CN108017293A - 一种基于铁尾矿的胶凝剂和建筑材料 - Google Patents
一种基于铁尾矿的胶凝剂和建筑材料 Download PDFInfo
- Publication number
- CN108017293A CN108017293A CN201711203080.0A CN201711203080A CN108017293A CN 108017293 A CN108017293 A CN 108017293A CN 201711203080 A CN201711203080 A CN 201711203080A CN 108017293 A CN108017293 A CN 108017293A
- Authority
- CN
- China
- Prior art keywords
- iron tailings
- parts
- gelling agent
- agricultural
- forestry biomass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种基于铁尾矿的胶凝剂和建筑材料。基于铁尾矿的胶凝剂由以下质量份的原料组成:22~35份铁尾矿,18~25份农林生物质,40~50份水泥熟料,1~6份生石灰,2~8份脱硫石膏。同时也公开了一种基于铁尾矿的建筑材料。本发明利用铁尾矿及农林生物质为主要原料,制备得到一种性能优良的建筑材料,能够解决铁尾矿堆放带来的污染和资源浪费问题,同时还可以综合利用资源,达到环保的目的,具有良好的应用前景。
Description
技术领域
本发明涉及一种基于铁尾矿的胶凝剂和建筑材料。
背景技术
铁尾矿是铁选厂在特定经济技术条件下,将铁矿石磨细,选取有用组分后排放的废弃物,也就是铁矿石经过选取铁精矿后剩余的固体废物。改革开放以来,我国矿山开采出现了前所未有的高峰。据工业和信息化部近期的初步排查,截至2014年,我国有15.3万个矿山;2700多座大型尾矿库积存总量超过50亿吨,其中铁尾矿占30亿吨,大量的尾矿不仅占用了土地和造成资源的浪费,而且也给人类的生活环境带来了严重的污染和危害,破坏生态平衡等问题,为铁尾矿找到一种新的利用途径,不仅能节省资源还能消除其带来的安全隐患。
发明内容
本发明的目的在于提供一种基于铁尾矿的胶凝剂和建筑材料。
本发明所采取的技术方案是:
一种基于铁尾矿的胶凝剂,由以下质量份的原料组成:22~35份铁尾矿,18~25份农林生物质,40~50份水泥熟料,1~6份生石灰,2~8份脱硫石膏。
优选的,一种基于铁尾矿的胶凝剂,由以下质量份的原料组成:25~30份铁尾矿,20~22份农林生物质,42~45份水泥熟料,2~5份生石灰,3~5份脱硫石膏。
进一步的,铁尾矿的化学成分及质量分数为:SiO2占34~35%,CaO占8~23%,Al2O3占5~7%,MgO占3~6%,Na2O占0.5~2%,Fe2O3占16~29%,S的氧化物占7~12%。
进一步的,农林生物质的粒径为300~900μm。
进一步的,农林生物质是由麦秆、玉米杆、稻草、稻壳、锯末和核桃壳粒组成的混合物。
进一步的,农林生物质中,麦秆、玉米杆、稻草、稻壳、锯末和核桃壳粒的质量比为(25~30):(10~15):(30~40):(25~30):(20~30):(1~5)。
一种基于铁尾矿的建筑材料,包括上述的胶凝剂和水。
进一步的,水和胶凝剂的质量比为(0.4~0.5):1。
本发明的有益效果是:
本发明利用铁尾矿及农林生物质为主要原料,制备得到一种性能优良的建筑材料,能够解决铁尾矿堆放带来的污染和资源浪费问题,同时还可以综合利用资源,达到环保的目的,具有良好的应用前景。
具体实施方式
一种基于铁尾矿的胶凝剂,由以下质量份的原料组成:22~35份铁尾矿,18~25份农林生物质,40~50份水泥熟料,1~6份生石灰,2~8份脱硫石膏。
优选的,一种基于铁尾矿的胶凝剂,由以下质量份的原料组成:25~30份铁尾矿,20~22份农林生物质,42~45份水泥熟料,2~5份生石灰,3~5份脱硫石膏。
进一步的,铁尾矿的化学成分及质量分数为:SiO2占34~35%,CaO占8~23%,Al2O3占5~7%,MgO占3~6%,Na2O占0.5~2%,Fe2O3占16~29%,S的氧化物占7~12%。
进一步的,农林生物质的粒径为300~900μm。
进一步的,农林生物质是由麦秆、玉米杆、稻草、稻壳、锯末和核桃壳粒组成的混合物。
进一步的,农林生物质中,麦秆、玉米杆、稻草、稻壳、锯末和核桃壳粒的质量比为(25~30):(10~15):(30~40):(25~30):(20~30):(1~5)。
进一步的,脱硫石膏的粒径分布为:小于3.15μm的占10wt%,小于5.32μm的占30wt%,小于6.75μm的占50%,小于10.71μm的占60%,小于26.24μm的占90wt%。
一种基于铁尾矿的建筑材料,包括上述的胶凝剂和水。
进一步的,水和胶凝剂的质量比为(0.4~0.5):1;优选的,水和胶凝剂的质量比为0.48:1。
以下通过具体的实施例对本发明的内容作进一步详细的说明。
实施例1:
实施例1的胶凝剂原料组成见表1。
表1实施例1的胶凝剂
原料 | 质量份 |
铁尾矿 | 25 |
农林生物质 | 20 |
水泥熟料 | 45 |
生石灰 | 5 |
脱硫石膏 | 5 |
实施例2:
实施例2的胶凝剂原料组成见表2。
表2实施例2的胶凝剂
原料 | 质量份 |
铁尾矿 | 28 |
农林生物质 | 20 |
水泥熟料 | 42 |
生石灰 | 5 |
脱硫石膏 | 5 |
实施例3:
实施例3的胶凝剂原料组成见表3。
表3实施例3的胶凝剂
原料 | 质量份 |
铁尾矿 | 30 |
农林生物质 | 22 |
水泥熟料 | 43 |
生石灰 | 2 |
脱硫石膏 | 3 |
实施例4:
实施例4的胶凝剂原料组成见表4。
表4实施例4的胶凝剂
原料 | 质量份 |
铁尾矿 | 26 |
农林生物质 | 22 |
水泥熟料 | 43 |
生石灰 | 5 |
脱硫石膏 | 4 |
实施例1~4中,所用的铁尾矿的化学成分及质量分数为:SiO2占34.5%,CaO占18.8%,Al2O3占6.2%,MgO占4.3%,Na2O占1.1%,Fe2O3占24.6%,S的氧化物占9.4%;所用的农林生物质是麦秆、玉米杆、稻草、稻壳、锯末和核桃壳粒的以质量比为27:13:35:28:25:2组成的混合物,使用前按配比将各种生物质原料称量混合,磨成粉末状,其粒径为300~900μm;所用的脱硫石膏其粒径分布为:小于3.15μm的占10wt%,小于5.32μm的占30wt%,小于6.75μm的占50%,小于10.71μm的占60%,小于26.24μm的占90wt%。
制备及测试方法:
1、根据实施例1~4所述的组成称取原材料,倒入搅拌机,搅拌180s,使其完全均匀,制得胶凝剂;
2、按照水胶比0.48的质量浓度,称取定量的水,分别加入实施例1~4的胶凝剂,搅拌60s;
3、将锅壁四周浆体刮入锅内后,再搅拌60s,由此分别制成实施例1~4的建筑料浆材料;
4、将充分混合的浆料依次均匀倒入内壁刷满润滑油的100*100*100mm大小的标准三联试模中,每组样品浇注三组,分别用以测量28天的强度;
5、将试块放入温度为(20±1)℃,相对湿度为95%的标准养护箱内,养护24h后脱模将试块重新放入养护箱中养护至相应龄期,用全自动压力试验机以100N/s的速度按照GB/T50081-2016《普通混凝土力学性能试验方法标准》测试其28天强度,共测试3个试块,取其平均值作为该龄期充填体的单轴抗压强度。
实施例1~4制备所得的建筑材料强度性能如下表5所示:
表5建筑材料性能
从表5可以看出,实施例1~4制成的建材试块强度均满足大于MU15的要求,其吸水率均小于18%,软化性能大于0.8。因此可以利用此法生产建材,减少铁尾矿堆放带来的不利影响。
Claims (8)
1.一种基于铁尾矿的胶凝剂,其特征在于:由以下质量份的原料组成:22~35份铁尾矿,18~25份农林生物质,40~50份水泥熟料,1~6份生石灰,2~8份脱硫石膏。
2.根据权利要求1所述的一种基于铁尾矿的胶凝剂,其特征在于:由以下质量份的原料组成:25~30份铁尾矿,20~22份农林生物质,42~45份水泥熟料,2~5份生石灰,3~5份脱硫石膏。
3.根据权利要求1或2所述的一种基于铁尾矿的胶凝剂,其特征在于:铁尾矿的化学成分及质量分数为:SiO2占34~35%,CaO占8~23%,Al2O3占5~7%,MgO占3~6%,Na2O占0.5~2%,Fe2O3占16~29%,S的氧化物占7~12%。
4.根据权利要求1或2所述的一种基于铁尾矿的胶凝剂,其特征在于:农林生物质的粒径为300~900μm。
5.根据权利要求4所述的一种基于铁尾矿的胶凝剂,其特征在于:农林生物质是由麦秆、玉米杆、稻草、稻壳、锯末和核桃壳粒组成的混合物。
6.根据权利要求5所述的一种基于铁尾矿的胶凝剂,其特征在于:农林生物质中,麦秆、玉米杆、稻草、稻壳、锯末和核桃壳粒的质量比为(25~30):(10~15):(30~40):(25~30):(20~30):(1~5)。
7.一种基于铁尾矿的建筑材料,其特征在于:包括权利要求1~6任一项所述的胶凝剂和水。
8.根据权利要求7所述的一种基于铁尾矿的建筑材料,其特征在于:水和胶凝剂的质量比为(0.4~0.5):1。