CN108046611A - 一种玻璃刻蚀液 - Google Patents
一种玻璃刻蚀液 Download PDFInfo
- Publication number
- CN108046611A CN108046611A CN201711481630.5A CN201711481630A CN108046611A CN 108046611 A CN108046611 A CN 108046611A CN 201711481630 A CN201711481630 A CN 201711481630A CN 108046611 A CN108046611 A CN 108046611A
- Authority
- CN
- China
- Prior art keywords
- parts
- acid
- etching liquid
- glass etching
- rare earth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种玻璃刻蚀液,由下列物质组成:硫酸、磷酸、植酸、柠檬酸、酒石酸、硫酸铵、硫酸钾、二乙醇胺、氟化钙、硝酸稀土盐、氧化剂、表面活性剂、络合剂、水。本发明刻蚀液具有处理效果好、效率高、可靠性强、耐久性长等优点,极具推广应用价值。
Description
技术领域
本发明属于玻璃加工制造技术领域,具体涉及一种玻璃刻蚀液。
背景技术
目前国内外市场上所销售的防眩玻璃一般通过两种方法来实现:一种是对玻璃表面进行镀膜来实现,另一种是通过酸刻蚀玻璃表面来实现。镀膜防眩玻璃的防眩效果较好,但是成本较高,且镀膜容易脱落,表面容易留下划痕等,影响了玻璃的透明度。一般的酸蚀防眩玻璃是先对玻璃进行表面蒙砂,然后对玻璃蒙砂面进行抛光,有效的克服了镀膜易脱落、表面易划损的缺陷。但因市面上的玻璃刻蚀液功能单一,刻蚀效率不高,导致刻蚀的工艺相对复杂,生产周期长,成品率低等问题,需要进一步的改进。
发明内容
本发明的目的是针对现有的问题,提供了一种玻璃刻蚀液。
本发明是通过以下技术方案实现的:
一种玻璃刻蚀液,由如下重量份的物质组成:
15~18份硫酸、4~7份磷酸、3~6份植酸、2~5份柠檬酸、1~3份酒石酸、5~8份硫酸铵、6~9份硫酸钾、2~4份二乙醇胺、3~6份氟化钙、1~1.5份硝酸稀土盐、2~3份氧化剂、3~5份表面活性剂、1~2份络合剂、50~60份水。
优选的,由如下重量份的物质组成:
17~18份硫酸、6~7份磷酸、5~6份植酸、4~5份柠檬酸、2~3份酒石酸、7~8份硫酸铵、8~9份硫酸钾、3~4份二乙醇胺、5~6份氟化钙、1.2~1.5份硝酸稀土盐、2.5~3份氧化剂、4~5份表面活性剂、1.5~2份络合剂、55~60份水。
优选的,由如下重量份的物质组成:
17份硫酸、6份磷酸、5份植酸、4份柠檬酸、2份酒石酸、7份硫酸铵、8份硫酸钾、3份二乙醇胺、5份氟化钙、1.2份硝酸稀土盐、2.5份氧化剂、4份表面活性剂、1.5份络合剂、55份水。
进一步的,所述硝酸稀土盐为硝酸钇、硝酸镧、硝酸铈中的任意一种。
进一步的,所述氧化剂为双氧水、碘酸钾、过氧乙酸中的任意一种。
进一步的,所述表面活性剂为十二烷基苯磺酸钠、十六烷基苯磺酸钠、脂肪醇聚氧乙烯醚中的任意一种。
进一步的,所述络合剂为乙二胺四乙酸二钠。
本发明相比现有技术具有以下优点:
本发明对玻璃刻蚀液的组分进行了特殊的搭配调整,添加的硫酸、磷酸、植酸、柠檬酸、酒石酸成分复配使用后,有效的保证了刻蚀的效果和效率,添加的硝酸稀土盐配合络合剂的使用提升了防眩处理效果。在各成分的共同配合作用下,本发明刻蚀液具有处理效果好、效率高、可靠性强、耐久性长等优点,极具推广应用价值。
具体实施方式
实施例1
一种玻璃刻蚀液,由如下重量份的物质组成:
15份硫酸、4份磷酸、3份植酸、2份柠檬酸、1份酒石酸、5份硫酸铵、6份硫酸钾、2份二乙醇胺、3份氟化钙、1份硝酸稀土盐、2份氧化剂、3份表面活性剂、1份络合剂、50份水。
进一步的,所述硝酸稀土盐为硝酸钇。
进一步的,所述氧化剂为双氧水。
进一步的,所述表面活性剂为十二烷基苯磺酸钠。
进一步的,所述络合剂为乙二胺四乙酸二钠。
实施例2
一种玻璃刻蚀液,由如下重量份的物质组成:
17份硫酸、6份磷酸、5份植酸、4份柠檬酸、2份酒石酸、7份硫酸铵、8份硫酸钾、3份二乙醇胺、5份氟化钙、1.2份硝酸稀土盐、2.5份氧化剂、4份表面活性剂、1.5份络合剂、55份水。
进一步的,所述硝酸稀土盐为硝酸镧。
进一步的,所述氧化剂为碘酸钾。
进一步的,所述表面活性剂为十六烷基苯磺酸钠。
进一步的,所述络合剂为乙二胺四乙酸二钠。
实施例3
一种玻璃刻蚀液,由如下重量份的物质组成:
18份硫酸、7份磷酸、6份植酸、5份柠檬酸、3份酒石酸、8份硫酸铵、9份硫酸钾、4份二乙醇胺、6份氟化钙、1.5份硝酸稀土盐、3份氧化剂、5份表面活性剂、2份络合剂、60份水。
进一步的,所述硝酸稀土盐为硝酸铈。
进一步的,所述氧化剂为过氧乙酸。
进一步的,所述表面活性剂为脂肪醇聚氧乙烯醚。
进一步的,所述络合剂为乙二胺四乙酸二钠。
本发明刻蚀液的制备方法是将所有的原料成分共同放入到搅拌罐内,以1500~1700转/分钟的转速搅拌均匀后取出即可。
本发明刻蚀液具有处理效果好、效率高、可靠性强、耐久性长等优点,极具推广应用价值。
Claims (7)
1.一种玻璃刻蚀液,其特征在于,由如下重量份的物质组成:
15~18份硫酸、4~7份磷酸、3~6份植酸、2~5份柠檬酸、1~3份酒石酸、5~8份硫酸铵、6~9份硫酸钾、2~4份二乙醇胺、3~6份氟化钙、1~1.5份硝酸稀土盐、2~3份氧化剂、3~5份表面活性剂、1~2份络合剂、50~60份水。
2.根据权利要求1所述的一种玻璃刻蚀液,其特征在于,由如下重量份的物质组成:
17~18份硫酸、6~7份磷酸、5~6份植酸、4~5份柠檬酸、2~3份酒石酸、7~8份硫酸铵、8~9份硫酸钾、3~4份二乙醇胺、5~6份氟化钙、1.2~1.5份硝酸稀土盐、2.5~3份氧化剂、4~5份表面活性剂、1.5~2份络合剂、55~60份水。
3.根据权利要求1所述的一种玻璃刻蚀液,其特征在于,由如下重量份的物质组成:
17份硫酸、6份磷酸、5份植酸、4份柠檬酸、2份酒石酸、7份硫酸铵、8份硫酸钾、3份二乙醇胺、5份氟化钙、1.2份硝酸稀土盐、2.5份氧化剂、4份表面活性剂、1.5份络合剂、55份水。
4.根据权利要求1~3中任意一项所述的一种玻璃刻蚀液,其特征在于,所述硝酸稀土盐为硝酸钇、硝酸镧、硝酸铈中的任意一种。
5.根据权利要求1~3中任意一项所述的一种玻璃刻蚀液,其特征在于,所述氧化剂为双氧水、碘酸钾、过氧乙酸中的任意一种。
6.根据权利要求1~3中任意一项所述的一种玻璃刻蚀液,其特征在于,所述表面活性剂为十二烷基苯磺酸钠、十六烷基苯磺酸钠、脂肪醇聚氧乙烯醚中的任意一种。
7.根据权利要求1~3中任意一项所述的一种玻璃刻蚀液,其特征在于,所述络合剂为乙二胺四乙酸二钠。