CN102533066A - Manufacturing method of silver gray matt projection/writing board and manufacturing method of baking coating thereof - Google Patents
Manufacturing method of silver gray matt projection/writing board and manufacturing method of baking coating thereof Download PDFInfo
- Publication number
- CN102533066A CN102533066A CN2011103833507A CN201110383350A CN102533066A CN 102533066 A CN102533066 A CN 102533066A CN 2011103833507 A CN2011103833507 A CN 2011103833507A CN 201110383350 A CN201110383350 A CN 201110383350A CN 102533066 A CN102533066 A CN 102533066A
- Authority
- CN
- China
- Prior art keywords
- acrylic acid
- acid resin
- agent
- coating
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a manufacturing method of a silver gray matt projection/writing board and a manufacturing method of a baking coating thereof. By adopting the product, the teaching writing needs of the traditional board writing can be satisfied, and the needs of interactive teaching via the modern information technology multimedia projection can also be satisfied. When the product is used together with easy-to-wipe teaching writing ink, the serious problem of dust pollution caused by use of chalks in teaching in the majority of schools in China can be solved completely, and the healthy school construction in China can be promoted. The baking coating comprises resin, pigments, additives, solvents and the like. The coating is coated on a galvanized steel plate and baked at high temperature of 240-260DEG C for formation. Therefore, the product has a tough coating, good wear resistance, good chemical resistance, strong adhesion and good matt effects. When the product is used together with the easy-to-wipe teaching writing ink, the advantages of smooth writing, easy wiping, no dust pollution and long service life can be realized. The color of the product is soft, so that students can maintain good visual and mental state. During the long-term use, the product is conducive to the health of teachers and students.
Description
Technical field
The making method that the present invention relates to the inferior light projection writing of a kind of silver gray plate with and the making method of baked paint.
Background technology
At present, the ubiquitous problem of blackboard for education and the drawback of the use of the vast school of China are broadly divided into following several kinds:
(1) blank and beige board get into the classroom to be used for teaching writing are the color requirements that does not meet the blackboard safety and health request industry standard (WS99-1998) of Ministry of Health's promulgation, and life-time service influences student's eyesight.
(2) chalk that in teaching process, adopts is write and is produced a large amount of dust, has a strong impact on teachers and students' physical and mental health.
(3) part school uses blank and beige board, and such clipboard gloss is high, influences the student and looks and see, and influenced teaching efficiency.
(4) also have minority school to use pad pasting (green, yellow etc.), bonding strength is poor, unfairness, not attractive in appearance, work-ing life short, writing effect is poor, influence is imparted knowledge to students.
Summary of the invention
To above problem and drawback, the making method that the present invention provides the inferior light projection writing of a kind of silver gray plate with and the making method of baked paint.
For achieving the above object, the inferior light projection writing of silver gray of the present invention plate is characterized in that with the making method of baked paint it is processed according to following method:
1) batching;
Accurately metering, and take off the raw material of stating weight part in order: vibrin D1554-55 part; Acrylic acid Resin A 1454-35 part; Acrylic acid resin XP26454-35 part; Disponer904 dispersion agent 0.5-5 part, Disponer983 dispersion agent 0.5-5 part, anti-settling agent 1-10 part, solvent 5-20 part is metered in the agitation vat respectively;
Temperature is controlled at less than 40 ℃ and stirs; Add carbon black FW-2000.1-2.5 part by formula ratio successively in the whipping process, phthalocyanine blue b F4010.1-5 part, Phthalocyanine Green G 5339D 0.1-5 part; Phthalocyanine Green G 5309H 0.1-5 part was stirred after 10 minutes; Add white titanium pigment TR8110-60 part again, anti-settling agent 1-10 part continues to stir 20 minutes;
The above-mentioned material that stirs is ground;
2) preparation blender;
Take off the raw material of stating weight part: vibrin D1554-55 part; Acrylic acid Resin A 1454-35 part, acrylic acid resin XP26454-35 part, aminoresin VPLS21531-30 part; Flow agent 0.1-5 part; Sticking power promotor 0.1-3 part, curing catalyst Catacure KC 1-4 part, solvent 5-45 part; Be metered in the agitation vat respectively and stir;
3) allotment coating: get above-mentioned mill base 30-60 part, blender 40-70 part by weight, under agitation add flatting silica HP340M 1-20 part, be stirred into the coating of predetermined viscosity, finished product.
For achieving the above object, the making method of the inferior light projection writing of silver gray of the present invention plate is characterized in that it is processed according to following method:
1) batching;
Accurately metering, and take off the raw material of stating weight part in order: vibrin D1554-55 part; Acrylic acid Resin A 1454-35 part; Acrylic acid resin XP26454-35 part; Disponer904 dispersion agent 0.5-5 part, Disponer983 dispersion agent 0.5-5 part, anti-settling agent 1-10 part, solvent 5-20 part is metered in the agitation vat respectively and stirs;
Temperature is controlled at less than 40 ℃; Add carbon black FW-2000.1-2.5 part by formula ratio successively, phthalocyanine blue b F4010.1-5 part, Phthalocyanine Green G 5339D 0.1-5 part; Phthalocyanine Green G 5309H 0.1-5 part was stirred after 10 minutes; Add white titanium pigment TR8110-60 part again, anti-settling agent 1-10 part continues to stir 20 minutes;
The above-mentioned material that stirs is ground;
2) preparation blender;
Take off the raw material of stating weight part: vibrin D1554-55 part; Acrylic acid Resin A 1454-35 part, acrylic acid resin XP26454-35 part, aminoresin VPLS21531-30 part; Flow agent 0.1-5 part; Sticking power promotor 0.1-3 part, curing catalyst Catacure KC 1-4 part, solvent 5-45 part; Be metered in the agitation vat respectively and stir;
3) allotment coating: get above-mentioned mill base 70-90 part, blender 10-25 part by weight, under agitation add flatting silica HP340M 1-20 part, be stirred into the coating of predetermined viscosity;
4) above-mentioned coating is coated on the steel plate galvanized,, is finished product through 240 ℃ of-260 ℃ of high bake moulding.
Coating of the present invention has following outstanding advantage:
(1) color is a silver gray, and color and luster is soft, and avidity is strong, makes the student can keep good visual psychology state.Meet of the requirement of the blackboard safety and sanitation industry standard (WS99-1998) of the health ministry and Board of Education promulgation fully to the blackboard color.
(2) use the protecting teaching writing board after this coating applies to have tough and tensile, the strong adhesion of filming; Supporting use environment protection liquid lettering pen is write easy wiping, fluent writing well, and long service life thoroughly solves the advantages such as dust pollution in the teaching writing process.
(3) use the protecting teaching writing board gloss after this coating applies low, make the student keep good visual effect.
Adopt above-mentioned coating to be coated on the existing steel blackboard, blackboard for education has tough and tensile, the strong adhesion, not reflective of filming; Supporting use environment-friendly liquid lettering pen is write advantages such as easy wiping, fluent writing, no dust pollution, long service life well; Color and luster is soft, makes the student can keep good visual psychology state, and life-time service does not damage student eyesight; Help teachers and students' physical and mental health.
Embodiment
Below in conjunction with embodiment the present invention is done explanation further.
The inferior light projection writing of silver gray of the present invention plate is used mill base with baked paint, is processed by the raw material of following weight parts:
1) batching;
Accurately metering, and take off the raw material of stating weight part in order: vibrin D1554-55 part; Acrylic acid Resin A 1454-35 part; Acrylic acid resin XP26454-35 part; Disponer904 dispersion agent 0.5-5 part, Disponer983 dispersion agent 0.5-5 part, anti-settling agent 1-10 part, solvent 5-20 part is metered in the agitation vat respectively;
Temperature is controlled at less than 40 ℃ and stirs; Add carbon black FW-2000.1-2.5 part by formula ratio successively in the whipping process, phthalocyanine blue b F4010.1-5 part, Phthalocyanine Green G 5339D 0.1-5 part; Phthalocyanine Green G 5309H 0.1-5 part was stirred after 10 minutes; Add white titanium pigment TR8110-60 part again, anti-settling agent 1-10 part continues to stir 20 minutes;
The above-mentioned material that stirs is ground;
2) preparation blender;
Take off the raw material of stating weight part: vibrin D1554-55 part; Acrylic acid Resin A 1454-35 part, acrylic acid resin XP26454-35 part, aminoresin VPLS21531-30 part; Flow agent 0.1-5 part; Sticking power promotor 0.1-3 part, curing catalyst Catacure KC 1-4 part, solvent 5-45 part; Be metered in the agitation vat respectively and stir;
3) allotment coating: get above-mentioned mill base 30-60 part, blender 40-70 part by weight, under agitation add flatting silica HP340M 1-20 part, be stirred into the coating of predetermined viscosity, finished product.
(1) batching
Accurately metering, and take off the raw material of stating weight part in order: vibrin D1556-60 part; Acrylic acid Resin A 1456-60 part; Acrylic acid resin XP26456-60 part; , Disponer904 dispersion agent 0.5-5 part, Disponer983 dispersion agent 0.5-5 part, anti-settling agent 1-10 part, solvent 5-20 part is metered in the agitation vat respectively.
After various resins, solvent and various auxiliary agent mixed thoroughly, start height and stir machine, open water coolant simultaneously; Temperature is controlled at less than 40 ℃, adds carbon black FW-2000.1-2.5 part by formula ratio successively, phthalocyanine blue b F4010.1-5 part; Phthalocyanine Green G 5339D 0.1-5 part, Phthalocyanine Green G 5309H 0.1-5 part was stirred after 10 minutes, added white titanium pigment TR8110-65 part again; Anti-settling agent 1-10 part continues to stir 20 minutes, to the surface of pigments complete wetting; After becoming even pasty state and not having dry colour, stop to stir, close water coolant.
It is subsequent use that the above-mentioned material that stirs is ground to the regulation fineness.
2) preparation blender;
Take off the raw material of stating weight part: vibrin D1554-55 part; Acrylic acid Resin A 1454-35 part, acrylic acid resin XP26454-35 part, aminoresin VPLS21531-30 part; Flow agent 0.1-5 part; Sticking power promotor 0.1-3 part, curing catalyst Catacure KC 1-4 part, solvent 5-45 part; Be metered in the agitation vat respectively and stir;
3) allotment coating: get above-mentioned mill base 30-60 part, blender 40-70 part by weight, under agitation add flatting silica HP340M 1-20 part, be stirred into the coating of predetermined viscosity, finished product.
Wherein, in the above-mentioned raw materials, what of each pigment can determine the depth of color, and pigment what therefore can increase as required.The effect of resin, auxiliary agent and solvent mainly is the viscosity and the set time of control paint film; The increase and decrease of aminoresin; Can regulate the performance (hardness, sticking power, wear resistance, solvent resistance) of filming, those of ordinary skill in the art can adjust as required.
Above-mentioned raw materials market is all on sale, wherein
1) vibrin D155, acrylic acid Resin A 145, acrylic acid resin XP2645 and aminoresin VPLS2153 are that Bayer material science and technology trade (Shanghai) Co., Ltd. produces;
2) flow agent, sticking power promotor, anti-settling agent; Disponer904 dispersion agent, Disponer983 dispersion agent, flatting silica HP340M are that favour just capable chemical industry ltd in Shanghai sells
3) white titanium pigment TIOXIDE TR81; Carbon black FW-200 Guangzhou China Guangdong industry development company sells.
4) phthalocyanine blue b F401; Phthalocyanine Green G 5339D; Phthalocyanine Green G 5309H: Jiangsu Yabang Chemical Group Co., Ltd
5) solvent 5-45 part: Jiangsu Miki Group
6) curing catalyst Catacure KC produces for Taiwan Deuchem Co., Ltd.
According to embodiment the present invention is done explanation further below.
Embodiment 1
(1) batching
Accurately metering, and take off the raw material of stating weight part in order: vibrin D15530 part; 1456 parts of acrylic acid Resin A; Acrylic acid resin XP26454 part; , 0.5 part of Disponer904 dispersion agent, 0.5 part of Disponer983 dispersion agent, 1 part of anti-settling agent, 7.3 parts of solvents are metered in the agitation vat respectively.
(2) spice
After earlier various resins, solvent and various auxiliary agent being mixed thoroughly, start height again and stir machine, open water coolant simultaneously, temperature is controlled at less than 40 ℃; Add carbon black FW-2000.1 part by formula ratio successively, phthalocyanine blue b F4010.1 part, 0.2 part of Phthalocyanine Green G 5339D; Phthalocyanine Green G 5309H stirs after 10 minutes for 0.2 part, adds white titanium pigment TR8150 part again, 1 part of anti-settling agent; 7.3 parts of solvents continue to stir 20 minutes, to the surface of pigments complete wetting; After becoming even pasty state and not having dry colour, stop to stir, close water coolant.
(3) grind
Be ground to the regulation fineness, subsequent use, and equipment and instrument cleaned up.
(4) preparation blender;
Accurately metering, and take off the raw material of stating weight part in order: vibrin D15550 part, 14530 parts of acrylic acid Resin A; Acrylic acid resin XP264530 part, aminoresin VPLS215330 part, 5 parts of flow agents; 3 parts of sticking power promotors, 4 parts of curing catalyst Catacure KC, 40 parts of solvents; Be metered in the agitation vat respectively and stir;
(5) allotment coating: get 50 parts of above-mentioned mill bases, 50 parts of blenders by weight, under agitation add 10 parts of flatting silica HP340M, be stirred into the coating of predetermined viscosity, finished product.
Embodiment 2
(1) batching
Accurately metering, and take off the raw material of stating weight part in order: vibrin D15520 part; 1455 parts of acrylic acid Resin A; Acrylic acid resin XP26455 part; , 0.5 part of Disponer904 dispersion agent, 0.5 part of Disponer983 dispersion agent, 1 part of anti-settling agent, 7.4 parts of solvents are metered in the agitation vat respectively.
(2) spice
After earlier various resins, solvent and various auxiliary agent being mixed thoroughly, start height again and stir machine, open water coolant simultaneously, temperature is controlled at less than 40 ℃; Add carbon black FW-2000.2 part by formula ratio successively, phthalocyanine blue b F4010.2 part, 0.1 part of Phthalocyanine Green G 5339D, Phthalocyanine Green G 5309H stirs after 10 minutes for 0.1 part; Add white titanium pigment TR8160 part again, continue to stir 20 minutes, to the surface of pigments complete wetting; After becoming even pasty state and not having dry colour, stop to stir, close water coolant.
(3) grind
Be ground to the regulation fineness, subsequent use, and equipment and instrument cleaned up.
(4) preparation blender;
Accurately metering, and take off the raw material of stating weight part in order: vibrin D15530 part, 14520 parts of acrylic acid Resin A; Acrylic acid resin XP264520 part, aminoresin VPLS215320 part, 2 parts of flow agents; 2 parts of sticking power promotors, 4 parts of curing catalyst Catacure KC, 40 parts of solvents; Under condition of stirring, be metered into respectively in the agitation vat, stirred about 30 minutes, can become blending agents.
(5) allotment coating: get 30 parts of above-mentioned mill bases, 40 parts of blenders by weight, under agitation add 5 parts of flatting silica HP340M, be stirred into the coating of predetermined viscosity, finished product.
Embodiment 3
(1) batching
Accurately metering, and take off the raw material of stating weight part in order: vibrin D15525 part; 1458 parts of acrylic acid Resin A; Acrylic acid resin XP26455 part; , 0.2 part of Disponer904 dispersion agent, 0.5 part of Disponer983 dispersion agent, 1 part of anti-settling agent, 6 parts of solvents are metered in the agitation vat respectively.
(2) spice
After earlier various resins, solvent and various auxiliary agent being mixed thoroughly, start height again and stir machine, open water coolant simultaneously, temperature is controlled at less than 40 ℃; Add carbon black FW-2000.1 part by formula ratio successively, phthalocyanine blue b F4010.3 part, 0.1 part of Phthalocyanine Green G 5339D; Phthalocyanine Green G 5309H stirs after 10 minutes for 0.1 part, adds white titanium pigment TR8140 part again, anti-settling agent 1-10 part; Continue to stir 20 minutes, to the surface of pigments complete wetting, after becoming even pasty state and not having dry colour; Stop to stir, close water coolant, about about 30 minutes altogether.
(3) grind
Be ground to the regulation fineness, subsequent use.
(4) preparation blender;
Accurately metering, and take off the raw material of stating weight part in order: vibrin D15534 part, 1455 parts of acrylic acid Resin A; Acrylic acid resin XP264510 part, aminoresin VPLS215325,0.1 part of flow agent; 0.5 part of sticking power promotor, 2 parts of curing catalyst Catacure KC; 23.4 parts of solvents;
Under condition of stirring, be metered into respectively in the agitation vat, stirred about 25 minutes, can become blending agents.
(5) allotment coating: get 40 parts of above-mentioned mill bases, 43 parts of blenders by weight, the P340M flatting silica is metered into respectively in the agitation vat under condition of stirring for 17 parts, stirs about 30 minutes, promptly can be finished product.
Adopt the made clipboard of coating of present embodiment, two in Chongqing middle schools of process are trying out of totally 24 classes, adopt common blank pen to write advantages such as easy wiping, fluent writing, no dust pollution, long service life well; Color and luster is soft.
With the making method of the similar silver gray low light of the invention described above book plate, it is characterized in that it is processed according to following method with baked paint:
1) preparation mill base;
Its concrete steps are to take off the raw material of stating weight part:
Vibrin 6-60 part, acrylic acid resin 12-120 part, aminoresin 1-30 part, wax powder 0.1-20 part, white titanium pigment 10-60 part; Carbon black 0.1-2.5 part, iron oxide yellow 0.1-5 part, phthalocyanine blue 0.1-5 part, phthalocyanine green 0.2-10 part, talcum powder 2-15 part; Permanent white 1-8 part, lime carbonate 1-8 part, matting agent 1-20 part, dispersion agent 1-10 part; Flow agent 0.1-5 part, sticking power promotor 0.1-3 part, anti-settling agent 1-10 part, solvent 5-45 part;
With stirring after above-mentioned each raw materials mix, and the above-mentioned raw material that stirs is ground to the regulation fineness;
2) preparation blender;
Its concrete steps are: take off the raw material of stating weight part: acrylic acid resin 6-60 part, flow agent 0.1-5 part, solvent 5-45 part;
3) allotment coating: get above-mentioned mill base 75-90 part, blender 10-25 part by weight, be stirred into the coating of processing predetermined viscosity, finished product.
Embodiment 4
1) preparation mill base;
Its concrete steps are to take off the raw material of stating weight part:
50 parts in vibrin, 36 parts of acrylic acid resins, 20 parts in aminoresin, 10 parts in wax powder, 10 parts of white titanium pigments; 2.5 parts of carbon blacks, 4 parts of iron oxide yellows, 45 parts of phthalocyanine blues, 6 parts of phthalocyanine greens, 8 parts of talcum powder; 6 parts in permanent white, 6 parts in lime carbonate, 10 parts of matting agents, 5 parts of dispersion agents; 4 parts of flow agents, 2 parts of sticking power promotors, 8 parts of anti-settling agents, 40 parts of solvents;
With stirring after above-mentioned each raw materials mix, and the above-mentioned raw material that stirs is ground to the regulation fineness;
2) preparation blender;
Its concrete steps are: take off the raw material of stating weight part: 50 parts of acrylic acid resins, 4 parts of flow agents, 40 parts of solvents;
3) allotment coating: get 80 parts of above-mentioned mill bases, 20 parts of blenders by weight, be stirred into the coating of processing predetermined viscosity, finished product.
Above-mentioned mill base also can be by the preparation of raw material of following weight parts:
Vibrin 506116-60 part, acrylic acid resin 92206-60 part, acrylic acid resin 26016-60 part, aminoresin 1-30, wax powder 0.1-20; White titanium pigment 10-60 part, carbon black 0.1-2.5 part, iron oxide yellow 0.1-5 part, phthalocyanine blue 0.1-5 part; Phthalocyanine green 53190.1-5 part, phthalocyanine green 53400.1-5 part, talcum powder 2-15 part, permanent white 1-8 part; Lime carbonate 1-8 part, matting agent 1-20 part, dispersion agent 50270.5-5 part, dispersion agent 50400.5-5 part; Flow agent 0.1-5 part, sticking power promotor 0.1-3 part, anti-settling agent 1-10 part, solvent 5-45 part.
Can know that to sum up coating of the present invention can be used for the steel blackboard, adopt above-mentioned coating to be coated on the steel blackboard, blackboard has tough and tensile, the strong adhesion, not reflective of filming; Supporting use environment-friendly liquid lettering pen is write advantages such as easy wiping, fluent writing, no dust pollution, long service life well; Color and luster is soft, makes the student can keep good visual psychology state, and life-time service does not damage student eyesight.
Obviously, those skilled in the art can carry out various changes and not break away from spirit of the present invention prescription of the present invention.If therefore these changes belong in claims of the present invention and the equivalent technologies scope thereof, then the present invention also is intended to contain these changes.
Claims (4)
1. the inferior light projection/clipboard of a silver gray is characterized in that with the making method of baked paint it is processed according to following method:
1) batching;
Accurately metering, and take off the raw material of stating weight part in order: vibrin D1554-55 part; Acrylic acid Resin A 1454-35 part; Acrylic acid resin XP26454-35 part; Disponer904 dispersion agent 0.5-5 part, Disponer 983 dispersion agent 0.5-5 parts, anti-settling agent 1-10 part, solvent 5-20 part is metered in the agitation vat respectively;
Temperature is controlled at less than 40 ℃ and stirs; Add carbon black FW-2000.1-2.5 part by formula ratio successively in the whipping process, phthalocyanine blue b F4010.1-5 part, Phthalocyanine Green G 5339D 0.1-5 part; Phthalocyanine Green G 5309H 0.1-5 part was stirred after 10 minutes; Add white titanium pigment TR8110-60 part again, anti-settling agent 1-10 part continues to stir 20 minutes;
The above-mentioned material that stirs is ground;
2) preparation blender;
Take off the raw material of stating weight part: vibrin D1554-55 part; Acrylic acid Resin A 1454-35 part, acrylic acid resin XP26454-35 part, aminoresin VPLS21531-30 part; Flow agent 0.1-5 part; Sticking power promotor 0.1-3 part, curing catalyst Catacure KC 1-4 part, solvent 5-45 part; Be metered in the agitation vat respectively and stir;
3) allotment coating: get above-mentioned mill base 30-60 part, blender 40-70 part by weight, under agitation add flatting silica HP340M 1-20 part, be stirred into the coating of predetermined viscosity, finished product.
2. the making method of the inferior light projection/clipboard of a silver gray is characterized in that it is processed according to following method:
1) batching;
Accurately metering, and take off the raw material of stating weight part in order: vibrin D1554-55 part; Acrylic acid Resin A 1454-35 part; Acrylic acid resin XP26454-35 part; Disponer904 dispersion agent 0.5-5 part, Disponer 983 dispersion agent 0.5-5 parts, anti-settling agent 1-10 part, solvent 5-20 part is metered in the agitation vat respectively and stirs;
Temperature is controlled at less than 40 ℃; Add carbon black FW-2000.1-2.5 part by formula ratio successively, phthalocyanine blue b F4010.1-5 part, Phthalocyanine Green G 5339D 0.1-5 part; Phthalocyanine Green G 5309H 0.1-5 part was stirred after 10 minutes; Add white titanium pigment TR8110-60 part again, anti-settling agent 1-10 part continues to stir 20 minutes;
The above-mentioned material that stirs is ground;
2) preparation blender;
Take off the raw material of stating weight part: vibrin D1554-55 part, acrylic acid Resin A 1454-35 part, acrylic acid resin XP26454-35 part; Aminoresin VPLS21531-30 part, flow agent 0.1-5 part, sticking power promotor 0.1-3 part; Curing catalyst Catacure KC 1-4 part, solvent
5-45 part; Be metered in the agitation vat respectively and stir;
3) allotment coating: get above-mentioned mill base 70-90 part, blender 10-25 part by weight, under agitation add flatting silica HP340M 1-20 part, be stirred into the coating of predetermined viscosity;
4) above-mentioned coating is coated on the steel plate galvanized,, is finished product through 240 ℃ of-260 ℃ of high bake moulding.
3. a silver gray clipboard is characterized in that with the making method of baked paint it is processed according to following method:
1) preparation mill base;
Its concrete steps are to take off the raw material of stating weight part:
Vibrin 6-60 part, acrylic acid resin 12-120 part, aminoresin 1-30 part, wax powder 0.1-20 part, white titanium pigment 10-60 part; Carbon black 0.1-2.5 part, iron oxide yellow 0.1-5 part, phthalocyanine blue 0.1-5 part, phthalocyanine green 0.2-10 part, talcum powder 2-15 part; Permanent white 1-8 part, lime carbonate 1-8 part, matting agent 1-20 part, dispersion agent 1-10 part; Flow agent 0.1-5 part, sticking power promotor 0.1-3 part, anti-settling agent 1-10 part, solvent 5-45 part;
With stirring after above-mentioned each raw materials mix, and the above-mentioned raw material that stirs is ground to the regulation fineness;
2) preparation blender;
Its concrete steps are: take off the raw material of stating weight part: acrylic acid resin 6-60 part, flow agent 0.1-5 part, solvent 5-45 part;
3) allotment coating: get above-mentioned mill base 75-90 part, blender 10-25 part by weight, be stirred into the coating of processing predetermined viscosity, finished product.
4. silver gray clipboard as claimed in claim 3 is characterized in that with the making method of baked paint it is processed according to following method:
Described mill base is the preparation of raw material by following weight parts:
Vibrin 506116-60 part, acrylic acid resin 92206-60 part, acrylic acid resin 2601 6-60 parts, aminoresin 1-30, wax powder 0.1-20; White titanium pigment 10-60 part, carbon black 0.1-2.5 part, iron oxide yellow 0.1-5 part, phthalocyanine blue 0.1-5 part; Phthalocyanine green 53190.1-5 part, phthalocyanine green 53400.1-5 part, talcum powder 2-15 part, permanent white 1-8 part; Lime carbonate 1-8 part, matting agent 1-20 part, dispersion agent 50270.5-5 part, dispersion agent 50400.5-5 part; Flow agent 0.1-5 part, sticking power promotor 0.1-3 part, anti-settling agent 1-10 part, solvent 5-45 part.