CN108250812A - 一种石墨烯通用型防水涂料 - Google Patents
一种石墨烯通用型防水涂料 Download PDFInfo
- Publication number
- CN108250812A CN108250812A CN201810041496.5A CN201810041496A CN108250812A CN 108250812 A CN108250812 A CN 108250812A CN 201810041496 A CN201810041496 A CN 201810041496A CN 108250812 A CN108250812 A CN 108250812A
- Authority
- CN
- China
- Prior art keywords
- parts
- graphene
- water
- powder
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种石墨烯通用型防水涂料,其由重量比为60%‑70%的粉料和重量比为30%‑40%的液料组成,其中,粉料由以下组分和重量份组成:普通硅酸盐水泥50‑60份,石英砂40‑50份,石墨烯纳米片10‑15份,减水剂1‑3份,消泡粉0.1‑0.3份;液料由以下组分和重量份组成:丙烯酸乳液45‑50份,氧化石墨烯5‑8份,水50‑60份,防腐剂0.5‑1份,消泡剂0.03‑0.05份。本发明比现有的通用型水泥基防水涂料在拉伸强度、断裂伸长率、粘结强度及抗渗性上都能显著提高。
Description
技术领域
本发明属于建筑材料技术领域,具体涉及一种石墨烯通用型防水涂料。
背景技术
市场上的防水材料有两大类:一是聚氨脂类防水涂料。这类材料一般是由聚氨脂与煤焦油作为原材料制成。它所挥发的焦油气毒性大,且不容易清除。尚在销售的聚氨脂防水涂料,是用沥青代替煤焦油作为原料。但在使用这种涂料时,一般采用含有甲苯、二甲苯等有机溶剂来稀释,因而也含有毒性;另一类为聚合物水泥基防水涂料。它由多种水性聚合物合成的乳液与掺有各种添加剂的优质水泥组成,聚合物的柔性与水泥的刚性结为一体,使得它在抗渗性与稳定性方面表现优异。它的优点是施工方便、综合造价低,工期短,且无毒环保,因此,聚合物水泥基已经成为防水涂料市场的主角。但现有的通用型水泥基防水涂料拉伸强度、断裂伸长率、粘结强度及抗渗性上未能满足一定的施工要求,本领域技术人员一般不会想到还有改进的空间,而满足于目前的性能。
发明内容
但是,发明人并不满足于目前的水泥基防水涂料的性能要求,为此,申请人做出了许多次的试验,试验了许多种不同的组分和用量,付出了创造性劳动,才得到了本发明。
本发明的目的在于提供一种比现有的通用型水泥基防水涂料在拉伸强度、断裂伸长率、粘结强度及抗渗性上都能显著提高的石墨烯通用型防水涂料。
所采用的技术方案为:
一种石墨烯通用型防水涂料,其由重量比为60%-70%的粉料和重量比为30%-40%的液料组成,其中,
粉料由以下组分和重量份组成:
液料由以下组分和重量份组成:
优选地,所述石英砂为80-100目的石英砂。
优选地,所述普通硅酸盐水泥为42.5R普通硅酸盐水泥。
在本发明技术方案中,硅酸盐水泥的作用是提高凝结的速度,减水剂有助于缩减产品的水量,增加产品的整体强度。
石墨烯纳米片具有大于35m2/g的高比表面积和发达的中孔,孔隙结构分布合理,发明人发现,石墨烯纳米片加入防水涂料中,其能显著提高产品整体的拉伸强度、断裂伸长率、粘结强度及抗渗性。
氧化石墨烯具有优异的力学性能也可以显著提高产品整体的拉伸强度、断裂伸长率、粘结强度及抗渗性。
石墨烯纳米片和氧化石墨烯两者协同作用,能够更大限度地提高产品整体的拉伸强度、断裂伸长率、粘结强度及抗渗性。
粉料制备时,将粉料的各种组分倒入搅拌机中,充分搅拌均匀,即可制得,制备方便。
液料制备时,将液料倒入容器中并充分搅拌至均匀无粉粒、无沉淀的胶浆,即可制得,制备方便。
使用时,先将液料加入到搅拌器中,开启搅拌器,逐步加入粉料,待加完后,继续搅拌均匀,即得成品。
本发明的有益效果在于:
本石墨烯通用型防水涂料比现有的通用型水泥基防水涂料在拉伸强度、断裂伸长率、粘结强度及抗渗性上都能显著提高。
具体实施方式
下面结合实施例进一步描述本发明的技术方案,但只是从申请人众多实验中例举的部分实施例,本发明要求的保护范围并不局限于此。
实施例1
本实施例的石墨烯通用型防水涂料,其由重量比为70%的粉料和重量比为30%的液料组成,其中,
粉料由以下组分和重量份组成:
液料由以下组分和重量份组成:
实施例2
本实施例的石墨烯通用型防水涂料,其由重量比为66%的粉料和重量比为34%的液料组成,其中,
粉料由以下组分和重量份组成:
液料由以下组分和重量份组成:
实施例3
本实施例的石墨烯通用型防水涂料,其由重量比为64%的粉料和重量比为36%的液料组成,其中,
粉料由以下组分和重量份组成:
液料由以下组分和重量份组成:
实施例4
本实施例的石墨烯通用型防水涂料,其由重量比为62%的粉料和重量比为38%的液料组成,其中,
粉料由以下组分和重量份组成:
液料由以下组分和重量份组成:
实施例5
本实施例的石墨烯通用型防水涂料,其由重量比为60%的粉料和重量比为40%的液料组成,其中,
粉料由以下组分和重量份组成:
液料由以下组分和重量份组成:
对比例1
一种通用型防水涂料,它由重量比为66%的粉料和重量比为34%的液料组成,其中,
粉料由以下重量份的组分组成:
液料由以下重量份的组分组成:
对比例2
一种环保型强化柔性防水涂料,它是由重量比为1:1.5的组分A和组分B组成;所述组分A由重量百分比为85%的纯丙烯酸乳液、0.8%的消泡剂、0.12%的环保杀菌剂和14.08%的水组成;所述组分B由重量百分比为50%的硅酸盐水泥42.5、35%的石英砂70-140、14.75%的石英砂200和0.25%的减水剂组成;其中消泡剂为巴斯夫(中国)有限公司制造的Foamstar,环保杀菌剂为PCTS化工制造的2-METHYL-2H-ISOTHIAZOL-3-ONE,减水剂是龙湖科技制造的。
其制备方法如下:
组分A的制备:
(1)称取重量百分比为85%的纯丙烯酸乳液、0.8%的消泡剂、0.12%的环保杀菌剂和14.08%的水;
(2)在搅拌器中低速转速下准确的加入85%的纯丙烯酸乳液,然后加入0.8%的消泡剂,搅拌3min;
(3)加入0.12%的环保杀菌剂,然后加入14.08%的水,搅拌15min,出料,即得组分A;
组分B的制备:
(1)称取重量百分比为50%的硅酸盐水泥42.5、35%的石英砂70-140、14.75%的石英砂200和0.25%的减水剂;
(2)依次在混合设备中加入50%的硅酸盐水泥42.5、35%的石英砂70-140、14.75%的石英砂200和0.25%的减水剂,混合均匀,出料,即得组分B;称取重量比为1:1.5的组分A和组分B,先将组分A加入到搅拌器中,开启搅拌器,逐步加入组分B,待加完后,继续搅拌7min,然后静置14min,即得成品。
将以上实施例1-5的石墨烯通用型防水涂料与对比例1的通用型防水涂料,进行性能检测,采用GB/T23445-2009的标准进行测试,得下表1:
表1
从上表可知,本发明的石墨烯通用型防水涂料在拉伸强度、断裂伸长率、粘结强度和抗渗性上,均比现有的通用型防水涂料都得到了大幅度的提高,增幅超出了预期,取得了预料不到的技术效果。
Claims (3)
1.一种石墨烯通用型防水涂料,其特征在于,其由重量比为60%-70%的粉料和重量比为30%-40%的液料组成,其中,
粉料由以下组分和重量份组成:
液料由以下组分和重量份组成:
2.根据权利要求1所述的石墨烯通用型防水涂料,其特征在于,所述石英砂为80-100目的石英砂。
3.根据权利要求1所述的石墨烯通用型防水涂料,其特征在于,所述普通硅酸盐水泥为42.5R普通硅酸盐水泥。