method has a soft, durable, environmentally friendly, good water absorption, nontoxic non-stimulated no sensitization, it is easy to use comfortable the advantages that.
Description
Art
The present invention relates to non-woven fabrics manufacturing field, more particularly to a kind of production method of spunlace non-woven cloth.
Background technology
Spunlace non-woven cloth is by the fine water flow jet of high pressure to one or more layers web, fiber is mutually become entangled in one
Rise, so that fibre web is able to reinforce and possesses certain strength, obtained fabric is spunlace non-woven cloth.The fiber of spunlace non-woven cloth
Raw material sources are extensive, can be terylene, polyamide fibre, polypropylene fibre, viscose rayon, chitin fiber, superfine fibre, tencel, silk, bamboo fibre
Dimension, wood pulp cellulose, alginate fibre etc..
Natural cotton has soft, environmental protection, good water absorption, nontoxic non-stimulated no cause because raw material is sufficient, processing is simple
Quick property, it is easy to use comfortable the advantages that, be widely used in spunlace non-woven cloth raw material production in, use cotton fiber production spun lacing
Non-woven fabrics, can avoiding non-woven fabrics of synthetic fiber, in general cotton fiber is all to use cotton because of infringement of its chemical composition to human body
Flower is made, and the fiber and thing containing glue of cotton piece root are not utilized then well, causes the wasting of resources, while spun lacing
Viscose rayon is generally needed to be added in the production process of non-woven fabrics, viscose rayon is a kind of synthetic regenerated chemical fibre, if with
Amount can excessively cause health hazard to user, also not meet energy-conserving and environment-protective, the main trend of health and safety.
The content of the invention
The purpose of the present invention is to be directed to the above-mentioned problems in the prior art, there is provided a kind of producer of spunlace non-woven cloth
Method, the durable quality of spunlace non-woven cloth that this method produces to obtain is good, has good water absorbing properties, and energy-saving ring is ensured public security
Entirely.
The technical solution adopted for the present invention to solve the technical problems is：
A kind of production method of spunlace non-woven cloth, comprises the following steps：
(1) root of cotton piece is won；
(2) the cotton piece root thing that step (1) obtains is smashed；
(3) thing of smashing for obtaining step (2) is heated to 70-75 DEG C, and keeps 40-60min at such a temperature, is starched
Shape thing；
(4) slurry for obtaining step (3) stirs 20-25min at 70-75 DEG C, obtains being used to produce spun lacing nonwoven
The ultra-fine cotton fiber of cloth；
(5) viscose rayon is added in the ultra-fine cotton fiber obtained to step (4), obtains spunlace non-woven cloth.
Further, the root of the cotton piece described in step (1) includes cotton seed, impurity and thing containing glue.
Further, it is 1mm-2mm to smash described cotton piece root thing to length in step (2).
Further, the retention time described in step (3) is 40-50min.
Further, the stir speed (S.S.) of slurry is 500-800r/min in step (4).
Further, the percentage by weight of viscose fiber is 30-50% in step (5), the weight percent of ultra-fine cotton fiber
Than for 50-70%.
Compared with prior art, the beneficial effect comprise that：Using cotton piece root material, by smashing, add
Hot pulp, stirring and glue is added to obtain spunlace non-woven cloth, technique is simple, easily realizes industrialization, and obtained spunlace non-woven cloth is more
Add it is solid endure hardships, water absorption rate is higher, simultaneously because containing colloid in cotton root material, portion adhesive is replaced with lac
Fiber, it is possible to reduce the usage amount of viscose rayon, more energy-saving environmental protection safety
Embodiment
With reference to embodiment, the present invention will be further described：
Embodiment 1
A kind of production method of spunlace non-woven cloth, comprises the following steps：
(1) root of cotton piece is won；
(2) the cotton piece root thing that step (1) obtains is smashed to 1mm；
(3) thing of smashing for obtaining step (2) is heated to 70 DEG C, and keeps 40min at such a temperature, obtains slurry；
(4) slurry for obtaining step (3) stirs 20min at 70 DEG C, obtains for producing the super of spunlace non-woven cloth
Thin cotton fiber, stir speed (S.S.) 500r/min；
(5) viscose rayon is added in the ultra-fine cotton fiber obtained to step (4), obtains spunlace non-woven cloth.
In the present embodiment, the percentage by weight of viscose rayon is 30%, and the percentage by weight of ultra-fine cotton fiber is 70%.
Embodiment 2
A kind of production method of spunlace non-woven cloth, comprises the following steps：
(1) root of cotton piece is won；
(2) the cotton piece root thing that step (1) obtains is smashed to 2mm；
(3) thing of smashing for obtaining step (2) is heated to 75 DEG C, and keeps 60min at such a temperature, obtains slurry；
(4) slurry for obtaining step (3) stirs 25min at 75 DEG C, obtains for producing the super of spunlace non-woven cloth
Thin cotton fiber, stir speed (S.S.) 800r/min；
(5) viscose rayon is added in the ultra-fine cotton fiber obtained to step (4), obtains spunlace non-woven cloth.
In the present embodiment, the percentage by weight of viscose rayon is 50%, and the percentage by weight of ultra-fine cotton fiber is 50%.
Embodiment 3
A kind of production method of spunlace non-woven cloth, comprises the following steps：
(1) root of cotton piece is won；
(2) the cotton piece root thing that step (1) obtains is smashed to 1mm；
(3) thing of smashing for obtaining step (2) is heated to 75 DEG C, and keeps 40min at such a temperature, obtains slurry；
(4) slurry for obtaining step (3) stirs 25min at 75 DEG C, obtains for producing the super of spunlace non-woven cloth
Thin cotton fiber, stir speed (S.S.) 500r/min；
(5) viscose rayon is added in the ultra-fine cotton fiber obtained to step (4), obtains spunlace non-woven cloth.
In the present embodiment, the percentage by weight of viscose rayon is 40%, and the percentage by weight of ultra-fine cotton fiber is 60%.
The spunlace non-woven cloth obtained using the production method has soft, durable, environmentally friendly, good water absorption, nontoxic nothing
Stimulate without sensitization, it is easy to use comfortable the advantages that.
The present invention is described in detail above by embodiment, but the content is only the preferable implementation of the present invention
Example, it is impossible to be considered as the practical range for limiting the present invention.All equivalent changes made according to the present patent application scope and improvement
Deng, all should still belong to the present invention patent covering scope within.
Claims (4)
1. a kind of production method of spunlace non-woven cloth, it is characterised in that comprise the following steps：
(1) root of cotton piece, including cotton seed, impurity and thing containing glue are won；
(2) the cotton piece root thing that step (1) obtains is smashed；
(3) thing of smashing for obtaining step (2) is heated to 70-75 DEG C, and keeps 40-60min at such a temperature, obtains pulpous state
Thing；
(4) slurry for obtaining step (3) stirs 20-25min at 70-75 DEG C, obtains for producing spunlace non-woven cloth
Ultra-fine cotton fiber；
(5) viscose rayon is added in the ultra-fine cotton fiber obtained to step (4), obtains spunlace non-woven cloth, the weight of viscose rayon
Percentage is 30-50%, and the percentage by weight of ultra-fine cotton fiber is 50-70%.
2. the production method of spunlace non-woven cloth according to claim 1, it is characterised in that：By the cotton in step (2)
It is 1mm-2mm that piece root thing, which is smashed to length,.
3. the production method of spunlace non-woven cloth according to claim 1, it is characterised in that：When being kept described in step (3)
Between be 40-50min.
4. the production method of spunlace non-woven cloth according to claim 1, it is characterised in that：Slurry stirs in step (4)
It is 500-800r/min to mix speed.