CN108248169A - Plank in a kind of composite hollow type incubator - Google Patents
Plank in a kind of composite hollow type incubator Download PDFInfo
- Publication number
- CN108248169A CN108248169A CN201810076362.7A CN201810076362A CN108248169A CN 108248169 A CN108248169 A CN 108248169A CN 201810076362 A CN201810076362 A CN 201810076362A CN 108248169 A CN108248169 A CN 108248169A
- Authority
- CN
- China
- Prior art keywords
- parts
- hollow
- heat
- insulated
- junctional membrane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses planks in a kind of composite hollow type incubator, it includes hard plastic substrate, it is characterised in that tiling to glue to stick successively by adhesive layer on hard plastic substrate is fixed with the second hollow heat preservation board, the second heat-insulated junctional membrane, the first hollow heat preservation board, the first heat-insulated junctional membrane and alloy aluminium foil layer;First hollow heat preservation board is identical with whole specification with the structure of the second hollow heat preservation board;Vacuum layer is equipped in the first hollow heat preservation board and the second hollow heat preservation board, wherein the height of hollow layer is more than the height of vacuum layer in the second hollow heat preservation board in the first hollow insulation;The first heat-insulated junctional membrane is identical with the structure of the second heat-insulated junctional membrane, and the thickness of the first heat-insulated junctional membrane is more than the thickness of the second heat-insulated junctional membrane.
Description
Technical field
The present invention relates to thermal insulation material technical field, plank in specially a kind of composite hollow type incubator.
Background technology
With the improvement of living standards with the leap of catering industry, take out and increase as one new profit of catering industry
Point, enjoyed jointly with household at home it is all kinds of it is delicious also become a kind of health, natural life style, developed countries compared with
To be universal, also increasingly popularize at home.Incubator is with safety and environmental protection, cold insulation thermal protection, concept easy to carry by catering industry
Concern;Incubator is divided into variety classes according to product quality difference, including plastics, foam, metal material, wooden
Etc. various incubators.
Traditional incubator is conducted oneself with dignity to reduce, and mostly makes incubator using foam sheet material, and weight is although light,
But heat insulation effect and structural stability are poor, when there is juice to enter inside thermal-insulating body, cleanablity is poor, easily
Grow bacterium;Cause entire incubator recycling rate of waterused low, unusual waste of resource, therefore urgently improve.
Invention content
The purpose of the present invention is to provide plank in a kind of composite hollow type incubator, to solve to carry in above-mentioned background technology
The problem of going out.
To achieve the above object, the present invention provides following technical solution:
Plank in a kind of composite hollow type incubator including hard plastic substrate, is tiled successively on hard plastic substrate by adhesive layer
Viscous stick is fixed with the second hollow heat preservation board, the second heat-insulated junctional membrane, the first hollow heat preservation board, the first heat-insulated junctional membrane and alloy
Aluminium foil layer;First hollow heat preservation board is identical with whole specification with the structure of the second hollow heat preservation board;The first hollow heat preservation board with
And second be equipped with vacuum layer in hollow heat preservation board, wherein the height of hollow layer is more than the second hollow insulation in the first hollow insulation
The height of vacuum layer in plate;The first heat-insulated junctional membrane is identical with the structure of the second heat-insulated junctional membrane, the first heat-insulated junctional membrane
Thickness be more than the second heat-insulated junctional membrane thickness;
Above-mentioned first hollow heat preservation board is prepared with the second hollow heat preservation board each component including following parts by weight:Polypropylene
50-80 parts, 10-25 parts of polyolefin, 6-12 parts of polyethylene octene elastomer, 1-5 parts of sodium hydroxide, 1-5 parts of zinc chloride, castor-oil plant
0.5-1.5 parts oily, 1-3 parts of nano silicon dioxide, 1-5 parts of antioxidant, 0.5-3 parts of weather resisting agent, 1-3 parts of crosslinking agent, high temperature resistant
1-3 parts of agent, 1-3 parts of lubricant;
Above-mentioned first heat-insulated junctional membrane 2 is prepared from the following raw materials in parts by weight with the second heat-insulated junctional membrane 5 to be made:Acrylic resin
20-30 parts, 10-20 parts of bentonite, 5-15 parts of kaolin, 1-5 parts of dispersant, 1-3 parts of levelling agent, nano silicon dioxide 0.3-
0.6 part, 1-2 parts of thickener.
The dispersant is polyethylene wax, the mixture of one or both of polypropylene wax, matter when the two is used in mixed way
Amount is than being 2:3.
The levelling agent is dimethyl silicone polymer, the mixture of one or both of polymethylphenylsiloxane, two
Mass ratio is 1 when person is used in mixed way:2.
The thickener is polypropylene phthalein amine, the mixture of polyvinyl alcohol, one or both of polyethylene glycol oxide, the two
Mass ratio is 1 when being used in mixed way:1.
The preparation method of first heat-insulated junctional membrane 2 and the second heat-insulated junctional membrane 5 includes:(1) by acrylic resin 20-30
Part, 10-20 parts of bentonite, 5-15 parts of kaolin, 0.3-0.6 parts of nano silicon dioxide mix at 65-70 DEG C, fully stir
It mixes uniformly;(2) 1-5 parts of dispersant, 1-3 parts of levelling agent, 1-2 parts of thickener are sequentially added into said mixture, it is lasting to stir
Until form finely dispersed dope;(3) by above-mentioned dope be sent into film laminator, be pressed into film, after static cooling up to every
Film finished product is thermally connected, tensile strength, the compactness of heat-insulated junctional membrane can effectively be promoted by adding in a small amount of nano silicon dioxide
With surface extra coarse degree, it is connect convenient for the promotion of heat insulation and with other working linings.
As the further technical solution of the present invention, the height of hollow layer is the second hollow insulation in the first hollow insulation
Twice of vacuum layer height in plate.
As the further technical solution of the present invention, the thickness of the first heat-insulated junctional membrane is the second heat-insulated connection film thickness
Three times.
As the further technical solution of the present invention, the antioxidant is phosphorous triphenyl phosphate vinegar.
The weather resisting agent is 2- through one 4 one oxy-octyl benzophenone of base.
The high temperature resistant agent is poly- phthalimide.
The crosslinking agent is liquor-saturated for hexahydrophthalic acid.
Plank uses the composite structure of two layers of hollow plate body in a kind of composite hollow type incubator provided by the present invention,
With light weight, structural strength is high, the advantages of can recycling, has heat insulation effect good by the incubator of its making, carries
It is convenient;The advantages of anti-seismic performance is good, it is very useful.
Description of the drawings
Fig. 1 is the structure diagram of plank in a kind of composite hollow type incubator of the present invention.
In figure:1- alloy aluminium foil layers, the first heat-insulated junctional membranes of 2-, the first hollow heat preservation boards of 3-, 4- vacuum layers, 5- second every
It is thermally connected film, the second hollow heat preservation boards of 6-, 7- hard plastic substrates.
Specific embodiment
The technical solution of this patent is described in more detail With reference to embodiment.
Referring to Fig. 1, plank in a kind of composite hollow type incubator, including hard plastic substrate 7, leads on hard plastic substrate 7
It crosses adhesive layer and tiles successively and viscous glutinous be fixed with the second hollow heat preservation board 6, the second heat-insulated junctional membrane 5, the first hollow heat preservation board 3, the
One heat-insulated junctional membrane 2 and alloy aluminium foil layer 1;The structure of first hollow insulation, 3 plate and the second hollow heat preservation board 6 and whole specification
It is identical;Vacuum layer 4 is equipped in 3 plate of the first hollow insulation and the second hollow heat preservation board 6, wherein in the first hollow insulation 3
The height of hollow layer is more than the height of vacuum layer in the second hollow heat preservation board 6;In a preferred embodiment of the invention, first is hollow
Twice of the height of hollow layer in 3 for vacuum layer height in the second hollow heat preservation board 6 is kept the temperature, such structure can improve babinet
Internal heat insulation effect improves the compression strength outside babinet;The first heat-insulated 2 and second heat-insulated junctional membrane 3 of junctional membrane
Structure is identical, and the thickness of the first heat-insulated junctional membrane 2 is more than the thickness of the second heat-insulated junctional membrane 3, in the preferred embodiment of the present invention
In, the thickness of the first heat-insulated junctional membrane 2 is the second heat-insulated connect film thickness three times, can so be ensured inside incubator
Heat insulation, two improve the bonding strength of babinet.
In a preferred embodiment of the invention, first hollow heat preservation board includes following heavy with the second hollow heat preservation board
The each component of amount part is prepared:50-80 parts of polypropylene, 10-25 parts of polyolefin, 6-12 parts of polyethylene octene elastomer, hydrogen
It is 1-5 parts of sodium oxide molybdena, 1-5 parts of zinc chloride, 0.5-1.5 parts of castor oil, 1-3 parts of nano silicon dioxide, 1-5 parts of antioxidant, weather-proof
0.5-3 parts of agent, 1-3 parts of crosslinking agent, 1-3 parts of high temperature resistant agent, 1-3 parts of lubricant.
The antioxidant is phosphorous triphenyl phosphate vinegar.
The weather resisting agent is 2- through one 4 one oxy-octyl benzophenone of base.
The high temperature resistant agent is poly- phthalimide.
The crosslinking agent is liquor-saturated for hexahydrophthalic acid.
In a preferred embodiment of the invention, the first heat-insulated 2 and second heat-insulated junctional membrane 5 of junctional membrane is by following parts by weight
Several raw materials are made:20-30 parts of acrylic resin, 10-20 parts of bentonite, 5-15 parts of kaolin, 1-5 parts of dispersant, levelling agent
1-3 parts, 0.3-0.6 parts of nano silicon dioxide, 1-2 parts of thickener.
The dispersant is polyethylene wax, the mixture of one or both of polypropylene wax, matter when the two is used in mixed way
Amount is than being 2:3.
The levelling agent is dimethyl silicone polymer, the mixture of one or both of polymethylphenylsiloxane, two
Mass ratio is 1 when person is used in mixed way:2.
The thickener is polypropylene phthalein amine, the mixture of polyvinyl alcohol, one or both of polyethylene glycol oxide, the two
Mass ratio is 1 when being used in mixed way:1.
The preparation method of above-mentioned first heat-insulated junctional membrane 2 and the second heat-insulated junctional membrane 5 includes:(1) by acrylic resin
20-30 parts, 10-20 parts of bentonite, 5-15 parts of kaolin, 0.3-0.6 parts of nano silicon dioxide mixed at 65-70 DEG C,
It stirs;(2) 1-5 parts of dispersant, 1-3 parts of levelling agent, 1-2 parts of thickener are sequentially added into said mixture, is held
Continuous stirring is until form finely dispersed dope;(3) above-mentioned dope is sent into film laminator, film is pressed into, after static cooling
Up to heat-insulated junctional membrane finished product, add in a small amount of nano silicon dioxide can effectively be promoted heat-insulated junctional membrane tensile strength,
Compactness and surface extra coarse degree, connect convenient for the promotion of heat insulation and with other working linings.
In conclusion plank answering using two layers hollow plate body in a kind of composite hollow type incubator provided by the present invention
Box-like structure has light weight, and structural strength is high, the advantages of can recycling, by the incubator of its making there is heat preservation to imitate
Fruit is good, easy to carry;The advantages of anti-seismic performance is good, it is very useful.
The better embodiment of this patent is explained in detail above, but this patent is not limited to above-mentioned embodiment party
Formula, can also be under the premise of this patent objective not be departed from the knowledge that one skilled in the relevant art has
Various changes can be made.
Claims (4)
1. plank in a kind of composite hollow type incubator, including hard plastic substrate, it is characterised in that pass through glue on hard plastic substrate
Glutinous layer, which tiles to glue to stick successively, is fixed with the second hollow heat preservation board, the second heat-insulated junctional membrane, the first hollow heat preservation board, the first heat-insulated company
Connect film and alloy aluminium foil layer;First hollow heat preservation board is identical with whole specification with the structure of the second hollow heat preservation board;First
Vacuum layer is equipped in hollow heat preservation board and the second hollow heat preservation board, wherein the height of hollow layer is more than in the first hollow insulation
The height of vacuum layer in second hollow heat preservation board;The first heat-insulated junctional membrane is identical with the structure of the second heat-insulated junctional membrane, the
The thickness of one heat-insulated junctional membrane is more than the thickness of the second heat-insulated junctional membrane;
Above-mentioned first hollow heat preservation board is prepared with the second hollow heat preservation board each component including following parts by weight:Polypropylene
50-80 parts, 10-25 parts of polyolefin, 6-12 parts of polyethylene octene elastomer, 1-5 parts of sodium hydroxide, 1-5 parts of zinc chloride, castor-oil plant
0.5-1.5 parts oily, 1-3 parts of nano silicon dioxide, 1-5 parts of antioxidant, 0.5-3 parts of weather resisting agent, 1-3 parts of crosslinking agent, high temperature resistant
1-3 parts of agent, 1-3 parts of lubricant;
Above-mentioned first heat-insulated junctional membrane 2 is prepared from the following raw materials in parts by weight with the second heat-insulated junctional membrane 5 to be made:Acrylic resin
20-30 parts, 10-20 parts of bentonite, 5-15 parts of kaolin, 1-5 parts of dispersant, 1-3 parts of levelling agent, nano silicon dioxide 0.3-
0.6 part, 1-2 parts of thickener.
2. plank in a kind of composite hollow type incubator according to claim 1, which is characterized in that in the first hollow insulation
The height of hollow layer is twice of vacuum layer height in the second hollow heat preservation board.
3. plank in a kind of composite hollow type incubator according to claim 1, which is characterized in that the first heat-insulated junctional membrane
Thickness be the second heat-insulated connection three times of film thickness.
4. plank in a kind of composite hollow type incubator according to claim 1, which is characterized in that the first heat-insulated junctional membrane
2 include with the preparation method of the second heat-insulated junctional membrane 5:(1) by 20-30 parts of acrylic resin, 10-20 parts of bentonite, kaolinite
5-15 parts native, 0.3-0.6 parts of nano silicon dioxide mixes at 65-70 DEG C, stirs;(2) to said mixture
In sequentially add 1-5 parts of dispersant, 1-3 parts of levelling agent, 1-2 parts of thickener, be stirred continuously until to be formed it is finely dispersed sticky
Object;(3) above-mentioned dope is sent into film laminator, is pressed into film, up to heat-insulated junctional membrane finished product after static cooling.