CN108099338A - A kind of consolidated floor manufacturing method - Google Patents
A kind of consolidated floor manufacturing method Download PDFInfo
- Publication number
- CN108099338A CN108099338A CN201711366427.3A CN201711366427A CN108099338A CN 108099338 A CN108099338 A CN 108099338A CN 201711366427 A CN201711366427 A CN 201711366427A CN 108099338 A CN108099338 A CN 108099338A
- Authority
- CN
- China
- Prior art keywords
- paper
- base
- abrasion
- balance
- proof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of consolidated floor manufacturing methods, are related to floor field.The present invention comprises the following steps：Step A, abrasion-proof paper, facing paper and balance paper are subjected to impregnation；Step B, abrasion-proof paper, facing paper and the balance paper after dipping are subjected to drying and processing；Step C, handled the upper and lower surface of base to improve the surface roughness on the upper and lower surface of base；Step D, apply glue on the upper and lower surface of base；Step E, abrasion-proof paper, facing paper, base and balance paper are overlapped from top to bottom and placed；Step F, by abrasion-proof paper, facing paper, base and balance paper using it is cold into it is cold go out hot pressing mode press.The deformation and each layer occurred in the fabrication process as the floor of base using PVC stone-plastic plates or WPC plates it is an object of the invention to overcome the problems, such as existing combines unstable, provides and a kind of overcome thes problems, such as that ground board finished product deformation and each layer combine insecure consolidated floor manufacturing method.
Description
Technical field
The present invention relates to a kind of floor, more specifically to a kind of consolidated floor manufacturing method.
Background technology
In recent years, indoor decoration is largely using solid wooden floor board, composite floor board, impregnated-paper laminated wood floor (consolidated floor)
Etc. making floor decorative material.Solid wooden floor board need to make raw material using a large amount of heavy caliber logs, it is however generally that, the timber of solid wooden floor board
Utilization rate is only 30%~40%, need to select decades even upper century-old high-quality solid wood, raw material selection standard height is, it is necessary to disappear
Consume the substantial amounts of forest reserves.Thus, there are the problem of high-quality timber is in short supply, timber utilization rate is not high.And consume substantial amounts of forest
Resource can cause the destruction of ecological environment, this problem also has attracted increasing attention.And on using, solid wooden floor board is also
There are yielding, easy harmomegathus, not wear-resisting and the defects of involve great expense, it is more difficult to the problems such as solving waterproof, moisture-proof, Anti-moth-eating, therefore
Affect using effect and service life.
With the continuous improvement of the performance requirements such as people are beautiful to floor, practical and durable wear-resistant, production intensity is high, size
Stability is strong, wearability is high, service life is long and both artistic and practical composite floor board is increasingly becoming the trend that floor industry develops.
Have a large amount of different types of composite floor boards in the prior art to disclose, such as patent publication No.：CN
101173553A, publication date：On May 7th, 2008, invention and created name are：Heat-proof composite floor board, this application discloses one kind
Heat-proof composite floor board, it is desirable to provide it is big that one kind adapts to difference variation, is laid on above caliduct, not easy to crack resistance to of dash board
Heat composite floor.It includes dash board and substrate, and gluing has one or more layers paper between dash board and substrate.
For another example patent publication No.：CN 101761212A, publication date：On June 30th, 2010, invention and created name are：Modeling wood
Composite floor board, this application discloses a kind of plastic-wood composite floor, including PVC floor surface layer and the wooden base material of modeling, PVC floor surface layer
It is combined with the wooden base material of modeling by environment-friendly waterproof gluing.The PVC floor of various colors and good waterproof is selected to be used as surface layer
Family can be selected the pattern of indoor floor by personal like.Simultaneously using modeling wood base board, with adhesive adherence under PVC floor surface layer
Side, compared with traditional PVC floor, mats formation more convenient, does not have soldered after assembly is complete, and it is at low cost to mat formation.
But dash board and substrate are bonded in one by composite floor board of the prior art essentially by the mode of a hot pressing
Rise, and it is adhesion-molded after floor often occur deforming and each layer combine unstable problem, this be always PVC stones modeling ground
Technological deficiency of plate or the WPC ground in board manufacturing process.In conclusion how to overcome existing using PVC stone-plastic plates or WPC plate conducts
Deformation that the floor of base occurs in the fabrication process and each layer combine unstable problem, are urgent need to resolve in the prior art
The technical issues of.
The content of the invention
1. technical problems to be solved by the inivention
It is an object of the invention to overcome it is existing using PVC stone-plastic plates or WPC plates as base floor in manufacturing process
The middle deformation occurred and each layer combine unstable problem, provide one kind and ground board finished product deformation and each layer is overcome to combine not
The consolidated floor manufacturing method of secured problem.
2. technical solution
In order to achieve the above objectives, technical solution provided by the invention is：
The consolidated floor manufacturing method of the present invention, comprises the following steps：
Step A, abrasion-proof paper, facing paper and balance paper are subjected to impregnation；
Step B, abrasion-proof paper, facing paper and the balance paper after dipping are subjected to drying and processing；
Step C, handled the upper and lower surface of base to improve the surface roughness on the upper and lower surface of base；
Step D, apply glue on the upper and lower surface of base；
Step E, abrasion-proof paper, facing paper, base and balance paper are overlapped from top to bottom and placed；
Step F, by abrasion-proof paper, facing paper, base and balance paper using it is cold into it is cold go out hot pressing mode press.
As further improvement of the present invention, in step A, abrasion-proof paper, facing paper and balance paper are subjected to leaching trimerization
Cyanamide processing or leaching phenolic resin processing.
As further improvement of the present invention, the base is PVC stone-plastic plates or WPC plates.
As further improvement of the present invention, in step C, the upper and lower surface of base is carried out at grinding process or corona
Reason or wharf's pavement quality.
As further improvement of the present invention, in step C, processing is carried out to the upper and lower surface of base until removal base
The wax coat on upper and lower surface.
As further improvement of the present invention, step F include it is following step by step：
F1 step by step：Abrasion-proof paper, facing paper, base and balance paper are put into hot press；
F2 step by step：Using the heating platen in the first design temperature to abrasion-proof paper, facing paper, base and balance paper into
Row pressing；
F3 step by step：The temperature of heating platen is gradually increased to the second design temperature, and one is maintained in the second design temperature
It fixes time；
F4 step by step：The temperature of heating platen is gradually decreased into the 3rd design temperature；
F5 step by step：Floor after pressing is taken out from hot press.
As further improvement of the present invention, in step F, second design temperature is 30-160 DEG C, the pressure of pressing
Power is 5-205MPa, and the time of pressing is 10-60min.
As further improvement of the present invention, first design temperature and the 3rd design temperature are respectively less than critical
Value, the critical value=+ 10 DEG C of environment temperature.
As further improvement of the present invention, step A, the process of step B and step C, the process of step D are without successively suitable
Sequence limits.
3. advantageous effect
Using technical solution provided by the invention, compared with prior art, there is following remarkable result：
(1) present invention in, abrasion-proof paper, facing paper and balance paper are impregnated first, drying and processing, at the same using as
The PVC stone-plastic plates of base material or the upper and lower surface of WPC plates are handled, to improve the surface roughness on the upper and lower surface of base, and
It applies glue on the upper and lower surface of base, then abrasion-proof paper, facing paper, base and balance paper is overlapped from top to bottom and placed, most
Afterwards using it is cold into it is cold go out hot pressing mode pressed, crucial improvement is：By base's independent coating adhesive in upper and lower surface
Hydraulic art with it is cold into it is cold go out heat pressing process be combined, find by production inspection, gone out using process above final production
Floor, effectively overcome and serious and each layer deformed after the hot pressing of floor with reference to unstable problem, significantly improve product matter
Amount improves the competitiveness of product.
(2) in the present invention, the upper and lower surface of base is individually coated glue can be effectively increased gluing between base and other layers
Close effect, but only so do not enough, it is also necessary to it is cold into it is cold go out heat pressing process correspondence be engaged, it is cold into it is cold go out hot pressing work
In skill, abrasion-proof paper, facing paper, base and balance paper experienced the hot pressing temperature of room temperature, heating, heat preservation, cooling, room temperature, match somebody with somebody
Close the pressing pressure of specific settings and pressing total time in entire hot pressing so that after the completion of hot pressing, the upper and lower surface of base
The glue individually coated gives full play to adhesive effect, improves the firmness combined between each layer, while avoids existing hot pressing
The floor deformation problem occurred after technique.
(3) in the present invention, handled using the base of PVC stone-plastic plates or WPC plates, the processing of leaching melamine or leaching phenolic resin
Abrasion-proof paper, facing paper and during balance paper production floor, it is corresponding to coordinate the independent coating technique in the upper and lower surface of base and spy
Determine step, parameter it is cold into it is cold go out heat pressing process, solve after being produced using existing process existing floor deformation it is serious and
Each layer combines unstable problem, is one kind to its manufacturing method of floor of particular substrate material and specific impregnated material composition
It is specially modified.
Description of the drawings
It in order to illustrate the technical solution of the embodiments of the present invention more clearly, below will be to needed in the embodiment attached
Figure is briefly described, it should be understood that the following drawings illustrates only certain embodiments of the present invention, therefore is not construed as pair
The restriction of scope, for those of ordinary skill in the art, without creative efforts, can also be according to this
A little attached drawings obtain other relevant attached drawings.
Fig. 1 is the flow chart of the consolidated floor manufacturing method of embodiment 1-4.
Specific embodiment
To make the purpose, technical scheme and advantage of the embodiment of the present invention clearer, below in conjunction with the embodiment of the present invention
In attached drawing, the technical solution in the embodiment of the present invention is clearly and completely described, it is clear that described embodiment is
Part of the embodiment of the present invention, instead of all the embodiments.Therefore, the embodiment of the present invention to providing in the accompanying drawings below
Detailed description be not intended to limit the scope of claimed invention, but be merely representative of the present invention selected embodiment.
Based on the embodiments of the present invention, what those of ordinary skill in the art were obtained without creative efforts is all
Other embodiment belongs to the scope of protection of the invention.
To further appreciate that present disclosure, the present invention is described in detail in conjunction with the accompanying drawings and embodiments.
Embodiment 1
With reference to Fig. 1, the consolidated floor manufacturing method of the present embodiment comprises the following steps：
Step A, by abrasion-proof paper, facing paper and balance paper carry out impregnation, specifically, by abrasion-proof paper, facing paper with
And balance paper carries out the processing of leaching melamine or leaching phenolic resin processing；
Step B, abrasion-proof paper, facing paper and the balance paper after dipping are subjected to drying and processing；
Step C, handled the upper and lower surface of base to improve the surface roughness on the upper and lower surface of base, wherein, base
Layer is PVC stone-plastic plates or WPC plates, specifically can carry out grinding process or sided corona treatment or wharf's pavement quality to the upper and lower surface of base,
Main purpose is to remove the smooth wax coat in the upper and lower surface of base so that the upper and lower surface of base becomes more coarse, so as to have
Adhere to beneficial to stablizing for glue in follow-up coating process；In specific the present embodiment, the surface after being surface-treated above and below for base
Roughness meets the following conditions：After carrying out grinding process or sided corona treatment or wharf's pavement quality to the upper and lower surface of base, use
Dyne pen that dyne value is 30 writes the upper and lower surface of base, and what ink after finding to write can be stablized is attached to base
During the upper and lower surface of layer, illustrate that the surface roughness on the upper and lower surface of base meets the requirements, in follow-up coating process, glue can be steady
Surely it is attached to the upper and lower surface of base；
Step D, apply glue on the upper and lower surface of base；
Step E, abrasion-proof paper, facing paper, base and balance paper are overlapped from top to bottom and placed；
Step F, by abrasion-proof paper, facing paper, base and balance paper using it is cold into it is cold go out hot pressing mode press, should
It is cold into it is cold go out hot pressing mode mainly include it is following step by step：
F1 step by step：Abrasion-proof paper, facing paper, base and balance paper are put into hot press；
F2 step by step：Using the heating platen in the first design temperature to abrasion-proof paper, facing paper, base and balance paper into
Row pressing；
F3 step by step：The temperature of heating platen is gradually increased to the second design temperature, and one is maintained in the second design temperature
It fixes time；
F4 step by step：The temperature of heating platen is gradually decreased into the 3rd design temperature；
F5 step by step：Floor after pressing is taken out from hot press.Finally, progress health, burst, fluting obtain floor
Finished product.
Wherein, the second design temperature is limited as 30-160 DEG C, and the pressure of pressing is 5-20MPa, and the total time of pressing is 10-
60min；First design temperature and the 3rd design temperature are respectively less than critical value, critical value=+ 10 DEG C of environment temperature, i.e. abrasion-proof paper,
When facing paper, base and balance paper are put into and leave hot press, heating platen is in relatively low temperature, specifically in (ring
+ 10 DEG C of border temperature) below.In specific the present embodiment, the second design temperature of recommendation is 135 DEG C, and the pressure of pressing is 15MPa,
The total time of pressing is 40min, and the first design temperature and the 3rd design temperature are environment temperature.
It should be noted that step B is carried out before step A, step D is carried out before step C, and step A, step B
Process and step C, step D process without sequencing limit, i.e., the dipping of abrasion-proof paper, facing paper and balance paper, dry
The raising surface roughness on processing and the upper and lower surface of base, gluing processing can be carried out individually, the limitation in no sequential.
In the prior art using PVC stone-plastic plates or WPC plates as base floor essentially by a hot pressing by the way of will
Surface layer and base are bonded together, and it is adhesion-molded after floor often occur deforming and each layer is combined and unstable asked
Topic, inventor is the study found that the main reason for causing the above problem is：(1) can soften after PVC stone-plastic plates or WPC plate hot pressing, but
Surface layer and base are not same materials, and the two can not achieve the effect that well mutually to melt during hot pressing；(2) base and table
The thermal stress that layer is subject to during hot pressing is different, and PVC stone-plastic plates or WPC plates after hot pressing as base easily occur
Contraction distortion, the ground board finished product deformation caused are serious；(3) in existing heat pressing process, after the separation of upper and lower heating platen,
Each layer often separates in floor after pressing, that is, each layer occurs with reference to unstable phenomenon.
In view of the above-mentioned problems, present applicant has proposed a solution, it is specially the applying date：2017-10-
11, a kind of entitled application for a patent for invention (application number of PVC stone plastic floors manufacturing method：2017109457571) carry, but wherein
Independent hot pressing+the surface layer in surface layer gone out and the combination process that base is cold-pressed operate relative complex in actual production, it is proposed that another
Kind solves the problems, such as that more than floor deformation, each layer combine insecure technical solution.
In the present embodiment, abrasion-proof paper, facing paper and balance paper are impregnated first, drying and processing, at the same using as
The PVC stone-plastic plates of base material or the upper and lower surface of WPC plates are handled, to improve the surface roughness on the upper and lower surface of base, and
It applies glue on the upper and lower surface of base, then abrasion-proof paper, facing paper, base and balance paper is overlapped from top to bottom and placed, most
Afterwards using it is cold into it is cold go out hot pressing mode pressed, crucial improvement is：By base's independent coating adhesive in upper and lower surface
Hydraulic art with it is cold into it is cold go out heat pressing process be combined, find by production inspection, gone out using process above final production
Floor, effectively overcome and serious and each layer deformed after the hot pressing of floor with reference to unstable problem, significantly improve product matter
Amount improves the competitiveness of product.Wherein, base and other layers can be effectively increased by the upper and lower surface of base individually being coated glue
Between bonding effect, but only so do not enough, it is also necessary to it is cold into it is cold go out heat pressing process correspondence be engaged, cold into cold
Go out in heat pressing process, abrasion-proof paper, facing paper, base and balance paper experienced the hot pressing of room temperature, heating, heat preservation, cooling, room temperature
Temperature coordinates the pressing pressure of specific settings and pressing total time in entire hot pressing so that after the completion of hot pressing, base
The glue that upper and lower surface individually coats gives full play to adhesive effect, improves the firmness combined between each layer, avoids simultaneously
The floor deformation problem occurred after existing heat pressing process.
It should be noted that in the present embodiment, the base of PVC stone-plastic plates or WPC plates, the processing of leaching melamine or leaching are utilized
It is corresponding that the upper and lower surface of base is coordinated individually to apply when abrasion-proof paper, facing paper and the balance paper of phenolic resin processing produce floor
Adhesive process and particular step, parameter it is cold into it is cold go out heat pressing process, solve existing floor after being produced using existing process
Serious and each layer is deformed with reference to unstable problem, is to particular substrate material (PVC stone-plastic plates or WPC plates) and specific dipping
Its manufacture of floor of material (abrasion-proof paper, facing paper and the balance paper of the processing of leaching melamine or leaching phenolic resin processing) composition
One kind of method is specially modified.
Embodiment 2
The consolidated floor manufacturing method of the present embodiment, it is substantially the same manner as Example 1, the difference is that：Second sets
Constant temperature degree is 100 DEG C, and the pressure of pressing is 10MPa, and the total time of pressing is 10min, the first design temperature and the 3rd setting temperature
Degree is+5 DEG C of environment temperature.
Embodiment 3
The consolidated floor manufacturing method of the present embodiment, it is substantially the same manner as Example 1, the difference is that：Second sets
Constant temperature degree is 40 DEG C, and the pressure of pressing is 5MPa, and the total time of pressing is 55min, the first design temperature and the 3rd design temperature
It is+10 DEG C of environment temperature.
Embodiment 4
The consolidated floor manufacturing method of the present embodiment, it is substantially the same manner as Example 1, the difference is that：Second sets
Constant temperature degree is 60 DEG C, and the pressure of pressing is 8MPa, and the total time of pressing is 30min, the first design temperature and the 3rd design temperature
It is+8 DEG C of environment temperature.
Schematically the present invention and embodiments thereof are described above, this describes no restricted, institute in attached drawing
What is shown is also one of embodiments of the present invention, and actual structure is not limited thereto.So if common skill of this field
Art personnel are enlightened by it, without departing from the spirit of the invention, are not inventively designed and the technical solution
Similar frame mode and embodiment, are within the scope of protection of the invention.
Claims (9)
1. a kind of consolidated floor manufacturing method, it is characterised in that comprise the following steps：
Step A, the abrasion-proof paper, facing paper and balance paper are subjected to impregnation；
Step B, abrasion-proof paper, facing paper and the balance paper after dipping are subjected to drying and processing；
Step C, handled the upper and lower surface of base to improve the surface roughness on the upper and lower surface of base；
Step D, apply glue on the upper and lower surface of base；
Step E, abrasion-proof paper, facing paper, base and balance paper are overlapped from top to bottom and placed；
Step F, by abrasion-proof paper, facing paper, base and balance paper using it is cold into it is cold go out hot pressing mode press.
2. consolidated floor manufacturing method according to claim 1 or 2, it is characterised in that：In step A, by abrasion-proof paper, decoration
Paper and balance paper carry out the processing of leaching melamine or leaching phenolic resin processing.
3. consolidated floor manufacturing method according to claim 1, it is characterised in that：The base is PVC stone-plastic plates or WPC
Plate.
4. consolidated floor manufacturing method according to claim 3, it is characterised in that：In step C, to the upper and lower surface of base
Carry out grinding process or sided corona treatment or wharf's pavement quality.
5. consolidated floor manufacturing method according to claim 3, it is characterised in that：In step C, to the upper and lower surface of base
Processing is carried out until the wax coat on the upper and lower surface of removal base.
6. consolidated floor manufacturing method according to claim 4 or 5, which is characterized in that step F include it is following step by step：
F1 step by step：Abrasion-proof paper, facing paper, base and balance paper are put into hot press；
F2 step by step：Abrasion-proof paper, facing paper, base and balance paper are pressed using the heating platen in the first design temperature
It closes；
F3 step by step：The temperature of heating platen is gradually increased to the second design temperature, and a timing is maintained in the second design temperature
Between；
F4 step by step：The temperature of heating platen is gradually decreased into the 3rd design temperature；
F5 step by step：Floor after pressing is taken out from hot press.
7. consolidated floor manufacturing method according to claim 6, it is characterised in that：In step F, second design temperature
For 30-160 DEG C, the pressure of pressing is 5-205MPa, and the time of pressing is 10-60min.
8. consolidated floor manufacturing method according to claim 7, which is characterized in that first design temperature and described
Three design temperatures are respectively less than critical value, the critical value=+ 10 DEG C of environment temperature.
9. consolidated floor manufacturing method according to any one of claims 1 to 8, which is characterized in that step A, step B
Process and step C, the process of step D are limited without sequencing.