CN108176519A - 一种钛铁矿高效捕收剂及其制备方法 - Google Patents
一种钛铁矿高效捕收剂及其制备方法 Download PDFInfo
- Publication number
- CN108176519A CN108176519A CN201711238271.0A CN201711238271A CN108176519A CN 108176519 A CN108176519 A CN 108176519A CN 201711238271 A CN201711238271 A CN 201711238271A CN 108176519 A CN108176519 A CN 108176519A
- Authority
- CN
- China
- Prior art keywords
- ilmenite
- collecting agent
- weight
- efficient collecting
- mentioned parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种钛铁矿高效捕收剂及其制备方法,包括以下重量百分比的各组分:松香58~62%、亚硫酸氢钠18~20%、乙醇胺11~13%、烷基磺酸盐7~9%。本发明的钛铁矿高效捕收剂的制备方法为:将上述重量份的松香倒入反应釜中,第一步加入上述重量份亚硫酸氢钠,在70~80℃反应60~90分钟;第二步加入上述重量份乙醇胺,在120~130℃反应40~60分钟;第三步再加入上述重量份烷基磺酸盐,搅拌均匀即得钛铁矿高效捕收剂。本发明的钛铁矿高效捕收剂,适用于低品位钛铁矿的浮选,能够获得较高品位和较高回收率的钛精矿。另外,该捕收剂捕收力强、选择性好、成本低、环境友好,具有良好的市场推广价值。
Description
技术领域
本发明涉及一种钛铁矿高效捕收剂及其制备方法,属于矿物加工过程选矿药剂领域。
背景技术
我国钛资源较为丰富,在自然界分布极广,但有工业价值的主要为钛铁矿和金红石。全国有20多省市分布有钛矿,尤其以四川攀西地区和河北承德地区蕴藏丰富。我国钛资源主要呈以下特点:钛铁矿多,金红石少;原生矿多,次生矿少;贫矿多,富矿少,这更增加了钛矿的综合利用难度。因此立足于现状,强化资源高效开发利用是转变我国钛资源优势的必然选择。
对于难选低品位钛铁矿来说,钛的高效综合利用不仅取决于选矿工艺的革新进步,而且与选矿药剂的开发和利用紧密相关,并且有时浮选药剂往往成为解决关键问题的核心技术。常用的钛铁矿浮选的捕收剂主要有油酸、氧化石蜡皂、羟肟酸、苯乙烯膦酸、苯乙烯胂酸以及组合捕收剂MOS、MOH系列捕收剂等,实践证明大部分药剂目前已经取得了较为理想的指标,但仍存在不足,如脂肪酸类捕收剂具有选择性差、苯乙烯胂酸毒性大、苯乙烯膦酸价格昂贵等缺点。工业上应用最多的主要为苯甲羟肟酸、水杨羟肟酸、5,9-羟肟酸和辛基羟肟酸等短碳链羟肟酸,虽然在选择性上具有较好的优势,但是其捕收能力稍弱,使其应用受到限制。
发明内容
本发明的目的针对上述已有技术存在的不足,提供一种钛铁矿高效捕收剂及其制备方法,本发明的钛铁矿高效捕收剂能有效克服现有捕收剂的缺陷,具有捕收性能好、选择性好、成本低、用量少等优点。
一种钛铁矿高效捕收剂,其特征在于由下述重量份的原料制备而成:松香58~62%、亚硫酸氢钠18~20%、乙醇胺11~13%、烷基磺酸盐7~9%。
所述的乙醇胺为单乙醇胺、二乙醇胺或三乙醇胺。
所述的烷基磺酸盐为十二烷基磺酸钠、十四烷基磺酸钠、十六烷基磺酸钠或十八烷基磺酸钠。
一种钛铁矿高效捕收剂的制备方法,其特征在于按以下步骤进行:将上述重量份的松香倒入反应釜中,第一步加入上述重量份亚硫酸氢钠,在70~80℃反应60~90分钟;第二步加入上述重量份乙醇胺,在120~130℃反应40~60分钟;第三步再加入上述重量份烷基磺酸盐,搅拌均匀即得钛铁矿高效捕收剂。
本发明的一种钛铁矿高效捕收剂,适用于低品位钛铁矿的浮选,能够获得较高品位和较高回收率的钛精矿。另外,该捕收剂捕收力强、选择性好、成本低、环境友好,具有良好的市场推广价值。
具体实施方式
本发明结合具体实施例对本发明的制备方法作进一步说明,但不受这些实施例的限制。
实施例1
将重量份的58%松香倒入反应釜中,第一步加入重量份20%亚硫酸氢钠,在75℃反应70分钟;第二步加入重量份单乙醇胺13%,在120℃反应60分钟;第三步再加入上述重量份十二烷基磺酸钠9%,搅拌均匀即得本发明的钛铁矿高效捕收剂产品。
某中低品位钛铁矿TiO2品位为19.36%,调整矿浆pH,本发明的捕收剂用量450g/t,经一次粗选可获得TiO2品位为36.58%的钛精矿,回收率84.84%。
实施例2
将重量份的60%松香倒入反应釜中,第一步加入重量份19%亚硫酸氢钠,在80℃反应90分钟;第二步加入重量份二乙醇胺13%,在130℃反应40分钟;第三步再加入上述重量份十八烷基磺酸钠8%,搅拌均匀即得本发明的钛铁矿高效捕收剂产品。
某中低品位钛铁矿TiO2品位为18.08%,调整矿浆pH,捕收剂用量500g/t,经一次粗选可获得TiO2品位为35.68%的钛精矿,回收率85.45%。
实施例3
将重量份的59%松香倒入反应釜中,第一步加入重量份20%亚硫酸氢钠,在75℃反应75分钟;第二步加入重量份三乙醇胺12%,在120℃反应50分钟;第三步再加入上述重量份十六烷基磺酸钠9%,搅拌均匀即得本发明的钛铁矿高效捕收剂产品。
某中低品位钛铁矿TiO2品位为21.62%,调整矿浆pH,捕收剂用量400g/t,经一次粗选可获得TiO2品位为38.83%的钛精矿,回收率89.66%。
实施例4
将重量份的62%松香倒入反应釜中,第一步加入重量份18%亚硫酸氢钠,在70℃反应60分钟;第二步加入重量份三乙醇胺11%,在125℃反应50分钟;第三步再加入上述重量份十四烷基磺酸钠7%,搅拌均匀即得本发明的钛铁矿高效捕收剂产品。
某中低品位钛铁矿TiO2品位为20.58%,调整矿浆pH,捕收剂用量400g/t,经一次粗选可获得TiO2品位为37.88%的钛精矿,回收率88.96%。
Claims (4)
1.一种钛铁矿高效捕收剂,其特征在于由下述重量份的原料制备而成:松香58~62%、亚硫酸氢钠18~20%、乙醇胺11~13%、烷基磺酸盐7~9%。
2.根据权利要求1所述的钛铁矿高效捕收剂,其特征在于:所述的乙醇胺为单乙醇胺、二乙醇胺或三乙醇胺。
3.根据权利要求1所述的钛铁矿高效捕收剂,其特征在于:所述的烷基磺酸盐为十二烷基磺酸钠、十四烷基磺酸钠、十六烷基磺酸钠或十八烷基磺酸钠。
4.一种根据权利要求1所述的钛铁矿高效捕收剂的制备方法,其特征在于按以下步骤进行:将上述重量份的松香倒入反应釜中,第一步加入上述重量份亚硫酸氢钠,在70~80℃反应60~90分钟;第二步加入上述重量份乙醇胺,在120~130℃反应40~60分钟;第三步再加入上述重量份烷基磺酸盐,搅拌均匀即得钛铁矿高效捕收剂。