CN108048230A - A kind of ultraviolet ray proof automobile bath of glass and its preparation process - Google Patents
A kind of ultraviolet ray proof automobile bath of glass and its preparation process Download PDFInfo
- Publication number
- CN108048230A CN108048230A CN201711379561.7A CN201711379561A CN108048230A CN 108048230 A CN108048230 A CN 108048230A CN 201711379561 A CN201711379561 A CN 201711379561A CN 108048230 A CN108048230 A CN 108048230A
- Authority
- CN
- China
- Prior art keywords
- parts
- bath
- ultraviolet ray
- glass
- proof automobile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of ultraviolet ray proof automobile bath of glass, the formula of raw material by weight is as follows：50 70 parts of deionized water, 37 parts of water-soluble silicon oil, 37 parts of coconut oil diethanol amide, 37 parts of propylene glycol monomethyl ether, 35 parts of nano-titanium dioxide, 35 parts of ultra-violet absorber, 13 parts of surfactant, 13 parts of antifoggant, 13 parts of corrosion inhibitor.The present invention also provides a kind of preparation processes of ultraviolet ray proof automobile bath of glass.The present invention enables to the ability that the present invention not only has cleaning glass surface spot, additionally it is possible to effectively prevent spot from resting on glass surface, also having prevents ultraviolet light direct projection from entering interior ability.
Description
Technical field
The present invention relates to auto parts and components preparing technical field more particularly to a kind of ultraviolet ray proof automobile bath of glass and its systems
Standby technique.
Background technology
Vehicle glass is essential in automobile body accessories, primarily serves protective action.Vehicle glass mainly have with
Lower three classes：Laminated glass, tempered glass and local toughened glass can bear stronger impact force.Vehicle glass presses the position at place
It puts and is divided into：Four kinds of front windshield, side window glass, rear seat windscreen and skylight glass.And front windshield state compulsion provides
Must be laminated glass, it is sufficient to prove its importance, front windshield needs fixed time cleaning in vehicle when driving, so as to remove
The impurity on its surface is removed, also needs to absorb ultraviolet light using substance, for this purpose, we have proposed a kind of ultraviolet ray proof automobile glass
Glass water and its preparation process.
The content of the invention
The present invention proposes a kind of ultraviolet ray proof automobile bath of glass and its preparation process, to solve to carry in above-mentioned background technology
The problem of going out.
The present invention proposes a kind of ultraviolet ray proof automobile bath of glass, and the formula of raw material by weight is as follows：Deionized water 50-
70 parts, 3-7 parts of water-soluble silicon oil, 3-7 parts of coconut oil diethanol amide, 3-7 parts of propylene glycol monomethyl ether, 3-5 parts of nano-titanium dioxide,
3-5 parts of ultra-violet absorber, 1-3 parts of surfactant, 1-3 parts of antifoggant, 1-3 parts of corrosion inhibitor.
Preferably, water-soluble silicon oil, coconut oil diethanol amide, the weight ratio of propylene glycol monomethyl ether are 4-6：4-6：4-6.
Preferably, nano-titanium dioxide, the weight ratio of ultra-violet absorber are 3.5-4.5：3.5-4.5.
Preferably, surfactant, antifoggant, the weight ratio of corrosion inhibitor are 1.5-2.5：1.5-2.5：1.5-2.5.
Preferably, the formula of raw material by weight is as follows：
55-65 parts of deionized water, 4-6 parts of water-soluble silicon oil, 4-6 parts of coconut oil diethanol amide, propylene glycol monomethyl ether 4-6
Part, 3.5-4.5 parts of nano-titanium dioxide, 3.5-4.5 parts of ultra-violet absorber, 1.5-2.5 parts of surfactant, antifoggant 1.5-
2.5 parts, 1.5-2.5 parts of corrosion inhibitor.
Preferably, the optimization formula of raw material by weight is as follows：
60 parts of deionized water, 5 parts of water-soluble silicon oil, 5 parts of coconut oil diethanol amide, 5 parts of propylene glycol monomethyl ether, nano-silica
Change 4 parts of titanium, 4 parts of ultra-violet absorber, 3 parts of surfactant, 3 parts of antifoggant, 3 parts of corrosion inhibitor.
The present invention also provides a kind of preparation processes of ultraviolet ray proof automobile bath of glass, include the following steps：
S1, selection blender are auxiliary tool, and at the sterilization that carries out disinfection to it under conditions of 120-130 degrees Celsius
Reason, after finishing, dry cooling in the environment of sealing；
S2, deionized water is slowly inserted in blender in proportion, and is mixed in adding procedure, added
Cheng Hou raises the temperature to 45-65 degrees Celsius, then into blender add water-soluble silicon oil, coconut oil diethanol amide with
And propylene glycol monomethyl ether, and continue that 20-40min is mixed；
S3, after the completion of S2, nano-titanium dioxide and ultra-violet absorber into blender, then reduce temperature again
To 30-45 degrees Celsius, after it is stirred evenly, continue to add surfactant, antifoggant and corrosion successively into blender
Inhibitor, and it is slowly stirred 90-120min；
S4, it is above-mentioned after the completion of, take out, is placed cool place confined space in, carry out cooling processing, treat that temperature is down to
After 20-25 degrees Celsius, the floating material on liquid upper strata is removed, obtained mixed liquor carries out concentration, i.e., to it again
Obtain ultraviolet ray proof automobile bath of glass.
In the present invention, addition and rational proportion by plurality of raw materials enable to the present invention not only to have cleaning glass
The ability of glass surface blot, additionally it is possible to effectively prevent spot from resting on glass surface, pass through nano-titanium dioxide and ultraviolet light
The addition of absorbent, can have the bath of glass prevents ultraviolet light direct projection from entering interior ability, and the processing compound is simple, production
It is at low cost, and with good effect, it is suitable for large-scale promotion.
Specific embodiment
With reference to specific embodiment, the present invention will be further described.
Embodiment 1
The present invention proposes a kind of ultraviolet ray proof automobile bath of glass, and the formula of raw material by weight is as follows：Deionized water 50
Part, 3 parts of water-soluble silicon oil, 3 parts of coconut oil diethanol amide, 3 parts of propylene glycol monomethyl ether, 3 parts of nano-titanium dioxide, ultraviolet radiation absorption
3 parts of agent, 1 part of surfactant, 1 part of antifoggant, 1 part of corrosion inhibitor.
The present invention also provides a kind of preparation processes of ultraviolet ray proof automobile bath of glass, include the following steps：
S1, selection blender are auxiliary tool, and the sterilization processing that carries out disinfection to it under conditions of 120 degrees Celsius is complete
Cheng Hou, dry cooling in the environment of sealing；
S2, deionized water is slowly inserted in blender in proportion, and is mixed in adding procedure, added
Cheng Hou raises the temperature to 45 degrees Celsius, and water-soluble silicon oil, coconut oil diethanol amide and third are then added into blender
Glycol methyl ether, and continue that 20min is mixed；
S3, after the completion of S2, nano-titanium dioxide and ultra-violet absorber into blender, then reduce temperature again
To 30 degrees Celsius, after it is stirred evenly, continue to add surfactant, antifoggant and corrosion inhibition successively into blender
Agent, and it is slowly stirred 90min；
S4, it is above-mentioned after the completion of, take out, is placed cool place confined space in, carry out cooling processing, treat that temperature is down to 20
After degree Celsius, the floating material on liquid upper strata is removed, obtained mixed liquor, it is carried out again concentration to get to
Ultraviolet ray proof automobile bath of glass.
Embodiment 2
The present invention proposes a kind of ultraviolet ray proof automobile bath of glass, and the formula of raw material by weight is as follows：Deionized water 55
Part, 4 parts of water-soluble silicon oil, 4 parts of coconut oil diethanol amide, 4 parts of propylene glycol monomethyl ether, 3.5 parts of nano-titanium dioxide, ultraviolet light are inhaled
Receive 3.5 parts of agent, 1.5 parts of surfactant, 1.5 parts of antifoggant, 1.5 parts of corrosion inhibitor.
The present invention also provides a kind of preparation processes of ultraviolet ray proof automobile bath of glass, include the following steps：
S1, selection blender are auxiliary tool, and the sterilization processing that carries out disinfection to it under conditions of 123 degrees Celsius is complete
Cheng Hou, dry cooling in the environment of sealing；
S2, deionized water is slowly inserted in blender in proportion, and is mixed in adding procedure, added
Cheng Hou raises the temperature to 47 degrees Celsius, and water-soluble silicon oil, coconut oil diethanol amide and third are then added into blender
Glycol methyl ether, and continue that 25min is mixed；
S3, after the completion of S2, nano-titanium dioxide and ultra-violet absorber into blender, then reduce temperature again
To 35 degrees Celsius, after it is stirred evenly, continue to add surfactant, antifoggant and corrosion inhibition successively into blender
Agent, and it is slowly stirred 100min；
S4, it is above-mentioned after the completion of, take out, is placed cool place confined space in, carry out cooling processing, treat that temperature is down to 21
After degree Celsius, the floating material on liquid upper strata is removed, obtained mixed liquor, it is carried out again concentration to get to
Ultraviolet ray proof automobile bath of glass.
Embodiment 3
The present invention proposes a kind of ultraviolet ray proof automobile bath of glass, and the formula of raw material by weight is as follows：Deionized water 60
Part, 5 parts of water-soluble silicon oil, 5 parts of coconut oil diethanol amide, 5 parts of propylene glycol monomethyl ether, 4 parts of nano-titanium dioxide, ultraviolet radiation absorption
4 parts of agent, 3 parts of surfactant, 3 parts of antifoggant, 3 parts of corrosion inhibitor.
The present invention also provides a kind of preparation processes of ultraviolet ray proof automobile bath of glass, include the following steps：
S1, selection blender are auxiliary tool, and the sterilization processing that carries out disinfection to it under conditions of 125 degrees Celsius is complete
Cheng Hou, dry cooling in the environment of sealing；
S2, deionized water is slowly inserted in blender in proportion, and is mixed in adding procedure, added
Cheng Hou raises the temperature to 55 degrees Celsius, and water-soluble silicon oil, coconut oil diethanol amide and third are then added into blender
Glycol methyl ether, and continue that 30min is mixed；
S3, after the completion of S2, nano-titanium dioxide and ultra-violet absorber into blender, then reduce temperature again
To 38 degrees Celsius, after it is stirred evenly, continue to add surfactant, antifoggant and corrosion inhibition successively into blender
Agent, and it is slowly stirred 105min；
S4, it is above-mentioned after the completion of, take out, is placed cool place confined space in, carry out cooling processing, treat that temperature is down to 23
After degree Celsius, the floating material on liquid upper strata is removed, obtained mixed liquor, it is carried out again concentration to get to
Ultraviolet ray proof automobile bath of glass.
Embodiment 4
The present invention proposes a kind of ultraviolet ray proof automobile bath of glass, and the formula of raw material by weight is as follows：Deionized water 65
Part, 6 parts of water-soluble silicon oil, 6 parts of coconut oil diethanol amide, 6 parts of propylene glycol monomethyl ether, 4.5 parts of nano-titanium dioxide, ultraviolet light are inhaled
Receive 4.5 parts of agent, 2.5 parts of surfactant, 2.5 parts of antifoggant, 2.5 parts of corrosion inhibitor.
The present invention also provides a kind of preparation processes of ultraviolet ray proof automobile bath of glass, include the following steps：
S1, selection blender are auxiliary tool, and the sterilization processing that carries out disinfection to it under conditions of 127 degrees Celsius is complete
Cheng Hou, dry cooling in the environment of sealing；
S2, deionized water is slowly inserted in blender in proportion, and is mixed in adding procedure, added
Cheng Hou raises the temperature to 60 degrees Celsius, and water-soluble silicon oil, coconut oil diethanol amide and third are then added into blender
Glycol methyl ether, and continue that 35min is mixed；
S3, after the completion of S2, nano-titanium dioxide and ultra-violet absorber into blender, then reduce temperature again
To 40 degrees Celsius, after it is stirred evenly, continue to add surfactant, antifoggant and corrosion inhibition successively into blender
Agent, and it is slowly stirred 110min；
S4, it is above-mentioned after the completion of, take out, is placed cool place confined space in, carry out cooling processing, treat that temperature is down to 24
After degree Celsius, the floating material on liquid upper strata is removed, obtained mixed liquor, it is carried out again concentration to get to
Ultraviolet ray proof automobile bath of glass.
Embodiment 5
The present invention proposes a kind of ultraviolet ray proof automobile bath of glass, and the formula of raw material by weight is as follows：Deionized water 70
Part, 7 parts of water-soluble silicon oil, 7 parts of coconut oil diethanol amide, 7 parts of propylene glycol monomethyl ether, 5 parts of nano-titanium dioxide, ultraviolet radiation absorption
5 parts of agent, 3 parts of surfactant, 3 parts of antifoggant, 3 parts of corrosion inhibitor.
The present invention also provides a kind of preparation processes of ultraviolet ray proof automobile bath of glass, include the following steps：
S1, selection blender are auxiliary tool, and the sterilization processing that carries out disinfection to it under conditions of 130 degrees Celsius is complete
Cheng Hou, dry cooling in the environment of sealing；
S2, deionized water is slowly inserted in blender in proportion, and is mixed in adding procedure, added
Cheng Hou raises the temperature to 65 degrees Celsius, and water-soluble silicon oil, coconut oil diethanol amide and third are then added into blender
Glycol methyl ether, and continue that 40min is mixed；
S3, after the completion of S2, nano-titanium dioxide and ultra-violet absorber into blender, then reduce temperature again
To 45 degrees Celsius, after it is stirred evenly, continue to add surfactant, antifoggant and corrosion inhibition successively into blender
Agent, and it is slowly stirred 120min；
S4, it is above-mentioned after the completion of, take out, is placed cool place confined space in, carry out cooling processing, treat that temperature is down to 25
After degree Celsius, the floating material on liquid upper strata is removed, obtained mixed liquor, it is carried out again concentration to get to
Ultraviolet ray proof automobile bath of glass.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (7)
1. a kind of ultraviolet ray proof automobile bath of glass, which is characterized in that the formula of its raw material by weight is as follows：Deionized water 50-70
Part, 3-7 parts of water-soluble silicon oil, 3-7 parts of coconut oil diethanol amide, 3-7 parts of propylene glycol monomethyl ether, 3-5 parts of nano-titanium dioxide, purple
3-5 parts of ultraviolet absorbers, 1-3 parts of surfactant, 1-3 parts of antifoggant, 1-3 parts of corrosion inhibitor.
2. ultraviolet ray proof automobile bath of glass according to claim 1, which is characterized in that water-soluble silicon oil, coconut oil diethyl
Alkylolamides, the weight ratio of propylene glycol monomethyl ether are 4-6: 4-6: 4-6.
3. ultraviolet ray proof automobile bath of glass according to claim 1, which is characterized in that nano-titanium dioxide, ultraviolet light are inhaled
The weight ratio for receiving agent is 3.5-4.5: 3.5-4.5.
4. ultraviolet ray proof automobile bath of glass according to claim 1, which is characterized in that surfactant, antifoggant, corrosion
The weight ratio of inhibitor is 1.5-2.5: 1.5-2.5: 1.5-2.5.
5. the ultraviolet ray proof automobile bath of glass according to claim 1-4, which is characterized in that the formula of its raw material by weight is such as
Under：
55-65 parts of deionized water, 4-6 parts of water-soluble silicon oil, 4-6 parts of propylene glycol monomethyl ether, are received 4-6 parts of coconut oil diethanol amide
3.5-4.5 parts of titanium dioxide of rice, 3.5-4.5 parts of ultra-violet absorber, 1.5-2.5 parts of surfactant, antifoggant 1.5-2.5
Part, 1.5-2.5 parts of corrosion inhibitor.
6. ultraviolet ray proof automobile bath of glass according to claim 1, which is characterized in that the optimization formula of its raw material by weight
It is as follows：
60 parts of deionized water, 5 parts of water-soluble silicon oil, 5 parts of coconut oil diethanol amide, 5 parts of propylene glycol monomethyl ether, nano-titanium dioxide
4 parts, 4 parts of ultra-violet absorber, 3 parts of surfactant, 3 parts of antifoggant, 3 parts of corrosion inhibitor.
7. a kind of preparation process of ultraviolet ray proof automobile bath of glass according to claim 1, which is characterized in that including as follows
Step：
S1, selection blender are auxiliary tool, and the sterilization processing that carries out disinfection to it under conditions of 120-130 degrees Celsius is complete
Cheng Hou, dry cooling in the environment of sealing；
S2, deionized water is slowly inserted in blender in proportion, and is mixed in adding procedure, addition is completed
Afterwards, raise the temperature to 45-65 degrees Celsius, then into blender add water-soluble silicon oil, coconut oil diethanol amide and
Propylene glycol monomethyl ether, and continue that 20-40min is mixed；
S3, after the completion of S2, temperature, is then reduced to by nano-titanium dioxide and ultra-violet absorber into blender again
30-45 degrees Celsius, after it is stirred evenly, continue to add surfactant, antifoggant and corrosion suppression successively into blender
Preparation, and it is slowly stirred 90-120min；
S4, it is above-mentioned after the completion of, take out, is placed cool place confined space in, carry out cooling processing, treat that temperature is down to 20-25
After degree Celsius, the floating material on liquid upper strata is removed, obtained mixed liquor, it is carried out again concentration to get to
Ultraviolet ray proof automobile bath of glass.