CN108118349A - A kind of water base metal cleaning agent and preparation method thereof - Google Patents
A kind of water base metal cleaning agent and preparation method thereof Download PDFInfo
- Publication number
- CN108118349A CN108118349A CN201711385491.6A CN201711385491A CN108118349A CN 108118349 A CN108118349 A CN 108118349A CN 201711385491 A CN201711385491 A CN 201711385491A CN 108118349 A CN108118349 A CN 108118349A
- Authority
- CN
- China
- Prior art keywords
- parts
- sodium
- base metal
- water
- cleaning agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of water base metal cleaning agent and preparation method thereof, which is made of the raw material of following parts by weight：15 20 parts of polyacrylamide, 15 20 parts of fatty alcohol polyoxyethylene ether, 15 20 parts of lauryl glucosyl, 20 40 parts of dodecyl sodium sulfate, 10 12 parts of sodium citrate, 6 10 parts of sodium alginate, 35 parts of sodium carbonate, 35 parts of carboxymethyl cellulose, 24 parts of antifoaming agent, 80 120 parts of water；First polyacrylamide, fatty alcohol polyoxyethylene ether, lauryl glucosyl, dodecyl sodium sulfate are mixed in mass ratio with water, stirring is to being completely dissolved, then sodium citrate, sodium alginate, sodium carbonate and carboxymethyl cellulose are sequentially added in proportion under conditions of stirring, continue stirring to solution to be translucent shape, antifoaming agent is eventually adding, is stirred evenly.The scientific formula of the present invention is reasonable, and cleaning ability is strong, safety and environmental protection；It is easy to operate, it is of low cost.
Description
Technical field
The invention belongs to industry cleaning link fields, are related to a kind of metal cleaner, and in particular to a kind of water base metal cleaning agent.
Background technology
In the industrial production, either the process and assemble of part or heat treatment, plating and product preservation and packaging and open
Envelope, will clean metal surface.The quality of the pre-treatment of metal surface directly affects application or deposition material and metal
The combination power of basis material and the integrality of its coating.At present, industrial cleaning agent is broadly divided into aqueous-base cleaning according to its ingredient
Agent, semi-aqueous cleaning agent, leaning solvent.Wherein, aqueous cleaning agent has of low cost, safe and efficient, environmentally protective, raw
Many advantages, such as object degradation property is good, is widely used.Aqueous cleaning agent generally by surfactant, builder and is gone from water etc.
It compounds according to a certain percentage, main wash principle is to utilize the emulsification of surfactant, infiltration, scattered and antiredeposition
Ability is dirty to greasy dirt to clean.
Existing water base metal cleaning agent, oil removing is indifferent, and cleaning ability is weaker, and rust-preventing characteristic is not strong.
The content of the invention
The object of the present invention is to provide a kind of water base metal cleaning agents, and cleaning ability is strong, and environmental pollution is small.
To achieve the above object, a kind of water base metal cleaning agent of the invention, is made of by weight following raw material：Poly- third
15-20 parts of acrylamide, 15-20 parts of fatty alcohol polyoxyethylene ether, 15-20 parts of lauryl glucosyl, dodecyl sodium sulfate
20-40 parts, 10-12 parts of sodium citrate, 6-10 parts of sodium alginate, 3-5 parts of sodium carbonate, 3-5 parts of carboxymethyl cellulose, antifoaming agent 2-
4 parts, 80-120 parts of water.
Preferably, the water base metal cleaning agent is made of by weight following raw material：18 parts of polyacrylamide, fat
18 parts of fat alcohol polyoxyethylene ether, 18 parts of lauryl glucosyl, 36 parts of dodecyl sodium sulfate, 11 parts of sodium citrate, seaweed
Sour 8 parts of sodium, 4 parts of sodium carbonate, 4 parts of carboxymethyl cellulose, 3 parts of antifoaming agent, 100 parts of water.
Preferably, the fatty alcohol polyoxyethylene ether is AEO-7.
Preferably, the antifoaming agent is modified silicon oil.
The physical and chemical index of this cleaning agent is as follows：Appearance：Translucent liquid；PH value：7~8；Density (20 DEG C) g/ml：1.1~
1.2。
It is easy to operate it is a further object of the present invention to provide the preparation method of above-mentioned water base metal cleaning agent, it is of low cost.
To achieve the above object, the preparation method of water base metal cleaning agent of the invention, comprises the following steps：Room temperature condition
Under, polyacrylamide, fatty alcohol polyoxyethylene ether, lauryl glucosyl, dodecyl sodium sulfate and water are first pressed into quality
Than mixing, stir to being completely dissolved, then under conditions of stirring by formula rate sequentially add sodium citrate, sodium alginate,
Sodium carbonate and carboxymethyl cellulose continue stirring to solution and are translucent shape, be eventually adding antifoaming agent, stir evenly.
In the present invention, polyacrylamide, fatty alcohol polyoxyethylene ether, lauryl glucosyl belong to non-ionic surface
Activating agent, dodecyl sodium sulfate belong to anion surfactant, and four mixing have synergistic effect, can effectively remove gold
The polarity dirt of metal surface, meanwhile, the interfacial tension between greasy dirt and aqueous solution reduces, and emulsification occurs for greasy dirt and water.
In the present invention, sodium citrate, sodium alginate are organic washing-assisting detergent, and sodium carbonate is inorganic builders, are had significant
Peptizaiton, can be larger soil dispersion into the particle close to colloidal particle size, so as to improve cleaning ability；Carboxymethyl is fine
It is thickener to tie up element, for improving and increasing the viscosity of cleaning agent；Antifoaming agent can reduce surface tension, inhibit foam and generate.
Water base metal cleaning agent scientific formula provided by the invention is reasonable, and raw material materials are few and source is wide, has excellent
Ability of cleaning greasy dirt, it is low bubble property and dispersibility, it is washed after metal surface without visible oil film；Without organic solvent, nitrous
The harmful substances such as hydrochlorate, tasteless and nonirritant is not unhealthful, safety and environmental protection；It is easy to operate, it is of low cost, it is widely used.
Specific embodiment
With reference to embodiment, the invention will be further described.
Involved reagent and material, unless otherwise specified, commercially obtain in following embodiments.
Embodiment 1
A kind of water base metal cleaning agent is made of by weight following raw material：18 parts of polyacrylamide, AEO-718 parts, ten
18 parts of dialkyl group glucoside, 36 parts of dodecyl sodium sulfate, 11 parts of sodium citrate, 8 parts of sodium alginate, 4 parts of sodium carbonate, carboxylic first
4 parts of base cellulose, 3 parts of antifoaming agent, 100 parts of water.
The preparation method of above-mentioned water base metal cleaning agent, comprises the following steps：Under room temperature, first by polyacrylamide,
AEO-7, lauryl glucosyl, dodecyl sodium sulfate mix in mass ratio with water, stir to being completely dissolved, are then stirring
Sodium citrate, sodium alginate, sodium carbonate and carboxymethyl cellulose are sequentially added by formula rate under conditions of mixing, continues stirring extremely
Solution is translucent shape, is eventually adding antifoaming agent, stirs evenly.
Embodiment 2
A kind of water base metal cleaning agent is made of by weight following raw material：15 parts of polyacrylamide, AEO-715 parts, ten
15 parts of dialkyl group glucoside, 20 parts of dodecyl sodium sulfate, 10 parts of sodium citrate, 6 parts of sodium alginate, 3 parts of sodium carbonate, carboxylic first
3 parts of base cellulose, 2 parts of antifoaming agent, 80 parts of water.
Its preparation method is the same as embodiment 1.
Embodiment 3
A kind of water base metal cleaning agent is made of by weight following raw material：20 parts of polyacrylamide, AEO-720 parts, ten
20 parts of dialkyl group glucoside, 40 parts of dodecyl sodium sulfate, 12 parts of sodium citrate, 10 parts of sodium alginate, 5 parts of sodium carbonate, carboxylic
5 parts of methylcellulose, 4 parts of antifoaming agent, 120 parts of water.
Its preparation method is the same as embodiment 1.
Claims (5)
1. a kind of water base metal cleaning agent, which is characterized in that it is made of by weight following raw material：Polyacrylamide 15-20
Part, 15-20 parts of fatty alcohol polyoxyethylene ether, 15-20 parts of lauryl glucosyl, 20-40 parts of dodecyl sodium sulfate, lemon
Sour sodium 10-12 parts, 6-10 parts of sodium alginate, 3-5 parts of sodium carbonate, 3-5 parts of carboxymethyl cellulose, 2-4 parts of antifoaming agent, water 80-120
Part.
2. water base metal cleaning agent according to claim 1, which is characterized in that it is made of by weight following raw material：
18 parts of polyacrylamide, 18 parts of fatty alcohol polyoxyethylene ether, 18 parts of lauryl glucosyl, 36 parts of dodecyl sodium sulfate,
11 parts of sodium citrate, 8 parts of sodium alginate, 4 parts of sodium carbonate, 4 parts of carboxymethyl cellulose, 3 parts of antifoaming agent, 100 parts of water.
3. water base metal cleaning agent according to claim 1 or 2, which is characterized in that the fatty alcohol polyoxyethylene ether
For AEO-7.
4. water base metal cleaning agent according to claim 1 or 2, which is characterized in that the antifoaming agent is modified silicon oil.
5. the preparation method of the water base metal cleaning agent described in a kind of claim 1 or 2, which is characterized in that comprise the following steps：
Under room temperature, first by polyacrylamide, fatty alcohol polyoxyethylene ether, lauryl glucosyl, dodecyl sodium sulfate with
Water mixes in mass ratio, stirs to being completely dissolved, then sequentially adds sodium citrate, sea by formula rate under conditions of stirring
Mosanom, sodium carbonate and carboxymethyl cellulose continue stirring to solution and are translucent shape, be eventually adding antifoaming agent, stir evenly
.