CN108193348A - A kind of production method for avenging Neil fabric - Google Patents
A kind of production method for avenging Neil fabric Download PDFInfo
- Publication number
- CN108193348A CN108193348A CN201810088409.1A CN201810088409A CN108193348A CN 108193348 A CN108193348 A CN 108193348A CN 201810088409 A CN201810088409 A CN 201810088409A CN 108193348 A CN108193348 A CN 108193348A
- Authority
- CN
- China
- Prior art keywords
- yarn
- fabric
- neil fabric
- warp
- weft
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production methods for avenging Neil fabric, include the following steps：S1, raw material is selected：The staple fiber or long filament of different fineness and strength are selected, and chooses suitable terylene；S2, spinning：The staple fiber or long filament of different fineness and strength and terylene are subjected to twisted rear spinning, gained scribbled is as surface yarn or decorative yarn, again by spinning after the staple fiber or long filament of different fineness and strength and terylene progress heavy twist, gained scribbled is as heart yarn, heart yarn can increase the strength of Chenille Yarns, the 25% ~ 30% of Chenille Yarns composition is accounted for, decorative yarn is main body, accounts for 70% ~ 75%.Compared with other production methods, technical price is cheap, saves space, technical maturity, can efficiently solve the yielding situation of tradition snow Neil fabric, improve the elasticity of snow Neil fabric, while snow Neil fabric can also be made to have significant antistatic effect.
Description
Technical field
The present invention relates to textile technology field, more specifically more particularly to a kind of production method for avenging Neil fabric.
Background technology
Snow Neil fabric is that staple fiber by different fineness and strength or long filament pass through the twisted fabric formed.Because of its plumage
Suede is plentiful, soft, fabric is thick and solid and the characteristics of quality is slim and graceful, be widely used in home textile and knitted dress field, shape
Slip cover, bedcover, bed blanket, platform blanket, carpet, wall coverings, curtain can be made in new highlight snow Neil decorative products into product development
The interior decorations ornaments such as curtain, the use of Chenille Yarns impart a kind of thick and solid feeling of a textile fabric, have high-grade luxurious, hand
The advantages that sense is soft, matte is plentiful, drapability is good, water imbibition is especially good.Avenge Neil curtain both can dim light, shading, to adapt to people
To light varying strength demand, and can windproof, dedusting, heat-insulated, warming, noise elimination, improvement room weather and environment.
But snow Neil fabric functionality currently on the market is all relatively simple, it is also very inconvenient to use, traditional
Avenge Neil fabric when in use, there are some shortcomings due to the characteristic of its material in itself, it will appear deformation, after the washing can
There is shrink phenomenon, so can not be smoothed by flatiron, in order to avoid window curtain fabric is caused to fall the front of suede, random suede, particularly curtain, such as
As soon as this, curtain is also not much ornamental value, and traditional snow Neil fabric is dyed by vertical cylinder, due to yarn
It is fixed, dyestuff recycles in dye vat, causes to dye the Chenille Yarns that the yarn come is flat, while quality is not to manage very much
Think, be not suitable for producing use in enormous quantities, for this purpose, it is proposed that a kind of production method for avenging Neil fabric.
Invention content
The purpose of the present invention is to solve shortcoming in the prior art, and a kind of system of the snow Neil fabric proposed
Make method, technical price is cheap, saves space, technical maturity, can efficiently solve the yielding situation of tradition snow Neil fabric,
The elasticity of snow Neil fabric is improved, while can also make snow Neil fabric that there is significant antistatic effect.
To achieve the above object, the present invention provides following technical solution：A kind of production method for avenging Neil fabric, including such as
Lower step：
S1, raw material is selected：The staple fiber or long filament of different fineness and strength are selected, and chooses suitable terylene；
S2, spinning：The staple fiber or long filament of different fineness and strength and terylene are subjected to twisted rear spinning, gained scribbled is made
Spinning after heavy twist is carried out for surface yarn or decorative yarn, then by the staple fiber or long filament of different fineness and strength and terylene, gained is blended
Yarn can increase the strength of Chenille Yarns as heart yarn, heart yarn, account for the 25% ~ 30% of Chenille Yarns composition, decorative yarn is main body, is accounted for
70%~75%；
S3, spinning：As ring spinner, decorative yarn is rotating the center for entering hollow spindle from machine upper portion, on spindle
Blade cuts decorative yarn by certain gauge, and decorative yarn fallen between heart yarn, is exported by roller and directive wheel, and roller and directive wheel are by two
Root heart yarn is fed against decorative yarn, and due to the twisting of ring spinner spindle, decorative yarn is fixed between two heart yarns, is then wound onto small
On type snow Neil bobbin (about 600 g), the sliver exporting speed of Chenille Yarns is the m/min of 8 m/min ~ 18, and two are produced on a spindle
The identical Chenille Yarns of root, this two yarns are finally winding on one big bobbin, then form Chenille Yarns；
S4, section dye：Chenille Yarns is divided into back warp, table warp, the first weft yarn and the second weft yarn, then by back warp, table warp, the first weft yarn
It is put into spray cylinder and is dyed with the second weft yarn, then table is passed through again, the first weft yarn and the second weft yarn carry out section dye respectively, make it
Multiple color sections are presented respectively, each color segment length differs；
S5, warping starching：Table warp, the first weft yarn and the second weft yarn after back warp and section dye is carried out respectively by warping starching machine
Warping and starching；
S6, weaving：Back warp, table warp, the first weft yarn and the second weft yarn are sent into weaving loom to weave, the first weft yarn and the second latitude
Yarn is stacked up and down, forms outer weft, and table latitude and longitude goes out upper strata fabric along direction of warp and weft weaving, then by back warp and upper strata fabric
It carries out going out to avenge Neil fabric along direction of warp and weft weaving；
S7, antistatic finish：Snow Neil fabric upper and lower surface is coated with antistatic finishing agent, it then again will be after coating
Snow Neil fabric, which is put into dryer, carries out drying and processing, and drying terminates that antistatic layer can be formed.
S8, hot-pressing processing：Snow Neil fabric after antistatic finish is arranged is put into cloth hot press, then carries out heat
Pressure processing, is finally drawn off, so as to complete the making of snow Neil fabric.
Preferably, the snow Neil fabric to complete can be cut into required size.
Preferably, 100% is carried out to the appearance and quality of avenging Neil fabric and checks that separate the sheep from the goats quality.
Preferably, it is rear to survey：The snow Neil fabric made is put into warm water, come detect snow Neil fabric whether fade or
Deformation.
The technique effect and advantage of the present invention：
1st, by adding in suitable terylene in raw material, it may be such that snow Neil fabric in dry, wet elastic and wearability all
Preferably, dimensionally stable, washing shrinkage is small, have the characteristics that it is tall and straight, be not easy fold, be washable, quick-drying, efficiently solve tradition snow Neil
The yielding situation of fabric.
2nd, the antistatic layer formed by antistatic finish can effectively eliminate the exterior static of snow Neil fabric, so as to
It can make snow Neil fabric that there is significant antistatic effect, practicability and applicability have obtained significant increase.
3rd, it is dyed by using the technique of spray cylinder so that in dyeing course, Chenille Yarns be free to hang,
Suede yarn is allowed to stand up, round yarn effect is just produced after heat treatment, due to adequately contacting, makes the feel of snow Neil fabric more
It is good, can more meet the needs of present people, it is more successful compared to traditional coloring in vertical cylinder.
Specific embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, below in conjunction with specific embodiment, to this
Invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, not
For limiting the present invention.Based on the embodiments of the present invention, those of ordinary skill in the art are not before creative work is made
All other embodiments obtained are put, shall fall within the protection scope of the present invention.
Embodiment
A kind of production method for avenging Neil fabric, includes the following steps：
S1, raw material is selected：The staple fiber or long filament of different fineness and strength are selected, and chooses suitable terylene；
S2, spinning：The staple fiber or long filament of different fineness and strength and terylene are subjected to twisted rear spinning, gained scribbled is made
Spinning after heavy twist is carried out for surface yarn or decorative yarn, then by the staple fiber or long filament of different fineness and strength and terylene, gained is blended
Yarn can increase the strength of Chenille Yarns as heart yarn, heart yarn, account for the 25% ~ 30% of Chenille Yarns composition, decorative yarn is main body, is accounted for
70%~75%；
S3, spinning：As ring spinner, decorative yarn is rotating the center for entering hollow spindle from machine upper portion, on spindle
Blade cuts decorative yarn by certain gauge, and decorative yarn fallen between heart yarn, is exported by roller and directive wheel, and roller and directive wheel are by two
Root heart yarn is fed against decorative yarn, and due to the twisting of ring spinner spindle, decorative yarn is fixed between two heart yarns, is then wound onto small
On type snow Neil bobbin (about 600 g), the sliver exporting speed of Chenille Yarns is the m/min of 8 m/min ~ 18, and two are produced on a spindle
The identical Chenille Yarns of root, this two yarns are finally winding on one big bobbin, then form Chenille Yarns；
S4, section dye：Chenille Yarns is divided into back warp, table warp, the first weft yarn and the second weft yarn, then by back warp, table warp, the first weft yarn
It is put into spray cylinder and is dyed with the second weft yarn, then table is passed through again, the first weft yarn and the second weft yarn carry out section dye respectively, make it
Multiple color sections are presented respectively, each color segment length differs；
S5, warping starching：Table warp, the first weft yarn and the second weft yarn after back warp and section dye is carried out respectively by warping starching machine
Warping and starching；
S6, weaving：Back warp, table warp, the first weft yarn and the second weft yarn are sent into weaving loom to weave, the first weft yarn and the second latitude
Yarn is stacked up and down, forms outer weft, and table latitude and longitude goes out upper strata fabric along direction of warp and weft weaving, then by back warp and upper strata fabric
It carries out going out to avenge Neil fabric along direction of warp and weft weaving；
S7, antistatic finish：Snow Neil fabric upper and lower surface is coated with antistatic finishing agent, it then again will be after coating
Snow Neil fabric, which is put into dryer, carries out drying and processing, and drying terminates that antistatic layer can be formed.
S8, hot-pressing processing：Snow Neil fabric after antistatic finish is arranged is put into cloth hot press, then carries out heat
Pressure processing, is finally drawn off, so as to complete the making of snow Neil fabric.
In summary：A kind of production method for avenging Neil fabric provided by the invention, compared with other production methods, technology
Cheap, saving space, technical maturity can efficiently solve the yielding situation of tradition snow Neil fabric, improve snow Buddhist nun
The elasticity of your fabric, while can also make snow Neil fabric that there is significant antistatic effect.
Finally it should be noted that：The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention,
Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art, still may be used
To modify to the technical solution recorded in foregoing embodiments or carry out equivalent replacement to which part technical characteristic,
All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in the present invention's
Within protection domain.
Claims (4)
1. a kind of production method for avenging Neil fabric, it is characterised in that：Include the following steps：
S1, raw material is selected：The staple fiber or long filament of different fineness and strength are selected, and chooses suitable terylene；
S2, spinning：The staple fiber or long filament of different fineness and strength and terylene are subjected to twisted rear spinning, gained scribbled is made
Spinning after heavy twist is carried out for surface yarn or decorative yarn, then by the staple fiber or long filament of different fineness and strength and terylene, gained is blended
Yarn can increase the strength of Chenille Yarns as heart yarn, heart yarn, account for the 25% ~ 30% of Chenille Yarns composition, decorative yarn is main body, is accounted for
70%~75%；
S3, spinning：As ring spinner, decorative yarn is rotating the center for entering hollow spindle from machine upper portion, on spindle
Blade cuts decorative yarn by certain gauge, and decorative yarn fallen between heart yarn, is exported by roller and directive wheel, and roller and directive wheel are by two
Root heart yarn is fed against decorative yarn, and due to the twisting of ring spinner spindle, decorative yarn is fixed between two heart yarns, is then wound onto small
On type snow Neil bobbin (about 600 g), the sliver exporting speed of Chenille Yarns is the m/min of 8 m/min ~ 18, and two are produced on a spindle
The identical Chenille Yarns of root, this two yarns are finally winding on one big bobbin, then form Chenille Yarns；
S4, section dye：Chenille Yarns is divided into back warp, table warp, the first weft yarn and the second weft yarn, then by back warp, table warp, the first weft yarn
It is put into spray cylinder and is dyed with the second weft yarn, then table is passed through again, the first weft yarn and the second weft yarn carry out section dye respectively, make it
Multiple color sections are presented respectively, each color segment length differs；
S5, warping starching：Table warp, the first weft yarn and the second weft yarn after back warp and section dye is carried out respectively by warping starching machine
Warping and starching；
S6, weaving：Back warp, table warp, the first weft yarn and the second weft yarn are sent into weaving loom to weave, the first weft yarn and the second latitude
Yarn is stacked up and down, forms outer weft, and table latitude and longitude goes out upper strata fabric along direction of warp and weft weaving, then by back warp and upper strata fabric
It carries out going out to avenge Neil fabric along direction of warp and weft weaving；
S7, antistatic finish：Snow Neil fabric upper and lower surface is coated with antistatic finishing agent, it then again will be after coating
Snow Neil fabric, which is put into dryer, carries out drying and processing, and drying terminates that antistatic layer can be formed.
S8, hot-pressing processing：Snow Neil fabric after antistatic finish is arranged is put into cloth hot press, is then carried out at hot pressing
Reason, is finally drawn off, so as to complete the making of snow Neil fabric.
2. a kind of production method for avenging Neil fabric according to claim 1, it is characterised in that：The snow that can will be completed
Neil fabric is cut into required size.
3. a kind of production method for avenging Neil fabric according to claim 1, it is characterised in that：To the outer of snow Neil fabric
It sees and quality carries out 100% and checks that separate the sheep from the goats quality.
4. a kind of production method for avenging Neil fabric according to claim 1, it is characterised in that：After survey：By what is made
Snow Neil fabric is put into warm water, to detect whether snow Neil fabric fades or deform.