CN108103810A - A kind of high-strength anti-bacterial flame-retardant fabric - Google Patents
A kind of high-strength anti-bacterial flame-retardant fabric Download PDFInfo
- Publication number
- CN108103810A CN108103810A CN201711199151.4A CN201711199151A CN108103810A CN 108103810 A CN108103810 A CN 108103810A CN 201711199151 A CN201711199151 A CN 201711199151A CN 108103810 A CN108103810 A CN 108103810A
- Authority
- CN
- China
- Prior art keywords
- retardant
- fibers
- cotton
- fire
- dyeing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of high-strength anti-bacterial flame-retardant fabric, its manufacturing method comprises the following steps:(1)Yarn constituent matches:9 ~ 48wt% polyacrylonitrile carbon fibers, 50 ~ 90wt% cotton fibers, 10 ~ 20wt% nano Ag antibacterial fibers and 1 ~ 2wt% conductive fibers(2)Spinning:Each ingredient mixture uniformity, cotton fiber use long-staple cotton, and spinning system uses SEILE textile technique;(3)Woven fabric:Using air-jet loom or rapier loom;(4)Dyeing:Using cotton long vehicle knot dyeing technology;Then carried out successively according to following flow:Singe → desizing, kiering, bleaching → mercerising → dyeing → fire-retardant → ammonia cure → oxidation → washing → dry → bake → preshrunk → test package.The fabric that the technique makes is soft, and high resilience, color can be customized according to customer requirement, and dress is comfortable, and anti-microbial property is good, and sexual valence is higher, i.e., can be used for fashionable dress again suitable for frock.
Description
Technical field
The invention belongs to the fabricating technology fields of inflaming retarding fabric, and in particular to a kind of high-strength anti-bacterial flame-retardant fabric.
Background technology
A kind of flame-retardant textile of the bicomponent fibre of skin-core structure is disclosed in Chinese patent CN1732295A, using with
The polymer of flame retardant property is as skin portion, and for thermoplastic polymer as core component, but since the feel of the fabric is harder, heat is steady
Qualitative difference, thus it is limited in very many applications.A kind of containing cellulose weaving material is disclosed in Chinese patent CN1331767A
The production method of material, due to needing to use substantial amounts of crosslinking agent in that patent, although crosslinking agent can be such that fiber has well
Mechanical strength, but crosslinking agent is poor to the pollution and environmental stability of environment, it is impossible to material be made to keep lasting mechanical property
Energy.With the continuous improvement of people's awareness of safety, to the flame retardant property of fabric there has also been corresponding requirements, particularly fabric for
Prevent, delay or terminate the effect of fire.Since general fire retardant is mostly halogen system and phosphorus system, major part all has larger
Toxicity, and need in preparation process to use formaldehyde or toluene so that organic substance residues generate health certain danger
Danger, meanwhile, fabric feeling after processing is hard, strength damage is big, and wearing comfort is low, seriously affect flame-retardant textile quality and
Using effect.
The content of the invention
The present invention provides a kind of high-strength anti-bacterial flame-retardant fabric, the fabric hand for the shortcomings of the prior art
Sense is soft, and high resilience, color can be customized according to customer requirement, and dress is comfortable, and anti-microbial property is good, and sexual valence is higher, i.e., suitable
It can be used for fashionable dress again for frock.
The purpose of the present invention is what is realized in the following manner:
The present invention provides a kind of high-strength anti-bacterial flame-retardant fabric, its manufacturing method comprises the following steps:
(1)Yarn constituent matches:9 ~ 48wt% polyacrylonitrile carbon fibers, 50 ~ 90wt% cotton fibers, 10 ~ 20wt% nanometer silver antimicrobials are fine
Peacekeeping 1 ~ 2wt% conductive fibers;
(2)Spinning:Each ingredient mixture uniformity, cotton fiber use long-staple cotton, and spinning system uses SEILE textile technique, using leading
Electric fiber be blended into other fibers together with to ensure all to contain conductive fiber on each yarn, using twine, moderate is added to twist with the fingers;
(3)Woven fabric:Using air-jet loom or rapier loom;
(4)Dyeing:Using cotton long vehicle knot dyeing technology;
(5)Then carried out successively according to following flow:Turn over cloth margin to seam → singe → desizing, kiering, bleaching → mercerising → dyeing →
→ preshrunk → test package is dried → baked in fire-retardant → ammonia cure → oxidation → washing →.
According to above-mentioned high-strength anti-bacterial flame-retardant fabric, step(1)Middle Yarn constituent proportioning:35wt% polyacrylonitrile carbon fibers,
63wt% cotton fibers, 15wt% nano Ag antibacterial fibers and 2wt% conductive fibers.
According to above-mentioned high-strength anti-bacterial flame-retardant fabric, step(5)In it is fire-retardant during fire retardant by following ingredient system
Into:It is 300~400g/l of tetramethylol chloride urea condensate, 1~3g/l of penetrating agent JFC, 10~20g/l of softening agent, anti-
Oily water repellent 40g~80g/l.
According to the preparation method of above-mentioned high-strength anti-bacterial flame-retardant fabric, step(5)In it is fire-retardant during fire retardant by
Following ingredient is made:Tetramethylol chloride urea condensate 350g/l, penetrating agent JFC 2g/l, softening agent 15g/l, oil resistant
Water repellent 50g/l.
Compared with prior art, beneficial effects of the present invention:
It is a kind of the characteristics of high-strength anti-bacterial flame-retardant fabric provided by the invention, several high-performance fibers of the process makes full use, real
Show mutual supplement with each other's advantages, the good fabric of fabric good permeability, wear-resisting, fire-retardant, antistatic, anti-microbial property successfully developed, dress
Comfortably.
Specific embodiment
Embodiment 1:
The present invention provides a kind of high-strength anti-bacterial flame-retardant fabric, its manufacturing method comprises the following steps:
(1)Yarn constituent matches:9 ~ 48wt% polyacrylonitrile carbon fibers, 50 ~ 90wt% cotton fibers, 10 ~ 20wt% nanometer silver antimicrobials are fine
Peacekeeping 1 ~ 2wt% conductive fibers;(2)Spinning:Each ingredient mixture uniformity, cotton fiber use long-staple cotton, and spinning system is using match
Network spinning process;(3)Woven fabric:Using air-jet loom or rapier loom;(4)Dyeing:Using cotton long vehicle knot dyeing technology;(5)Then
It is carried out successively according to following flow:Singe → desizing, kiering, bleaching → mercerising → dyeing → fire-retardant → ammonia cure → oxidation → washing
→ drying → bakes → preshrunk → test package.
Step(5)In it is fire-retardant during fire retardant be made of following ingredient:Tetramethylol chloride urea condensate
300~400g/l, 1~3g/l of penetrating agent JFC, 10~20g/l of softening agent, oil resistant water repellent 40g~80g/l.
Embodiment 2:
Part same as Example 1 is no longer repeated, the difference is that:Step(1)Middle Yarn constituent proportioning:35wt% polypropylene
Nitrile carbon fiber, 63wt% cotton fibers, 15wt% nano Ag antibacterial fibers and 2wt% conductive fibers.
Embodiment 3:
Part same as Example 1 is no longer repeated, the difference is that:Step(5)In it is fire-retardant during fire retardant by such as
Lower ingredient is made:Tetramethylol chloride urea condensate 350g/l, penetrating agent JFC 2g/l, softening agent 15g/l, oil resistant are refused
Aqua 50g/l.
Above-described is only the preferred embodiment of the present invention, it is noted that for those skilled in the art,
Under the premise of general idea of the present invention is not departed from, several changes and improvements can also be made, these should also be considered as the present invention's
Protection domain.
Claims (4)
1. a kind of high-strength anti-bacterial flame-retardant fabric, it is characterised in that its manufacturing method comprises the following steps:
(1)Yarn constituent matches:9 ~ 48wt% polyacrylonitrile carbon fibers, 50 ~ 90wt% cotton fibers, 10 ~ 20wt% nanometer silver antimicrobials are fine
Peacekeeping 1 ~ 2wt% conductive fibers;
(2)Spinning:Each ingredient mixture uniformity, cotton fiber use long-staple cotton, and spinning system uses SEILE textile technique;
(3)Woven fabric:Using air-jet loom or rapier loom;
(4)Dyeing:Using cotton long vehicle knot dyeing technology;
(5)Then carried out successively according to following flow:Singe → desizing, kiering, bleaching → mercerising → dyeing → fire-retardant → ammonia cure
→ preshrunk → test package is dried → baked in → oxidation → washing →.
2. high-strength anti-bacterial flame-retardant fabric according to claim 1, it is characterised in that:Step(1)Middle Yarn constituent proportioning:
35wt% polyacrylonitrile carbon fibers, 63wt% cotton fibers, 15wt% nano Ag antibacterial fibers and 2wt% conductive fibers.
3. high-strength anti-bacterial flame-retardant fabric according to claim 1, it is characterised in that:Step(5)In it is fire-retardant during
Fire retardant is made of following ingredient:300~400g/l of tetramethylol chloride urea condensate, 1~3g/l of penetrating agent JFC,
Oil resistant water repellent 40g~80g/l.
4. the preparation method of high-strength anti-bacterial flame-retardant fabric according to claim 3, it is characterised in that:Step(5)In it is fire-retardant
Fire retardant in the process is made of following ingredient:Tetramethylol chloride urea condensate 350g/l, penetrating agent JFC 2g/
L, softening agent 15g/l, oil resistant water repellent 50g/l.