CN108147726A - A kind of water-repellent paint and preparation method thereof - Google Patents
A kind of water-repellent paint and preparation method thereof Download PDFInfo
- Publication number
- CN108147726A CN108147726A CN201711499271.6A CN201711499271A CN108147726A CN 108147726 A CN108147726 A CN 108147726A CN 201711499271 A CN201711499271 A CN 201711499271A CN 108147726 A CN108147726 A CN 108147726A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- repellent paint
- powder
- slurry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of water-repellent paints and preparation method thereof, are related to paint field.A kind of water-repellent paint, including powder and slurry, powder is counted in parts by weight including 0.1 0.5 parts of 80 120 parts of cement, 30 70 parts of quartz sand, 80 120 parts of coarse whiting and cellulose；Slurry is counted in parts by weight including 20 30 parts of 100 150 parts of acrylic emulsion and water.A kind of preparation method of water-repellent paint, is uniformly mixed including above-mentioned powder and slurry.The water-repellent paint has preferable tensile strength and excellent elongation at break, good water-proof effect.
Description
Technical field
The present invention relates to paint field, in particular to a kind of water-repellent paint and preparation method thereof.
Background technology
Water-proof acrylic acid paint be using pure acrylic acid polymer emulsion as base-material, prepared by adding in other additives single group
Part water-emulsifying type waterproof coatings.The waterproofing membrane formed after water-repellent paint is cured has certain extensibility, elastoplasticity, cracking resistance
Property, impermeability and weatherability, waterproof can be played, anti-blend protective effect.Water-repellent paint has good thermal adaptability, operation letter
Just, for ease of maintenaince with maintenance.But the tensile strength of existing water-repellent paint is weak, is easily broken off, and causes waterproof effect poor.
Invention content
The purpose of the present invention is to provide a kind of water-repellent paints, are stretched with preferable tensile strength and excellent fracture
Long rate, good water-proof effect.
Another object of the present invention is to provide a kind of preparation method of above-mentioned water-repellent paint, preparation method is simple, more
Being conducive to the homogeneity of water-repellent paint, water-repellent paint obtained has preferable tensile strength and excellent elongation at break,
Its good water-proof effect.
What the embodiment of the present invention was realized in：
A kind of water-repellent paint, including powder and slurry, powder is counted in parts by weight including 80-120 parts of cement, quartz sand
0.1-0.5 parts of 30-70 parts, 80-120 parts of coarse whiting and cellulose；Slurry is counted in parts by weight including 100-150 parts of acrylic emulsion
With 20-30 parts of water.
Optionally, the one kind of above-mentioned acrylic emulsion in acrylate and vinyl acetate emulsion, styrene-acrylic emulsion, pure-acrylic emulsion, silicone acrylic emulsion
It is or a variety of.
Optionally, the model RS-300S of above-mentioned acrylic emulsion.
Optionally, above-mentioned powder is counted in parts by weight further includes 0.1-0.5 parts of the first antifoaming agent, it is preferable that the first defoaming
The model of agent is one or more in antifoaming agent KS603, antifoaming agent SE47, antifoaming agent A-10 and antifoaming agent P803.
Optionally, above-mentioned powder is counted in parts by weight further includes 0.5-1 parts of water-reducing agent, and the model of water-reducing agent is delayed selected from JCBH
Coagulate any one in high efficiency water reducing agent, powder polycarboxylic acids water reducing agent and water-reducing agent F10.
Optionally, above-mentioned slurry further includes 0.5-1 parts of the second antifoaming agent in parts by weight, it is preferable that the second defoaming
The model NXZ that agent is selected from.
Optionally, above-mentioned slurry further includes 0.1-0.5 parts of fungicide in parts by weight, it is preferable that the type of fungicide
Number be LXE.
Optionally, above-mentioned cellulose is selected from sodium carboxymethylcellulose, hydroxyethyl cellulose, carboxymethyl cellulose and hydroxypropyl
One kind in ylmethyl cellulose.
A kind of preparation method of water-repellent paint, including powder and slurry are uniformly mixed, wherein, powder is in parts by weight
Meter includes 0.1-0.5 parts of 80-120 parts of cement, 30-70 parts of quartz sand, 80-120 parts of coarse whiting and cellulose；Slurry is in parts by weight
Meter includes 20-30 parts of 100-150 parts of acrylic emulsion and water.
Optionally, it is above-mentioned by powder and slurry be uniformly mixed including：60-80 DEG C is first heated water to, cellulose is added in, stirs
After mixing dissolving, it is cooled to room temperature according to the cooling velocity stirring of 1-2 DEG C/min, is subsequently added into acrylic emulsion, after stirring evenly,
Cement and quartz sand are sequentially added, stirs 10-20min, then adds in coarse whiting, stirs 10-20min.
The advantageous effect of the embodiment of the present invention for example including：
Water-repellent paint provided in this embodiment, by regarding cement, quartz sand, coarse whiting and cellulose as powder, with third
The slurries such as olefin(e) acid lotion and water be uniformly mixed it is obtained, quartz sand can effectively be promoted water-repellent paint obtained tensile strength and
Elongation at break, coarse whiting are conducive to adjust the viscosity and rheological property of water-repellent paint, and cellulose is conducive to promote waterproof material
Cementability, while the crack mixed between the component that can be filled up in quartz sand and coarse whiting, so as to keep waterproof material surface equal
One, and then be conducive to be promoted the waterproof effect of the water-repellent paint.
The preparation method of water-repellent paint provided by the invention, preparation method is simple, is more advantageous to the uniform of water-repellent paint
Property, water-repellent paint obtained has preferable tensile strength and excellent elongation at break, good water-proof effect.
Specific embodiment
Embodiment of the present invention is described in detail below in conjunction with embodiment, but those skilled in the art will
Understand, the following example is merely to illustrate the present invention, and is not construed as limiting the scope of the invention.It is not specified in embodiment specific
Condition person, the condition suggested according to normal condition or manufacturer carry out.Reagents or instruments used without specified manufacturer is
The conventional products that can be obtained by commercially available purchase.
Water-repellent paint of the embodiment of the present invention and preparation method thereof is specifically described below.
A kind of water-repellent paint, including powder and slurry.Next emphasis is illustrated to the composition and proportioning of powder and slurry.
Powder is counted in parts by weight including 80-120 parts of cement, 30-70 parts of quartz sand, 80-120 parts of coarse whiting and cellulose
0.1-0.5 parts.
Cement belongs to powdery hydraulicity inorganic coagulation material, add water stir after into slurry, can harden in air or
It is preferably hardened in water, and can the materials such as quartz sand, coarse whiting and cellulose are cemented together securely.
Quartz sand is quartz through the broken quartz particles being process.Quartz is a kind of nonmetallic mineral, is one
Hard, wear-resisting, stable chemical performance the silicate mineral of kind, main mineral constituent is SiO2.Quartz sand in it due to dividing
Subchain structure, crystal shape and lattice variations rule, the high temperature resistant made it have, coefficient of thermal expansion are small, high-insulation, corrosion resistant
Erosion, piezoelectric effect, resonance effect and its unique optical characteristics, in the present embodiment, using quartz sand as one kind in raw material,
The tensile strength and elongation at break of water-repellent paint obtained can be effectively promoted, and then is conducive to promote the water-repellent paint
Waterproof effect.The grain size of quartz sand used in the present embodiment is 80-120 mesh, the quartz sand uniform and smooth in the particle size range,
Water-repellent paint obtained is evenly.
Coarse whiting is exactly calcite in powder, is the abbreviation of powdered whiting, is by natural carbonate mineral such as calcite, Dali
Stone, lime stone are ground.It is common powdery inorganic filler, has that chemical purity is high, inertia is big, is not easy to chemically react, heat
Stability is good, will not be decomposed below 400 DEG C, whiteness is high, oil absorbency is low, index of refraction is low, matter is soft, it is dry, without the crystallization water, firmly
The advantages that spending small low wearing valve, nontoxic, tasteless, odorless, good dispersion.In the present embodiment, add in coarse whiting and be conducive to adjust waterproof
The viscosity and rheological property of coating, while heat resistance, wearability, anti-flammability, whiteness, glossiness for improving coating etc., and again
Calcium also is able to increase the volume of water-repellent paint, and then reduces production cost.The grain size of coarse whiting used in the present embodiment is 300-
360 mesh, preferably 320-340 mesh, more preferably 325 mesh.
Cellulose can also be sodium carboxymethylcellulose, hydroxyethyl cellulose, carboxymethyl cellulose and hydroxypropyl methyl
One kind in cellulose, cellulose are conducive to be promoted the cementability of waterproof material, while can fill up the component in waterproof material
Between the crack that mixes, so as to keep waterproof material uniform surface.Specifically, the cellulose in the present embodiment is preferably hydroxypropyl
Methylcellulose, the model 100000S of the hydroxypropyl methyl cellulose, the hydroxypropyl methyl cellulose of the model have compared with
Good water-retaining property, lubricity and film forming, while it can effectively keep the shape invariance of water-repellent paint with viscoelastic property.
Hydroxypropyl methyl cellulose can be as the water-retaining agent of cement mortar, while can also be by cement, quartz sand and coarse whiting
Fully bonding, becomes entirety, and can improve the smear of waterproof material and extend operable time.Add in hydroxypropyl
Methylcellulose can reduce coefficient of friction and improve the lubricity of water-repellent paint.
Further, powder is counted in parts by weight further includes 0.1-0.5 parts of the first antifoaming agent.First antifoaming agent can reduce
The surface tension of water-repellent paint inhibits foam to generate or eliminate and has generated foam.Preferably, the model of the first antifoaming agent is selected from and disappears
It is one or more in infusion KS603, antifoaming agent SE47, antifoaming agent A-10 and antifoaming agent P803.
Further, powder is counted in parts by weight further includes 0.5-1 parts of water-reducing agent, and water-reducing agent is a kind of in maintenance concrete
Under conditions of the slump is basically unchanged, the concrete admixture of mixing water amount can be reduced.In the present embodiment, by adding in diminishing
Agent is conducive to dispersed material, reduces unit consumption of water, improves the mobility of water-repellent paint.Preferably in the present embodiment, water-reducing agent
Any one in JCBH efficient retarding and water reducing agents, powder polycarboxylic acids water reducing agent and water-reducing agent F10 of model.More specifically
For, in the present embodiment, the model water-reducing agent F10 of water-reducing agent.The water-reducing agent of the model has high-performance and good dispersion.F10 is one kind by melamine type sulfonic acid polycondensates powder, mobility made of drying process with atomizing
It is splendid with application property, plasticising and diminishing particularly suitable for cement base and gypsum base power-product.It is strong that product early stage can be improved
Degree, while ultimate strength, isolation stability are improved, accelerate cure applications, the same cement of energy, quartz sand, coarse whiting and cellulose are compatible,
More preferably, quality is more excellent for the water-repellent paint uniformity obtained.
Slurry is counted in parts by weight including 20-30 parts of 100-150 parts of acrylic emulsion and water
Acrylic emulsion is one or more in acrylate and vinyl acetate emulsion, styrene-acrylic emulsion, pure-acrylic emulsion, silicone acrylic emulsion.Specifically
For, the model RS-300S of acrylic emulsion.
RS-300S is a kind of soft, self-cross linking type acrylic emulsion, and film has fabulous waterproof alkaline resistance properties, with
Cement and powder have good compatibility, and with preferable resilience, elongation and toughness.Acrylic emulsion and cement and
Powder has good compatibility；There are fabulous resilience, elongation and tensile strength；Outstanding alkali resistance and weatherability.
Further, slurry further includes 0.5-1 parts of the second antifoaming agent in parts by weight, and the second antifoaming agent can reduce
The surface tension of water-repellent paint inhibits foam to generate or eliminate and has generated foam.Preferably, the model that the second antifoaming agent is selected from
NXZ。
Further, slurry further includes 0.1-0.5 parts of fungicide in parts by weight, and fungicide can effectively control anti-
Microorganism in water paint, and then extend shelf-life and the service life of water-repellent paint.Preferably, fungicide in the present embodiment
Model LXE.
LXE is a kind of efficient, less toxic fungicide developed by Rhom and Hass, suitable for emulsion paint, macromolecule
Polymer emulsion, graining paste and all kinds of water paints；Also can be used for inhibit bacteria with fungi production and memory print ink and
Growth in other aqueous organic products.A large amount of experiment and practical application prove that LXE has acrylic emulsion fabulous sterilization
Anti-corrosion function, and have fabulous compatibility with the organic and inorganic matter ingredient of acrylic emulsion.The primary chemical of LXE into
Part：5-Chloro-2-methyl-4-isothiazolin-3-one 1.15% and 2-methyl-4-isothiazolin-3-one 0.35%.
The present embodiment additionally provides a kind of preparation method of water-repellent paint, including powder and slurry are uniformly mixed,
In, powder is counted in parts by weight including 80-120 parts of cement, 30-70 parts of quartz sand, 80-120 parts of coarse whiting and cellulose 0.1-0.5
Part；Slurry is counted in parts by weight including 20-30 parts of 100-150 parts of acrylic emulsion and water.
Specifically, it first heats water to 60-80 DEG C, adds in cellulose, after stirring and dissolving, according to the cold of 1-2 DEG C/min
But speed stirring is cooled to room temperature, and is subsequently added into acrylic emulsion, after stirring evenly, is sequentially added cement and quartz sand, is stirred
Then 10-20min adds in coarse whiting, stir 10-20min.
When further including the first antifoaming agent and water-reducing agent in powder, the second antifoaming agent and fungicide being further included in slurry, press
It is mixed according to following steps：
It first heats water to 60-80 DEG C, adds in cellulose, after stirring and dissolving, stirred according to the cooling velocity of 1-2 DEG C/min
It is cooled to room temperature, is subsequently added into acrylic emulsion, after stirring evenly, add in the first antifoaming agent, stir 3-5min, then add successively
Enter cement and quartz sand, stir 10-20min, then add in the second antifoaming agent, be stirred for 3-5min, be subsequently added into coarse whiting, stir
10-20min is eventually adding water-reducing agent and fungicide, stirs evenly.
Water-repellent paint of the present invention and preparation method thereof is further illustrated with reference to embodiments.
Embodiment 1
A kind of water-repellent paint is present embodiments provided, raw material includes powder and slurry.Powder, which is pressed, includes cement 80kg, stone
Sand 30kg, coarse whiting 80kg and sodium carboxymethylcellulose 0.1kg；Slurry includes acrylate and vinyl acetate emulsion 100kg and water 20kg.
Preparation method is as follows：It first heats water to 60 DEG C, adds in sodium carboxymethylcellulose, after stirring and dissolving, according to 1
DEG C/stirring of the cooling velocity of min is cooled to room temperature, acrylate and vinyl acetate emulsion is subsequently added into, after stirring evenly, sequentially adds cement and quartz
Sand stirs 10min, then adds in coarse whiting, stirs 10min.
Embodiment 2
A kind of water-repellent paint is present embodiments provided, raw material includes powder and slurry.Powder by include cement 120kg,
Quartz sand 70kg, coarse whiting 120kg, hydroxyethyl cellulose 0.5kg and 0.5kg antifoaming agent KS603；Slurry includes RS-300S third
Olefin(e) acid lotion 150kg and water 30kg.
Preparation method is as follows：First heat water to 80 DEG C, add in hydroxyethyl cellulose, after stirring and dissolving, according to 2 DEG C/
The cooling velocity stirring of min is cooled to room temperature, and is subsequently added into RS-300S acrylic emulsions, after stirring evenly, adds in antifoaming agent
KS603 stirs 5min, sequentially adds cement and quartz sand, stirs 20min, then adds in coarse whiting, stirs 20min.
Embodiment 3
A kind of water-repellent paint is present embodiments provided, raw material includes powder and slurry.Powder by include 100 parts of cement,
0.6 part of 40 parts of quartz sand, 10 parts of coarse whiting, 0.2 part of carboxymethyl cellulose and JCBH efficient retarding and water reducing agents；Slurry includes RS-
23 parts of 120 parts of 300S acrylic emulsions and water.
Preparation method is as follows：It first heats water to 60-80 DEG C, adds in carboxymethyl cellulose, after stirring and dissolving, according to 1-
The cooling velocity stirring of 2 DEG C/min is cooled to room temperature, and is subsequently added into RS-300S acrylic emulsions, after stirring evenly, is sequentially added
Cement and quartz sand stir 10-20min, then add in coarse whiting, stir 10-20min, are eventually adding JCBH retardation setting high efficiency diminishings
Agent stirs evenly.
Embodiment 4
A kind of water-repellent paint is present embodiments provided, raw material includes powder and slurry.Powder, which is pressed, includes 90 parts of cement, stone
0.2 part of 60 parts of sand, 90 parts of coarse whiting and hydroxypropyl methyl cellulose；Slurry includes 110 parts of silicone acrylic emulsion, 24 parts of water and model
1 part of the second antifoaming agent of NXZ.
Preparation method is as follows：It first heats water to 62 DEG C, adds in hydroxypropyl methyl cellulose, after stirring and dissolving, according to
The cooling velocity stirring of 1.5 DEG C/min is cooled to room temperature, and is subsequently added into silicone acrylic emulsion, after stirring evenly, is sequentially added cement and stone
Sand stirs 13min, then adds in the second antifoaming agent of model NXZ, is stirred for 4min, then adds in coarse whiting, stirs 14min.
Embodiment 5
A kind of water-repellent paint is present embodiments provided, raw material includes powder and slurry.Powder, which is pressed, includes 95 parts of cement, stone
0.7 part of 46 parts of sand, 95 parts of coarse whiting, 0.3 part of hydroxypropyl methyl cellulose and powder polycarboxylic acids water reducing agent；Slurry includes acrylic acid
0.4 part of the fungicide of 140 parts of lotion, 26 parts of water and model LXE.
Preparation method is as follows：First heat water to 60-80 DEG C, add in cellulose, after stirring and dissolving, according to 1-2 DEG C/
The cooling velocity stirring of min is cooled to room temperature, and is subsequently added into acrylic emulsion, after stirring evenly, is sequentially added cement and quartz
Sand stirs 10-20min, then adds in coarse whiting, stirs 10-20min, is eventually adding powder polycarboxylic acids water reducing agent and model LXE
Fungicide, stir evenly.
Embodiment 6
A kind of water-repellent paint is present embodiments provided, raw material includes powder and slurry.Powder by include 100 parts of cement,
50 parts of quartz sand, 100 parts of coarse whiting, 0.25 part of hydroxypropyl methyl cellulose, 0.25 part of antifoaming agent P803 and 0.75 part of diminishing
Agent F10；Slurry count in parts by weight including 127.5 parts of acrylic emulsion, 22.5 parts of water, model NXZ the second antifoaming agent
0.75 part and model LXE of 0.225 part of fungicide.
Preparation method is as follows：It first heats water to 70 DEG C, adds in hydroxypropyl methyl cellulose, after stirring and dissolving, according to
The cooling velocity stirring of 1-2 DEG C/min is cooled to room temperature, and is subsequently added into acrylic emulsion, after stirring evenly, adds in antifoaming agent
P803 stirs 3-5min, then sequentially adds cement and quartz sand, stirs 10-20min, then adds in the second of model NXZ
Antifoaming agent is stirred for 3-5min, is subsequently added into coarse whiting, stirs 10-20min, is eventually adding water-reducing agent F10's and model LXE
Fungicide stirs evenly.
Embodiment 6 is detected in national chemical building material inspection center in the present embodiment, detection environment is：Room
Temperature：23 ± 2 DEG C, 50 ± 5%RH of relative humidity, examining report please refers to table 1.
1. examining report of table
In conclusion water-repellent paint provided in this embodiment, by the way that cement, quartz sand, coarse whiting and cellulose are used as
Powder, is uniformly mixed obtained with slurries such as acrylic emulsion and water, and quartz sand can effectively promote the drawing of water-repellent paint obtained
Intensity and elongation at break are stretched, coarse whiting is conducive to adjust the viscosity and rheological property of water-repellent paint, and cellulose is conducive to be promoted
The cementability of waterproof material, while the crack mixed between the component that can be filled up in quartz sand and coarse whiting, so as to keep waterproof
Material surface is uniform, and then is conducive to be promoted the waterproof effect of the water-repellent paint.
The preparation method of water-repellent paint provided by the invention, preparation method is simple, is more advantageous to the uniform of water-repellent paint
Property, water-repellent paint obtained has preferable tensile strength and excellent elongation at break, good water-proof effect.
It these are only the preferred embodiment of the present invention, be not intended to restrict the invention, for those skilled in the art
For member, the invention may be variously modified and varied.Any modification for all within the spirits and principles of the present invention, being made,
Equivalent replacement, improvement etc., should all be included in the protection scope of the present invention.
Claims (10)
1. a kind of water-repellent paint, which is characterized in that it includes powder and slurry, and the powder is counted in parts by weight including cement
0.1-0.5 parts of 80-120 parts, 30-70 parts of quartz sand, 80-120 parts of coarse whiting and cellulose；The slurry count in parts by weight including
20-30 parts of 100-150 parts of acrylic emulsion and water.
2. water-repellent paint according to claim 1, which is characterized in that the acrylic emulsion is selected from acrylate and vinyl acetate emulsion, phenylpropyl alcohol
It is one or more in lotion, pure-acrylic emulsion, silicone acrylic emulsion.
3. water-repellent paint according to claim 1, which is characterized in that the model RS-300S of the acrylic emulsion.
4. water-repellent paint according to claim 1, which is characterized in that the powder is counted in parts by weight to be further included first and disappear
0.1-0.5 parts of infusion,
Preferably, the model of first antifoaming agent is selected from antifoaming agent KS603, antifoaming agent SE47, antifoaming agent A-10 and antifoaming agent
It is one or more in P803.
5. water-repellent paint according to claim 1, which is characterized in that the powder is counted in parts by weight further includes water-reducing agent
0.5-1 parts,
The model of the water-reducing agent is in JCBH efficient retarding and water reducing agents, powder polycarboxylic acids water reducing agent and water-reducing agent F10
Any one.
6. water-repellent paint according to claim 1, which is characterized in that the slurry further includes second in parts by weight
0.5-1 parts of antifoaming agent, it is preferable that the model NXZ that second antifoaming agent is selected from.
7. water-repellent paint according to claim 1, which is characterized in that the slurry further includes sterilization in parts by weight
0.1-0.5 parts of agent, it is preferable that the model LXE of the fungicide.
8. water-repellent paint according to claim 1, which is characterized in that the cellulose is selected from sodium carboxymethylcellulose, hydroxyl
One kind in ethyl cellulose, carboxymethyl cellulose and hydroxypropyl methyl cellulose.
9. a kind of preparation method of water-repellent paint, which is characterized in that it includes powder and slurry being uniformly mixed, wherein, it is described
Powder is counted in parts by weight including 0.1-0.5 parts of 80-120 parts of cement, 30-70 parts of quartz sand, 80-120 parts of coarse whiting and cellulose；
The slurry is counted in parts by weight including 20-30 parts of 100-150 parts of acrylic emulsion and water.
10. the preparation method of water-repellent paint according to claim 9, which is characterized in that by the powder and the slurry
It is uniformly mixed and includes：60-80 DEG C is first heated water to, adds in the cellulose, after stirring and dissolving, according to the cold of 1-2 DEG C/min
But speed stirring is cooled to room temperature, and is subsequently added into the acrylic emulsion, after stirring evenly, sequentially adds the cement and described
Quartz sand stirs 10-20min, then adds in the coarse whiting, stirs 10-20min.