CN108193337A - A kind of blended corespun composite yarn of high emulation cashmere and its fabric - Google Patents
A kind of blended corespun composite yarn of high emulation cashmere and its fabric Download PDFInfo
- Publication number
- CN108193337A CN108193337A CN201810188187.0A CN201810188187A CN108193337A CN 108193337 A CN108193337 A CN 108193337A CN 201810188187 A CN201810188187 A CN 201810188187A CN 108193337 A CN108193337 A CN 108193337A
- Authority
- CN
- China
- Prior art keywords
- cashmere
- emulation
- blended
- fiber
- high emulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of high emulation blended corespun composite yarns of cashmere, by being coated with high emulation cashmere blended yarn in core filaments, height emulation cashmere blended yarn is coated on core filaments outer surface, the high emulation cashmere blended yarn is spinned by blend fibre, the blend fibre adds wool, acrylic fibers, polyamide fibre and terylene thereto based on height emulation cashmere fiber；Terylene accounts for the 35 55% of blend fibre gross mass, the polyamide fibre accounts for the 15 20% of blend fibre gross mass, acrylic fibers account for the 4 15% of blend fibre gross mass, the high emulation cashmere fiber accounts for the 20 30% of blend fibre gross mass, the wool accounts for the 4 15% of blend fibre gross mass, and the blended corespun composite yarn number of the high emulation cashmere is 14.8tex 48tex.The present invention emulates cashmere fiber by using the rabbit hair, Hair style high-shrinkage acrylic fiber and the blended height that obtains of Hair style acrylic fiber, compared to traditional cashmere fiber, cost substantially reduces, and has anti-static function, and it ensure that the appearance of plentiful fabric, in turn ensure the feel of natural cashmere.
Description
Technical field
The invention belongs to textile manufacturing processing technique fields, and in particular to a kind of blended corespun composite yarn of high emulation cashmere and
Its fabric.
Background technology
Cashmere is fiber that is thin one by one and being bent, wherein containing many air, and air layer is formed, it can defend outer
Carry out the invasion of cold air, retaining body temperature will not lower.Cashmere is thinner than wool very much, and outer scale is also finer and closely woven than wool, smooth, because
This, light-weight, soft, good toughness.It is particularly suitable for manufacturing underwear, it is light, soft, soft, sliding when wearing next to the skin, as snug as a bug in a rug, still,
The easy pilling mostly of cashmere sweater made of cashmere, once there is pilling, just affects the aesthetics of cashmere sweater；Simultaneously
Cashmere resources are limited, and cashmere product is very expensive.
Invention content
In view of the above-mentioned deficiencies in the prior art, it is an object of the present invention to now provide a kind of elasticity it is larger, it is effective reduction fabric into
This, and ensure the blended corespun composite yarn of high emulation cashmere and its fabric of fabric wool characteristic.
In order to solve the above technical problems, the technical solution adopted by the present invention is：A kind of high emulation blended cored of cashmere is compound
Yarn, innovative point are：By being coated with high emulation cashmere blended yarn, the high emulation cashmere blended yarn helical form in core filaments
It is wrapped around in core filaments outer surface, the high emulation cashmere blended yarn is spinned by blend fibre, and the blend fibre is with height
It emulates based on cashmere fiber, adds wool, acrylic fibers, polyamide fibre and terylene thereto；
The terylene accounts for the 35-55% of blend fibre gross mass, and the polyamide fibre accounts for the 15-20% of blend fibre gross mass,
Acrylic fibers account for the 4-15% of blend fibre gross mass, and the high emulation cashmere fiber accounts for the 20-30% of blend fibre gross mass, described
Wool accounts for the 4-15% of blend fibre gross mass, and the blended corespun composite yarn number of the high emulation cashmere is 14.8tex-48tex.
Further, the high emulation cashmere fiber is by rabbit fur fibre, Hair style high-shrinkage acrylic fiber and Hair style nitrile
Synthetic fibre fiber forms, and height emulation cashmere fiber is made of rabbit fur fibre, Hair style high-shrinkage acrylic fiber and Hair style acrylic fiber,
Rabbit fur fibre accounts for the 10-40% of high emulation cashmere fiber gross mass, and Hair style high-shrinkage acrylic fiber accounts for high emulation cashmere fiber
The 25-40% of gross mass, Hair style acrylic fiber account for the 25-60% of high emulation cashmere fiber gross mass.
Further, the core filaments select spandex and the compound long filament of graphene or chinlon filament and graphene compound
One or two do core filaments and form single or twin-core composite yarn in long filament；Meanwhile spandex and the compound length of graphene also can be selected
A kind of and viscose filament yarn or PTT long filaments in silk or the chinlon filament long filament compound with graphene that twin-core is collectively formed is compound
Covering yarn.
Further, the fineness of the Hair style high-shrinkage acrylic fiber be 0.8-1.5 daniers, length 38-40mm.
Another object of the present invention is to disclose a kind of high emulation fleece fabrics, and innovative point is：Cashmere is emulated by height
Blended corespun composite yarn is directly over warp thread and completes high emulation fleece fabrics with weft yarns weaving, dyeing and final finishing step
Production.
Further, by the height blended corespun composite yarn of emulation cashmere by plying double twisting, dyeing, knitting and final finishing step
Complete the production of high emulation fleece fabrics.
Beneficial effects of the present invention are as follows：
(1) present invention is by using the rabbit hair, Hair style high-shrinkage acrylic fiber and Hair style acrylic fiber is blended obtains height
Cashmere fiber is emulated, compared to traditional cashmere fiber, cost substantially reduces, and ensure that plentiful appearance of fabrics,
In turn ensure the feel of natural cashmere.
(2) present invention, using spandex fibre as core filaments, can effectively increase the bullet of fabric by using the mode of cored
Property, snugness of fit bigger, meanwhile, the compound long filament of graphene is added in core filaments, can realize anlistatig effect.
Specific embodiment
Embodiments of the present invention are illustrated by particular specific embodiment below, those skilled in the art can be by this explanation
Content disclosed by book understands other advantages and effect of the present invention easily.
A kind of high emulation blended corespun composite yarn of cashmere, it is described by being coated with high emulation cashmere blended yarn in core filaments
Height emulation cashmere blended yarn is coated on core filaments outer surface, and the high emulation cashmere blended yarn is spinned by blend fibre, described
Blend fibre adds wool, acrylic fibers, polyamide fibre and terylene thereto based on height emulation cashmere fiber；
The terylene accounts for the 35-55% of blend fibre gross mass, and the polyamide fibre accounts for the 15-20% of blend fibre gross mass,
Acrylic fibers account for the 4-15% of blend fibre gross mass, and the high emulation cashmere fiber accounts for the 20-30% of blend fibre gross mass, described
Wool accounts for the 4-15% of blend fibre gross mass, and the blended corespun composite yarn number of the high emulation cashmere is 14.8tex-48tex.
Height emulation cashmere fiber is made of rabbit fur fibre, Hair style high-shrinkage acrylic fiber and Hair style acrylic fiber, rabbit
Wool fibre accounts for the 10-40% of high emulation cashmere fiber gross mass, and it is total that Hair style high-shrinkage acrylic fiber accounts for high emulation cashmere fiber
The 25-40% of quality, Hair style acrylic fiber account for the 25-60% of high emulation cashmere fiber gross mass.
The core filaments select spandex and the compound long filament of graphene or chinlon filament and the compound long filament of graphene, meanwhile,
Also twin-core composite core-spun yarn can be collectively formed with a kind of in viscose filament yarn and PTT, there is anti-static function.
The fineness of Hair style high-shrinkage acrylic fiber is 0.8-1.5 daniers, and length is
38-40mm。
A kind of high emulation fleece fabrics is directly over warp thread by the height emulation blended corespun composite yarn of cashmere and is knitted with weft yarns
It makes, dye and final finishing step completes the production of high emulation fleece fabrics；Can also the blended corespun composite yarn of cashmere be emulated by height
The production of high emulation fleece fabrics is completed by combining double twisting, dyeing, knitting and final finishing step.
Embodiment 1
(1) it spins
The height emulation blended corespun composite yarn of cashmere is coated with high emulation using spandex and the compound long filament of graphene as core filaments
Cashmere blended yarn, height emulation cashmere blended yarn specification is 26 yarns, by 15% wool, 15% acrylic fibers, 15% polyamide fibre, 35% terylene
With 20% high emulation cashmere fiber composition, it is fine by 10% rabbit fur fibre, 30% Hair style high shrinkage acrylic that height emulates cashmere fiber
60% Hair style acrylic fiber of peacekeeping forms, and the fineness of Hair style high-shrinkage acrylic fiber is 0.8 danier, length 38mm,
Corespun composite yarn number is 14.8tex.
The performance parameter of yarn obtained by the present embodiment is：
(2) it weaves
A kind of high emulation fleece fabrics is walked by height emulation cashmere blended yarn by plying double twisting, dyeing, knitting and final finishing
The rapid production for completing high emulation fleece fabrics.
The performance parameter of fabric obtained by the present embodiment is：
By above table it is found that the present invention weaves to obtain the effect of cashmere by using acrylic fiber, in economic benefit
While substantially reducing, pilling resistance, antistatic property are all far superior to Cashmere core-spun yarn and cashmere cored fabric.
Embodiment 2
The height emulation blended corespun composite yarn of cashmere, spandex make heart yarn with the compound long filament of graphene and PTT long filament twin-cores, outside
High emulation cashmere blended yarn is coated with, height emulation cashmere blended yarn specification is 28 yarns, by 11% wool, 4% acrylic fibers, 20% brocade
The high emulation cashmere fiber composition of synthetic fibre, 40% terylene and 25%, height emulation cashmere fiber are high by 20% rabbit fur fibre, 25% Hair style
Acrylic fiber and 55% Hair style acrylic fiber composition are shunk, the fineness of Hair style high-shrinkage acrylic fiber is 1.5 daniers, long
It spends for 40mm, corespun composite yarn number is 48tex.
The performance parameter of yarn obtained by the present embodiment is：
(2) it weaves
A kind of high emulation fleece fabrics is walked by height emulation cashmere blended yarn by plying double twisting, dyeing, knitting and final finishing
The rapid production for completing high emulation fleece fabrics.
The performance parameter of fabric obtained by the present embodiment is：
By above table it is found that the present invention weaves to obtain the effect of cashmere by using acrylic fiber, in economic benefit
While substantially reducing, pilling resistance, antistatic property are all far superior to Cashmere core-spun yarn and cashmere cored fabric.
Embodiment 3
(1) it spins
The height emulation blended corespun composite yarn of cashmere, chinlon filament is core filaments with the compound long filament of graphene, is coated with height
Cashmere blended yarn is emulated, height emulation cashmere blended yarn specification is 32 yarns, is washed by 5% wool, 5% acrylic fibers, 16% polyamide fibre, 54%
Synthetic fibre and 20% high emulation cashmere fiber composition, height emulation cashmere fiber is by 40% rabbit fur fibre, 28% Hair style high shrinkage acrylic
Fiber and 32% Hair style acrylic fiber composition, the fineness of Hair style high-shrinkage acrylic fiber is 1.5 daniers, and length is
38mm, corespun composite yarn number are 32tex.
The performance parameter of yarn obtained by the present embodiment is：
(2) it weaves
A kind of high emulation fleece fabrics is walked by height emulation cashmere blended yarn by plying double twisting, dyeing, knitting and final finishing
The rapid production for completing high emulation fleece fabrics.
The performance parameter of fabric obtained by the present embodiment is：
By above table it is found that the present invention weaves to obtain the effect of cashmere by using acrylic fiber, in economic benefit
While substantially reducing, pilling resistance, antistatic property are all far superior to Cashmere core-spun yarn and cashmere cored fabric.
The present invention is by using the rabbit hair, Hair style high-shrinkage acrylic fiber and Hair style acrylic fiber is blended obtains high emulation
Cashmere fiber, compared to traditional cashmere fiber, cost substantially reduces, and ensure that the appearance of the plentiful rabbit hair, again
It ensure that the feel of natural cashmere.The present invention, using spandex fibre as core filaments, can effectively increase by using the mode of cored
Add the elasticity of fabric, snugness of fit bigger, meanwhile, the compound long filament of graphene is added in core filaments, can be realized anti-quiet
The effect of electric.
Above-described embodiment is presently preferred embodiments of the present invention, is not the limitation to technical solution of the present invention, as long as
Without the technical solution that creative work can be realized on the basis of above-described embodiment, it is regarded as falling into patent of the present invention
Rights protection scope in.
Claims (6)
1. a kind of high emulation blended corespun composite yarn of cashmere, it is characterised in that：It is mixed by being coated with high emulation cashmere in core filaments
Spinning, the high emulation cashmere blended yarn are coated on core filaments outer surface, and the high emulation cashmere blended yarn is spinned by blend fibre
It forms, the blend fibre adds wool, acrylic fibers, polyamide fibre and terylene thereto based on height emulation cashmere fiber；
The terylene accounts for the 35-55% of blend fibre gross mass, and the polyamide fibre accounts for the 15-20% of blend fibre gross mass, acrylic fibers
The 4-15% of blend fibre gross mass is accounted for, the high emulation cashmere fiber accounts for the 20-30% of blend fibre gross mass, the wool
The 4-15% of blend fibre gross mass is accounted for, the blended corespun composite yarn number of the high emulation cashmere is 14.8tex-48tex.
2. a kind of high emulation blended corespun composite yarn of cashmere according to claim 1, it is characterised in that：The high emulation sheep
Down Fiber is made of rabbit fur fibre, Hair style high-shrinkage acrylic fiber and Hair style acrylic fiber, and height emulation cashmere fiber is by rabbit
Wool fibre, Hair style high-shrinkage acrylic fiber and Hair style acrylic fiber composition, rabbit fur fibre account for the high emulation total matter of cashmere fiber
The 10-40% of amount, Hair style high-shrinkage acrylic fiber account for the 25-40% of high emulation cashmere fiber gross mass, and Hair style acrylic fibers are fine
Dimension accounts for the 25-60% of high emulation cashmere fiber gross mass.
3. a kind of high emulation blended corespun composite yarn of cashmere according to claim 1, it is characterised in that：The core filaments are selected
Spandex does core filaments with one or two in the compound long filament of graphene with the compound long filament of graphene or chinlon filament and forms single
Or twin-core composite yarn；Meanwhile spandex and the compound long filament of graphene or chinlon filament and the compound long filament of graphene also can be selected
In it is a kind of with viscose filament yarn or twin-core composite core-spun yarn is collectively formed in PTT long filaments.
4. a kind of high emulation blended corespun composite yarn of cashmere according to claim 1, it is characterised in that：The Hair style is high
The fineness of acrylic fiber is shunk for 0.8-1.5 daniers, length 38-40mm.
5. a kind of high emulation fleece fabrics as described in claim 1, it is characterised in that：It is compound by the height emulation blended cored of cashmere
Yarn is directly over the production that warp thread completes high emulation fleece fabrics with weft yarns weaving, dyeing and final finishing step.
6. a kind of high emulation fleece fabrics according to claim 4, it is characterised in that：It is answered by the height emulation blended cored of cashmere
Close the production that yarn completes high emulation fleece fabrics by plying double twisting, dyeing, knitting and final finishing step.