CN108034374A - A kind of plastic uptake adhesive tape - Google Patents
A kind of plastic uptake adhesive tape Download PDFInfo
- Publication number
- CN108034374A CN108034374A CN201711449732.9A CN201711449732A CN108034374A CN 108034374 A CN108034374 A CN 108034374A CN 201711449732 A CN201711449732 A CN 201711449732A CN 108034374 A CN108034374 A CN 108034374A
- Authority
- CN
- China
- Prior art keywords
- micelle
- parts
- glue
- adhesive tape
- plastic uptake
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of plastic uptake adhesive tape, which further includes the micelle for being scattered in the film surface, and the adhesion strength of the glue-line is more than the adhesion strength of the micelle, it is characterised in that：The micelle includes micelle made of following number raw material：24~26 parts of toluene；23~25 parts of asphalt；0.9~1.1 part of dibutyl phthalate；0.5~0.7 part of zinc oxide；48~52 parts of neoprene；0.4~0.6 part of stearic acid；0.05~0.07 part of tetramethylthiuram disulfide；1.9~2.1 parts of sodium hydroxide；1~5 part of adhesion agent.A kind of plastic uptake adhesive tape proposed by the present invention, has the air absorbed in packaging, and leakproofness is strong.
Description
Technical field
The present invention relates to a kind of adhesive tape, especially a kind of plastic uptake adhesive tape.
Background technology
Generally two workpiece are bonded together using viscose glue at present in consumer electronic product.On the one hand, viscose glue needs to have
There is preferable caking property to bond part with firm；On the other hand, need that there is preferable sealing effect after viscose glue；I.e. viscose glue both needs to have
There is preferable caking property to have sealing effect again.Taken into account however, current viscose glue is difficult for both.
The content of the invention
A kind of plastic uptake adhesive tape is provided the purpose of the present invention is to solve above-mentioned the deficiencies in the prior art.
A kind of plastic uptake adhesive tape of the present invention, its glue-line for including substrate and being formed in the substrate, which further includes scattered
In the micelle of the film surface, the adhesion strength of the glue-line is more than the adhesion strength of the micelle, it is characterised in that：The micelle include with
Micelle made of lower number raw material：24~26 parts of toluene；23~25 parts of asphalt；Dibutyl phthalate 0.9~1.1
Part；0.5~0.7 part of zinc oxide；48~52 parts of neoprene；0.4~0.6 part of stearic acid；Tetramethylthiuram disulfide 0.05
~0.07 part；1.9~2.1 parts of sodium hydroxide；1~5 part of adhesion agent.
Further, the micelle includes micelle made of following number raw material：25 parts of toluene；24 parts of asphalt；Adjacent benzene
1 part of dibutyl carboxylic acid；0.6 part of zinc oxide；50 parts of neoprene；0.5 part of stearic acid；Tetramethylthiuram disulfide 0.06
Part；2 parts of sodium hydroxide；3 parts of adhesion agent.
Further, the distribution density of the micelle is 20%-60%.
Further, a diameter of 50 microns of the micelle.
Further, the micelle, which is prepared by the following method, forms：
S1, first dissolve asphalt heating and be in a liquid state, and sloughs moisture, removes impurity；While agitating, 50 are added
The toluene of weight %, is uniformly mixed, and cold primer-oil is made；
S2, by neoprene, dibutyl phthalate, zinc oxide, neoprene, stearic acid tetramethyl autumn it is blue
Nurse and sodium hydroxide are put on rubber mixing machine together to be kneaded, and obtains micelle；
The micelle is pressed into the thin slice of 1~2 millimeters thick；The thin slice is cut into fractionlet；Afterwards, will be described small broken
The toluene of piece and remaining 50 weight % are put into mixer together, when stirring 3~5 is small, obtain chloroprene rubber solution；Finally,
Cold primer-oil and chloroprene rubber solution are put together, stirred evenly, glue is made, then add adhesion agent and glue is made as requested
Grain is adhered on glue-line.
So compared with current technology, a kind of plastic uptake adhesive tape proposed by the present invention, has the air absorbed in packaging, and
Leakproofness is strong.
Brief description of the drawings：
Fig. 1 is a kind of schematic cross-section of plastic uptake adhesive tape in embodiment 1.
In reference numeral：1. substrate；2. glue-line；3. micelle.
Embodiment
The invention is described further with reference to embodiment.
Embodiment 1：
As shown in Figure 1, a kind of plastic uptake adhesive tape provided in this embodiment, its glue for including substrate 1 and being formed in the substrate 1
Layer 2, the adhesive tape further include the micelle 3 for being scattered in 2 surface of glue-line, and the adhesion strength of the glue-line 2 is more than the adhesion strength of the micelle 3,
The micelle 3 includes micelle 3 made of following number raw material：24~26 parts of toluene；23~25 parts of asphalt；Phthalic acid
0.9~1.1 part of dibutyl ester；0.5~0.7 part of zinc oxide；48~52 parts of neoprene；0.4~0.6 part of stearic acid；Curing four
0.05~0.07 part of methyl thiuram；1.9~2.1 parts of sodium hydroxide；1~5 part of adhesion agent.
In the present embodiment, the micelle 3 includes micelle 3 made of following number raw material：25 parts of toluene；Asphalt 24
Part；1 part of dibutyl phthalate；0.6 part of zinc oxide；50 parts of neoprene；0.5 part of stearic acid；The tetramethyl autumn is blue
0.06 part of nurse；2 parts of sodium hydroxide；3 parts of adhesion agent.
Further, the distribution density of the micelle 3 is 20%-60%, and the distribution density of micelle 3 is in the present embodiment
40%；
Further, a diameter of 50 microns of the micelle 3.
Further, the micelle 3, which is prepared by the following method, forms：
S1, first dissolve asphalt heating and be in a liquid state, and sloughs moisture, removes impurity；While agitating, 50 are added
The toluene of weight %, is uniformly mixed, and cold primer-oil is made；
S2, by neoprene, dibutyl phthalate, zinc oxide, neoprene, stearic acid tetramethyl autumn it is blue
Nurse and sodium hydroxide are put on rubber mixing machine together to be kneaded, and obtains micelle；
The micelle is pressed into the thin slice of 1~2 millimeters thick；The thin slice is cut into fractionlet；Afterwards, will be described small broken
The toluene of piece and remaining 50 weight % are put into mixer together, when stirring 3~5 is small, obtain chloroprene rubber solution；Finally,
Cold primer-oil and chloroprene rubber solution are put together, stirred evenly, glue is made, then add adhesion agent and glue is made as requested
Grain 3 is adhered on glue-line 2.
So compared with current technology, a kind of plastic uptake adhesive tape proposed by the present invention, has the air absorbed in packaging, and
Leakproofness is strong.
Embodiment 2：
A kind of plastic uptake adhesive tape provided in this embodiment, its glue-line 2 for including substrate 1 and being formed in the substrate 1, the adhesive tape
The micelle 3 for being scattered in 2 surface of glue-line is further included, the adhesion strength of the glue-line 2 is more than the adhesion strength of the micelle 3, and the micelle 3 wraps
Include micelle 3 made of following number raw material：24~26 parts of toluene；23~25 parts of asphalt；Dibutyl phthalate 0.9~
1.1 part；0.5~0.7 part of zinc oxide；48~52 parts of neoprene；0.4~0.6 part of stearic acid；Tetramethylthiuram disulfide
0.05~0.07 part；1.9~2.1 parts of sodium hydroxide；1~5 part of adhesion agent.
In the present embodiment, the micelle 3 includes micelle 3 made of following number raw material：23 parts of toluene；Asphalt 23
Part；0.9 part of dibutyl phthalate；0.5 part of zinc oxide；48 parts of neoprene；0.4 part of stearic acid；The tetramethyl autumn
Blue 0.05 part of nurse；1.9 parts of sodium hydroxide；1 part of adhesion agent.
Further, the distribution density of the micelle 3 is 30%.
Embodiment 3：
A kind of plastic uptake adhesive tape provided in this embodiment, its glue-line 2 for including substrate 1 and being formed in the substrate 1, the adhesive tape
The micelle 3 for being scattered in 2 surface of glue-line is further included, the adhesion strength of the glue-line 2 is more than the adhesion strength of the micelle 3, and the micelle 3 wraps
Include micelle 3 made of following number raw material：26 parts of toluene；25 parts of asphalt；1.1 parts of dibutyl phthalate；Zinc oxide
0.7 part；52 parts of neoprene；0.6 part of stearic acid；0.07 part of tetramethylthiuram disulfide；2.1 parts of sodium hydroxide；Adhesion agent 5
Part.
Further, the distribution density of the micelle 3 is 60%.
Embodiment 4：
A kind of plastic uptake adhesive tape provided in this embodiment, its glue-line 2 for including substrate 1 and being formed in the substrate 1, the adhesive tape
The micelle 3 for being scattered in 2 surface of glue-line is further included, the adhesion strength of the glue-line 2 is more than the adhesion strength of the micelle 3, and the micelle 3 wraps
Include micelle 3 made of following number raw material：24.5 parts of toluene；24.5 parts of asphalt；0.95 part of dibutyl phthalate；Oxygen
Change 0.65 part of zinc；49 parts of neoprene；0.55 part of stearic acid；0.065 part of tetramethylthiuram disulfide；2.0 parts of sodium hydroxide；
4 parts of adhesion agent.
Further, the distribution density of the micelle 3 is 55%.
Embodiment 5：
A kind of plastic uptake adhesive tape provided in this embodiment, its glue-line 2 for including substrate 1 and being formed in the substrate 1, the adhesive tape
The micelle 3 for being scattered in 2 surface of glue-line is further included, the adhesion strength of the glue-line 2 is more than the adhesion strength of the micelle 3, and the micelle 3 wraps
Include micelle 3 made of following number raw material：25.8 parts of toluene；23.8 parts of asphalt；1.08 parts of dibutyl phthalate；Oxygen
Change 0.68 part of zinc；51 parts of neoprene；0.45 part of stearic acid；0.06 part of tetramethylthiuram disulfide；2.05 parts of sodium hydroxide；
3.5 parts of adhesion agent.
Further, the distribution density of the micelle 3 is 20%.
Since the present invention is adhered to initially by glue-line 2, in addition micelle is set, and micelle by toluene, asphalt,
Dibutyl phthalate, zinc oxide, neoprene, stearic acid, tetramethylthiuram disulfide and sodium hydroxide are made so that
At the initial stage of fitting, it is easier to tear off；After gel bed permeability, the cohesive force of plastic uptake adhesive tape is higher, so as to ensure the viscous of plastic uptake adhesive tape
Knot property is preferable, while the weather-resistant property of micelle is preferable, adapts to the acute variation of the environment temperature between h and c, sealing effect
It is good, while sodium hydroxide has moisture resistance, can absorb the air in packaging, further improve sealing intensity.
Those skilled in the art can also do other changes in spirit of the invention, be imitated without departing from the technology of the present invention
Fruit.These changes done according to present invention spirit, should all be included within scope of the present invention.
Claims (5)
1. a kind of plastic uptake adhesive tape, its glue-line (2) for including substrate (1) and being formed in the substrate (1), which further includes scattered
Micelle (3) in glue-line (2) surface, the adhesion strength of the glue-line (2) are more than the adhesion strength of the micelle (3), it is characterised in that：Institute
Stating micelle (3) includes micelle (3) made of following number raw material：24~26 parts of toluene；23~25 parts of asphalt；O-phthalic
0.9~1.1 part of dibutyl phthalate；0.5~0.7 part of zinc oxide；48~52 parts of neoprene；0.4~0.6 part of stearic acid；Curing
0.05~0.07 part of tetra methylthiuram；1.9~2.1 parts of sodium hydroxide；1~5 part of adhesion agent.
A kind of 2. plastic uptake adhesive tape according to claim 1, it is characterised in that：The micelle (3) includes following number raw material
Manufactured micelle (3)：25 parts of toluene；24 parts of asphalt；1 part of dibutyl phthalate；0.6 part of zinc oxide；Neoprene
50 parts；0.5 part of stearic acid；0.06 part of tetramethylthiuram disulfide；2 parts of sodium hydroxide；3 parts of adhesion agent.
A kind of 3. plastic uptake adhesive tape according to claim 2, it is characterised in that：The distribution density of the micelle (3) is 20%-
60%.
A kind of 4. plastic uptake adhesive tape according to claim 2, it is characterised in that：A diameter of 50 microns of the micelle (3).
A kind of 5. plastic uptake adhesive tape according to any one claim in above-mentioned 1-4, it is characterised in that：The micelle (3) is logical
Following methods are crossed to be prepared：
S1, first dissolve asphalt heating and be in a liquid state, and sloughs moisture, removes impurity；While agitating, 50 weights are added
The toluene of % is measured, is uniformly mixed, cold primer-oil is made；
S2, by neoprene, dibutyl phthalate, zinc oxide, neoprene, stearic acid tetramethylthiuram disulfide and
Sodium hydroxide puts on rubber mixing machine and is kneaded together, obtains micelle；
S3, the thin slice that the micelle is pressed into 1~2 millimeters thick；The thin slice is cut into fractionlet；Afterwards, will be described small broken
The toluene of piece and remaining 50 weight % are put into mixer together, when stirring 3~5 is small, obtain chloroprene rubber solution；Finally,
Cold primer-oil and chloroprene rubber solution are put together, stirred evenly, glue is made, then add adhesion agent and glue is made as requested
Grain (3) is adhered on glue-line (2).