CN104877570A - Preparation method of water-resistant paint - Google Patents
Preparation method of water-resistant paint Download PDFInfo
- Publication number
- CN104877570A CN104877570A CN201510273484.1A CN201510273484A CN104877570A CN 104877570 A CN104877570 A CN 104877570A CN 201510273484 A CN201510273484 A CN 201510273484A CN 104877570 A CN104877570 A CN 104877570A
- Authority
- CN
- China
- Prior art keywords
- parts
- emulsification
- water
- coating
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of water-resistant paint, and belongs to the technical field of building materials. The water-resistant paint comprises the following raw materials by weight: 20 t0 40 parts of asphalt, 25 to 35 parts of a subgroup boron nitride high-temperature ointment, 15 to 28 parts of mica powder, 12 to 22 parts of aluminium powder, 16 to 30 parts of turpentine oil, 11 to 23 parts of a styrene-acrylic emulsion, 5 to 12 parts of low-heat Portland cement, and 3 to 10 parts of an emulsifier. The preparation method comprises the following steps: A, stirring to mix the raw materials; B, emulsifying the mixture: adding the emulsifier, and obtaining paint according to an emulsifying technology; C, diluting the paint obtained in the step B. Compared with the prior art, the water-resistant paint is used for resisting water on a roof, and is water-resistant, sun-proof and freeze-proof.
Description
Technical field
The present invention relates to building material technical field, especially a kind of making method of waterproof paint.
Background technology
Roofing is the important component part in house, and undergo for a long time exposes to the weather drenches with rain, and the most easily occurs leaking, the problem of seepage, and roofing once occur leaks or the problem of seepage, directly affects the life-span in house and normally to use.In the residential quarters in city, the problem of roof leakage is the problem that owner complains at most, often needs every year to spend a large amount of expenses in the solution of Water-proof Measures of Roofs.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of making method of waterproof paint, and it can solve roof leakage or ooze water problem.
In order to solve the problem, the technical solution adopted in the present invention is: the making method of this waterproof paint, adopt the raw material of following weight part: pitch 20 ~ 40 parts, subgroup boron nitride high-temperature ointment 25 ~ 35 parts, mica powder 15 ~ 28 parts, aluminium powder 12 ~ 22 parts, 16 ~ 30 parts, turps, benzene emulsion 11 ~ 23 parts, low-heat portland cement 5 ~ 12 parts, emulsifying agent 3 ~ 10 parts; Its making step is:
A. raw material is uniformly mixed: by pitch, subgroup boron nitride high-temperature ointment, mica powder, aluminium powder, benzene emulsion, low-heat portland cement mixing, adopt low-speed mixer to stir, the rotating speed of stirrer is 80 ~ 120 revs/min, churning time 30 ~ 45 minutes; After stirring, place 1 ~ 2 hour, obtain the first mixture;
B. emulsification first mixture: mix emulsifying agent in described first mixture, adopt ultrasonic emulsification, the temperature of emulsification is 40 ~ 60 DEG C, and the time of emulsification is 15 ~ 25 minutes, obtains coating after emulsification.
C. coating is diluted: in coating, mix turps, dilution coating.
Owing to have employed technique scheme, the present invention compared with prior art has following beneficial effect:
1, pitch is a kind of waterproof and dampproof and rot-resistant organic gel gel material, has good waterproof action; Subgroup boron nitride high-temperature ointment has good water resistant and moisture resistance and freeze proof effect, and high thermal stability and good stopping property are anticorrosive stronger; Low-heat portland cement has the effect preventing crack; Mica powder has good elasticity, high temperature resistant, corrosion-resistant, strong adhesion; Benzene emulsion has stronger waterproof effect.Using the mixing of pitch, subgroup boron nitride high-temperature ointment, mica powder, benzene emulsion and low-heat portland cement as waterproof paint, made waterproof paint has the effect of stronger waterproof, protection against the tide, protection against corrosion, high temperature resistant, cracking resistance, is suitable as the water-proof material of roofing.
2, turps is for diluting the waterproof paint of gained, and the performance neither affecting waterproof paint can strengthen again the mobility of waterproof paint.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described:
Embodiment 1:
The making method of this waterproof paint, adopts the raw material of following weight part: pitch 20 parts, subgroup boron nitride high-temperature ointment 25 parts, mica powder 15 parts, aluminium powder 12 parts, 16 parts, turps, benzene emulsion 11 parts, low-heat portland cement 5 parts, emulsifying agent 3 parts; Its making step is:
A. raw material is uniformly mixed: by pitch, subgroup boron nitride high-temperature ointment, mica powder, aluminium powder, benzene emulsion, low-heat portland cement mixing, adopt low-speed mixer to stir, the rotating speed of stirrer is 80 ~ 120 revs/min, churning time 30 minutes; After stirring, place 1 hour, obtain the first mixture;
B. emulsification first mixture: mix emulsifying agent in described first mixture, adopt ultrasonic emulsification, the temperature of emulsification is 40 DEG C, and the time of emulsification is 15 minutes, obtains coating after emulsification.
C. coating is diluted: in coating, mix turps, dilution coating.
According to GB/T19250-2003 examination criteria, detect that the tensile strength of waterproof paint of the present invention and elongation at break reach II class standard.
Embodiment 2:
The making method of this waterproof paint, adopts the raw material of following weight part: pitch 40 parts, subgroup boron nitride high-temperature ointment 35 parts, mica powder 28 parts, aluminium powder 22 parts, 30 parts, turps, benzene emulsion 23 parts, low-heat portland cement 12 parts, emulsifying agent 10 parts; Its making step is:
A. raw material is uniformly mixed: by pitch, subgroup boron nitride high-temperature ointment, mica powder, aluminium powder, benzene emulsion, low-heat portland cement mixing, adopt low-speed mixer to stir, the rotating speed of stirrer is 80 ~ 120 revs/min, churning time 45 minutes; After stirring, place 2 hours, obtain the first mixture;
B. emulsification first mixture: mix emulsifying agent in described first mixture, adopt ultrasonic emulsification, the temperature of emulsification is 60 DEG C, and the time of emulsification is 25 minutes, obtains coating after emulsification.
C. coating is diluted: in coating, mix turps, dilution coating.
According to GB/T19250-2003 examination criteria, detect that the tensile strength of waterproof paint of the present invention and elongation at break reach II class standard.
Embodiment 3:
The making method of this waterproof paint, adopts the raw material of following weight part: pitch 30 parts, subgroup boron nitride high-temperature ointment 30 parts, mica powder 22 parts, aluminium powder 17 parts, 21 parts, turps, benzene emulsion 17 parts, low-heat portland cement 8 parts, emulsifying agent 6 parts; Its making step is:
A. raw material is uniformly mixed: by pitch, subgroup boron nitride high-temperature ointment, mica powder, aluminium powder, benzene emulsion, low-heat portland cement mixing, adopt low-speed mixer to stir, the rotating speed of stirrer is 80 ~ 120 revs/min, churning time 38 minutes; After stirring, place 1.5 hours, obtain the first mixture;
B. emulsification first mixture: mix emulsifying agent in described first mixture, adopt ultrasonic emulsification, the temperature of emulsification is 50 DEG C, and the time of emulsification is 18 minutes, obtains coating after emulsification.
C. coating is diluted: in coating, mix turps, dilution coating.
According to GB/T19250-2003 examination criteria, detect that the tensile strength of waterproof paint of the present invention and elongation at break reach II class standard.
Claims (1)
1. a making method for waterproof paint, is characterized in that:
Adopt the raw material of following weight part: pitch 20 ~ 40 parts, subgroup boron nitride high-temperature ointment 25 ~ 35 parts, mica powder 15 ~ 28 parts, aluminium powder 12 ~ 22 parts, 16 ~ 30 parts, turps, benzene emulsion 11 ~ 23 parts, low-heat portland cement 5 ~ 12 parts, emulsifying agent 3 ~ 10 parts;
Its making step is:
A. raw material is uniformly mixed: by pitch, subgroup boron nitride high-temperature ointment, mica powder, aluminium powder, benzene emulsion, low-heat portland cement mixing, adopt low-speed mixer to stir, the rotating speed of stirrer is 80 ~ 120 revs/min, churning time 30 ~ 45 minutes; After stirring, place 1 ~ 2 hour, obtain the first mixture;
B. emulsification first mixture: mix emulsifying agent in described first mixture, adopt ultrasonic emulsification, the temperature of emulsification is 40 ~ 60 DEG C, and the time of emulsification is 15 ~ 25 minutes, obtains coating after emulsification;
C. coating is diluted: in coating, mix turps, dilution coating.