CN108014442A - 一种锂电池灭火剂 - Google Patents
一种锂电池灭火剂 Download PDFInfo
- Publication number
- CN108014442A CN108014442A CN201711166647.1A CN201711166647A CN108014442A CN 108014442 A CN108014442 A CN 108014442A CN 201711166647 A CN201711166647 A CN 201711166647A CN 108014442 A CN108014442 A CN 108014442A
- Authority
- CN
- China
- Prior art keywords
- parts
- extinguishing chemical
- lithium battery
- compounding
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种锂电池灭火剂,其特征在于,按重量份数由以下原料制成:氟化烷基甜菜碱2‑3份、月桂酰胺丙基二甲胺乙内酯15‑25份、有机硅季铵盐0.5‑2.5份、十二烷基甜菜碱5‑15份、乙二醇与丙三醇的复配40‑55份、二乙二醇丁醚与正丁醇复配5‑20份、尿素5‑10份、黄原胶0.03‑0.08份、海藻酸钠0.5‑1份、乙二胺四乙酸钠或乙二胺四乙酸或柠檬酸钠2‑10份、三乙醇胺0.1‑1份、水80‑100份。本发明具有极低的腐蚀性,不损坏储存罐、消防设施及被保护物品灭火后残留物非常易于清理,可自行降解,特别适用于铝电池灭火。
Description
技术领域
本发明涉及灭火剂领域,具体涉及一种锂电池灭火剂。
背景技术
锂电池是一类由锂金属或锂合金为负极材料、使用非水电解质溶液的电池,锂电池大致可分为两类:锂金属电池和锂离子电池。锂离子电池不含有金属态的锂,并且是可以充电的。锂离子电池一般是使用锂合金金属氧化物为正极材料、石墨为负极材料、使用非水电解质的电池。着数码产品如手机、笔记本电脑等产品的广泛使用,锂离子电池以优异的性能在这类产品中得到广泛应用,并在逐步向其他产品应用领域发展。锂离子电池已经成为了主流。
电池在出厂之前都会进行首次充电、搁置并进行检测,充电之后如果出现短路情况,就会引发自燃现象。“短路分内部短路和外部短路两种,外部短路的原因可能是在储存、运输等过程中造成,而内部短路则是产品本身的问题”,这些问题包括:在生产过程中,环境不洁净,导致正负极片上沾染别的物质;内部隔膜不能有效的分隔正负极,存在瑕疵。这都会导致存储在电池中的电量会迅速通过连接点释放,瞬间放出大量的热,电池温度急剧升高,首先导致电解液、隔膜等可燃物燃烧,待温度上升到一定程度后,正负极物质及铝箔也会剧烈燃烧,中心温度上升到1000摄氏度以上,并发生类似爆炸的现象。如果在工厂内部,大量电池集中存放,会导致连锁起火爆炸。
由于电池内部自燃爆炸,此时用干粉灭火器就无法奏效,目前最好的方法是用水去降温,尚无针对性的有效灭火产品。
发明内容
有鉴于此,本发明的目的在于提供一种:一种锂电池灭火剂。
为了实现上述目的,本发明采用的技术方案一为:一种锂电池灭火剂,按重量份数由以下原料制成:氟化烷基甜菜碱2-3份、月桂酰胺丙基二甲胺乙内酯15-25份、有机硅季铵盐0.5-2.5份、十二烷基甜菜碱5-15份、乙二醇与丙三醇的复配40-55份、二乙二醇丁醚与正丁醇复配5-20份、尿素5-10份、黄原胶0.03-0.08份、海藻酸钠0.5-1份、乙二胺四乙酸钠或乙二胺四乙酸或柠檬酸钠2-10份、三乙醇胺 0.1-1份、水80-100份。
进一步的,按重量份数由以下原料制成:氟化烷基甜菜碱3份、月桂酰胺丙基二甲胺乙内酯24.8份、有机硅季铵盐2份、十二烷基甜菜碱14份、乙二醇与丙三醇的复配40.2份、二乙二醇丁醚与正丁醇复配5.6份、尿素5.6份、黄原胶0.03份、海藻酸钠0.5份、乙二胺四乙酸钠2.1份、三乙醇胺 0.2份、水80份。
进一步的,按重量份数由以下原料制成:氟化烷基甜菜碱2.5份、月桂酰胺丙基二甲胺乙内酯20.2份、有机硅季铵盐1.5份、十二烷基甜菜碱10份、乙二醇与丙三醇的复配50份、二乙二醇丁醚与正丁醇复配12份、尿素7份、黄原胶0.05份、海藻酸钠0.75份、乙二胺四乙酸6份、三乙醇胺0.5份、水90份。
进一步的,其特征在于,按重量份数由以下原料制成:氟化烷基甜菜碱2份、月桂酰胺丙基二甲胺乙内酯15.3份、有机硅季铵盐0.51份、十二烷基甜菜碱5.2份、乙二醇与丙三醇的复配55份、二乙二醇丁醚与正丁醇复配19.5份、尿素9.5份、黄原胶0.08份、海藻酸钠1份、柠檬酸钠9.9份、三乙醇胺1份、水100份。
上述技术方案的关键构思及有益效果在于:
一、铝电池着火优选快速降温的方式,针对性的所选的灭火剂增加化学抑制性能。灭火剂中的成分与自由基发生化学反应,生成稳定性物质,抑制新的自由基产生;
二、铝电池中的活性金属离子能跟二氧化碳反应产生可燃气体,因此减少灭火剂中的钠盐等可起反应助燃成分;
三、相应的减少发泡倍数、增加含水量,利用水的比热大特点快速降低温度;
四、合成原料均为低毒或无毒、无腐蚀性的天然提取物,或对皮肤低刺激性、生物降解性好的化合物;
五、选用乙二醇与丙三醇的复配作为抗冻剂,既保证灭火剂的抗冻性能,又降低灭火剂的腐蚀性;
六、皮肤接触实验中,皮肤无任何不适反应,漱口实验证明对人体粘膜组织无任何损伤极低的腐蚀性,不损坏储存罐、消防设施及被保护物品灭火后残留物非常易于清理,可自行降解,特别适用于铝电池类灭火。
一种锂电池灭火剂的制备方法,包括如下步骤:
步骤一、按上述重量称取氟化烷基甜菜碱、月桂酰胺丙基二甲胺乙内酯、十二烷基甜菜碱、尿素、黄原胶、海藻酸钠、乙二胺四乙酸钠或乙二胺四乙酸或柠檬酸钠,在搅拌机中搅拌均匀,搅拌机转速为2200-2400转/分钟;
步骤二、按上述重量称取乙二醇或乙二醇与丙三醇的复配、二乙二醇丁醚与正丁醇复配、三乙醇胺、水,加入反应釜中搅拌均匀,然后加入步骤一制得的混合物充分搅拌至完全溶解制得锂电池灭火剂。
上述技术方案的关键构思在于:将上述固态原料充分混合搅拌后,再加入到已经充分融合的液态原料中混合均匀,反应速度快,生产效率高。
上述技术方案的有益效果是:生产过程中不产生任何有毒有害物质,操作简便、安全,产品生产效率高,成品良品率高。
具体实施方式
下面结合具体实施例对本发明做进一步的说明如下:
实施例一:
步骤一、称取氟化烷基甜菜碱3份、月桂酰胺丙基二甲胺乙内酯24.8份、有机硅季铵盐2份、十二烷基甜菜碱14份、尿素5.6份、黄原胶0.03份、海藻酸钠0.5份、乙二胺四乙酸钠2.1份,在搅拌机中搅拌均匀,搅拌机转速为2400转/分钟;
步骤二、称取乙二醇与丙三醇的复配40.2份、二乙二醇丁醚或正丁醇或二者复配5.6份、三乙醇胺0.2份、水80份,加入反应釜中搅拌均匀,然后加入步骤一制得的混合物充分搅拌至完全溶解制得锂电池灭火剂。
施例二:
步骤一、称取氟化烷基甜菜碱2.5份、月桂酰胺丙基二甲胺乙内酯20.2份、有机硅季铵盐1.5份、十二烷基甜菜碱10份、尿素7份、黄原胶0.05份、海藻酸钠0.75份、乙二胺四乙酸6份,在搅拌机中搅拌均匀,搅拌机转速为2300转/分钟;
步骤二、称取乙二醇与丙三醇的复配50份、二乙二醇丁醚与正丁醇复配12份、三乙醇胺0.5份、水90份,加入反应釜中搅拌均匀,然后加入步骤一制得的混合物充分搅拌至完全溶解制得锂电池灭火剂。
施例三:
步骤一、称取氟化烷基甜菜碱2份、月桂酰胺丙基二甲胺乙内酯15.3份、有机硅季铵盐0.51份、十二烷基甜菜碱5.2份、尿素9.5份、黄原胶0.08份、海藻酸钠1份、柠檬酸钠9.9份,在搅拌机中搅拌均匀,搅拌机转速为2200转/分钟;
步骤二、称取乙二醇与丙三醇的复配55份、二乙二醇丁醚与正丁醇复配19.5份、三乙醇胺1份、水100份,加入反应釜中搅拌均匀,然后加入步骤一制得的混合物充分搅拌至完全溶解制得锂电池灭火剂。
上述实施例1-3所得本发明的锂电池灭火剂产品特性如下:
。
本发明已由上述相关实施例加以描述,然而上述实施例仅为实施本发明的范例。必须指出的是,已揭露的实施例并未限制本发明的范围。相反地,包括于权利要求的精神及范围的修改及均等设置均包括于本发明的范围内。
Claims (5)
1.一种锂电池灭火剂,其特征在于,按重量份数由以下原料制成:氟化烷基甜菜碱2-3份、月桂酰胺丙基二甲胺乙内酯15-25份、有机硅季铵盐0.5-2.5份、十二烷基甜菜碱5-15份、乙二醇与丙三醇的复配40-55份、二乙二醇丁醚与正丁醇复配5-20份、尿素5-10份、黄原胶0.03-0.08份、海藻酸钠0.5-1份、乙二胺四乙酸钠或乙二胺四乙酸或柠檬酸钠2-10份、三乙醇胺 0.1-1份、水80-100份。
2.根据权利要求1所述的一种锂电池灭火剂,其特征在于,按重量份数由以下原料制成:氟化烷基甜菜碱3份、月桂酰胺丙基二甲胺乙内酯24.8份、有机硅季铵盐2份、十二烷基甜菜碱14份、乙二醇与丙三醇的复配40.2份、二乙二醇丁醚与正丁醇复配5.6份、尿素5.6份、黄原胶0.03份、海藻酸钠0.5份、乙二胺四乙酸钠2.1份、三乙醇胺 0.2份、水80份。
3.根据权利要求1所述的一种锂电池灭火剂,其特征在于,按重量份数由以下原料制成:氟化烷基甜菜碱2.5份、月桂酰胺丙基二甲胺乙内酯20.2份、有机硅季铵盐1.5份、十二烷基甜菜碱10份、乙二醇与丙三醇的复配50份、二乙二醇丁醚与正丁醇复配12份、尿素7份、黄原胶0.05份、海藻酸钠0.75份、乙二胺四乙酸6份、三乙醇胺0.5份、水90份。
4.根据权利要求1所述的一种锂电池灭火剂,其特征在于,按重量份数由以下原料制成:氟化烷基甜菜碱2份、月桂酰胺丙基二甲胺乙内酯15.3份、有机硅季铵盐0.51份、十二烷基甜菜碱5.2份、乙二醇与丙三醇的复配55份、二乙二醇丁醚与正丁醇复配19.5份、尿素9.5份、黄原胶0.08份、海藻酸钠1份、柠檬酸钠9.9份、三乙醇胺1份、水100份。
5.根据权利要求1-4任一权利要求所述的一种锂电池灭火剂的制备方法,其特征在于,包括如下步骤:
步骤一、按上述重量称取氟化烷基甜菜碱、月桂酰胺丙基二甲胺乙内酯、十二烷基甜菜碱、尿素、黄原胶、海藻酸钠、乙二胺四乙酸钠或乙二胺四乙酸或柠檬酸钠,在搅拌机中搅拌均匀,搅拌机转速为2200-2400转/分钟;
步骤二、按上述重量称取乙二醇或乙二醇与丙三醇的复配、二乙二醇丁醚与正丁醇复配、三乙醇胺、水,加入反应釜中搅拌均匀,然后加入步骤一制得的混合物充分搅拌至完全溶解制得锂电池灭火剂。