CN108214708A - A kind of melamine multilayer solid wood board and its processing method - Google Patents

A kind of melamine multilayer solid wood board and its processing method Download PDF

Info

Publication number
CN108214708A
CN108214708A CN201810045559.4A CN201810045559A CN108214708A CN 108214708 A CN108214708 A CN 108214708A CN 201810045559 A CN201810045559 A CN 201810045559A CN 108214708 A CN108214708 A CN 108214708A
Authority
CN
China
Prior art keywords
melamine
solid wood
multilayer solid
wood board
processing method
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810045559.4A
Other languages
Chinese (zh)
Inventor
李玉杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201810045559.4A priority Critical patent/CN108214708A/en
Publication of CN108214708A publication Critical patent/CN108214708A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of melamine multilayer solid wood boards and its processing method of technical field of board processing, the melamine multilayer solid wood board mutually bonds hot pressing into the processing method is as follows by substrate, splash guard, reinforcing plate and melamine decorative layer successively from below to up：S1：Poplar, China fir and paulownia wood are peeled into multi-disc, substrate is formed after dry；S2：Solidification glue is uniformly smeared on the surface of substrate, is compressed using hot press；S3：Melamine decorative layer Jing Guo melamine-impregnated is combined on the surface for strengthening plate, obtain melamine solid wood multi-layer board finished product, present invention addition borax, make it have anti-flammability, using the technique pressed layer by layer, the multiple-plate stability of melamine is improved, there is qualification rate height according to finished product prepared by this method, the characteristics of production cost is low is suitble to promote the use of on a large scale.

Description

A kind of melamine multilayer solid wood board and its processing method
Technical field
The invention discloses a kind of melamine multilayer solid wood board and its processing method, specially sheet fabrication technology is led Domain.
Background technology
Melamine plate, referred to as three cyanogen plates, prefer to be ecological board in industry, full name is melamine-impregnated bond paper Face artificial board.It is that the paper with different colours or texture is put into melamine resin adehsive stick to impregnate, is then dried to Certain curing degree, mated formation particieboard, moist-proof board, medium density fibre board (MDF), glued board, core-board, multi-layer board or its His hard fibre plate surface, the decorative panel formed through hot pressing.In the production of melamine plate, on the one hand to the flatness of substrate It is required that very high, the qualification rate of another aspect finished product is also very low, and processing cost also remains high always.For this purpose, we have proposed one Kind melamine multilayer solid wood board and its processing method come into operation, to solve the above problems.
Invention content
The purpose of the present invention is to provide a kind of melamine multilayer solid wood board and its processing method, to solve above-mentioned background The problem of being proposed in technology.
To achieve the above object, the present invention provides following technical solution：A kind of melamine multilayer solid wood board, the melamine Amine multilayer solid wood board mutually bonds hot pressing by substrate, splash guard, reinforcing plate and melamine decorative layer successively from below to up Into.
Preferably, the substrate is one kind in poplar, China fir or paulownia wood.
Preferably, the splash guard is formed by veneer and the waterproof layer being covered on veneer by squeezing.
Preferably, the waterproof layer is using low-pressure high-density polyethylene as raw material, and mixed carbon black, age resister, anti-oxidant Agent and stabilizer composition.
Preferably, a kind of processing method of melamine multilayer solid wood board, the processing method are as follows：
S1：Poplar, China fir and paulownia wood are peeled into multi-disc, adhesive is then smeared between wood chip, passes through hydraulic press Plate construction is pressed into, substrate is formed after dry；
S2：Solidification glue is uniformly smeared on the surface of substrate, splash guard is superimposed upon on substrate, is equally smeared on splash guard Solidification glue will be strengthened plate and be placed on splash guard, compressed using hot press；
S3：After drying, the melamine decorative layer Jing Guo melamine-impregnated is combined on the surface for strengthening plate, is utilized It is dry to get to melamine solid wood multi-layer board finished product after hot press compresses.
Preferably, in the step S1, adhesive is the mixture of epoxy resin, borax and rosin, wherein epoxy Resin：Borax：Rosin=3:1.2:3.
Preferably, in the step S2, solidification glue is phenolic resin and Lauxite according to 1:1 proportional arrangement forms.
Preferably, in the step S2, hot press is heated using steam, and heating temperature is 60--80 DEG C, heating time For 20--40min, application pressure is 0.7--1.7MPa.
Preferably, in the step S3, after hot pressing, pacify according at multiple-plate length direction interval 25--30cm A fixture is filled, after dry end molding, fixture is removed.
Compared with prior art, the beneficial effects of the invention are as follows：Present invention addition borax, makes it have anti-flammability, uses The technique pressed layer by layer improves the multiple-plate stability of melamine, has qualification rate height according to finished product prepared by this method, raw The characteristics of at low cost is produced, is suitble to promote the use of on a large scale.
Description of the drawings
Fig. 1 is schematic structural view of the invention；
Fig. 2 is processing method flow chart of the present invention.
In figure：Plate, 4 melamine decorative layers are strengthened in 1 substrate, 2 splash guards, 3.
Specific embodiment
Below in conjunction with the attached drawing in the embodiment of the present invention, the technical solution in the embodiment of the present invention is carried out clear, complete Site preparation describes, it is clear that described embodiment is only part of the embodiment of the present invention, instead of all the embodiments.It is based on Embodiment in the present invention, those of ordinary skill in the art are obtained every other without making creative work Embodiment shall fall within the protection scope of the present invention.
It please refers to Fig.1 with 2, the present invention provides a kind of technical solution：A kind of melamine multilayer solid wood board, the melamine Multilayer solid wood board is from below to up successively by the mutually bonding hot pressing of substrate 1, splash guard 2, reinforcing plate 3 and melamine decorative layer 4 It is formed.
Wherein, the substrate 1 is one kind in poplar, China fir or paulownia wood, and the splash guard 2 is by veneer and is covered in list Waterproof layer on plate is formed by squeezing, and the waterproof layer is and mixed carbon black, anti-aging using low-pressure high-density polyethylene as raw material Agent, antioxidant and stabilizer composition.
The present invention also provides a kind of processing methods of melamine multilayer solid wood board, and the specific steps of the processing method are such as Under：
S1：Poplar, China fir and paulownia wood are peeled into multi-disc, adhesive is then smeared between wood chip, passes through hydraulic press Plate construction is pressed into, substrate 1 is formed after dry, adhesive is the mixture of epoxy resin, borax and rosin, Epoxy resin：Borax：Rosin=3:1.2:3；
S2：Solidification glue is uniformly smeared on the surface of substrate 1, splash guard 2 is superimposed on substrate 1, equally on splash guard 2 Solidification glue is smeared, plate 3 will be strengthened and be placed on splash guard 2, compressed using hot press, solidification glue is phenolic resin and ureaformaldehyde Resin is according to 1:1 proportional arrangement forms, and hot press is heated using steam, and heating temperature is 60--80 DEG C, and heating time is 20--40min, application pressure are 0.7--1.7MPa；
S3：After drying, the melamine decorative layer 4 Jing Guo melamine-impregnated is combined on the surface for strengthening plate 3, profit It is dry to get to melamine solid wood multi-layer board finished product after being compressed with hot press, after hot pressing, according to multiple-plate length One fixture at the 25--30cm of direction interval is installed, after dry end molding, fixture is removed.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of variations, modification, replace And modification, the scope of the present invention is defined by the appended.

Claims (9)

1. a kind of melamine multilayer solid wood board, it is characterised in that：The melamine multilayer solid wood board is from below to up successively by base Plate (1), splash guard (2), strengthen plate (3) and melamine decorative layer (4) mutually bonding hot pressing into.
2. a kind of melamine multilayer solid wood board according to claim 1, it is characterised in that：The substrate (1) for poplar, One kind in China fir or paulownia wood.
3. a kind of melamine multilayer solid wood board according to claim 1, it is characterised in that：The splash guard (2) is by list Plate and the waterproof layer being covered on veneer are formed by squeezing.
4. a kind of melamine multilayer solid wood board according to claim 2, it is characterised in that：The waterproof layer is with low pressure height Density polyethylene is raw material, and mixed carbon black, age resister, antioxidant and stabilizer form.
5. a kind of processing method of melamine multilayer solid wood board, it is characterised in that：The processing method is as follows：
S1：Poplar, China fir and paulownia wood are peeled into multi-disc, adhesive is then smeared between wood chip, by hydraulic press by its Plate construction is pressed into, substrate (1) is formed after dry；
S2：Solidification glue is uniformly smeared on the surface of substrate (1), splash guard (2) is superimposed upon on substrate (1), equally in splash guard (2) solidification glue is smeared on, plate (3) will be strengthened and be placed on splash guard (2), compressed using hot press；
S3：After drying, the melamine decorative layer (4) Jing Guo melamine-impregnated is combined on the surface for strengthening plate (3), profit It is dry to get to melamine solid wood multi-layer board finished product after being compressed with hot press.
6. a kind of processing method of melamine multilayer solid wood board according to claim 5, it is characterised in that：The step In S1, mixture of the adhesive for epoxy resin, borax and rosin, epoxy resin：Borax：Rosin=3:1.2: 3。
7. a kind of processing method of melamine multilayer solid wood board according to claim 5, it is characterised in that：The step In S2, solidification glue is phenolic resin and Lauxite according to 1:1 proportional arrangement forms.
8. a kind of processing method of melamine multilayer solid wood board according to claim 5, it is characterised in that：The step In S2, hot press is heated using steam, and heating temperature is 60--80 DEG C, heating time 20--40min, is applied pressure and is 0.7--1.7MPa。
9. a kind of processing method of melamine multilayer solid wood board according to claim 5, it is characterised in that：The step In S3, after hot pressing, according to installing a fixture at multiple-plate length direction interval 25--30cm, it is dry terminate into After type, fixture is removed.
CN201810045559.4A 2018-01-17 2018-01-17 A kind of melamine multilayer solid wood board and its processing method Pending CN108214708A (en)