CN108219557A - A kind of chemistry waterproof coating material - Google Patents
A kind of chemistry waterproof coating material Download PDFInfo
- Publication number
- CN108219557A CN108219557A CN201810064919.5A CN201810064919A CN108219557A CN 108219557 A CN108219557 A CN 108219557A CN 201810064919 A CN201810064919 A CN 201810064919A CN 108219557 A CN108219557 A CN 108219557A
- Authority
- CN
- China
- Prior art keywords
- accounts
- styrene
- account
- ethylene
- coating material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of chemical waterproof coating material, by ethylene-vinyl acetate copolymer, titanium dioxide, elastomer, chrome alum, acrylate, styrene, subgroup boron nitride high-temperature ointment, quartz sand, calcined kaolin powder, Petropols, pitch, poly- milling by, styrene-acrylic emulsion, neoprene, ethylene propylene diene rubber, polyisobutene, polyurethane, polyacrylamide dimethicone and tetrafluoroethene carburetion form.Compared with prior art, the waterproofing membrane formed after natural air drying cures after water-repellent paint coating of the present invention has certain extensibility, elastoplasticity, crack resistance, impermeability and weatherability, can play waterproof, prevent blending protective effect, have the value of popularization and application.
Description
Technical field
The present invention relates to technical field of chemistry more particularly to a kind of chemical waterproof coating materials.
Background technology
Water-repellent paint refers to a kind of coating that the film that coating is formed can prevent rainwater or underground water from leaking.The prior art
In, while water-repellent paint is mostly waterproof, it is impossible to it is durable, during by exposing to the weather, it can cause to crack, and viscosity is not enough, leads
Water resistance is caused to reduce, therefore, in line with excelsior spirit, constantly improvement and innovation is needed, improves the property of water-repellent paint
Energy.
Invention content
The purpose of the present invention is that solve the above-mentioned problems and provides a kind of chemical waterproof coating material.
The present invention is achieved through the following technical solutions above-mentioned purpose：
The present invention is by ethylene-vinyl acetate copolymer, titanium dioxide, elastomer, chrome alum, acrylate, styrene, subgroup
Boron nitride high-temperature ointment, quartz sand, calcined kaolin powder, Petropols, pitch, poly- milling are pressed, styrene-acrylic emulsion, neoprene, three
First EP rubbers, polyisobutene, polyurethane, polyacrylamide dimethicone and tetrafluoroethene carburetion composition.
Specifically, by weight, the ethylene-vinyl acetate copolymer, which accounts for 2%, titanium dioxide and accounts for 2%, elastomer, accounts for
5%th, chrome alum account for 3%, acrylate account for 5%, styrene account for 3%, subgroup boron nitride high-temperature ointment account for 7%, quartz sand account for 2%,
Calcined kaolin powder accounts for 2%, Petropols and accounts for 4%, pitch and account for 20%, poly- milling accounts for 15%, neoprene rubber by 1%, styrene-acrylic emulsion is accounted for
Glue, which accounts for 10%, ethylene propylene diene rubber and accounts for 8%, polyisobutene and account for 2%, polyurethane and account for 2%, polyacrylamide dimethicone, to be accounted for
2%th, tetrafluoroethene carburetion accounts for 5%.
Preparation method of the present invention includes the following steps：
(1) by subgroup boron nitride high-temperature ointment, Petropols, pitch, styrene-acrylic emulsion, neoprene, ethylene propylene diene rubber
It adds in heating container, 220-240 DEG C of heating for dissolving；
(2) polyisobutene, polyurethane, polyacrylamide dimethicone and tetrafluoroethene carburetion is added in after dissolving to keep
20min is stirred with 500r/min in the state of temperature；
(3) ethylene-vinyl acetate copolymer, titanium dioxide, elastomer, chrome alum, acrylate, styrene, quartz are added in
Sand, calcined kaolin powder and poly- milling are pressed stirs 30min with the speed that 2000r/min turns；
(4) stop stirring, get product after cooling；
(5) it is sealed packaging.
The beneficial effects of the present invention are：
The present invention is a kind of chemical waterproof coating material, compared with prior art, is passed through certainly after water-repellent paint coating of the present invention
The waterproofing membrane formed after right air dry cure has certain extensibility, elastoplasticity, crack resistance, impermeability and weatherability, can rise
To waterproof, prevent blending protective effect, have the value of popularization and application.
Specific embodiment
The invention will be further described below：
The present invention is by ethylene-vinyl acetate copolymer, titanium dioxide, elastomer, chrome alum, acrylate, styrene, subgroup
Boron nitride high-temperature ointment, quartz sand, calcined kaolin powder, Petropols, pitch, poly- milling are pressed, styrene-acrylic emulsion, neoprene, three
First EP rubbers, polyisobutene, polyurethane, polyacrylamide dimethicone and tetrafluoroethene carburetion composition.
Specifically, by weight, the ethylene-vinyl acetate copolymer, which accounts for 2%, titanium dioxide and accounts for 2%, elastomer, accounts for
5%th, chrome alum account for 3%, acrylate account for 5%, styrene account for 3%, subgroup boron nitride high-temperature ointment account for 7%, quartz sand account for 2%,
Calcined kaolin powder accounts for 2%, Petropols and accounts for 4%, pitch and account for 20%, poly- milling accounts for 15%, neoprene rubber by 1%, styrene-acrylic emulsion is accounted for
Glue, which accounts for 10%, ethylene propylene diene rubber and accounts for 8%, polyisobutene and account for 2%, polyurethane and account for 2%, polyacrylamide dimethicone, to be accounted for
2%th, tetrafluoroethene carburetion accounts for 5%.
Preparation method of the present invention includes the following steps：
(1) by subgroup boron nitride high-temperature ointment, Petropols, pitch, styrene-acrylic emulsion, neoprene, ethylene propylene diene rubber
It adds in heating container, 220-240 DEG C of heating for dissolving；
(2) polyisobutene, polyurethane, polyacrylamide dimethicone and tetrafluoroethene carburetion is added in after dissolving to keep
20min is stirred with 500r/min in the state of temperature；
(3) ethylene-vinyl acetate copolymer, titanium dioxide, elastomer, chrome alum, acrylate, styrene, quartz are added in
Sand, calcined kaolin powder and poly- milling are pressed stirs 30min with the speed that 2000r/min turns；
(4) stop stirring, get product after cooling；
(5) it is sealed packaging.
Basic principle of the invention and main feature and advantages of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (3)
1. a kind of chemistry waterproof coating material, it is characterised in that：By ethylene-vinyl acetate copolymer, titanium dioxide, elastomer,
Chrome alum, styrene, subgroup boron nitride high-temperature ointment, quartz sand, calcined kaolin powder, Petropols, pitch, gathers acrylate
Milling is pressed, styrene-acrylic emulsion, neoprene, ethylene propylene diene rubber, polyisobutene, polyurethane, polyacrylamide dimethicone and four
Vinyl fluoride carburetion forms.
2. a kind of chemical waterproof coating material according to claim 1, it is characterised in that：By weight, the ethylene-vinegar
Sour ethylene copolymer, which accounts for 2%, titanium dioxide and accounts for 2%, elastomer and account for 5%, chrome alum and account for 3%, acrylate and account for 5%, styrene, to be accounted for
3%th, subgroup boron nitride high-temperature ointment, which accounts for 7%, quartz sand and accounts for 2%, calcined kaolin powder and account for 2%, Petropols, accounts for 4%, pitch
It accounts for 20%, poly- milling and accounts for by accounting for 1%, styrene-acrylic emulsion and account for 15%, neoprene and account for 10%, ethylene propylene diene rubber and account for 8%, polyisobutene
2%th, polyurethane, which accounts for 2%, polyacrylamide dimethicone and accounts for 2%, tetrafluoroethene carburetion, accounts for 5%.
3. a kind of chemical waterproof coating material according to claim 1, which is characterized in that preparation method includes following step
Suddenly：
(1) subgroup boron nitride high-temperature ointment, Petropols, pitch, styrene-acrylic emulsion, neoprene, ethylene propylene diene rubber are added in
It heats in container, 220-240 DEG C of heating for dissolving；
(2) polyisobutene, polyurethane, polyacrylamide dimethicone and tetrafluoroethene carburetion are added in after dissolving and is keeping temperature
In the state of with 500r/min stir 20min；
(3) it adds in ethylene-vinyl acetate copolymer, titanium dioxide, elastomer, chrome alum, acrylate, styrene, quartz sand, forge
It burns kaolin powder and poly- milling presses and stirs 30min with the speed that 2000r/min turns；
(4) stop stirring, get product after cooling；
(5) it is sealed packaging.