CN108193344A - A kind of radiation-proof pregnant woman clothes fabric and its production technology - Google Patents
A kind of radiation-proof pregnant woman clothes fabric and its production technology Download PDFInfo
- Publication number
- CN108193344A CN108193344A CN201810172023.9A CN201810172023A CN108193344A CN 108193344 A CN108193344 A CN 108193344A CN 201810172023 A CN201810172023 A CN 201810172023A CN 108193344 A CN108193344 A CN 108193344A
- Authority
- CN
- China
- Prior art keywords
- fiber
- radiation
- fabric
- proof
- pregnant woman
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of radiation-proof pregnant woman clothes fabric, including radiation-proof pregnant woman clothes fabric body, the radiation-proof pregnant woman clothes fabric body is formed by warp thread and weft yarns, the warp and weft are multi cord, the multi cord is by scribbled a, scribbled b, scribbled c is twisted, from the braiding combination of latitude and longitude, the combinations of radiation proof material and fabric other compositions improves the taking of fabric and radiation-proof effect, the present invention also provides the production technologies of the radiation-proof pregnant woman clothes fabric, screen the raw fibre of the radiation protection of uniform quality, electromagnetic shielding dressing liquid is carried out to fabric to pad, again last layer Ag films are plated on fabric surface layer, significantly increase the wearability and radiation protection ability of fabric.
Description
Technical field
The present invention relates to garment material fields, and in particular to a kind of radiation-proof pregnant woman clothes fabric and its production technology.
Background technology
In recent years, electronic product has obtained widely universal.On the one hand, popularizing for electronic product is brought to our life
It is great convenient, however, on the other hand also bringing serious electromagnetic radiation and pollution to us.The research of relevant expert is shown
To show, Long Term Contact electromagnetic radiation can cause greatly to injure to human body, and for being in pregnant woman and its belly of particular time
Fetus for, it is this harm it is then more obvious.Today's society with the improvement of living standards and breeds the weight of child's mass
Depending on more and more pregnant woman's selections wear radiation-proof maternity dress in the pregnancy period, this also provides boundless for radiation-proof maternity dress
Market prospects.
And radiation-proof fabric determines the radiation resistant fiber in the quality of radiation-proof maternity dress, especially radiation-proof fabric,
Determine the ability of one integral piece radiation-proof maternity dress shielding electromagnetic radiation, but light only leans on the capability of resistance to radiation of radiation resistant fiber itself
Not enough, it is also contemplated that the braiding combination of latitude and longitude, combination and face of the radiation proof material with fabric other compositions
The production technology of material.
General radiation-proof maternity dress only focuses on studying the capability of resistance to radiation of radiation resistant fiber, so manufactured clothes are taken
Property is poor, and radiation-proof effect is not notable.
Invention content
(One)Technical problems to be solved
The problem to be solved in the present invention is that existing radiation-proof pregnant woman clothes fabric taking is poor, and radiation-proof effect is not notable.
(Two)Technical solution
To solve the technical problem, the present invention provides a kind of radiation-proof pregnant woman clothes fabric, has good taking, high
Anti- width penetrate effect.
The radiation-proof pregnant woman clothes fabric, including radiation-proof pregnant woman clothes fabric body, the radiation-proof pregnant woman clothes face
Material ontology is formed by warp thread and weft yarns, and the warp and weft are multi cord, and the multi cord is by scribbled a, mixed
Yarn b, scribbled c are twisted, and the raw material of three mixed yarns penetrates fiber, 20-25 parts of wood by 25-28 parts of anti-width
Fiber, 17-20 part cotton fiber, 12-16 parts of polyester fibers, 10-12 parts of nanometer silver antimicrobial master batches, 8-10 parts of spandex fibres, 5-8 parts
Wire is formed;
The radiation resistant fiber includes the raw material of following mass percent:
Stainless steel fibre 22%
Nano silver fibre 28%
Conductive fiber 30%
Bamboo charcoal fiber 20%
Further, the scribbled a and scribbled b are discharged side by side, the scribbled c jointly in scribbled a and
Scribbled b peripheries are wound in " S " type.
Further, the chemical composition proportioning of the stainless steel fibre is:The content of C is
The content of 0.12-0.15, Si are 0.4-0.6, and the content of Mn is 0.4-0.6, and the content of Nb is<0.03, N content is
The content of 0.4-1.0, Cr are 6.5-18, and the content of Mo is 0.75-1.2, and the content of Ni is<0.2, surplus is iron.
Further, every three of the warp is alternately arranged and institute for one group and each one group
State that each one group of weft is oblique to be interwoven.
Further, every two adjacent warps surround one with every two adjacent wefts
A quadrangle.
Further, it is respectively 120 ° and 60 ° that two groups of the quadrangle diagonal.
Corresponding, the present invention also provides a kind of production technologies of radiation-proof pregnant woman clothes fabric, specifically include following
Step:
1)Fiber pre-processes:Anti pilling processing is carried out to each composition fiber in radiation proof material fiber respectively, then to blended
Yarn carries out anti pilling processing except the other compositions of radiation proof material fiber, and anti pilling processing comprises the concrete steps that:By each ingredient fibre
Dimension is placed in treatment fluid, and the control for the treatment of fluid temperature is being 40 ~ 45 °C, and processing time is 10 ~ 15min;
2)Stock-dye:Fiber is added in into container, 40 °C of softened water is injected in container, until softened water did not had fiber, then
1 ~ 2g/L of levelling agent, anhydrous sodium sulphate and several g/l of soda ash (dosage is selected according to the concentration of dyestuff) are added in, stirs evenly, stands
30 ~ 40min, then fiber is taken out drying, it is put into stock-dye machine and is dyed;
3)Fiber is combed:With hair-feather plucking-shredding-carding-drafting-air spinning
- automatic winding;
4)Make radiation resistant fiber:First each fiber put into respectively seperator isolate uniform quality thicker fiber come, press
Mass fraction takes 22% stainless steel fibre, 28% nano silver fibre, 30% conductive fiber, 20% bamboo charcoal fiber, then each composition fiber
It puts into fiber mixer and is uniformly sufficiently mixed;
5)Make mixed yarn:By above-mentioned steps 4)Radiation resistant fiber and wood-fibred, cotton fiber, polyester fiber, the nano silver of gained
Ribbon is respectively prepared by certain system process in antibacterial matrices, spandex fibre, wire, then by drafting, rove, thin
Mixed yarn is made in yarn winder;
6)Multi cord is made:Take three above-mentioned steps 5)The scribbled of gained is twisted with twisting equipment, wherein two yarns
Line discharges side by side, and in addition an one thread is wound in " S " type in this two one threads periphery jointly;
7)Face weave:Weft is woven by the requirements such as the density of fabric design, arrangement, tissue and warp with knitting machine;
8)Radiation protection post-processes:First fabric is carried out to pad electromagnetic shielding dressing liquid, one layer of Ag films is then plated with, finally carries out
It dries, bake, strengthen the radiation protection ability of fabric;
9)Fabric final finishing
1. wash contracting processing:In 25 ~ 35 DEG C of water temperature, for the bath raio used for 1: 20 ~ 25, it is that liquid hair can be net that the low temperature of selection, which washes contracting agent,
RC, dosage are 1.5 ~ 2.0%o.w.f, wash 10.0 ~ 20.0min, and then rinsing is primary, time 2min;
2. soft treatment:Fabric is put into softener solution and carries out soft treatment:First under the rotating speed of 300 ~ 500r/min
30 ~ 40min is stirred, then 15 ~ 25min of dual-frequency ultrasonic wave alternate treatment, finally stand 20 ~ 30min;
3. drying and processing:Fabric is subjected to drying and processing with fabric dryer.
(Three)Advantageous effect
(1)The radiation resistant fiber that anti-radiation garment fabric provided by the invention uses carried out screening with defibrator in advance,
The thick fiber of the comparison of uniform quality is filtered out, the void count for knitting fabric just can be reduced;And it is not radiation resistant fiber
It makes single thread and synthesizes multi cord into dividing sinker with other, but radiation resistant fiber and other fibers are made composite fibre in advance, then
Hybrid yams are made, are eventually fabricated multi cord, radiation resistant fiber can be made preferably to be mixed with other fibers in this way, be connected;
The fabric woven also padding by electromagnetic shielding dressing liquid, last layer Ag films are finally plated on surface layer, more enhance fabric
Capability of resistance to radiation.Fabric has very powerful radiation protection ability made of in this way, and capability of resistance to radiation reaches more than 90dB.
(2)Have bamboo charcoal fiber and cotton fiber in raw material of fabric, bamboo charcoal fiber have the advantages that moisture absorption breathe freely, bacteriostasis antibiosis,
And cotton fiber also has the advantages that moisture absorption is breathed freely, and adds in fabric made of both above fibers with stronger sucting wet air permeability
Energy;All fibres are because by anti pilling processing and subsequent combing so that the anti-pilling property of fabric significantly increases, unit plane
Long-pending ball top quantity substantially reduces.
(3)Every three of the warp is alternately arranged and each one group of oblique friendship of the weft for one group and each one group
It knits, such weaving manner so that the gap of two neighboring warp group is bigger so that the moisture-penetrable ventilated performance of fabric is good, this
Outer such weaving manner causes fabric better appearance and solid.
Description of the drawings
Fig. 1 is radiation-proof pregnant woman clothes fabric body braiding structure figure;
Fig. 2 is the twisted construction figure of multi cord.
Specific embodiment
With reference to embodiment, the embodiment of the present invention is furthur described in detail.Following embodiment is used for
Illustrate the present invention, but be not limited to the scope of the present invention.
A kind of radiation-proof pregnant woman clothes fabric is provided with reference to Fig. 1, with reference to Fig. 2 to the present invention, including:Radiation-proof pregnant woman clothes
Fabric body, the radiation-proof pregnant woman clothes fabric body are interwoven by warp thread 1 and weft yarn 2, and the warp 1 and weft 2 are equal
For multi cord, the multi cord is twisted by scribbled a3, scribbled b4, scribbled c5, three mixed yarns
Raw material penetrate fiber, 20-25 part wood-fibred, 17-20 parts of cotton fibers, 12-16 parts of polyester fibers, 10-12 by 25-28 parts of anti-width
Part nanometer silver antimicrobial master batch, 8-10 parts of spandex fibres, 5-8 parts of wires are formed;
The radiation resistant fiber includes the raw material of following mass percent:
Stainless steel fibre 22%
Nano silver fibre 28%
Conductive fiber 30%
Bamboo charcoal fiber 20%
Wherein, the scribbled a3 and scribbled b4 are discharged side by side, the scribbled c5 jointly in scribbled a3 and
Scribbled b4 peripheries are wound in " S " type.
Wherein, the chemical composition proportioning of the stainless steel fibre is:The content of C is
The content of 0.12-0.15, Si are 0.4-0.6, and the content of Mn is 0.4-0.6, and the content of Nb is<0.03, N content is
The content of 0.4-1.0, Cr are 6.5-18, and the content of Mo is 0.75-1.2, and the content of Ni is<0.2, surplus is iron.
Wherein, the warp 1 every three is alternately arranged oblique with 2 each one group of the weft for one group and each one group
To being interwoven.
Wherein, the every two adjacent warps 1 surround a quadrangle with every two adjacent wefts 2.
Finally, it is respectively 120 ° and 60 ° that two groups of the quadrangle diagonal.
The present invention also provides a kind of production technologies of radiation-proof pregnant woman clothes fabric, include the following steps:
1)Fiber pre-processes:Each composition fiber in radiation proof material fiber is resisted respectively
Pilling is handled, then to mixed yarn except the other compositions of radiation proof material fiber carry out anti pilling processing, anti pilling processing
Comprise the concrete steps that:Each composition fiber is placed in treatment fluid, the control for the treatment of fluid temperature is being 40 ~ 50 °C, processing time for 10 ~
20min;
2)Stock-dye:Fiber is added in into container, 40 °C of softened water is injected in container, with
Until softened water did not had fiber, 1 ~ 2g/L of levelling agent is added, anhydrous sodium sulphate and several g/l of soda ash are (according to the dense of dyestuff
Degree selection dosage), it stirs evenly, stands 30 ~ 40min, then fiber is taken out drying, be put into stock-dye machine and contaminated
Color;
3)Fiber is combed:With hair-feather plucking-shredding-carding-drafting-air spinning-automatic winding;
4)Make radiation resistant fiber:It is equal that each fiber is first put into seperator separation mass respectively
Even thicker fiber comes, and 22% stainless steel fibre, 28% nano silver fibre, 30% conductive fiber, 20% are taken by mass fraction
Bamboo charcoal fiber, then each composition fiber is put into fiber mixer and is uniformly sufficiently mixed;
5)Make mixed yarn:By above-mentioned steps 4)Radiation resistant fiber and wood-fibred, cotton fiber, polyester fiber, the nano silver of gained
Ribbon is respectively prepared by certain system process in antibacterial matrices, spandex fibre, wire, then by drafting, rove, thin
Mixed yarn is made in yarn winder;
6)Multi cord is made:Take three above-mentioned steps 5)The scribbled of gained is twisted with twisting equipment, wherein two yarns
Line discharges side by side, and in addition an one thread is wound in " S " type in this two one threads periphery jointly;
7)Face weave:Weft is woven by the requirements such as the density of fabric design, arrangement, tissue and warp with knitting machine;
8)Radiation protection post-processes:First fabric is carried out to pad electromagnetic shielding dressing liquid, one layer of Ag films is then plated with, finally carries out
It dries, bake, strengthen the radiation protection ability of fabric;
9)Fabric final finishing
1. wash contracting processing:In 25 ~ 35 DEG C of water temperature, for the bath raio used for 1: 20 ~ 25, it is that liquid hair can be net that the low temperature of selection, which washes contracting agent,
RC, dosage are 1.5 ~ 2.0%o.w.f, wash 10.0 ~ 20.0min, and then rinsing is primary, time 2min;
2. soft treatment:Fabric is put into softener solution and carries out soft treatment:First under the rotating speed of 300 ~ 500r/min
30 ~ 40min is stirred, then 15 ~ 25min of dual-frequency ultrasonic wave alternate treatment, finally stand 20 ~ 30min;
3. drying and processing:Fabric is subjected to drying and processing with fabric dryer.
With reference to specific embodiment, the present invention will be further elaborated:
Embodiment 1
First, fiber pre-processes:Anti pilling processing is carried out to each composition fiber in radiation proof material fiber respectively, then to mixed
Spinning carries out anti pilling processing except the other compositions of radiation proof material fiber, and anti pilling processing comprises the concrete steps that:By each ingredient
Fiber is placed in treatment fluid, and the control for the treatment of fluid temperature is being 40 °C, processing time 20min;Then, stock-dye:By fiber
Container is added in, 40 °C of softened water is injected in container, until softened water did not had fiber, adds levelling agent 1g/L, anhydrous sodium sulphate
With soda ash several g/l (selecting dosage according to the concentration of dyestuff), stir evenly, stand 40min, then fiber is taken out baking
It is dry, it is put into stock-dye machine and is dyed;Then, fiber is combed:With hair-feather plucking-shredding-carding-simultaneously
Item-air spinning-automatic winding;Then, radiation resistant fiber is made:It is equal that each fiber is first put into seperator separation mass respectively
Even thicker fiber comes, and 22% stainless steel fibre, 28% nano silver fibre, 30% conductive fiber, 20% bamboo charcoal are taken by mass fraction
Fiber, then each composition fiber is put into fiber mixer and is uniformly sufficiently mixed;Then, mixed yarn is made:By above-mentioned step
Rapid 4)Radiation resistant fiber and wood-fibred, cotton fiber, polyester fiber, nanometer silver antimicrobial master batch, spandex fibre, the wire of gained lead to
It crosses certain system process and ribbon is respectively prepared, mixed yarn then is made by drafting, rove, spun yarn winder;Then, it is made
Multi cord:Take three above-mentioned steps 5)The scribbled of gained is twisted with twisting equipment, wherein two one threads are arranged side by side
It puts, in addition an one thread is wound in " S " type in this two one threads periphery jointly;Then, face weave:Weft is pressed with knitting machine
The requirements such as density, arrangement, the tissue of fabric design and warp are woven;Then, radiation protection post-processes:First fabric is soaked
Electromagnetic shielding dressing liquid is rolled, one layer of Ag films is then plated with, is finally dried, baked, strengthen the radiation protection ability of fabric;Most
Afterwards, fabric final finishing:1. wash contracting processing:In 25 DEG C of water temperature, the bath raio used is 1:25, it is liquid hair that the low temperature of selection, which washes contracting agent,
The net RC of energy, dosage is 1.5%o.w.f, washs 20min, and then rinsing is primary, time 2min;2. soft treatment:Fabric is put
Enter and soft treatment is carried out in softener solution:40min is first stirred under the rotating speed of 300min, then dual-frequency ultrasonic wave replaces
25min is handled, finally stands 30min;3. drying and processing:Fabric is subjected to drying and processing with fabric dryer.
Embodiment 2
First, fiber pre-processes:Anti pilling processing is carried out to each composition fiber in radiation proof material fiber respectively, then to mixed
Spinning carries out anti pilling processing except the other compositions of radiation proof material fiber, and anti pilling processing comprises the concrete steps that:By each ingredient
Fiber is placed in treatment fluid, and the control for the treatment of fluid temperature is being 45 °C, processing time 15min;Then, stock-dye:By fiber
Container is added in, 40 °C of softened water is injected in container, until softened water did not had fiber, adds levelling agent 1.5g/L, member is bright
Powder and several g/l of soda ash (selecting dosage according to the concentration of dyestuff), stir evenly, stand 35min, then fiber is taken out baking
It is dry, it is put into stock-dye machine and is dyed;Then, fiber is combed:With hair-feather plucking-shredding-carding-simultaneously
Item-air spinning-automatic winding;Then, radiation resistant fiber is made:It is equal that each fiber is first put into seperator separation mass respectively
Even thicker fine fibre comes, and 22% stainless steel fibre, 28% nano silver fibre, 30% conductive fiber, 20% bamboo charcoal are taken by mass fraction
Fiber, then each composition fiber is put into fiber mixer and is uniformly sufficiently mixed;Then, mixed yarn is made:By above-mentioned step
Rapid 4)Radiation resistant fiber and wood-fibred, cotton fiber, polyester fiber, nanometer silver antimicrobial master batch, spandex fibre, the wire of gained lead to
It crosses certain system process and ribbon is respectively prepared, mixed yarn then is made by drafting, rove, spun yarn winder;Then, it is made
Multi cord:Take three above-mentioned steps 5)The scribbled of gained is twisted with twisting equipment, wherein two one threads are arranged side by side
It puts, in addition an one thread is wound in " S " type in this two one threads periphery jointly;Then, face weave:Weft is pressed with knitting machine
The requirements such as density, arrangement, the tissue of fabric design and warp are woven;Then, radiation protection post-processes:First fabric is soaked
Electromagnetic shielding dressing liquid is rolled, one layer of Ag films is then plated with, is finally dried, baked, strengthen the radiation protection ability of fabric;Most
Afterwards, fabric final finishing:1. wash contracting processing:In 30 DEG C of water temperature, for the bath raio used for 1: 22.5, it is liquid that the low temperature of selection, which washes contracting agent,
The net RC of hair energy, dosage is 1.75%o.w.f, washs 15min, and then rinsing is primary, time 2min;2. soft treatment:Face
Material, which is put into softener solution, carries out soft treatment:35min is first stirred under the rotating speed of 400min, then dual-frequency ultrasonic wave
Alternate treatment 20min, finally stands 25min;3. drying and processing:Fabric is subjected to drying and processing with fabric dryer.
Embodiment 3
First, fiber pre-processes:Anti pilling processing is carried out to each composition fiber in radiation proof material fiber respectively, then to mixed
Spinning carries out anti pilling processing except the other compositions of radiation proof material fiber, and anti pilling processing comprises the concrete steps that:By each ingredient
Fiber is placed in treatment fluid, and the control for the treatment of fluid temperature is being 50 °C, processing time 10min;Then, stock-dye:By fiber
Container is added in, 40 °C of softened water is injected in container, until softened water did not had fiber, adds levelling agent 2g/L, anhydrous sodium sulphate
With soda ash several g/l (selecting dosage according to the concentration of dyestuff), stir evenly, stand 30min, then fiber is taken out baking
It is dry, it is put into stock-dye machine and is dyed;Then, fiber is combed:With hair-feather plucking-shredding-carding-simultaneously
Item-air spinning-automatic winding;Then, radiation resistant fiber is made:It is equal that each fiber is first put into seperator separation mass respectively
Even thicker fiber comes, and 22% stainless steel fibre, 28% nano silver fibre, 30% conductive fiber, 20% bamboo charcoal are taken by mass fraction
Fiber, then each composition fiber is put into fiber mixer and is uniformly sufficiently mixed;Then, mixed yarn is made:By above-mentioned step
Rapid 4)Radiation resistant fiber and wood-fibred, cotton fiber, polyester fiber, nanometer silver antimicrobial master batch, spandex fibre, the wire of gained lead to
It crosses certain system process and ribbon is respectively prepared, mixed yarn then is made by drafting, rove, spun yarn winder;Then, it is made
Multi cord:Take three above-mentioned steps 5)The scribbled of gained is twisted with twisting equipment, wherein two one threads are arranged side by side
It puts, in addition an one thread is wound in " S " type in this two one threads periphery jointly;Then, face weave:Weft is pressed with knitting machine
The requirements such as density, arrangement, the tissue of fabric design and warp are woven;Then, radiation protection post-processes:First fabric is soaked
Electromagnetic shielding dressing liquid is rolled, one layer of Ag films is then plated with, is finally dried, baked, strengthen the radiation protection ability of fabric;Most
Afterwards, fabric final finishing:1. wash contracting processing:In 35 DEG C of water temperature, for the bath raio used for 1: 20, it is liquid hair that the low temperature of selection, which washes contracting agent,
The net RC of energy, dosage is 2%o.w.f, washs 10min, and then rinsing is primary, time 2min;2. soft treatment:Fabric is put into
Soft treatment is carried out in softener solution:35min is first stirred under the rotating speed of 500min, then at dual-frequency ultrasonic wave alternating
15min is managed, finally stands 20min;3. drying and processing:Fabric is subjected to drying and processing with fabric dryer.
Coordinate above-described embodiment, be compared, obtain a result as follows with general radiation-proof fabric in the market:
By table results it is found that the present invention exposure suit fabric wearability and radiation-proof effect be above it is common on the market
Radiation-proof fabric, synthetically, the wearability and radiation-proof effect of embodiment 1 are best.
In conclusion the restricted embodiment that it is the present invention that the above embodiment, which is not, all those skilled in the art
The modification carried out on the basis of the substantive content of the present invention or equivalent deformation, the technology scope in the present invention.
Claims (7)
1. a kind of radiation-proof pregnant woman clothes fabric, which is characterized in that including radiation-proof pregnant woman clothes fabric body, the radiation protection
Maternity dress fabric body is formed by warp thread and weft yarns, and the warp and weft are multi cord, and the multi cord is by mixing
Yarn a, scribbled b, scribbled c are twisted, and the raw material of three mixed yarns penetrates fibre by 25-28 parts of anti-width
Dimension, 20-25 parts of wood-fibreds, 17-20 parts of cotton fibers, 12-16 parts of polyester fibers, 10-12 parts of nanometer silver antimicrobial master batches, 8-10 parts of ammonia
Synthetic fibre fiber, 5-8 parts of wires are formed;
The radiation resistant fiber includes the raw material of following mass percent:
Stainless steel fibre 22%
Nano silver fibre 28%
Conductive fiber 30%
Bamboo charcoal fiber 20%.
A kind of 2. radiation-proof pregnant woman clothes fabric according to claim 1, which is characterized in that the scribbled a and mixed
Yarn b is discharged side by side, and the scribbled c is wound in " S " type in scribbled a and scribbled b peripheries jointly.
A kind of 3. radiation-proof pregnant woman clothes fabric according to claim 1, which is characterized in that the change of the stainless steel fibre
Studying distribution ratio is:The content of C is 0.12-0.15, and the content of Si is 0.4-0.6, and the content of Mn is 0.4-0.6, the content of Nb
For<0.03, N content is 0.4-1.0, and the content of Cr is 6.5-18, and the content of Mo is 0.75-1.2, and the content of Ni is<0.2,
Surplus is iron.
4. a kind of radiation-proof pregnant woman clothes fabric according to claim 1, which is characterized in that every three of the warp is one
Group and each one group are alternately arranged and each one group of the weft is oblique is interwoven.
A kind of 5. radiation-proof pregnant woman clothes fabric according to claim 1, which is characterized in that every two adjacent warps
Line surrounds a quadrangle with every two adjacent wefts.
A kind of 6. radiation-proof pregnant woman clothes fabric according to claim 1, which is characterized in that two groups pairs of the quadrangle
Angle is respectively 120 ° and 60 °.
7. a kind of production technology of radiation-proof pregnant woman clothes fabric, includes the following steps:
1)Fiber pre-processes:Anti pilling processing is carried out to each composition fiber in radiation proof material fiber respectively, then to blended
Yarn carries out anti pilling processing except the other compositions of radiation proof material fiber, and anti pilling processing comprises the concrete steps that:By each ingredient fibre
Dimension is placed in treatment fluid, and the control for the treatment of fluid temperature is being 40 ~ 45 °C, and processing time is 10 ~ 15min;
2)Stock-dye:Fiber is added in into container, 40 °C of softened water is injected in container, until softened water did not had fiber, then
Levelling agent 1-2g/L, anhydrous sodium sulphate and several g/l of soda ash (dosage is selected according to the concentration of dyestuff) are added in, stirs evenly, stands
30 ~ 40min, then fiber is taken out drying, it is put into stock-dye machine and is dyed;
3)Fiber is combed:With hair-feather plucking-shredding-carding-drafting-air spinning-automatic winding;
4)Make radiation resistant fiber:First each fiber put into respectively seperator isolate uniform quality fine fibre come, by quality
Score takes 22% stainless steel fibre, 28% nano silver fibre, 30% conductive fiber, 20% bamboo charcoal fiber, then each composition fiber is put into
It is uniformly sufficiently mixed in fiber mixer;
5)Make mixed yarn:By above-mentioned steps 4)Radiation resistant fiber and wood-fibred, cotton fiber, polyester fiber, the nano silver of gained
Ribbon is respectively prepared by certain system process in antibacterial matrices, spandex fibre, wire, then by drafting, rove, thin
Mixed yarn is made in yarn winder;
6)Multi cord is made:Take three above-mentioned steps 5)The scribbled of gained is twisted with twisting equipment, wherein two yarns
Line discharges side by side, and in addition an one thread is wound in " S " type in this two one threads periphery jointly;
7)Face weave:Weft is woven by the requirements such as the density of fabric design, arrangement, tissue and warp with knitting machine;
8)Radiation protection post-processes:First fabric is carried out to pad electromagnetic shielding dressing liquid, one layer of Ag films is then plated with, finally carries out
It dries, bake, strengthen the radiation protection ability of fabric;
9)Fabric final finishing
1. wash contracting processing:In 25-35 DEG C of water temperature, for the bath raio used for 1: 20-25, it is that liquid hair can be net that the low temperature of selection, which washes contracting agent,
RC, dosage are 1.5-2.0%o.w.f, wash 10.0-20.0min, and then rinsing is primary, time 2min;
2. soft treatment:Fabric is put into softener solution and carries out soft treatment:First under the rotating speed of 300-500r/min
30-40min is stirred, then dual-frequency ultrasonic wave alternate treatment 15-25min, finally stands 20-30min;
3. drying and processing:Fabric is subjected to drying and processing with fabric dryer.