CN107986703A - A kind of aerated bricks of weather resistance high compressive strength and preparation method thereof - Google Patents
A kind of aerated bricks of weather resistance high compressive strength and preparation method thereof Download PDFInfo
- Publication number
- CN107986703A CN107986703A CN201711204662.0A CN201711204662A CN107986703A CN 107986703 A CN107986703 A CN 107986703A CN 201711204662 A CN201711204662 A CN 201711204662A CN 107986703 A CN107986703 A CN 107986703A
- Authority
- CN
- China
- Prior art keywords
- aerated bricks
- weather resistance
- compressive strength
- thermal insulation
- high compressive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of aerated bricks of weather resistance high compressive strength and preparation method thereof, including brick body, brick body includes housing and reinforcing rib, the inside of the housing is fixed with high temperature resistant silicon glue plate layer, and the inner side of two sides up and down of the high temperature resistant silicon glue plate layer is equipped with thermal insulation layer, the inner side of two sides of described high temperature resistant silicon glue plate layer or so and the inner vertical of thermal insulation layer are spaced substantially equidistant equipped with three and the corresponding reinforcing plate of thermal insulation layer size, and the reinforcing rib is welded between adjacent thermal insulation layer and reinforcing plate and between reinforcing plate and reinforcing plate.Aerated bricks of the weather resistance high compressive strength and preparation method thereof, with light weight, anti-seismic performance is good, has good insulation, heat insulation concurrently, improves compression strength, resistance to weathering, reduces production cost, has good economic results in society.
Description
Technical field
The invention belongs to wall body building material technical field, more specifically, more particularly to a kind of high pressure resistance of weather resistance
The aerated bricks of degree.Meanwhile the invention further relates to a kind of preparation method of the aerated bricks of weather resistance high compressive strength.
Background technology
Pushing forward comprehensively and deepening constantly with China's Building Energy-saving Work, proposes multi-form insulation system urgent
It is essential and asks so that structure energy-saving integration becomes the important directions of structural system development and application；Structure and energy saving integrated
Architectural structure system is enriched, has also promoted the innovation of China's materials for wall and the development of Building Energy-saving Work；Building energy consumption accounts for
27% or so of social total energy consumption, building energy conservation are built a conservation-minded society and had great importance for realizing energy-saving and emission-reduction,
Therefore construction material needs to develop toward lightweight, the direction of multifunction.In the exploitation in mine, the collection of Mica Mine waste residue
It is not only the problem of field of environment protection is of interest with emission problem, and it is closely bound up with using energy source, and discarded Mica Mine is given up
Slag pollutes the environment, but since there is mica insulation, high temperature resistant, glossy, physical and chemical performance to stablize, has well
The characteristics such as thermal insulation, elasticity and toughness, are applied to building field by mica waste residue, are not exclusively advantageous for the abundant people profit of resource
With, additionally it is possible to environmental protection, the cost of material of building aerated bricks can be reduced, due to the insulation of mica, high temperature resistant, good
The characteristics such as thermal insulation, elasticity and toughness, are applied to aerated bricks plus raw materials such as clay, mineral fibres, white glue with vinyl, calcium silicate slags, can
To solve the problems, such as that aerated bricks compression strength is low, weather resistance intensity is low.
The content of the invention
It is an object of the invention to provide a kind of aerated bricks of weather resistance high compressive strength and preparation method thereof, with solution
State the problem of being proposed in background technology.
To achieve the above object, the present invention provides following technical solution：A kind of aerated bricks of weather resistance high compressive strength, bag
Brick body is included, brick body includes housing and reinforcing rib, and the inside of the housing is fixed with high temperature resistant silicon glue plate layer, and described resistance to
The inner side of two sides up and down of high-temperature silica gel flaggy is equipped with the interior of two sides of thermal insulation layer, the high temperature resistant silicon glue plate layer or so
The inner vertical of side and thermal insulation layer is spaced substantially equidistant equipped with three and the corresponding reinforcing plate of thermal insulation layer size, and it is described plus
Strengthening tendons is welded between adjacent thermal insulation layer and reinforcing plate and between reinforcing plate and reinforcing plate.
Preferably, brick body is rectangle brick body.
Preferably, the triangle stiffener that the reinforcing rib is welded to connect for head and the tail, and the reinforcing rib vertical equity
Arrangement, which is equipped with, is no less than six.
Preferably, honeycomb-like pores are densely covered with the reinforcing plate, and blanket of nitrogen is filled with honeycomb-like pores.
Preferably, the contact position of the reinforcing rib, thermal insulation layer and reinforcing plate between any two is welded to connect.
Present invention also offers a kind of preparation method of the aerated bricks of weather resistance high compressive strength, following step is specifically included
Suddenly：
Mica Mine waste residue utilization Mica Mine crusher, is first carried out broken roughly, the Mica Mine waste residue progress magnet after crushing by S1
Absorption, removes the miscellaneous iron in Mica Mine waste residue, then is matched with counterattack is broken with efficient fine crusher and jaw crusher by cloud
Female ore deposit waste residue crushes, and sieves waste residue, and taking particulate of the particle diameter no more than 2mm, particle diameter is unsatisfactory for the progress of ingredient requirement as raw material
Second-time breakage；
S2, by portland cement, Mica Mine waste residue, clay, mineral fibres, white glue with vinyl, calcium silicate slag, calcium phosphate, organic silicon water-proofing
Agent and additive add in agitator tank plus water is stirred, and slurry is made；
Slurry obtained above, be injected into mould by S3 by casting machine, 30-40s is suppressed by forcing press, into adobe
Die body, wherein pressure are 20-26MPa；
S4, by adobe die body obtained above under 46-55 DEG C of sealed environment, carry out sealing when 2-3 is small by a definite date and rest, from
And adobe is made；
S5, cut adobe adobe obtained above by cutting machine, so that aerated bricks be made；
Aerated bricks, be put into still kettle and carry out steam press maintenance by S6, you can obtains aerated bricks finished product.
Preferably, the mineral fibres in step S2 is sepiolite fibre, and it is strong that additive includes water-reducing agent, foaming agent and morning
Agent, and the occupation proportion of three is respectively 30%, 30% and 40%, and foaming agent is aluminium powder.
Preferably, in step S6 the pressure of still kettle be 1.3-1.5MPa, curing temperature be 120-180 DEG C, curing time
For 2-3 it is small when.
The technique effect and advantage of the present invention：Aerated bricks of the weather resistance high compressive strength and preparation method thereof, use cloud
The cheap raw materials such as female ore deposit waste residue, clay and calcium silicate slag, reduce the usage amount of the cement in aerated bricks production process, can
The Mica Mine waste residue in mining is made full use of, because Mica Mine waste residue has insulation, high temperature resistant, glossy, physical chemistry
It can stablize, there is the characteristics such as good thermal insulation, elasticity and toughness, coordinate other raw materials to use, there is light weight, anti-seismic performance
Well, good insulation, heat insulation are had concurrently, improves compression strength, resistance to weathering, reduce production cost, had well
Economic results in society.
Brief description of the drawings
Fig. 1 is the cross-sectional view of the present invention.
In figure：1 brick body, 2 housings, 3 high temperature resistant silicon glue plate layers, 4 thermal insulation layers, 5 reinforcing plates, 6 reinforcing ribs.
Embodiment
Below in conjunction with the attached drawing in the embodiment of the present invention, the technical solution in the embodiment of the present invention is carried out clear, complete
Site preparation describes, it is clear that described embodiment is only part of the embodiment of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art are obtained every other without making creative work
Embodiment, belongs to the scope of protection of the invention.
The present invention provides a kind of aerated bricks of weather resistance high compressive strength as shown in Figure 1, including brick body 1, the brick
Body 1 includes housing 2 and reinforcing rib 6, and the inside of the housing 2 is fixed with high temperature resistant silicon glue plate layer 3, and the high temperature resistant silica gel
The inner side of two sides up and down of flaggy 3 is equipped with thermal insulation layer 4, the inner side of 3 or so two sides of high temperature resistant silicon glue plate layer and
The inner vertical of thermal insulation layer 4 is spaced substantially equidistant equipped with three and the corresponding reinforcing plate 5 of 4 size of thermal insulation layer, and it is described plus
Strengthening tendons 6 is welded between adjacent thermal insulation layer 4 and reinforcing plate 5 and between reinforcing plate 5 and reinforcing plate.
Specifically, brick body 1 is rectangle brick body.
Specifically, the triangle stiffener that the reinforcing rib 6 is welded to connect for head and the tail, and the longitudinal water of the reinforcing rib 6
Flat raft row, which are equipped with, is no less than six.
Specifically, being densely covered with honeycomb-like pores in the reinforcing plate 5, and blanket of nitrogen is filled with honeycomb-like pores.
Specifically, the reinforcing rib 6, the contact position of thermal insulation layer 4 and reinforcing plate 5 between any two are welded to connect.
The present invention provides a kind of preparation method of the aerated bricks of weather resistance high compressive strength, following steps are specifically included：
Mica Mine waste residue utilization Mica Mine crusher, is first carried out broken roughly, the Mica Mine waste residue progress magnet after crushing by S1
Absorption, removes the miscellaneous iron in Mica Mine waste residue, then is matched with counterattack is broken with efficient fine crusher and jaw crusher by cloud
Female ore deposit waste residue crushes, and sieves waste residue, and taking particulate of the particle diameter no more than 2mm, particle diameter is unsatisfactory for the progress of ingredient requirement as raw material
Second-time breakage；
S2, by portland cement, Mica Mine waste residue, clay, mineral fibres, white glue with vinyl, calcium silicate slag, calcium phosphate, organic silicon water-proofing
Agent and additive add in agitator tank plus water is stirred, and slurry is made；
Slurry obtained above, be injected into mould by S3 by casting machine, 30-40s is suppressed by forcing press, into adobe
Die body, wherein pressure are 20-26MPa；
S4, by adobe die body obtained above under 46-55 DEG C of sealed environment, carry out sealing when 2-3 is small by a definite date and rest, from
And adobe is made；
S5, cut adobe adobe obtained above by cutting machine, so that aerated bricks be made；
Aerated bricks, be put into still kettle and carry out steam press maintenance by S6, you can obtains aerated bricks finished product.
Specifically, the mineral fibres in step S2 is sepiolite fibre, it is strong that additive includes water-reducing agent, foaming agent and morning
Agent, and the occupation proportion of three is respectively 30%, 30% and 40%, and foaming agent is aluminium powder.
Specifically, in step S6 the pressure of still kettle be 1.3-1.5MPa, curing temperature be 120-180 DEG C, curing time
For 2-3 it is small when.
Operation principle, the aerated bricks of the weather resistance high compressive strength and preparation method thereof, using Mica Mine waste residue, clay and
The cheap raw material such as calcium silicate slag, reduces the usage amount of the cement in aerated bricks production process, mine can be made full use of to open
Mica Mine waste residue in adopting, because there is Mica Mine waste residue insulation, high temperature resistant, glossy, physical and chemical performance to stablize, has good
The characteristic such as thermal insulation, elasticity and toughness, coordinate other raw materials to use, there is light weight, anti-seismic performance is good, has good guarantor concurrently
Temperature, heat insulation, improve compression strength, resistance to weathering, reduce production cost, have good economic results in society, with
And reinforcing rib 6 and reinforcing plate 5 have been set in brick body so that the stress-bearing capability of brick body greatly enhances, can meet needs high intensity by
The wall of power.
Finally it should be noted that：The foregoing is only a preferred embodiment of the present invention, is not intended to limit the invention,
Although the present invention is described in detail with reference to the foregoing embodiments, for those skilled in the art, it still may be used
To modify to the technical solution described in foregoing embodiments, or equivalent substitution is carried out to which part technical characteristic,
Within the spirit and principles of the invention, any modification, equivalent replacement, improvement and so on, should be included in the present invention's
Within protection domain.
Claims (8)
1. a kind of aerated bricks of weather resistance high compressive strength, including brick body（1）, it is characterised in that：Brick body（1）Including housing
（2）And reinforcing rib（6）, the housing（2）Inside be fixed with high temperature resistant silicon glue plate layer（3）, and the high temperature resistant silicon offset plate
Layer（3）The inner sides of two sides up and down be equipped with thermal insulation layer（4）, the high temperature resistant silicon glue plate layer（3）The side of left and right two it is interior
Side and thermal insulation layer（4）Inner vertical be spaced substantially equidistant equipped with three and thermal insulation layer（4）The corresponding reinforcing plate of size
（5）, and the reinforcing rib（6）It is welded in adjacent thermal insulation layer（4）And reinforcing plate（5）Between and reinforcing plate（5）And reinforcing plate
Between.
A kind of 2. aerated bricks of weather resistance high compressive strength according to claim 1, it is characterised in that：Brick body（1）
For rectangle brick body.
A kind of 3. aerated bricks of weather resistance high compressive strength according to claim 1, it is characterised in that：The reinforcing rib
（6）For the triangle stiffener being welded to connect from beginning to end, and the reinforcing rib（6）Vertical equity arrangement, which is equipped with, is no less than six.
A kind of 4. aerated bricks of weather resistance high compressive strength according to claim 1, it is characterised in that：The reinforcing plate
（5）On be densely covered with honeycomb-like pores, and be filled with blanket of nitrogen in honeycomb-like pores.
A kind of 5. aerated bricks of weather resistance high compressive strength according to claim 1, it is characterised in that：The reinforcing rib
（6）, thermal insulation layer（4）And reinforcing plate（5）Contact position between any two is welded to connect.
A kind of 6. preparation method of the aerated bricks of weather resistance high compressive strength according to claim 1, it is characterised in that tool
Body comprises the following steps：
Mica Mine waste residue utilization Mica Mine crusher, is first carried out broken roughly, the Mica Mine waste residue progress magnet after crushing by S1
Absorption, removes the miscellaneous iron in Mica Mine waste residue, then is matched with counterattack is broken with efficient fine crusher and jaw crusher by cloud
Female ore deposit waste residue crushes, and sieves waste residue, and taking particulate of the particle diameter no more than 2mm, particle diameter is unsatisfactory for the progress of ingredient requirement as raw material
Second-time breakage；
S2, by portland cement, Mica Mine waste residue, clay, mineral fibres, white glue with vinyl, calcium silicate slag, calcium phosphate, organic silicon water-proofing
Agent and additive add in agitator tank plus water is stirred, and slurry is made；
Slurry obtained above, be injected into mould by S3 by casting machine, 30-40s is suppressed by forcing press, into adobe mould
Body, wherein pressure are 20-26MPa；
S4, by adobe die body obtained above under 46-55 DEG C of sealed environment, carry out sealing when 2-3 is small by a definite date and rest, from
And adobe is made；
S5, cut adobe adobe obtained above by cutting machine, so that aerated bricks be made；
Aerated bricks, be put into still kettle and carry out steam press maintenance by S6, you can obtains aerated bricks finished product.
A kind of 7. preparation method of the aerated bricks of weather resistance high compressive strength according to claim 6, it is characterised in that：Step
Mineral fibres in rapid S2 is sepiolite fibre, and additive includes water-reducing agent, foaming agent and early strength agent, and the occupation proportion of three
Respectively 30%, 30% and 40%, and foaming agent is aluminium powder.
A kind of 8. preparation method of the aerated bricks of weather resistance high compressive strength according to claim 6, it is characterised in that：Step
In rapid S6 the pressure of still kettle be 1.3-1.5MPa, curing temperature be 120-180 DEG C, curing time for 2-3 it is small when.