CN108168970A - 一种金相试样的冷加工制样方法 - Google Patents

一种金相试样的冷加工制样方法 Download PDF

Info

Publication number
CN108168970A
CN108168970A CN201711365549.0A CN201711365549A CN108168970A CN 108168970 A CN108168970 A CN 108168970A CN 201711365549 A CN201711365549 A CN 201711365549A CN 108168970 A CN108168970 A CN 108168970A
Authority
CN
China
Prior art keywords
sample
metallographic specimen
acrylic resin
cold working
working method
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711365549.0A
Other languages
English (en)
Inventor
王海
杨晓康
罗斌莉
杨宏进
魏芬绒
金旭丹
祁函
崔文俊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
XI'AN SAITE SIMAI TITANIUM INDUSTRY Co Ltd
Original Assignee
XI'AN SAITE SIMAI TITANIUM INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by XI'AN SAITE SIMAI TITANIUM INDUSTRY Co Ltd filed Critical XI'AN SAITE SIMAI TITANIUM INDUSTRY Co Ltd
Priority to CN201711365549.0A priority Critical patent/CN108168970A/zh
Publication of CN108168970A publication Critical patent/CN108168970A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种金相试样的冷加工制样方法，根据待制备试样的形状及大小，使用软性材料制作简易模具，将待制备试样放置于模具中央，将粉末状牙托粉倒入模具，并充满模腔，倒入牙托水，使其自然凝固，凝固后得到加工后金相试样；使用本发明制备试样不受试样本身形状和尺寸限制，对于有裂纹、空隙的试样渗透性好，操作简单，使用后方便再取样。对样品要求低，不受试样形状尺寸限制，牙托粉固化迅速，平稳，对小孔和凹陷有优异的渗透能力；制备的样品具有足够的硬度和韧性，耐酸碱性能好；再次取样容易，用丙酮溶液去除牙托粉即可得到原始试样。

Description

一种金相试样的冷加工制样方法
【技术领域】
本发明属于金相检测技术领域，尤其是涉及一种金相试样的冷加工制样方法。
【背景技术】
目前多金属试样的制样多数采用自动镶嵌机(加热)，或直接使用夹具夹持试样进行金相试样的制备。传统的自动镶嵌机制备试样方法对样品本身尺寸、形状有要求，对于异型的、尺寸不规则试样不能进行镶嵌，而且抗酸耐腐蚀性能差；同时，自动镶嵌机制备的试样强度较高，再取样困难。使用夹具夹持试样进行操作简单易行，但是局限性也很大，主要不适用较小尺寸试样的制备，尺寸小不易夹持，磨光、抛光作业困难。
【发明内容】
本发明的目的是提供一种金相试样的冷加工制样方法，以解决异形、尺寸不规则金相试样的制备的问题。
本发明采用以下技术方案：一种金相试样的冷加工制样方法，根据待制备金相试样的形状及大小，使用软性材料制作简易模具，将待制备试样放置于模具中央，将粉末状牙托粉倒入模具，并充满模腔，倒入牙托水，使其自然凝固，凝固后得到加工后金相试样。
进一步地，粉末状牙托粉为甲基丙烯酸甲酯，且其粒度≥80目。
进一步地，粉末状牙托粉和牙托水的粉液比为5：3。
进一步地，模腔的高度为1-1.5cm。
进一步地，自然凝固时间为10-30min。
本发明的另一种技术方案，上述制得的金相试样的重复利用方法，通过有机溶剂将加工后的金相试样溶解，得到金相试样。
进一步地，有机溶剂为丙酮溶液。
本发明的有益效果是：使用本发明制备试样不受试样本身形状和尺寸限制，对于有裂纹、空隙的试样渗透性好，操作简单，使用后方便再取样。对样品要求低，不受试样形状尺寸限制，只要试样长宽不超过4*4cm均可采用本方法，牙托粉固化迅速，平稳，对小孔和凹陷有优异的渗透能力；制备的样品具有足够的硬度和韧性，耐酸碱性能好；再次取样容易，用丙酮溶液去除牙托粉即可得到原始试样。
【具体实施方式】
下面结合具体实施方式对本发明进行详细说明。
本发明公开了一种金相试样的冷加工制样方法，根据待制备试样的形状及大小，使用软性材料制作简易模具，软质材料可以为纸质、PVC管等，另外，模具本身必须要保证形状便于手持或夹持，以方便后续检测过程。
将待制备试样放置于模具中央，将粉末状牙托粉缓慢倒入模具，使其完全遮住样品，并充满模腔，模腔的高度为1-1.5cm。粉末状牙托粉一般为甲基丙烯酸甲酯，呈细小珠状，且其粒度≥80目。
倒入牙托水，使其完全渗透牙托粉，粉末状牙托粉和牙托水的粉液比为5：3，等待其自然凝固，牙托粉和牙托水的调和物完全调和，牙托水进一步挥发，形成坚硬体，一般持续时间10～30min，凝固后得到加工后金相试样。凝固后试样即可进行金相试样的研磨、抛光、腐蚀等后续制备工作。
本发明还公开了一种实用上述方法制得的金相试样的重复利用方法，通过有机溶剂将制备好的金相试样溶解，即使用丙酮溶液对试样进行浸泡，牙托粉自然溶解，最终得到金相试样，可继续利用。

Claims (7)

1.一种金相试样的冷加工制样方法，其特征在于，根据待制备金相试样的形状及大小，使用软性材料制作简易模具，将所述待制备试样放置于模具中央，将粉末状牙托粉倒入模具，并充满模腔，倒入牙托水，使其自然凝固，凝固后得到加工后金相试样。
2.如权利要求1所述的一种金相试样的冷加工制样方法，其特征在于，所述粉末状牙托粉为甲基丙烯酸甲酯，且其粒度≥80目。
3.如权利要求1或2所述的一种金相试样的冷加工制样方法，其特征在于，所述粉末状牙托粉和牙托水的粉液比为5：3。
4.如权利要求1或2所述的一种金相试样的冷加工制样方法，其特征在于，所述模腔的高度为1-1.5cm。
5.如权利要求1或2所述的一种金相试样的冷加工制样方法，其特征在于，所述自然凝固时间为10-30min。
6.如权利要求1-5任一项制得的金相试样的重复利用方法，其特征在于，通过有机溶剂将加工后的金相试样溶解，得到金相试样。
7.如权利要求6所述的金相试样的重复利用方法，其特征在于，所述有机溶剂为丙酮溶液。
CN201711365549.0A 2017-12-18 2017-12-18 一种金相试样的冷加工制样方法 Pending CN108168970A (zh)