CN108081404A - A kind of wearability veneer preparation method - Google Patents
A kind of wearability veneer preparation method Download PDFInfo
- Publication number
- CN108081404A CN108081404A CN201711345859.6A CN201711345859A CN108081404A CN 108081404 A CN108081404 A CN 108081404A CN 201711345859 A CN201711345859 A CN 201711345859A CN 108081404 A CN108081404 A CN 108081404A
- Authority
- CN
- China
- Prior art keywords
- veneer
- wearability
- time
- impregnation
- hot pressing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of wearability veneer preparation method, belongs to building material technical field, including slicing, first time hot pressing, glue modulation, the manufacture of transparent wear surface layer glued membrane paper, second of hot pressing, cutting edge and post processing.Instant component science, compared with the manufacturing method of traditional veneer, the present invention is in wearing coat paper and AL2O3Double action under, through non-painting veneer recombinant decorative veneer surface abrasion value ﹤ 50mg/100r made from the above method, improve the wear-resisting property of decorative panel, improve the service life and performance of decorative panel.
Description
Technical field
The invention belongs to building material technical fields, are related to a kind of manufacturing method of decorative panel, more particularly to a kind of resistance to
Mill property veneer preparation method.
Background technology
Decorative panel is a kind of artificial board, it is with a variety of special paper after chemical treatment, with high temperature and pressure gluing
Thermosetting property laminated plastic made of agent, plate face has various wood grains or pattern, bright smooth, bright in colour beautiful, many advanced
Wall, the roof in room, make exquisite cabinet, cupboard, table, bed, the workbench of precision instrument, the experimental bench in laboratory, television set,
The shell of radio and other broadcast telecommunication equipments, mostly using this new decorative panel.
The textured pattern of scientific and technological veneer simulative timber plays true to nature or super expected decorative effect, obtains one
Divide pursuing for the cultural fan of wood.Recombinant Wood industrial chain is made a general survey of, mostly using large diameters ripe ages such as fast growing wood poplar, African whitewoods
Material, product category are also conventional imitative precious seeds, such as oak, maple, the common textured pattern of redwood class.In production parquets aesthetics figure
During the miscellaneous line pattern of case, the imitative burr, fullsheet veneer is also dug up into extra part according to technological requirement, has both wasted material money
Source, and add the amount of labour of employee.And as the cutting of the above the average age for marriage material of available fast-growing is reduced increasingly, to the production of Recombinant Wood
Bring larger feed pressure.
The thickness of existing veneer is usually 0.15~1.00mm, and breadth is big, and soft bone free frame support structure, on its surface
It is relatively difficult to carry out continuous covering with paint operation.Conventional flow is that veneer is first pasted on to wood-base fibre and particle panel material substrate surface, Ran Houzai
The operations such as sanding, covering with paint are carried out, since it wears no resistance, using effect is not good enough, and service life is low.
The content of the invention
The present invention is thin for the thickness of existing veneer, and breadth is big, and soft bone free frame support structure, is connected on its surface
Continuous covering with paint operation is relatively difficult, and conventional flow is that veneer is first pasted on to wood-base fibre and particle panel material substrate surface, then carries out sand again
The operations such as light, covering with paint, the deficiencies such as since it wears no resistance, using effect is not good enough, and service life is low propose a kind of wearability veneer
Preparation method can promote the wear-resisting property of decorative panel, promote the service life and performance of decorative panel.
Technical scheme：A kind of wearability veneer preparation method, which is characterized in that manufacturing step is as follows：
(1) slicing：By recombinant decorative material slicing into thickness be 0.15~1.00mm recombinant decorative veneer；
(2) first time hot pressing：Flexible reinforced material, the flexibility are posted by first time hot pressing at the back side of recombinant decorative veneer
The thickness of reinforcing material is 0.05~0.15mm；
(3) glue is modulated：Tourmaline anion powder, AL2O are added in amino formaldehyde resin solution3, and stir evenly；Wherein
The mass ratio of amino formaldehyde resin solution and tourmaline powder is 12:1, amino formaldehyde resin solution and AL2O3Mass ratio be 40:
1；
(4) glued membrane paper in transparent wear surface layer manufactures：Transparent wear overlay paper is passed sequentially through into common glue and carries out first time impregnation
With by containing tourmaline powder, AL2O3Amino formaldehyde resin glue carry out second of impregnation, and dry；
(5) second of hot pressing：One wearing coat bond paper and a back side are posted to the recombinant decorative of flexible reinforcing material
Veneer is compound, and carries out second of hot pressing；
(6) cutting edge；
(7) post-process.
Step (2) the first time heat pressing process is：80~120 DEG C, 0.3~1.0Mpa of pressure of temperature, the time 50~
180s。
Curing agent and releasing agent are also added with during step (3) the glue modulation.
The impregnation resin content of step (4) the first time impregnation and second of impregnation is respectively 100%, 120%；Wearing coat glued membrane
Quantification of 12~16g/m of paper2。
Second of heat pressing process is in the step (5)：120 DEG C of temperature, pressure 1 .0Mpa, time 15min.
Cutting edge in the step (6) is that the product overlayed is cut out burr removing with chopper, neat to stack.
Post processing in the step (7) is will to exempt to paint recombinant decorative on-board check, grade, pack, being put in storage.
Beneficial effects of the present invention are：A kind of wearability veneer preparation method proposed by the present invention, component science, with tradition
The manufacturing method of veneer is compared, and the present invention is in wearing coat paper and AL2O3Double action under, through exempting to paint made from the above method
Facing recombinant decorative veneer surface abrasion value ﹤ 50mg/100r, improve the wear-resisting property of decorative panel, improve making for decorative panel
With service life and performance.
Specific embodiment
With reference to embodiment, the invention will be further described：
A kind of wearability veneer preparation method, manufacturing step are as follows：
(1) slicing：By recombinant decorative material slicing into thickness be 0.15~1.00mm recombinant decorative veneer；
(2) first time hot pressing：Flexible reinforced material, the flexibility are posted by first time hot pressing at the back side of recombinant decorative veneer
The thickness of reinforcing material is 0.05~0.15mm；
(3) glue is modulated：Tourmaline anion powder, AL2O are added in amino formaldehyde resin solution3, and stir evenly；Wherein
The mass ratio of amino formaldehyde resin solution and tourmaline powder is 12:1, amino formaldehyde resin solution and AL2O3Mass ratio be 40:
1；
(4) glued membrane paper in transparent wear surface layer manufactures：Transparent wear overlay paper is passed sequentially through into common glue and carries out first time impregnation
With by containing tourmaline powder, AL2O3Amino formaldehyde resin glue carry out second of impregnation, and dry；
(5) second of hot pressing：One wearing coat bond paper and a back side are posted to the recombinant decorative of flexible reinforcing material
Veneer is compound, and carries out second of hot pressing；
(6) cutting edge；
(7) post-process.
A kind of wearability veneer preparation method, step (2) first time heat pressing process are：80~120 DEG C of temperature, pressure 0.3
~1.0Mpa, 50~180s of time；Curing agent and releasing agent are also added with when step (3) glue is modulated；Step (4) is soaked for the first time
The impregnation resin content of glue and second of impregnation is respectively 100%, 120%；Quantification of 12~16g/m of wearing coat bond paper2；Step
(5) second of heat pressing process is in：120 DEG C of temperature, pressure 1 .0Mpa, time 15min；Cutting edge in step (6) is to use chopper
The product overlayed is cut out into burr removing, it is neat to stack；Post processing in step (7) is will to exempt to paint recombinant decorative on-board check, divide
Deng, packaging, storage.
Instant component science, compared with the manufacturing method of traditional veneer, the present invention is in wearing coat paper and AL2O3It is double
Under recast is used, through non-painting veneer recombinant decorative veneer surface abrasion value ﹤ 50mg/100r made from the above method, decoration is improved
The wear-resisting property of plate improves the service life and performance of decorative panel.
Claims (7)
1. a kind of wearability veneer preparation method, which is characterized in that manufacturing step is as follows：
(1) slicing：By recombinant decorative material slicing into thickness be 0.15~1.00mm recombinant decorative veneer；
(2) first time hot pressing：Flexible reinforced material, the flexibility are posted by first time hot pressing at the back side of recombinant decorative veneer
The thickness of reinforcing material is 0.05~0.15mm；
(3) glue is modulated：Tourmaline anion powder, AL2O are added in amino formaldehyde resin solution3, and stir evenly；Wherein ammonia
The mass ratio of base formaldehyde resin solution and tourmaline powder is 12:1, amino formaldehyde resin solution and AL2O3Mass ratio be 40:1；
(4) glued membrane paper in transparent wear surface layer manufactures：Transparent wear overlay paper is passed sequentially through into common glue and carries out first time impregnation
With by containing tourmaline powder, AL2O3Amino formaldehyde resin glue carry out second of impregnation, and dry；
(5) second of hot pressing：One wearing coat bond paper and a back side are posted to the recombinant decorative of flexible reinforcing material
Veneer is compound, and carries out second of hot pressing；
(6) cutting edge；
(7) post-process.
2. a kind of wearability veneer preparation method according to claim 1, it is characterised in that：The step (2) is for the first time
Heat pressing process is：80~120 DEG C, 0.3~1.0Mpa of pressure, 50~180s of time of temperature.
3. a kind of wearability veneer preparation method according to claim 1, it is characterised in that：Step (3) the glue tune
Curing agent and releasing agent are also added with when processed.
4. a kind of wearability veneer preparation method according to claim 1, it is characterised in that：The step (4) is for the first time
The impregnation resin content of impregnation and second of impregnation is respectively 100%, 120%；Quantification of 12~16g/m of wearing coat bond paper2。
5. a kind of wearability veneer preparation method according to claim 1, it is characterised in that：Second in the step (5)
Secondary heat pressing process is：120 DEG C of temperature, pressure 1 .0Mpa, time 15min.
6. a kind of wearability veneer preparation method according to claim 1, it is characterised in that：Sanction in the step (6)
While be that the product overlayed is cut out into burr removing with chopper, it is neat to stack.
7. a kind of wearability veneer preparation method according to claim 1, it is characterised in that：After in the step (7)
Processing is will to exempt to paint recombinant decorative on-board check, grade, pack, being put in storage.