CN107841240A - A kind of projection screen coating material and preparation method thereof - Google Patents
A kind of projection screen coating material and preparation method thereof Download PDFInfo
- Publication number
- CN107841240A CN107841240A CN201711115712.8A CN201711115712A CN107841240A CN 107841240 A CN107841240 A CN 107841240A CN 201711115712 A CN201711115712 A CN 201711115712A CN 107841240 A CN107841240 A CN 107841240A
- Authority
- CN
- China
- Prior art keywords
- parts
- projection screen
- defoamer
- coating material
- screen coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of projection screen coating material, wherein, the formula composition of the ink is:80~100 parts of silicones, 20~30 parts of titanium dioxide, 5~10 parts of silicon dioxide powder, 2~5 parts of alundum (Al2O3), 0.2~0.5 part of sodium oxide molybdena, 5~15 parts of magnesium silicate, 1~2 part of magnesia, 1.25~2.5 parts of curing agent, 0.25~1 part of defoamer, 0.75~1.25 part of levelling agent.The invention also discloses the preparation method of above-mentioned projection screen ink.The excellent heat stability of projection screen ink in the present invention, adhesive force are good, have preferable application prospect.
Description
Technical field
The present invention relates to field of ink manufacture, more particularly to a kind of projection screen coating material and preparation method thereof.
Background technology
Projection screen used in existing market is usually white modeling cloth, generally requires to use ink for screen printing in preparation technology,
Ink is printed onto on projection screen using screen printing mode, then using solidification measure so that projection screen is firmly prolonged
It is durable.
But existing ink for screen printing heat endurance and poor adhesive force, service life is short, easily comes off, and silk-screen surface
It is coarse thus greatly to add production cost, it is necessary to can be only achieved preferable coverage effect using substantial amounts of ink, without
Ji, and cause the waste of raw material.
For this reason, it is necessary in view of the above-mentioned problems, a kind of projection screen coating material and preparation method thereof is proposed, it can
Solve problems of the prior art.
The content of the invention
It is an object of the invention to provide a kind of projection screen coating material and preparation method thereof, to overcome prior art
In deficiency.
To achieve the above object, the present invention provides following technical scheme:
A kind of projection screen coating material, by weight composition are:80~100 parts of silicones, 20~30 parts of titanium dioxide,
5~10 parts of silicon dioxide powder, 2~5 parts of alundum (Al2O3), 0.2~0.5 part of sodium oxide molybdena, 5~15 parts of magnesium silicate, magnesia 1~2
Part, 1.25~2.5 parts of curing agent, 0.25~1 part of defoamer, 0.75~1.25 part of levelling agent.
Preferably, composition is by weight:80~90 parts of silicones, 25~30 parts of titanium dioxide, 5~8 parts of silicon dioxide powder,
3~5 parts of alundum (Al2O3), 0.2~0.3 part of sodium oxide molybdena, 5~10 parts of magnesium silicate, 1.5~2 parts of magnesia, curing agent 1.75~
2.5 parts, 0.25~0.75 part of defoamer, 1~1.25 part of levelling agent.
Preferably, composition is by weight:85~90 parts of silicones, 28~30 parts of titanium dioxide, 5~6 parts of silicon dioxide powder,
3~4 parts of alundum (Al2O3), 0.25~0.3 part of sodium oxide molybdena, 7.5~10 parts of magnesium silicate, 1.75~2 parts of magnesia, curing agent 1.75
~2 parts, 0.25~0.5 part of defoamer, 1.1~1.25 parts of levelling agent.
Preferably, the curing agent is cyanogen spy's resin CYMEL303, and the defoamer is organic silicon defoamer, the stream
Flat agent is esters of acrylic acid levelling agent.
The present invention also provides a kind of preparation method of projection screen coating material, including:
(1) by 80~100 parts of silicones, 5~10 parts of silicon dioxide powders, 2~5 parts of alundum (Al2O3)s, 0.2~0.5 part of oxygen
Change sodium mixing, 10~15min of ultrasonic disperse, add 20~30 parts of titanium dioxides, 5~15 parts of magnesium silicates, 1~2 part of magnesia, stir
Mix uniformly, 20~30min of ultrasonic disperse, obtain mixture;
(2) 1.25~2.5 parts of curing agent, 0.25~1 part of defoamer, 0.75~1.25 part of stream are added into said mixture
Flat agent, 20~30min of sonic oscillation, 2~3h is stirred, add bead and grind 5~8h, filtering, you can obtain projection screen use
Ink.
Compared with prior art, the advantage of the invention is that:The heat endurance of projection screen ink in the present invention is excellent
It is different, adhesive force is good, there is preferable application prospect.
Embodiment
The present invention is described further by the following example:According to following embodiments, the present invention may be better understood.
However, as it will be easily appreciated by one skilled in the art that specific material ratio, process conditions and its result described by embodiment are only used
In the explanation present invention, without should be also without limitation on the present invention described in detail in claims.
The present invention discloses a kind of projection screen coating material, and composition is by weight:80~100 parts of silicones, titanium white
20~30 parts of powder, 5~10 parts of silicon dioxide powder, 2~5 parts of alundum (Al2O3), 0.2~0.5 part of sodium oxide molybdena, 5~15 parts of magnesium silicate,
1~2 part of magnesia, 1.25~2.5 parts of curing agent, 0.25~1 part of defoamer, 0.75~1.25 part of levelling agent.
In an embodiment of the present invention, above-mentioned formula composition is:80~90 parts of silicones, titanium dioxide 25~30
Part, 5~8 parts of silicon dioxide powder, 3~5 parts of alundum (Al2O3), 0.2~0.3 part of sodium oxide molybdena, 5~10 parts of magnesium silicate, magnesia 1.5
~2 parts, 1.75~2.5 parts of curing agent, 0.25~0.75 part of defoamer, 1~1.25 part of levelling agent.
In still another embodiment of the process, above-mentioned formula composition is:85~90 parts of silicones, titanium dioxide 28~
30 parts, 5~6 parts of silicon dioxide powder, 3~4 parts of alundum (Al2O3), 0.25~0.3 part of sodium oxide molybdena, 7.5~10 parts of magnesium silicate, oxidation
1.75~2 parts of magnesium, 1.75~2 parts of curing agent, 0.25~0.5 part of defoamer, 1.1~1.25 parts of levelling agent.
Wherein, the curing agent is cyanogen spy's resin CYMEL303, and the defoamer is organic silicon defoamer, the levelling
Agent is esters of acrylic acid levelling agent.
Invention additionally discloses a kind of preparation method of projection screen coating material, including:
(1) by 80~100 parts of silicones, 5~10 parts of silicon dioxide powders, 2~5 parts of alundum (Al2O3)s, 0.2~0.5 part of oxygen
Change sodium mixing, 10~15min of ultrasonic disperse, add 20~30 parts of titanium dioxides, 5~15 parts of magnesium silicates, 1~2 part of magnesia, stir
Mix uniformly, 20~30min of ultrasonic disperse, obtain mixture;
(2) 1.25~2.5 parts of curing agent, 0.25~1 part of defoamer, 0.75~1.25 part of stream are added into said mixture
Flat agent, 20~30min of sonic oscillation, 2~3h is stirred, add bead and grind 5~8h, filtering, you can obtain projection screen use
Ink.
Embodiment
1st, projection screen ink is prepared
(1) 85 parts of silicones, 5 parts of silicon dioxide powders, 2.5 parts of alundum (Al2O3)s, 0.25 part of sodium oxide molybdena are mixed, ultrasound point
15min is dissipated, 30 parts of titanium dioxides, 6 parts of magnesium silicates, 1.75 parts of magnesia is added, stirs, ultrasonic disperse 25min, mixed
Compound;
(2) 1.75 parts of cyanogen spy's resin CYMEL303,0.25 part of organic silicon defoamer, 1.25 are added into said mixture
Part esters of acrylic acid levelling agent, sonic oscillation 30min, stirs 2.5h, adds bead grinding 6h, filtering, you can projected
Curtain ink.
In order to preferably embody the heat endurance of projection screen ink in the present invention, below with reference to specific experiment data
Illustrate.
Test method:
3 groups of ink samples are prepared, change the silicon dioxide powder in ink formulations, other compositions dosage is constant, detects this 3 groups
The heat endurance of ink, test result such as following table:
Test number | Sample 1 | Sample 2 | Sample 3 |
Silicon dioxide powder dosage | 2.5 part | 5 parts | 12.5 parts |
Sample is through 400 DEG C of processing | Crack at edge | Surface is good | Cracking |
According to result of the test as can be seen that in the present invention, when the dosage of silicon dioxide powder is 5 parts, obtained ink
With preferable excellent heat stability.Therefore, the ink in the present invention disclosure satisfy that printability requirement, have preferably application
Prospect.
Finally, it is to be noted that, term " comprising ", "comprising" or its any other variant be intended to it is non-exclusive
Property includes, so that process, method, article or equipment including a series of elements not only include those key elements, and
Also include the other element that is not expressly set out, or also include for this process, method, article or equipment inherently
Key element.
Claims (5)
1. a kind of projection screen coating material, it is characterised in that composition is by weight:80~100 parts of silicones, titanium dioxide
20~30 parts, 5~10 parts of silicon dioxide powder, 2~5 parts of alundum (Al2O3), 0.2~0.5 part of sodium oxide molybdena, 5~15 parts of magnesium silicate, oxygen
Change 1~2 part of magnesium, 1.25~2.5 parts of curing agent, 0.25~1 part of defoamer, 0.75~1.25 part of levelling agent.
2. projection screen coating material according to claim 1, it is characterised in that composition is by weight:Silicones
80~90 parts, 25~30 parts of titanium dioxide, 5~8 parts of silicon dioxide powder, 3~5 parts of alundum (Al2O3), 0.2~0.3 part of sodium oxide molybdena, silicon
Sour 5~10 parts of magnesium, 1.5~2 parts of magnesia, 1.75~2.5 parts of curing agent, 0.25~0.75 part of defoamer, levelling agent 1~1.25
Part.
3. projection screen coating material according to claim 1, it is characterised in that composition is by weight:Silicones
85~90 parts, 28~30 parts of titanium dioxide, 5~6 parts of silicon dioxide powder, 3~4 parts of alundum (Al2O3), 0.25~0.3 part of sodium oxide molybdena,
7.5~10 parts of magnesium silicate, 1.75~2 parts of magnesia, 1.75~2 parts of curing agent, 0.25~0.5 part of defoamer, levelling agent 1.1~
1.25 part.
4. projection screen coating material according to any one of claim 1 to 3, it is characterised in that the curing agent
For cyanogen spy's resin CYMEL303, the defoamer is organic silicon defoamer, and the levelling agent is esters of acrylic acid levelling agent.
A kind of 5. preparation method of projection screen coating material, it is characterised in that including:
(1) by 80~100 parts of silicones, 5~10 parts of silicon dioxide powders, 2~5 parts of alundum (Al2O3)s, 0.2~0.5 part of sodium oxide molybdena
Mixing, 10~15min of ultrasonic disperse add 20~30 parts of titanium dioxides, 5~15 parts of magnesium silicates, 1~2 part of magnesia, and stirring is equal
It is even, 20~30min of ultrasonic disperse, obtain mixture;
(2) 1.25~2.5 parts of curing agent, 0.25~1 part of defoamer, 0.75~1.25 part of levelling are added into said mixture
Agent, 20~30min of sonic oscillation, 2~3h is stirred, add bead and grind 5~8h, filtering, you can obtain projection screen oil
Ink.