CN106367217A - Anti-ultraviolet self-cleaning water scattering vehicle glass water - Google Patents
Anti-ultraviolet self-cleaning water scattering vehicle glass water Download PDFInfo
- Publication number
- CN106367217A CN106367217A CN201610751761.XA CN201610751761A CN106367217A CN 106367217 A CN106367217 A CN 106367217A CN 201610751761 A CN201610751761 A CN 201610751761A CN 106367217 A CN106367217 A CN 106367217A
- Authority
- CN
- China
- Prior art keywords
- water
- ultraviolet
- titanium oxide
- cleaning
- nano titanium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses anti-ultraviolet self-cleaning water scattering vehicle glass water which comprises the following raw materials in percentage by weight: 97.49-99.48 percent of water, 0.3-0.8 percent of coconut oil diethanolamide, 0.01-2 percent of nano titania and 0.01-0.05 percent of a corrosion inhibitor, and the sum of the percentages by weight of all the components is 100 percent. The anti-ultraviolet self-cleaning water scattering vehicle glass water disclosed by the invention not only has self-cleaning, antibacterial and deodorant functions, but also has an anti-ultraviolet function and a water scattering function.
Description
Technical field
The present invention relates to a kind of automotive glass water, in particular to a kind of anti-ultraviolet automatically cleaning aproll glass of automobile
Glass water.
Background technology
Existing products in markets only possesses the function of cleaning cleaning glass, and common formula is as follows:
Formula 1: propylene glycol monomethyl ether 2.5%, ethylene glycol 7%, isopropanol 40%, nonyl phenol (eo) 9~10 ether 0.5%, water
50%.
Formula 2: propylene glycol monomethyl ether 3%, isopropanol 19%, propylene glycol 3%, water 75%.
The raw material of these formula is mainly some alcohol derivatives, and in bath of glass, proportion is larger, not only wastes
Material can produce considerable degree of pollution to environment simultaneously.
Content of the invention
It is an object of the invention to the problem above overcoming prior art to exist, one kind is provided to possess automatically cleaning bacteriostasis, and deodorization
The anti-ultraviolet automatically cleaning aproll automobile glass water of function, anti-ultraviolet function and aproll function.
For realizing above-mentioned technical purpose, reach above-mentioned technique effect, the present invention is achieved through the following technical solutions:
A kind of anti-ultraviolet automatically cleaning aproll automobile glass water, formula includes following raw material by weight percentage:
Water: 97.49-99.48%;
Coconut oil diethanol amide: 0.3-0.8%;
Nano titanium oxide: 0.01-2%;
Corrosion inhibiter: 0.01-0.05%;
The summation of above-mentioned all components percentage composition is 100%.
Preferably, formula includes following raw material by weight percentage:
Water: 98.49%;
Coconut oil diethanol amide: 0.5%;
Nano titanium oxide: 1%;
Corrosion inhibiter: 0.01%.
Further, the granular size of described nano titanium oxide is 25-100 nanometer.
The present invention possesses following beneficial effect:
1. possess cleaning vehicle glass surface blot, be also equipped with self-cleaning function it is not easy to be infected with dirt;
2. deodorization, antibacterial, antifreeze;
3. make glass surface form one layer and stop the protecting film that penetrates of ultraviolet, isolation ultraviolet, sun-proof;
4. make glass surface form one layer and possess self-cleaning soiling protective film;
5. make glass surface form one layer of aproll nanometer film, be integrated into dewdrop on Folium Nelumbinis when rainwater falls immediately on glass when
Shape disperses rapidly, makes rainy day clear visual field such as no rain shape.
Described above is only the general introduction of technical solution of the present invention, in order to better understand the technological means of the present invention,
And can be practiced according to the content of description, after being described in detail such as with presently preferred embodiments of the present invention below.The tool of the present invention
Body embodiment is shown in detail in by following examples.
Specific embodiment
Below in conjunction with embodiment, to describe the present invention in detail.
Embodiment 1: a kind of anti-ultraviolet automatically cleaning aproll automobile glass water, formula includes following former by weight percentage
Material:
Water: 98.49%;
Coconut oil diethanol amide: 0.5%;
Nano titanium oxide: 1%;
Corrosion inhibiter: 0.01%.
Embodiment 2: a kind of anti-ultraviolet automatically cleaning aproll automobile glass water, formula includes following former by weight percentage
Material:
Water: 97.49%;
Coconut oil diethanol amide: 0.5%;
Nano titanium oxide: 2%;
Corrosion inhibiter: 0.01%.
Embodiment 3: a kind of anti-ultraviolet automatically cleaning aproll automobile glass water, formula includes following former by weight percentage
Material:
Water: 99.48%;
Coconut oil diethanol amide: 0.5%;
Nano titanium oxide: 0.01%;
Corrosion inhibiter: 0.01%.
Embodiment 4: a kind of anti-ultraviolet automatically cleaning aproll automobile glass water, formula includes following former by weight percentage
Material:
Water: 99%;
Coconut oil diethanol amide: 0.3%;
Nano titanium oxide: 0.65%;
Corrosion inhibiter: 0.05%.
Embodiment 5: a kind of anti-ultraviolet automatically cleaning aproll automobile glass water, formula includes following former by weight percentage
Material:
Water: 99%;
Coconut oil diethanol amide: 0.8%;
Nano titanium oxide: 0.15%;
Corrosion inhibiter: 0.05%.
Embodiment 6: a kind of anti-ultraviolet automatically cleaning aproll automobile glass water, formula includes following former by weight percentage
Material:
Water: 97.49%;
Coconut oil diethanol amide: 0.5%;
Nano titanium oxide: 1.98%;
Corrosion inhibiter: 0.03%.
In the formula of embodiment 1-6, coconut oil diethanol amide is a kind of neutral active agent, has stronger dirt-removing power,
Possesses cleaning vehicle glass surface blot function;Titanium dioxide nanoparticle in formula only has 25-100 nanosized, permissible
Fusion hydrone is sprayed at trickle after wiper scrapes repeatedly nano titanium oxide during glass surface and is attached to well
The surface of glass forms one layer of nanometer film, looks just as the structure of lotus leaf surface floss floss, when rainwater falls under high power microscope
When on the glass surface, nanometer film just serves the effect on similar Folium Nelumbinis top layer, globule landing quickly.
Nano titanium oxide under visible light illumination can be to Hydrocarbon decomposition, using the photocatalysis of titanium oxide
Reaction just can be decomposed into co by the organic pollution on nano titanium dioxide film surface absorption2And h2O, with remaining inorganic matters
Together can be clean by rain drop erosion, thus realizing self-cleaning function.
As above-mentioned glass surface defines one layer of nanometer layer, its thickness, between 25-100 nanometer, just can stop purple
Outside line passes through.
The strong anti-uv-ray of nano titanium oxide is because it has high refractivity and high photolytic activity.Its uvioresistant
Ability and its mechanism are relevant with its particle diameter: when particle diameter is larger, the obstruct to ultraviolet is based on reflecting, scattering, and centering
Ripple area and long-wavelength region ultraviolet are all effective.
The antibacterial mechanisms of nano titanium oxide are:
Nano titanium oxide makes bacterial decomposition reach antibacterial effect under photocatalysiss.Due to nano titanium oxide
Electronic structure feature be a full tio2Valence band and an empty conduction band, in the system of water and air, nanometer titanium dioxide
, in sunlight especially under ultraviolet irradiation, when electron energy meets or exceeds its band-gap energy, electronics can be from valence band for titanium
It is energized into conduction band, produces corresponding hole in valence band simultaneously, that is, generate electronics, hole, in the presence of electric field, electronics and hole
Occur to separate, move to the diverse location of particle surface, after then there is series reaction, absorption is dissolved in tio2The oxygen on surface
The ultra-oxygen anion free radical generating after trapped electron is reacted with most Organic substances, can react with the Organic substance in antibacterial simultaneously,
Generate co2And h2o;And hole then will be adsorbed in tio2Behind surface and h2O is oxidized to hydroxy radical, and hydroxy radical has very strong oxygen
Change ability, attacks the unsaturated bond of Organic substance or extracts the h atom new free radical of generation, excite chain reaction, finally cause antibacterial
Decompose.
tio2Bactericidal action be its quantum size effect although titanium dioxide (common tio2) also there are photocatalysiss,
Also electronics, hole pair can be produced, but it reaches the time of material surface more than Microsecond grade, easily occur compound, be difficult to send out
Wave antibacterial effect, and reach the tio of nanoscale degree of scatter2, by light activated electronics, hole from vivo migration to surface, only
Need the time of nanosecond, psec, even femtosecond, the compound in light induced electron and hole, in nanosecond order, can move to surface quickly,
Attack bacteria organism, plays corresponding antibacterial action.
The foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, for the skill of this area
For art personnel, the present invention can have various modifications and variations.All within the spirit and principles in the present invention, made any repair
Change, equivalent, improvement etc., should be included within the scope of the present invention.
Claims (3)
1. a kind of anti-ultraviolet automatically cleaning aproll automobile glass water it is characterised in that: formula includes following former by weight percentage
Material:
Water: 97.49-99.48%;
Coconut oil diethanol amide: 0.3-0.8%;
Nano titanium oxide: 0.01-2%;
Corrosion inhibiter: 0.01-0.05%;
The summation of above-mentioned all components percentage composition is 100%.
2. a kind of anti-ultraviolet automatically cleaning aproll automobile glass water according to claim 1 it is characterised in that: optimization formula
Include following raw material by weight percentage:
Water: 98.49%;
Coconut oil diethanol amide: 0.5%;
Nano titanium oxide: 1%;
Corrosion inhibiter: 0.01%.
3. a kind of anti-ultraviolet automatically cleaning aproll automobile glass water according to claim 1 and 2 it is characterised in that: described
The granular size of nano titanium oxide is 25-100 nanometer.