CN108018113A - A kind of environment protection type multifunctional fully synthetic cutting fluid - Google Patents
A kind of environment protection type multifunctional fully synthetic cutting fluid Download PDFInfo
- Publication number
- CN108018113A CN108018113A CN201711216481.XA CN201711216481A CN108018113A CN 108018113 A CN108018113 A CN 108018113A CN 201711216481 A CN201711216481 A CN 201711216481A CN 108018113 A CN108018113 A CN 108018113A
- Authority
- CN
- China
- Prior art keywords
- cutting fluid
- environment protection
- fully synthetic
- protection type
- type multifunctional
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environment protection type multifunctional fully synthetic cutting fluid, its formula is by weight percentage：Organic carboxyl acid 4%；Inorganic acid 5%；Organic base 18% 20%；Polyethylene glycol monooleate 6%；Extreme pressure agent 3%；Fungicide 2%；Defoamer 1%；Deionized water 59% -61%.The beneficial effects of the invention are as follows：Compounded by the science of triethanolamine organic carboxyl acid soap, triethanolamine borate and thiocarbamide so that the extreme boundary lubrication performance of cutting fluid increases substantially, and the dilution PB values of 5% cutting fluid reach more than 1000N, more than the requirements of GB/T6144-2010.Fully synthetic cutting fluid provided by the invention, compared with oil base cutting fluid, semi-synthetic cutting fluid, have it is of low cost, usage amount is few, and greasy property is good, and liquid waste processing is simple, can be recycled and is not easy the advantages that smelly.Environment protection type multifunctional fully synthetic cutting fluid of the present invention, during smooth surface products C NC process high for aluminium alloy, does not influence the glossiness of product surface.Environment protection type multifunctional fully synthetic cutting fluid of the present invention, free from extraneous odour, safety and environmental protection.
Description
Technical field
The present invention relates to a kind of cutting fluid, is specially a kind of environment protection type multifunctional fully synthetic cutting fluid, is widely used in steel
Cooling, lubrication, antirust and the cleaning of metal-cutting machine tool in the metal material CNC process such as iron, aluminium alloy, copper, belong to gold
Belong to processing technique field.It can also be used for the CNC process of glass.
Background technology
Cutting, drilling, edging are essential basic working procedures in metal product production and deep-processing process.Its quality will
Ask for：Metal product size is accurate, the more shallow better, no marking of section flat smooth, cutting mark, without chipping arrisdefect, do not influence height
Smooth faced metal product glossiness, metal-cutting machine tool service life length, this requires cutting liquid energy provides for metal-cutting machine tool
Excellent cooling, lubrication, cleaning metal fillings and rustless property.PBValue (maximum nonseizure load, similarly hereinafter) is to weigh cutting fluid profit
The canonical parameter of sliding abrasion resistance.By the requirements of GB/T6144-2010,5% cutting dilution presses the lubricants of GB/T3142-1982
Bearing capacity method of testing (four ball method) is detected, its PBValue should be not less than 540N (newton, similarly hereinafter).With oil base cutting fluid and half
Synthetic cutting fluid is compared, and fully synthetic cutting fluid has that cost is low, dosage is few, recycles that to be not easy smelly and liquid waste processing simple etc.
Advantage, has a vast market prospect.Therefore, it has been urgent to develop a kind of environment protection type multifunctional fully synthetic cutting fluid of function admirable
In the eyebrows and eyelashes.
The content of the invention
The technical problem to be solved in the present invention is：There is provided excellent a kind of low cost, greasy property, free from extraneous odour, circulation make
With not smelly environment protection type multifunctional fully synthetic cutting fluid.
In order to solve the above-mentioned technical problem, the present invention proposes following technical scheme：A kind of environment protection type multifunctional is fully synthetic to be cut
Liquid is cut, its formula is by weight percentage：
Further limit of above-mentioned technical proposal is：The organic carboxyl acid is vegetable oil acid, tall oil, C21Monocyclic double carboxylics
Acid, one kind in smart dimeric dibasic acid or its mixture；The inorganic acid is boric acid, and the organic base is triethanolamine；The poly- second
Glycol monooleate is polyethylene glycol 400 list oleic acid phosphate；The fungicide is phosphorus ketone fungicide, and the phosphorus ketone
Fungicide is commercially available LEX；The extreme pressure agent is thiocarbamide；The defoamer is organic silicon defoamer.
Further limit of above-mentioned technical proposal is：The manufacture method bag of the environment protection type multifunctional fully synthetic cutting fluid
Include following steps：
Step 1：By weight percentage, organic carboxyl acid, inorganic acid, organic base, polyethylene glycol 400 list oleic acid phosphate are weighed
Afterwards, bucket, turn on agitator and heater heating are entered；
Step 2：By weight percentage, deionized water, enters bucket and stirs evenly；
Step 3：By weight percentage, fungicide, extreme pressure agent, defoamer are weighed, pours into agitator.
Further limit of above-mentioned technical proposal is：Step 1 heating and temperature control is at 120 DEG C -130 DEG C, heating
Time is 30 minutes.
Further limit of above-mentioned technical proposal is：The step 2 deionized water degree is 59% -61%.
Further limit of above-mentioned technical proposal is：Step 3 stirring extent is to stir into homogeneous transparent liquid.
Further limit of above-mentioned technical proposal is：The required weighing bucket used in the process for preparation, blender plus
Hot device, agitator are both needed to 100 DEG C of high-temperature heatings of vacuum and disinfect before use.
Above-mentioned organic carboxyl acid is vegetable oil acid, tall oil, C21Monocyclic double carboxylic acids, one kind in smart dimeric dibasic acid or its mixing
Thing；Above-mentioned inorganic acid is boric acid；Above-mentioned organic base is triethanolamine；Above-mentioned polyethylene glycol monooleate is polyethylene glycol 400 list
Oleic acid phosphate；Above-mentioned fungicide is phosphorus ketone fungicide LEX；Above-mentioned extreme pressure agent is thiocarbamide.Above-mentioned defoamer is organic silicon
Defoamer.
A kind of environment protection type multifunctional fully synthetic cutting fluid proposed by the present invention, it adds CNC for metal material using object
The metal cutting tool of work is cooled down, lubricated, antirust and cleaning.The performance indicator of cutting fluid most critical is exactly that its lubrication is anti-
Grind performance, i.e. PBValue.PBValue is bigger, its lubrication abrasion resistance is better, to the metal cutting tool protectiveness of CNC intermetallic composite coatings
Can be better, metal cutting tool service life is longer.Required according to GB/T6144-2010,5% cutting dilution presses GB/
The load carrying capacity of lubricant of T3142-1982 method of testing (four ball method) is detected, its PBValue is not less than 540N.Classical lubrication resists
Mill property theory thinks：Borate is a kind of multifunction environment-protection type additive, its mechanism of action is that its friction surface forms physics
(or chemistry) adsorbed film, and friction chemical reaction generation such as H occurs due to boric acid esterolysis or with additive3BO3、
B2O3Etc. the non-sacrificial deposition film of composition, the collective effect of several films, effectively increases the tribological property of water-base cutting fluid.
Its feature is：
(1) film strength of borate is high, and friction coefficient is low, has excellent anti-wear and wear-resistant performance；
(2) there is good rustless property；
(3) there is antibacterial and sterilizing function, and nonhazardous acts on；
But it is still inadequate, it is necessary to add it using only borate its greasy property under high temperature and pressure machining condition
Its lubricant acts synergistically.Triethanolamine organic carboxyl acid soap is the water-soluble additives for having excellent lubricant effect.There is document to show
Show that triethanolamine organic carboxyl acid soap has good extreme boundary lubrication performance with thiocarbamide synergistic effect.
Compared with prior art, the invention has the advantages that：
1. compounded by the science of triethanolamine organic carboxyl acid soap, triethanolamine borate and thiocarbamide so that cutting fluid
Extreme boundary lubrication performance increases substantially, the dilution P of 5% cutting fluidBValue reaches more than 1000N, will more than GB/T6144-2010
Ask.
2. environment protection type multifunctional fully synthetic cutting fluid of the present invention, compared with oil base cutting fluid, semi-synthetic cutting fluid, have into
This is cheap, and usage amount is few, and greasy property is good, and liquid waste processing is simple, can be recycled and is not easy the advantages that smelly.
3. environment protection type multifunctional fully synthetic cutting fluid of the present invention, during smooth surface products C NC process high for aluminium alloy,
The glossiness of product surface is not influenced.
4. environment protection type multifunctional fully synthetic cutting fluid of the present invention, free from extraneous odour, safety and environmental protection.
Embodiment
Based on the embodiments of the present invention, those of ordinary skill in the art are obtained without making creative work
The every other embodiment obtained, belongs to the scope of protection of the invention.
A kind of environment protection type multifunctional fully synthetic cutting fluid proposed by the present invention, by following components group
Into：
Above-mentioned organic carboxyl acid includes but not limited to vegetable oil acid, tall oil, C21One kind in monocyclic double carboxylic acids, smart dimeric dibasic acid
Or its mixture；Above-mentioned inorganic acid includes but not limited to boric acid；Above-mentioned organic base includes but not limited to triethanolamine；Above-mentioned poly- second
Glycol monooleate includes but not limited to polyethylene glycol 400 list oleic acid phosphate；Above-mentioned fungicide includes but not limited to phosphorus ketone
Fungicide LEX；Above-mentioned extreme pressure agent includes but not limited to thiocarbamide；Above-mentioned defoamer includes but not limited to organic silicon defoamer.
The manufacture method of above-mentioned environment protection type multifunctional fully synthetic cutting fluid comprises the following steps：
Step 1：By weight percentage, organic carboxyl acid, inorganic acid, organic base, polyethylene glycol 400 list oleic acid phosphoric acid are weighed
Ester, enters bucket, turn on agitator and heater, is heated to 120 DEG C -130 DEG C, stops heating；
Step 2：By weight percentage, deionized water, enters bucket and stirs evenly；
Step 3：By weight percentage, fungicide, extreme pressure agent, defoamer are weighed, pours into agitator, stirs into homogeneous transparent
Liquid, that is, be made environment protection type multifunctional fully synthetic cutting fluid.
The preferred solution of above-mentioned environment protection type multifunctional fully synthetic cutting fluid proposed by the present invention, by it is following by weight percentage
The component composition of meter：
The manufacture method of above-mentioned environment protection type multifunctional fully synthetic cutting fluid comprises the following steps：
Step 1：By weight percentage, vegetable oil acid, tall oil, C are weighed21One kind in monocyclic double carboxylic acids, smart dimeric dibasic acid
Or its mixture 4%, boric acid 5% is weighed, weighs triethanolamine 18%-20%, weighs polyethylene glycol 400 list oleic acid phosphate
6%, enter bucket, turn on agitator and heater, be heated to 120 DEG C -130 DEG C, stop heating；
Step 2：By weight percentage, deionized water 59% -61%, enters bucket and stirs evenly；
Step 3：By weight percentage, phosphorus ketone fungicide LEX2%, thiocarbamide 3%, organic silicon defoamer 1% are weighed, is fallen
Enter agitator, stir into homogeneous transparent liquid, that is, environment protection type multifunctional fully synthetic cutting fluid is made.
Embodiment 1：
The component and content of environment protection type multifunctional fully synthetic cutting fluid are as shown in the table：
The manufacture method for manufacturing the above-mentioned environment protection type multifunctional fully synthetic cutting fluids of 100 ㎏ is as follows：
4 kilograms of vegetable oil acid is weighed, weighs 5 kilograms of boric acid, 18 kilograms of triethanolamine is weighed, weighs polyethylene glycol 400 list
6 kilograms of oleic acid phosphate, enters bucket, turn on agitator and heater, is heated to 120 DEG C -130 DEG C, stops heating；
61 kilograms of deionized water is weighed, enters bucket and stirs evenly；
LEX2 kilograms of phosphorus ketone fungicide, 3 kilograms of thiocarbamide, 1 kilogram of organic silicon defoamer are weighed, pours into agitator, is stirred
Into homogeneous transparent liquid, that is, environment protection type multifunctional fully synthetic cutting fluid is made.
Embodiment 2：
The component and content of environment protection type multifunctional fully synthetic cutting fluid are as shown in the table：
The manufacture method for manufacturing the above-mentioned environment protection type multifunctional fully synthetic cutting fluids of 100 ㎏ is as follows：
Weigh C21Monocyclic 4 kilograms of double carboxylic acids, weigh 5 kilograms of boric acid, weigh 20 kilograms of triethanolamine, weigh polyethylene glycol
400 single 6 kilograms of oleic acid phosphates, enter bucket, turn on agitator and heater, are heated to 120 DEG C -130 DEG C, stop heating；
59 kilograms of deionized water is weighed, enters bucket and stirs evenly；
LEX2 kilograms of phosphorus ketone fungicide, 3 kilograms of thiocarbamide, 1 kilogram of organic silicon defoamer are weighed, pours into agitator, is stirred
Into homogeneous transparent liquid, that is, environment protection type multifunctional fully synthetic cutting fluid is made.
Embodiment 3：
The component and content of environment protection type multifunctional fully synthetic cutting fluid are as shown in the table：
The manufacture method for manufacturing the above-mentioned environment protection type multifunctional fully synthetic cutting fluids of 100 ㎏ is as follows：
4 kilograms of tall oil is weighed, weighs 5 kilograms of boric acid, weighs 18 kilograms of triethanolamine, weighs polyethylene glycol 400 list oil
6 kilograms of acid phosphoric acid ester, enters bucket, turn on agitator and heater, is heated to 120 DEG C -130 DEG C, stops heating；
61 kilograms of deionized water is weighed, enters bucket and stirs evenly；
LEX2 kilograms of phosphorus ketone fungicide, 3 kilograms of thiocarbamide, 1 kilogram of organic silicon defoamer are weighed, pours into agitator, is stirred
Into homogeneous transparent liquid, that is, environment protection type multifunctional fully synthetic cutting fluid is made.
Embodiment 4：
The component and content of environment protection type multifunctional fully synthetic cutting fluid are as shown in the table：
The manufacture method for manufacturing the above-mentioned environment protection type multifunctional fully synthetic cutting fluids of 100 ㎏ is as follows：
Smart 4 kilograms of dimeric dibasic acid is weighed, weighs 5 kilograms of boric acid, 18 kilograms of triethanolamine is weighed, weighs polyethylene glycol 400 list
6 kilograms of oleic acid phosphate, enters bucket, turn on agitator and heater, is heated to 120 DEG C -130 DEG C, stops heating；
61 kilograms of deionized water is weighed, enters bucket and stirs evenly；
LEX2 kilograms of phosphorus ketone fungicide, 3 kilograms of thiocarbamide, 1 kilogram of organic silicon defoamer are weighed, pours into agitator, is stirred
Into homogeneous transparent liquid, that is, environment protection type multifunctional fully synthetic cutting fluid is made.
By the load carrying capacity of lubricant of GB/T3142-1982 method of testing (four ball method) testing result：
Embodiment 1, embodiment 2, embodiment 3,4 product P of embodimentbValue is all higher than 540N.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Profit requires rather than described above limits, it is intended that all in the implication and scope of the equivalency of claim by falling
Change is included in the present invention.
Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each embodiment is only wrapped
Containing an independent technical solution, this narrating mode of specification is only that those skilled in the art should for clarity
Using specification as an entirety, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
It is appreciated that other embodiment.
Claims (7)
- A kind of 1. environment protection type multifunctional fully synthetic cutting fluid, it is characterised in that：Its formula is by weight percentage：
- 2. environment protection type multifunctional fully synthetic cutting fluid according to claim 1, it is characterised in that：The organic carboxyl acid is plant Thing oleic acid, tall oil, C21Monocyclic double carboxylic acids, one kind in smart dimeric dibasic acid or its mixture；The inorganic acid is boric acid, described to have Machine alkali is triethanolamine；The polyethylene glycol monooleate is polyethylene glycol 400 list oleic acid phosphate；The fungicide is phosphorus ketone Series bactericidal agent, and the phosphorus ketone fungicide is commercially available LEX；The extreme pressure agent is thiocarbamide；The defoamer disappears for organic silicon Infusion.
- A kind of 3. environment protection type multifunctional fully synthetic cutting fluid, it is characterised in that：The environment protection type multifunctional fully synthetic cutting fluid Process for preparation comprises the following steps：Step 1：By weight percentage, organic carboxyl acid is weighed, inorganic acid, organic base, after polyethylene glycol 400 list oleic acid phosphate, Enter bucket, turn on agitator and heater heating；Step 2：By weight percentage, deionized water, enters bucket and stirs evenly；Step 3：By weight percentage, fungicide, extreme pressure agent, defoamer are weighed, pours into agitator.
- A kind of 4. environment protection type multifunctional fully synthetic cutting fluid process for preparation according to claim 3, it is characterised in that：It is described For step 1 heating and temperature control at 120 DEG C -130 DEG C, heating time is 30 minutes.
- A kind of 5. environment protection type multifunctional fully synthetic cutting fluid process for preparation according to claim 3, it is characterised in that：It is described Step 2 deionized water degree is 59% -61%.
- A kind of 6. environment protection type multifunctional fully synthetic cutting fluid process for preparation according to claim 3, it is characterised in that：It is described Step 3 stirring extent is to stir into homogeneous transparent liquid.
- A kind of 7. environment protection type multifunctional fully synthetic cutting fluid process for preparation according to claim 3, it is characterised in that：It is described The required weighing bucket used, blender, heater, agitator are both needed to 100 DEG C of high-temperature heatings of vacuum before use in process for preparation Disinfect.