CN108085810A - Plant chemical fibre and chemical fibre hybrid yams and preparation method thereof - Google Patents
Plant chemical fibre and chemical fibre hybrid yams and preparation method thereof Download PDFInfo
- Publication number
- CN108085810A CN108085810A CN201711036458.2A CN201711036458A CN108085810A CN 108085810 A CN108085810 A CN 108085810A CN 201711036458 A CN201711036458 A CN 201711036458A CN 108085810 A CN108085810 A CN 108085810A
- Authority
- CN
- China
- Prior art keywords
- chemical fibre
- parts
- fibre
- plant
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of plant chemical fibre and chemical fibre hybrid yams and preparation method thereof, the parts by weight proportioning of each raw material of the hybrid yams is：50 60 parts of sisal fiber, 50 60 parts of castor-oil plant fiber, 50 60 parts of abaca fibre etc..Present invention uses sisal fibers and castor-oil plant fiber and abaca fibre so that the permeability of entire fabric greatly reinforces, subsequent high speed centrifugation, centrifuge speed 300r/min；After three kinds of abundant Centrifugal dispersions of fiber the method for spreading will be used to remove mesophyll colloid；After spandex and three kinds of acrylic fibers and polyamide fibre are mixed with the mode of dry spinning, a kind of new synthetic fibers are formed on spinneret, plant chemical fibre and chemical fibre hybrid yams have the extensibility higher than common chemical fibre so that clothes it is entire stickiness it is more preferable, dress it is more comfortable.
Description
Technical field
The present invention relates to a kind of knitting fabrics and preparation method thereof, are in particular that a kind of plant chemical fibre is mixed with chemical fibre
Yarn and its manufacturing method.
Background technology
There are many textile fabric species, are generally divided into two major class of natural fiber and chemical fibre.Cotton is a kind of large natural
Cellulose fibre, be uniquely solved in agriculture major product grain, cotton, oil, vegetables the mankind wear, the product with demand.With chemical fibre
It compares, soft fabric comfort is good made of cotton fiber, and sucting wet air permeability is strong, and warmth retention property is good, and there is no electrostatic etc. no
Good reaction, and green health will not cause human skin adverse reaction.Spandex is a kind of work(with high resiliency and recovery
Energy fiber can greatly improve the elasticity and recovery of fabric, so as to improve knitting as long as a small amount of spandex thread is added in the fabric
The aptamer and wrinkle resistance of object are to take the most important fibrous raw material that kind fabric increases bullet.With reference to the advantages of cotton fiber and spandex and
Manufactured cotton spandex knitted fabric is not only soft, comfortable, moisture absorption, ventilative, warming but also resilient enough, particularly suitable for making
Standby underskirt and functional exercise class clothes.
But chemical fibre easily grows bacterium, service life is short, and tensile strength is low, still cannot meet people for fabric
The requirement of gas permeability, frivolous, heat preservation, antibacterial etc..
The content of the invention
For in the prior art the defects of, the technical problem to be solved in the present invention is to provide a kind of plant chemical fibres to mix with chemical fibre
Close yarn.
According to an aspect of the present invention, a kind of plant chemical fibre and chemical fibre hybrid yams and its manufacturing method are provided, including
The parts by weight of following raw material match：
Sisal fiber：50-60 parts；
Castor-oil plant fiber：50-60 parts；
Abaca fibre：50-60 parts；
Spandex：10-15 parts；
Acrylic fibers：20-25 parts；
Polyamide fibre：20-25 parts；
Modal：5-10 parts；
Tencel：15-20 parts；
Ethylene oxide：0.4-0.6 parts；
Propylene oxide：0.4-0.6 parts.
Preferably, the plant chemical fibre can keep every physical index with chemical fibre hybrid yams in -10 DEG C to 100 DEG C scopes
Stability, when artificial weathering test 5000 is small.
Preferably, the plant chemical fibre has the extensibility higher than common chemical fibre with chemical fibre hybrid yams, so that clothes is whole
A stickiness is more preferable, dress it is more comfortable.
Preferably, the plant chemical fibre and chemical fibre hybrid yams permeability are good, and sandblasting contains the bacterium solution of colon bacillus 0157
With material surface, the lethality of germ reaches 95% in half an hour, and 1 lethality of interior germ when small reaches 100%.
The present invention also provides a kind of plant chemical fibres and chemical fibre hybrid yams and its manufacturing method, comprise the following steps：
Step 1, the preparation and reaction of raw material, sisal fiber and castor-oil plant fiber and abaca fibre choose component in proportion, into
Row high speed centrifugation, centrifuge speed 300r/min, 65 DEG C of centrifuging temperature；
Step 2 will use the method for spreading to remove mesophyll colloid, in temperature conditionss 40- after three kinds of abundant Centrifugal dispersions of fiber
Be placed under conditions of 60 DEG C concentration be 0.4g/L sulfuric acid Rong Yiren in dipping 6 it is small when；
Step 3 by the composite fibre impregnated circulating water to flush wash clean, until pH is 6.7-6.8, adds in Chinese violet extraction
Liquid submerges, and when boiling 10 is small, dehydration is trembled and sent, oil supply, drying；
Step 4 after weighing spandex and acrylic fibers and polyamide fibre according to quantity, adds in high-speed mixer, the heating temperature of high-speed mixer
For 95 DEG C, 5min is heated, cools down 4min；
Step 5, synthetic fibers then re-melt into glassy state, during being then granulated again plus as Modal, tencel are mixed
It closes；
Composite fibre and synthetic fibers after granulation, are mixed and added into the ethylene oxide weighed, epoxy third by step 6
Alkane；
Step 7, after dyeing, item processed is then thick to the end then to three pins then to two pins then to scalp acupuncture, then arrives thick
Yarn, finally to spun yarn or covering yarn；
Step 8 is cut out, and makes ready-made clothes.
The positive effect of the present invention is：It uses sisal fiber and castor-oil plant fiber and abaca fibre so that
The permeability of entire fabric greatly reinforces, subsequent high speed centrifugation, centrifuge speed 300r/min；Three kinds of fibers are fully centrifuged
Mesophyll colloid is removed using the method for spreading after scattered；Spandex and three kinds of acrylic fibers and polyamide fibre are mixed with the mode of dry spinning
After together, a kind of new synthetic fibers are formed on spinneret, plant chemical fibre has the drawing higher than common chemical fibre with chemical fibre hybrid yams
Stretch rate so that clothes it is entire stickiness it is more preferable, dress it is more comfortable.Then by the compound fibre after synthetic fibers and centrifugation
Dimension is put into togerther high mixer and is dyed；After dyeing, item processed then to scalp acupuncture, then to two pins, then to three pins, then arrives
Head is thick, then to rove, finally to spun yarn or covering yarn.
Specific embodiment
With reference to specific embodiment, the present invention is described in detail.Following embodiment will be helpful to the technology of this field
Personnel further understand the present invention, but the invention is not limited in any way.It should be pointed out that the ordinary skill to this field
For personnel, without departing from the inventive concept of the premise, various modifications and improvements can be made.These belong to the present invention
Protection domain.
The parts by weight of plant chemical fibre of the present invention and each raw material of chemical fibre hybrid yams match：50-60 parts of sisal fiber, castor
50-60 parts of flaxen fiber, 50-60 parts of abaca fibre, 10-15 parts of spandex, 20-25 parts of acrylic fibers, 20-25 parts of polyamide fibre, Modal 5-10
Part, 15-20 parts of tencel, 0.4-0.6 parts of ethylene oxide, 0.4-0.6 parts of propylene oxide.
The manufacturing technique method of examples detailed above is：Sisal fiber and castor-oil plant fiber and abaca fibre elder generation high speed centrifugation, from
Scheming rotating speed 300r/min；After three kinds of abundant Centrifugal dispersions of fiber the method for spreading will be used to remove mesophyll colloid；Spandex and
After three kinds of acrylic fibers and polyamide fibre are mixed with the mode of dry spinning, a kind of new synthetic fibers are formed on spinneret.With
The composite fibre after synthetic fibers and centrifugation is put into togerther high mixer afterwards to dye；After dyeing, item processed, then to scalp acupuncture,
Then it is then thick to the end then to three pins to two pins, then to rove, finally to spun yarn or covering yarn.
Plant chemical fibre of the present invention comprises the following steps with chemical fibre hybrid yams and its manufacturing method：
Step 1, the preparation and reaction of raw material, sisal fiber and castor-oil plant fiber and abaca fibre choose component in proportion, into
Row high speed centrifugation, centrifuge speed 300r/min, 65 DEG C of centrifuging temperature；
Step 2 will use the method for spreading to remove mesophyll colloid, in temperature conditionss 40- after three kinds of abundant Centrifugal dispersions of fiber
Be placed under conditions of 60 DEG C concentration be 0.4g/L sulfuric acid Rong Yiren in dipping 6 it is small when；
Step 3 by the composite fibre impregnated circulating water to flush wash clean, until pH is 6.7-6.8, adds in Chinese violet extraction
Liquid submerges, and when boiling 10 is small, dehydration is trembled and sent, oil supply, drying；
Step 4 after weighing spandex and acrylic fibers and polyamide fibre according to quantity, adds in high-speed mixer, the heating temperature of high-speed mixer
For 95 DEG C, 5min is heated, cools down 4min；
Step 5, synthetic fibers then re-melt into glassy state, during being then granulated again plus as Modal, tencel are mixed
It closes；
Composite fibre and synthetic fibers after granulation, are mixed and added into the ethylene oxide weighed, epoxy third by step 6
Alkane；
Step 7, after dyeing, item processed is then thick to the end then to three pins then to two pins then to scalp acupuncture, then arrives thick
Yarn, finally to spun yarn or covering yarn；
Step 8 is cut out, and makes ready-made clothes.
The plant chemical fibre can keep the stabilization of every physical index with chemical fibre hybrid yams in -10 DEG C to 100 DEG C scopes
Property, when artificial weathering test 5000 is small.
The plant chemical fibre has the extensibility higher than common chemical fibre with chemical fibre hybrid yams, so that the fitting that clothes is entire
Property it is more preferable, dress it is more comfortable.
The plant chemical fibre and chemical fibre hybrid yams permeability are good, and sandblasting contains the bacterium solution of colon bacillus 0157 and material table
Face, the lethality of germ reaches 95% in half an hour, and 1 lethality of interior germ when small reaches 100%.
The extracting method of the Chinese violet extracting solution is：The flower of Chinese violet is collected, smashs to pieces, adds 70% ethyl alcohol water-soluble
Three times, merging filtrate, activated carbon decolorizing is evaporated to obtain powder liquid refluxing extraction, and powder is according to 1：1000 are dissolved in clear water.
What the raw material of following embodiment matched in parts by weight is made：
Embodiment 1
Sisal fiber：50 parts；
Castor-oil plant fiber：50 parts；
Abaca fibre：50 parts；
Spandex：10 parts；
Acrylic fibers：20 parts；
Polyamide fibre：20 parts；
Modal：5 parts；
Tencel：15 parts；
Ethylene oxide：0.4 part；
Propylene oxide：0.4 part.
First chooses 50 parts of selection sisal fiber and 50 parts of 50 parts of castor-oil plant fiber and abaca fibre in proportion, carries out at a high speed
Centrifugation, centrifuge speed 300r/min, 65 DEG C of centrifuging temperature；It will by the method that spreading is used after three kinds of abundant Centrifugal dispersions of fiber
Mesophyll colloid removes, and it is small that dipping 6 in the sulfuric acid Rong Yiren that concentration is 0.4g/L is placed under conditions of 40-60 DEG C of temperature conditionss
When；By the composite fibre impregnated circulating water to flush wash clean, until pH is 6.7-6.8, the submergence of Chinese violet extracting solution is added in, is steamed
Boil 10 it is small when, dehydration, tremble and give, oil supply, drying；After 20 parts of 20 parts of 10 parts of spandex and acrylic fibers and polyamide fibre are weighed according to quantity, add in
High-speed mixer, the heating temperature of high-speed mixer is 95 DEG C, heats 5min, cools down 4min；Synthetic fibers then re-melt
Into glassy state, during being then granulated again plus as 5 parts of Modal, 15 parts of tencel are mixed；After granulation, by composite fibre
0.4 part of 0.4 part of ethylene oxide, the propylene oxide weighed is mixed and added into synthetic fibers；After dyeing, item processed, then to the end
Pin, it is then thick to the end then to three pins then to two pins, then to rove, finally to spun yarn or covering yarn；It is cut out,
Make ready-made clothes.
Embodiment 2
Sisal fiber：55 parts；
Castor-oil plant fiber：55 parts；
Abaca fibre：55 parts；
Spandex：13 parts；
Acrylic fibers：23 parts；
Polyamide fibre：23 parts；
Modal：8 parts；
Tencel：18 parts；
Ethylene oxide：0.5 part；
Propylene oxide：0.5 part.
The preparation method of the present embodiment is identical with embodiment 1.
Embodiment 3
Sisal fiber：60 parts；
Castor-oil plant fiber：60 parts；
Abaca fibre：60 parts；
Spandex：15 parts；
Acrylic fibers：25 parts；
Polyamide fibre：25 parts；
Modal：10 parts；
Tencel：20 parts；
Ethylene oxide：0.6 part；
Propylene oxide：0.6 part.
The preparation method of the present embodiment is identical with embodiment 1.
Table 1 is plant chemical fibre and the quantitative measurement result of chemical fibre hybrid yams.
Table 1
| Confficient of static friction/N | Ultimate strength/N | |
| Embodiment 1 | 0.318 | 5.75 |
| Embodiment 2 | 0.326 | 6.37 |
| Embodiment 3 | 0.375 | 5.45 |
| The prior art | 0.548 | 1.96 |
Specific embodiments of the present invention are described above.It is to be appreciated that the invention is not limited in above-mentioned specific
Embodiment, those skilled in the art can make various deformations or amendments within the scope of the claims, this has no effect on this
The substantive content of invention.
Claims (5)
1. a kind of plant chemical fibre and chemical fibre hybrid yams, which is characterized in that the plant chemical fibre and each raw material of chemical fibre hybrid yams
Parts by weight match：
Sisal fiber：50-60 parts；
Castor-oil plant fiber：50-60 parts；
Abaca fibre：50-60 parts；
Spandex：10-15 parts；
Acrylic fibers：20-25 parts；
Polyamide fibre：20-25 parts；
Modal：5-10 parts；
Tencel：15-20 parts；
Ethylene oxide：0.4-0.6 parts；
Propylene oxide：0.4-0.6 parts.
2. plant chemical fibre according to claim 1 and chemical fibre hybrid yams, which is characterized in that the plant chemical fibre is mixed with chemical fibre
The stability that yarn keeps every physical index in -10 DEG C to 100 DEG C scopes is closed, when artificial weathering test 5000 is small.
3. plant chemical fibre according to claim 1 and chemical fibre hybrid yams, which is characterized in that the plant chemical fibre is mixed with chemical fibre
Closing yarn has the extensibility higher than common chemical fibre so that clothes it is entire stickiness it is more preferable, dress it is more comfortable.
4. plant chemical fibre according to claim 1 and chemical fibre hybrid yams, which is characterized in that the plant chemical fibre is mixed with chemical fibre
Conjunction yarn permeability is good, and sandblasting contains the bacterium solution and material surface of colon bacillus 0157, and the lethality of germ reaches in half an hour
95%, 1 lethality of interior germ when small reaches 100%.
5. a kind of plant chemical fibre and the preparation method of chemical fibre hybrid yams, which is characterized in that it is to carry out in accordance with the following steps：
Step 1, the preparation and reaction of raw material, sisal fiber and castor-oil plant fiber and abaca fibre choose component in proportion, into
Row high speed centrifugation, centrifuge speed 300r/min, 65 DEG C of centrifuging temperature；
Step 2 will use the method for spreading to remove mesophyll colloid, in temperature conditionss 40- after three kinds of abundant Centrifugal dispersions of fiber
Be placed under conditions of 60 DEG C concentration be 0.4g/L sulfuric acid Rong Yiren in dipping 6 it is small when；
Step 3 by the composite fibre impregnated circulating water to flush wash clean, until pH is 6.7-6.8, adds in Chinese violet extraction
Liquid submerges, and when boiling 10 is small, dehydration is trembled and sent, oil supply, drying；
Step 4 after weighing spandex and acrylic fibers and polyamide fibre according to quantity, adds in high-speed mixer, the heating temperature of high-speed mixer
For 95 DEG C, 5min is heated, cools down 4min；
Step 5, synthetic fibers then re-melt into glassy state, during being then granulated again plus as Modal, tencel are mixed
It closes；
Composite fibre and synthetic fibers after granulation, are mixed and added into the ethylene oxide weighed, epoxy third by step 6
Alkane；
Step 7, after dyeing, item processed is then thick to the end then to three pins then to two pins then to scalp acupuncture, then arrives thick
Yarn, finally to spun yarn or covering yarn；
Step 8 is cut out, and makes ready-made clothes.