CN107986614A - A kind of processing technology of instrument cloche - Google Patents
A kind of processing technology of instrument cloche Download PDFInfo
- Publication number
- CN107986614A CN107986614A CN201711359571.4A CN201711359571A CN107986614A CN 107986614 A CN107986614 A CN 107986614A CN 201711359571 A CN201711359571 A CN 201711359571A CN 107986614 A CN107986614 A CN 107986614A
- Authority
- CN
- China
- Prior art keywords
- glass
- cloche
- instrument
- mass percent
- waterborne
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of processing technology of instrument cloche, belong to glass working arts field.The processing technology of the instrument cloche comprises the following steps:(i) dispensing;(ii) heat and melt after the raw material of instrument cloche is mixed by the mass percent of each component, sheet glass is made;(iii) according to instrument with cloche need scribing is carried out to sheet glass, to the glass perforate as needed after scribing and chamfering;(iv) tempering processing is carried out to the glass after scribing;(v) waterborne glass coatings are sprayed;(vi) glass assemble affixed;(vii) sealing, obtained instrument cloche are carried out in the junction of glass.Oxide is more in the instrument cloche of the present invention, and adds rare earth element so that the performances such as glass transmission is heat-insulated are uniform, and service life is longer.
Description
Technical field
The present invention relates to a kind of processing technology of instrument cloche, belong to glass working arts field.
Background technology
Glass is fused together what is formed by sand and other chemical substances(Main production raw material is:Soda ash, lime stone,
Quartz).Contiguous network structure is formed in melting, cooling procedure medium viscosity gradually increases and harden the silicate for causing it to crystallize
Class nonmetallic materials.The chemical composition of simple glass is Na2O·CaO·6SiO2, main component is silica, is a kind of nothing
The non-crystalline solids of regular texture.It is widely used in building, for every wind printing opacity, belonging to mixture.Separately it has been mixed into some
The oxide or salt of metal and show the coloured glass of color, and pass through tempered glass made from specific process etc..
At present, to reach the various demands in production and living, people carry out ordinary plate glass deep processing processing, processing
Glass classification afterwards has:It is tempered glass, ground glass, sand blasting glass, wire glass, hollow glass, laminated glass, shellproof
Glass and heat-bending glass etc..
The content of the invention
The technical problem to be solved in the present invention is in view of the shortcomings of the prior art, propose a kind of instrument of corrosion resistance and good
The corrosion-resistant glass of disk.
The present invention is to solve the technical solution that above-mentioned technical problem proposes to be:A kind of processing technology of instrument cloche,
Comprise the following steps:
(i) dispensing:Instrument is with the mass percent of each component in the glass of cloche:Al2O3:0.83-1.03%, Y2O3:
0.11-0.14%, ZnO:0.24-0.35%, SrO:0.12-0.23%, ZrO2:0.02-0.05%, Gd2O3:0.01-
0.05%, MgO:0.65-0.83%, Mo:0.03-0.06%, Pd:0.02-0.05%, Nd:0.11-0.16%, Cr:0.02-
0.04%, Ni:0.12-0.26%, surplus SiO2;
(ii) heat and melt after the raw material of instrument cloche is mixed by the mass percent of each component, sheet glass is made;
(iii) according to instrument with cloche need scribing is carried out to sheet glass, to the glass perforate as needed after scribing and fall
Angle;
(iv) tempering processing is carried out to the glass after scribing;
(v) waterborne glass coatings are sprayed, are comprised the following steps that:
A, dispensing:The mass percent of each component is in waterborne glass coatings:Waterborne polyurethane resin:0.18-0.22%, acrylic acid
Ester:0.55-0.71%, polyvinyl alcohol:0.39-0.51%, talcum powder:0.53-0.85%, land plaster:1.14-1.27%, melon glue:
0.53-0.77%, fluororesin:0.73-1.51%, waterborne epoxy modified resin:1.32-1.53%、Cr:0.01-0.06%、Ni:
0.15-0.23%、Zn:0.35-0.44%、Mo:0.01-0.03%、Pd:0.01-0.05%、Nd:0.01-0.03%、Ce:0.02-
0.04%、Lu:0.01-0.03%, surplus are water;
B, the material modulated is subjected to filtering 2-3 times with 200 mesh filter clothes, thoroughly to remove impurity;
C, the dust of glass surface is removed with non-dust cloth, reaches thorough clean foreign;
D, using spray gun even application at least one layer waterborne glass coatings;
E, glass is dried after the completion of spraying, baking temperature is 40 DEG C -120 DEG C, is toasted 40-60 minutes;
(vi) glass assemble affixed;
(vii) sealing, obtained instrument cloche are carried out in the junction of glass.
The improvement of above-mentioned technical proposal is:Step (i) in the glass of Instrumental cloche each component mass percent
For:Al2O3:0.83%, Y2O3:0.11%, ZnO:0.24%, SrO:0.12%, ZrO2:0.02%, Gd2O3:0.01%, MgO:
0.65%, Mo:0.03%, Pd:0.02%, Nd:0.11%, Cr:0.02%, Ni:0.12%, surplus SiO2。
The improvement of above-mentioned technical proposal is:Step (i) in the glass of Instrumental cloche each component mass percent
For:Al2O3:1.03%, Y2O3:0.14%, ZnO:0.35%, SrO:0.23%, ZrO2:0.05%, Gd2O3:0.05%, MgO:
0.83%, Mo:0.06%, Pd:0.05%, Nd:0.16%, Cr:0.04%, Ni:0.26%, surplus SiO2。
The improvement of above-mentioned technical proposal is:(v) the mass percent of each component is step in middle waterborne glass coatings:It is water-based poly-
Urethane resin:0.19%th, acrylate:0.57%th, polyvinyl alcohol:0.45%th, talcum powder:0.58%th, land plaster:1.17%th, melon
Glue:0.57%th, fluororesin:0.75%th, waterborne epoxy modified resin:1.35%、Cr:0.01%、Ni:0.15%、Zn:0.35%、Mo:
0.01%、Pd:0.01%、Nd:0.03%、Ce:0.04%、Lu:0.01%, surplus is water.
It is of the invention to be using the beneficial effect of above-mentioned technical proposal:(1)The instrument of the present invention is added with cloche
Al2O3, ZnO and rare earth element, improve the corrosion resistance of instrument cloche, extend service life;(2)The present invention's
Oxide is more in instrument cloche so that the performances such as glass transmission is heat-insulated are uniform, and service life is longer;(3)According to the present invention
The instrument cloche that production. art is produced, it is easy to operate, waste of raw materials is few, while production efficiency is improved, product tool
There is good anti-condensation, reduce cold emission and there is certain security, ensure that the sealing of hollow glass is excellent, eliminate existing
Four corners sealing hidden danger that may be present in production technology, and the overall stability of glass in itself is considerably increased, this
Invented technology flow is perfect, product good seal, stable quality;(4)In the processing technology of the instrument cloche of the present invention,
Glass outer surface covers overlay, substantially increases the intensity of glass, prevents from, due to accidental impact fragmentation easily, extending
Service life;(5)The glass surface spraying waterborne glass coatings of the instrument cloche of the present invention, further increase cloche
Corrosion resistance, extends service life.
Embodiment
Embodiment one
The processing technology of the instrument cloche of the present embodiment, comprises the following steps:
(i) dispensing:Instrument is with the mass percent of each component in the glass of cloche:Al2O3:0.83%, Y2O3:0.11%,
ZnO:0.24%, SrO:0.12%, ZrO2:0.02%, Gd2O3:0.01%, MgO:0.65%, Mo:0.03%, Pd:0.02%,
Nd:0.11%, Cr:0.02%, Ni:0.12%, surplus SiO2;
(ii) heat and melt after the raw material of instrument cloche is mixed by the mass percent of each component, sheet glass is made;
(iii) according to instrument with cloche need scribing is carried out to sheet glass, to the glass perforate as needed after scribing and fall
Angle;
(iv) tempering processing is carried out to the glass after scribing;
(v) waterborne glass coatings are sprayed, are comprised the following steps that:
A, dispensing:The mass percent of each component is in waterborne glass coatings:Waterborne polyurethane resin:0.19%th, acrylate:
0.57%th, polyvinyl alcohol:0.45%th, talcum powder:0.58%th, land plaster:1.17%th, melon glue:0.57%th, fluororesin:0.75%th, it is water-based
Epoxy modified resin:1.35%、Cr:0.01%、Ni:0.15%、Zn:0.35%、Mo:0.01%、Pd:0.01%、Nd:0.03%、Ce:
0.04%、Lu:0.01%, surplus is water;
B, the material modulated is subjected to filtering 2-3 times with 200 mesh filter clothes, thoroughly to remove impurity;
C, the dust of glass surface is removed with non-dust cloth, reaches thorough clean foreign;
D, using spray gun even application at least one layer waterborne glass coatings;
E, glass is dried after the completion of spraying, baking temperature is 40 DEG C -120 DEG C, is toasted 40-60 minutes;
(vi) glass assemble affixed;
(vii) sealing, obtained instrument cloche are carried out in the junction of glass.
Embodiment two
The instrument board of the present embodiment is essentially identical with corrosion-resistant glass and embodiment one, and difference is instrument board with corrosion-resistant
The mass percent of each component is in glass:Al2O3:1.03%, Y2O3:0.14%, ZnO:0.35%, SrO:0.23%, ZrO2:
0.05%, Gd2O3:0.05%, MgO:0.83%, Mo:0.06%, Pd:0.05%, Nd:0.16%, Cr:0.04%, Ni:0.26%, it is remaining
Measure as SiO2。
The present invention is not limited to above-described embodiment.All technical solutions formed using equivalent substitution, all falling within the present invention will
The protection domain asked.
Claims (4)
- A kind of 1. processing technology of instrument cloche, it is characterised in that:Comprise the following steps:(i) dispensing:The instrument is with the mass percent of each component in the glass of cloche:Al2O3:0.83-1.03%, Y2O3: 0.11-0.14%, ZnO:0.24-0.35%, SrO:0.12-0.23%, ZrO2:0.02-0.05%, Gd2O3:0.01- 0.05%, MgO:0.65-0.83%, Mo:0.03-0.06%, Pd:0.02-0.05%, Nd:0.11-0.16%, Cr:0.02- 0.04%, Ni:0.12-0.26%, surplus SiO2;(ii) heat and melt after the raw material of instrument cloche is mixed by the mass percent of each component, sheet glass is made;(iii) according to instrument with cloche need scribing is carried out to sheet glass, to the glass perforate as needed after scribing and fall Angle;(iv) tempering processing is carried out to the glass after scribing;(v) waterborne glass coatings are sprayed, are comprised the following steps that:A, dispensing:The mass percent of each component is in the waterborne glass coatings:Waterborne polyurethane resin:0.18-0.22%, third Olefin(e) acid ester:0.55-0.71%, polyvinyl alcohol:0.39-0.51%, talcum powder:0.53-0.85%, land plaster:1.14-1.27%, melon Youngster's glue:0.53-0.77%, fluororesin:0.73-1.51%, waterborne epoxy modified resin:1.32-1.53%、Cr:0.01-0.06%、 Ni:0.15-0.23%、Zn:0.35-0.44%、Mo:0.01-0.03%、Pd:0.01-0.05%、Nd:0.01-0.03%、Ce: 0.02-0.04%、Lu:0.01-0.03%, surplus are water;B, the material modulated is subjected to filtering 2-3 times with 200 mesh filter clothes, thoroughly to remove impurity;C, the dust of glass surface is removed with non-dust cloth, reaches thorough clean foreign;D, using spray gun even application at least one layer waterborne glass coatings;E, glass is dried after the completion of spraying, baking temperature is 40 DEG C -120 DEG C, is toasted 40-60 minutes;(vi) glass assemble affixed;(vii) sealing, obtained instrument cloche are carried out in the junction of glass.
- 2. the processing technology of instrument cloche according to claim 1, it is characterised in that:Step (i) described in instrument use The mass percent of each component is in the glass of cloche:Al2O3:0.83%, Y2O3:0.11%, ZnO:0.24%, SrO: 0.12%, ZrO2:0.02%, Gd2O3:0.01%, MgO:0.65%, Mo:0.03%, Pd:0.02%, Nd:0.11%, Cr: 0.02%, Ni:0.12%, surplus SiO2。
- 3. the processing technology of instrument cloche according to claim 1, it is characterised in that:Step (i) described in instrument use The mass percent of each component is in the glass of cloche:Al2O3:1.03%, Y2O3:0.14%, ZnO:0.35%, SrO: 0.23%, ZrO2:0.05%, Gd2O3:0.05%, MgO:0.83%, Mo:0.06%, Pd:0.05%, Nd:0.16%, Cr: 0.04%, Ni:0.26%, surplus SiO2。
- 4. the processing technology of instrument cloche according to claim 1, it is characterised in that:Step (v) described in water-based glass The mass percent of each component is in glass paint:Waterborne polyurethane resin:0.19%th, acrylate:0.57%th, polyvinyl alcohol: 0.45%th, talcum powder:0.58%th, land plaster:1.17%th, melon glue:0.57%th, fluororesin:0.75%th, waterborne epoxy modified resin: 1.35%、Cr:0.01%、Ni:0.15%、Zn:0.35%、Mo:0.01%、Pd:0.01%、Nd:0.03%、Ce:0.04%、Lu: 0.01%, surplus is water.