CN108059875A - Screen coating material and preparation method thereof - Google Patents
Screen coating material and preparation method thereof Download PDFInfo
- Publication number
- CN108059875A CN108059875A CN201711173411.0A CN201711173411A CN108059875A CN 108059875 A CN108059875 A CN 108059875A CN 201711173411 A CN201711173411 A CN 201711173411A CN 108059875 A CN108059875 A CN 108059875A
- Authority
- CN
- China
- Prior art keywords
- resin
- coating material
- adhesive force
- agent
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of screen coating material and preparation method, wherein, the formula of the coating material forms by mass percentage is：Water-based acrylic resin 40~50%, film-forming resin 10~15%, aluminium powder 1~2.5%, adhesive force promote resin 5~12%, dispersant 2~5%, levelling agent 0.1~0.5%, antifoaming agent 0.1~0.5%, curing agent 0.5~2%, ethyl alcohol 5~10%, glycerine 5~15%.Screen in the present invention has preferable dispersiveness with coating material, and adhesive force and bending resistance are preferable.
Description
Technical field
The present invention relates to field of ink manufacture, more particularly to a kind of screen coating material and preparation method thereof.
Background technology
Projection screen used in existing market is usually white modeling cloth, generally requires to use ink for screen printing in preparation process,
Ink is printed onto on projection screen using screen printing mode, then using curing measure so that projection screen is securely prolonged
It is durable.However, ink bad dispersibility used by curtain of the prior art, so that the adhesion property of ink is poor.
For this reason, it is necessary in view of the above-mentioned problems, propose a kind of screen coating material and preparation method thereof, can solve
Problems of the prior art.
The content of the invention
It is of the prior art to overcome it is an object of the invention to provide a kind of screen coating material and preparation method thereof
Deficiency.
To achieve the above object, the present invention provides following technical solution：
A kind of screen coating material, by mass percentage composition be：Water-based acrylic resin 40~50%, film-forming resin
10~15%, aluminium powder 1~2.5%, adhesive force promotes resin 5~12%, dispersant 2~5%, and levelling agent 0.1~0.5% disappears
Infusion 0.1~0.5%, curing agent 0.5~2%, ethyl alcohol 5~10%, glycerine 5~15%.
Preferably, composition is by mass percentage：Water-based acrylic resin 40~45%, film-forming resin 10~12.5%,
Aluminium powder 1.5~2.5%, adhesive force promote resin 5~7.5%, dispersant 2~3%, levelling agent 0.1~0.3%, antifoaming agent 0.1
~0.3%, curing agent 0.5~1.5%, ethyl alcohol 7.5~10%, glycerine 10~15%.
Preferably, composition is by mass percentage：Water-based acrylic resin 42.5~45%, film-forming resin 10~12%,
Adhesive force promotes resin 5~6%, ethyl alcohol 7.5~9%, glycerine 12.5~15%.
The present invention also provides a kind of preparation method of screen coating material, including：
(1) weigh 40~50% water-based acrylic resins, 1~2.5% aluminium powder, 5~12% adhesive force promote resin, 2~
5% dispersant, 0.1~0.5% levelling agent, 0.1~0.5% antifoaming agent, 0.5~2% curing agent, 5~10% ethyl alcohol, 5~
15% glycerine is invested in container for stirring mixing, makes its pre-dispersed uniformly, is subsequently placed in mixer, with 400~500r/
Min stirs 2~3h, obtains Ji Mo；
(2) it is 1~3 according to mass ratio with film-forming resin by above-mentioned base ink:1 is mixed, and 1~2h of magnetic agitation is obtained
To screen coating material.
Preferably, 40~45% water-based acrylic resins of (1) weighing, 1.5~2.5% aluminium powders, 5~7.5% attachments are made every effort to promote
Into resin, 2~3% dispersants, 0.1~0.3% levelling agent, 0.1~0.3% antifoaming agent, 0.5~1.5% curing agent, 7.5~
10% ethyl alcohol, 10~15% glycerine are invested in container for stirring mixing, make its pre-dispersed uniform, are subsequently placed in mixer,
2~3h is stirred with 400~500r/min, obtains Ji Mo；
(2) it is 1~2 according to mass ratio with film-forming resin by above-mentioned base ink:1 is mixed, and 1~2h of magnetic agitation is obtained
To screen coating material.
Compared with prior art, the advantage of the invention is that：Screen in the present invention has preferable point with coating material
Property is dissipated, and adhesive force and bending resistance are preferable.
Specific embodiment
The present invention is described further by the following example：According to following embodiments, the present invention may be better understood.
However, as it will be easily appreciated by one skilled in the art that the described specific material ratio of embodiment, process conditions and its result are only used
In illustrating the present invention, without the present invention described in detail in claims should will not be limited.
The present invention discloses a kind of screen coating material, and composition is by mass percentage：Water-based acrylic resin 40~
50%, film-forming resin 10~15%, aluminium powder 1~2.5%, adhesive force promotion resin 5~12%, dispersant 2~5%, levelling agent
0.1~0.5%, antifoaming agent 0.1~0.5%, curing agent 0.5~2%, ethyl alcohol 5~10%, glycerine 5~15%.
In an embodiment of the present invention, above-mentioned formula forms by mass percentage is：Water-based acrylic resin 40~45%,
Film-forming resin 10~12.5%, aluminium powder 1.5~2.5%, adhesive force promote resin 5~7.5%, dispersant 2~3%, levelling agent
0.1~0.3%, antifoaming agent 0.1~0.3%, curing agent 0.5~1.5%, ethyl alcohol 7.5~10%, glycerine 10~15%.
In still another embodiment of the process, above-mentioned formula forms by mass percentage is：Water-based acrylic resin 42.5~
45%, film-forming resin 10~12%, adhesive force promotes resin 5~6%, ethyl alcohol 7.5~9%, glycerine 12.5~15%.
Invention additionally discloses a kind of preparation method of screen coating material, including：
(1) weigh 40~50% water-based acrylic resins, 1~2.5% aluminium powder, 5~12% adhesive force promote resin, 2~
5% dispersant, 0.1~0.5% levelling agent, 0.1~0.5% antifoaming agent, 0.5~2% curing agent, 5~10% ethyl alcohol, 5~
15% glycerine is invested in container for stirring mixing, makes its pre-dispersed uniformly, is subsequently placed in mixer, with 400~500r/
Min stirs 2~3h, obtains Ji Mo；
(2) it is 1~3 according to mass ratio with film-forming resin by above-mentioned base ink:1 is mixed, and 1~2h of magnetic agitation is obtained
To screen coating material.
It is following to be illustrated with specifically embodiment, to prepare the screen coating material in the present invention.
Embodiment 1
(1) 40% water-based acrylic resin, 1% aluminium powder, 5% adhesive force are weighed and promotes resin, 2% dispersant, 0.1% stream
Flat agent, 0.1% antifoaming agent, 0.5% curing agent, 5% ethyl alcohol, 5% glycerine are invested in container for stirring mixing, make its pre- point
It dissipates uniformly, is subsequently placed in mixer, 2h is stirred with 400r/min, obtains Ji Mo；
(2) it is 1 according to mass ratio with film-forming resin by above-mentioned base ink:1 is mixed, and magnetic agitation 1h obtains screen
Use coating material.
Embodiment 2
(1) weigh 45% water-based acrylic resin, 1.5% aluminium powder, 7.5% adhesive force promote resin, 3% dispersant,
0.3% levelling agent, 0.3% antifoaming agent, 1.5% curing agent, 7.5% ethyl alcohol, 10% glycerine, are invested in container for stirring and mix
It closes, makes its pre-dispersed uniform, be subsequently placed in mixer, 2.5h is stirred with 450r/min, obtains Ji Mo；
(2) it is 2 according to mass ratio with film-forming resin by above-mentioned base ink:1 is mixed, and magnetic agitation 1.5h is obtained glimmering
Curtain coating material.
Embodiment 3
(1) weighing 42.5% water-based acrylic resin, 1.75% aluminium powder, 10% adhesive force promotes resin, 2.5% to disperse
Agent, 0.25% levelling agent, 0.25% antifoaming agent, 1% curing agent, 6% ethyl alcohol, 7.5% glycerine, are invested in container for stirring and mix
It closes, makes its pre-dispersed uniform, be subsequently placed in mixer, 2.5h is stirred with 450r/min, obtains Ji Mo；
(2) it is 1.5 according to mass ratio with film-forming resin by above-mentioned base ink:1 is mixed, and 1~2h of magnetic agitation is obtained
Screen coating material.
Embodiment 4
(1) weigh 50% water-based acrylic resin, 2.5% aluminium powder, 12% adhesive force promote resin, 5% dispersant,
0.5% levelling agent, 0.5% antifoaming agent, 2% curing agent, 10% ethyl alcohol, 15% glycerine are invested in container for stirring mixing, make
Its is pre-dispersed uniform, is subsequently placed in mixer, stirs 3h with 500r/min, obtains Ji Mo；
(2) it is 3 according to mass ratio with film-forming resin by above-mentioned base ink:1 is mixed, and magnetic agitation 2h obtains screen
Use coating material.
A series of experiment is carried out by the adhesive force to ink in the present invention and bending resistance, the results showed that, according to upper
State the screen that the method in each embodiment is prepared has preferable dispersiveness, and adhesive force and bending resistance with coating material
Preferably.
Finally, it is to be noted that, term " comprising ", "comprising" or its any other variant be intended to it is non-exclusive
Property include so that process, method, article or equipment including a series of elements not only include those elements, but also
Further include other elements that are not explicitly listed or further include for this process, method, article or equipment it is intrinsic
Element.
Claims (5)
1. a kind of screen coating material, which is characterized in that composition is by mass percentage：Water-based acrylic resin 40~
50%, film-forming resin 10~15%, aluminium powder 1~2.5%, adhesive force promotion resin 5~12%, dispersant 2~5%, levelling agent
0.1~0.5%, antifoaming agent 0.1~0.5%, curing agent 0.5~2%, ethyl alcohol 5~10%, glycerine 5~15%.
2. screen coating material according to claim 1, which is characterized in that composition is by mass percentage：Aqueous third
Olefin(e) acid resin 40~45%, film-forming resin 10~12.5%, aluminium powder 1.5~2.5%, adhesive force promote resin 5~7.5%, point
Powder 2~3%, levelling agent 0.1~0.3%, antifoaming agent 0.1~0.3%, curing agent 0.5~1.5%, ethyl alcohol 7.5~10%,
Glycerine 10~15%.
3. screen coating material according to claim 2, which is characterized in that composition is by mass percentage：Aqueous third
Olefin(e) acid resin 42.5~45%, film-forming resin 10~12%, adhesive force promote resin 5~6%, ethyl alcohol 7.5~9%, glycerine
12.5~15%.
4. a kind of preparation method of screen coating material, which is characterized in that including：
(1) weigh 40~50% water-based acrylic resins, 1~2.5% aluminium powder, 5~12% adhesive force promote resin, 2~5% points
Powder, 0.1~0.5% levelling agent, 0.1~0.5% antifoaming agent, 0.5~2% curing agent, 5~10% ethyl alcohol, 5~15% the third three
Alcohol is invested in container for stirring mixing, makes its pre-dispersed uniform, is subsequently placed in mixer, 2 are stirred with 400~500r/min
~3h, obtains Ji Mo；
(2) it is 1~3 according to mass ratio with film-forming resin by above-mentioned base ink:1 is mixed, and 1~2h of magnetic agitation is obtained glimmering
Curtain coating material.
5. the preparation method of screen coating material according to claim 4, which is characterized in that including：
(1) weigh 40~45% water-based acrylic resins, 1.5~2.5% aluminium powders, 5~7.5% adhesive force promote resin, 2~
3% dispersant, 0.1~0.3% levelling agent, 0.1~0.3% antifoaming agent, 0.5~1.5% curing agent, 7.5~10% ethyl alcohol, 10
~15% glycerine is invested in container for stirring mixing, make its it is pre-dispersed be uniformly subsequently placed in mixer, with 400~
500r/min stirs 2~3h, obtains Ji Mo；
(2) it is 1~2 according to mass ratio with film-forming resin by above-mentioned base ink:1 is mixed, and 1~2h of magnetic agitation is obtained glimmering
Curtain coating material.