CN105295731A - Rubber asphalt waterproof paint and preparation method thereof - Google Patents
Rubber asphalt waterproof paint and preparation method thereof Download PDFInfo
- Publication number
- CN105295731A CN105295731A CN201510759852.3A CN201510759852A CN105295731A CN 105295731 A CN105295731 A CN 105295731A CN 201510759852 A CN201510759852 A CN 201510759852A CN 105295731 A CN105295731 A CN 105295731A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber asphalt
- asphalt waterproof
- rubber
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses rubber asphalt waterproof paint and a preparation method thereof. The rubber asphalt waterproof paint is prepared from, by weight, 35 parts of petroleum asphalt 60#, 13 parts of chlorinated rubber, 5 parts of chlorinated paraffin, 7 parts of isocyanate, 2 parts of calcium stearate, 8 parts of asbestos powder, 2 parts of zinc phosphate, 12 parts of talcum powder and 51 parts of xylene. The rubber asphalt waterproof paint can be used for roofs, gutters, balconies, outer walls, bathrooms, kitchens, basements, water ponds and other waterproof engineering and has the advantages of being convenient to transport and construct, free of toxin and pollution, waterproof, damppproof, preventive to corrosion, high in heat resistance, good in aging resistance, weather resistance, temperature resistance and extensibility and good in bonding performance with basic layers.
Description
Technical field
The present invention relates to paint field, be specifically related to a kind of construction waterproof coating, can be used for the rubber asphalt waterproof coating of the waterproofing works such as roof, gutter, balcony, exterior wall, toilet, kitchen, vault, pond, there is transport, easy construction, nontoxic, pollution-free, waterproof, moistureproof, advantages such as protection against corrosion, and it is high to have thermotolerance, resistance to deterioration is good, weather-proof, heat resistance is good, good-extensibility, with the feature such as basic unit's adhesive property is good.
Background technology
Pitch is the organic gel gel material of a kind of brown or chocolate, is indispensable material in civil engineering construction.Have a wide range of applications in the engineerings such as building, highway, bridge.Asphalt waterproofing paint be with pitch be base-material configuration solvent-borne type or water-emulsifying type waterproof coatings, solvent-borne type asphalt waterproofing paint refers to and is directly dissolved in gasoline equal solvent by unmodified petroleum pitch and is configured to, and is also called adhesive bitumen primer.Emulsified asphalt waterproofing coating refers to petroleum pitch under chemical emulsifier or the effect of mineral emulsifying agent, is scattered in water, forms the coating that stable water dispersion is formed.Rubber asphalt waterproof coating uses macromolecule synthesising technology, is novel superfine rubber water-proof paint, adds epoxy resin and resin group and this product is had more multi-functionally unify body with environmental protection, give product innovation and have more waterproof, anticorrosion, protection against the tide, the effects such as mildew-resistant.Have wide accommodation, weathering resistance, resistance to acid, resistance to deformation, long service life, tensile strength is high, and unit elongation is large.Becoming rubber-like snappiness without seam after products solidifying, jointless water-tight corrosion-proof layer, is continuous closed system.At end face, plane, facade, firmly bonding on the various dry basal plane such as inclined-plane.To any complex-shaped, all easily construct in pipeline position in length and breadth.Subject range: various industry, civil building, roof, gutter, balcony, exterior wall, toilet, kitchen, vault, pond, water drain, mine, tunnel, pipeline, the bridge cementation of fissures, underground is metallic conduit on the ground, high/low temperature pipeline, the waterproof such as insulating pipe inside and outside wall, moistureproof, the engineerings such as protection against corrosion.
Summary of the invention
The object of the present invention is to provide a kind of construction waterproof coating, can be used for the rubber asphalt waterproof coating of the waterproofing works such as roof, gutter, balcony, exterior wall, toilet, kitchen, vault, pond, there is transport, easy construction, nontoxic, pollution-free, waterproof, moistureproof, the advantages such as protection against corrosion, and it is high to have thermotolerance, resistance to deterioration is good, weather-proof, heat resistance is good, good-extensibility, with the feature such as basic unit's adhesive property is good.
Present invention employs such technical scheme: the material in described rubber asphalt waterproof coating and weight proportion respectively: 35 parts, 60# petroleum pitch, chlorinated rubber 13 parts, clorafin 5 parts, isocyanic ester 7 parts, calcium stearate 2 parts, asbestos powder 8 parts, zinc phosphate 2 parts, talcum powder 12 parts, dimethylbenzene 51 parts.
The present invention is specifically related to a kind of construction waterproof coating, can be used for the rubber asphalt waterproof coating of the waterproofing works such as roof, gutter, balcony, exterior wall, toilet, kitchen, vault, pond.
This product has transport, easy construction, nontoxic, pollution-free, waterproof, moistureproof, the advantages such as protection against corrosion, and it is high to have thermotolerance, resistance to deterioration is good, weather-proof, heat resistance is good, good-extensibility, with the feature such as basic unit's adhesive property is good.
Embodiment
Present invention employs such technical scheme: in described rubber asphalt waterproof coating, material and weight proportion are respectively: 35 parts, 60# petroleum pitch, chlorinated rubber 13 parts, clorafin 5 parts, isocyanic ester 7 parts, calcium stearate 2 parts, asbestos powder 8 parts, zinc phosphate 2 parts, talcum powder 12 parts, dimethylbenzene 51 parts.
Its preparation method is following steps:
Step one), add petroleum pitch in a kettle., dewater after being heated to 210 DEG C for subsequent use;
Step 2), by step one) material that obtains is cooled to 125 DEG C, add 1/2 dimethylbenzene, stir rear for subsequent use;
Step 3), by step 2) institute obtains in material and adds chlorinated rubber, fully mixes rear for subsequent use;
Step 4), in remaining dimethylbenzene, add clorafin, calcium stearate, asbestos powder, zinc phosphate, talcum powder successively, fully mix rear for subsequent use;
Step 5), by step 3), step 4) material that obtains fully mixes, is cooled to 60 DEG C, adds isocyanic ester, after stirring, finished product.
Claims (2)
1. a rubber asphalt waterproof coating, it is characterized in that, material and weight proportion respectively: 35 parts, 60# petroleum pitch, chlorinated rubber 13 parts, clorafin 5 parts, isocyanic ester 7 parts, calcium stearate 2 parts, asbestos powder 8 parts, zinc phosphate 2 parts, talcum powder 12 parts, dimethylbenzene 51 parts.
2. according to rubber asphalt waterproof coating according to claim 1, it is characterized in that, its preparation method, preparation method is following steps: step one), add petroleum pitch in a kettle., dewater after being heated to 210 DEG C for subsequent use;
Step 2), by step one) material that obtains is cooled to 125 DEG C, add 1/2 dimethylbenzene, stir rear for subsequent use;
Step 3), by step 2) institute obtains in material and adds chlorinated rubber, fully mixes rear for subsequent use;
Step 4), in remaining dimethylbenzene, add clorafin, calcium stearate, asbestos powder, zinc phosphate, talcum powder successively, fully mix rear for subsequent use;
Step 5), by step 3), step 4) material that obtains fully mixes, is cooled to 60 DEG C, adds isocyanic ester, after stirring, finished product.