CN107973589A - A kind of sponge city water-permeable brick - Google Patents

A kind of sponge city water-permeable brick Download PDF

Info

Publication number
CN107973589A
CN107973589A CN201711294130.0A CN201711294130A CN107973589A CN 107973589 A CN107973589 A CN 107973589A CN 201711294130 A CN201711294130 A CN 201711294130A CN 107973589 A CN107973589 A CN 107973589A
Authority
CN
China
Prior art keywords
permeable brick
water
sponge city
city water
raw material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711294130.0A
Other languages
Chinese (zh)
Inventor
陈洪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Energy Saving Technology Co Ltd
Original Assignee
Wuhu Energy Saving Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Energy Saving Technology Co Ltd filed Critical Wuhu Energy Saving Technology Co Ltd
Priority to CN201711294130.0A priority Critical patent/CN107973589A/en
Publication of CN107973589A publication Critical patent/CN107973589A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of sponge city water-permeable brick, raw material by percentage to the quality, is made of gold tailings 80% one 90%, gangue 2%~13%, bentonite 5%~9%, high molecular polymer 0%~0.2%.Bentonite includes montmorillonite, galapectite, quartz, and the content of montmorillonite is 75% 80%, and bentonitic cation exchange capacity is 69.7mmol/g.The compression strength of water-permeable brick is 40MPa~55MPa, and porosity is 27%~35%, coefficient of permeability 0.042cm/s~0.051cm/s.The water-permeable brick of the present invention can improve resource utilization, tailing is reduced to take up an area, carrying capacity of environment can be mitigated, the permeance property of brick body can be improved, the processing performance of raw material can be improved again, technique is simple and environmentally-friendly, and is easy to industrialized production, and manufactured water-permeable brick has the advantages that water permeability is good, intensity is high, cost is low etc., with good economic efficiency and social benefit.

Description

A kind of sponge city water-permeable brick
Technical field
The present invention relates to a kind of water-permeable brick, more particularly to a kind of sponge city water-permeable brick.
Background technology
Porous concrete product is the another application approach of pervious concrete in road and municipal works.Water-permeable brick is to use Particular stage with gather materials, cement, cementing agent and water etc. is through made of special process.Because aggregate grading is special, therefore containing big in concrete The interconnected pore of amount, when raining or surface gathered water, water successfully can permeate the ground or be stored in road along " circuit " of these perforations In base.Porous concrete product can be divided into three classes by permeable mode:Front permeable, side permeable and seam permeable.
For water-permeable brick as a kind of novel ecological product for alleviating urban environment decay pressure, its is distinctive to have larger connection The function of porosity and good water permeability, under ponding caused by ensure that the rainwater and road surface other reasons in city is smooth OK, directly penetrate under earth's surface, reduce the influence of pavement runoff.Larger porosity, can also play work in the noise reduction of city With, for saving moisture wherein, under dry climatic environment, can also be scattered and disappeared in atmosphere by the form of evaporation, So as to improve the thermal climate environment in city.As a kind of new Improvement of Ecological Environment product, continuous with application is expanded Greatly, its distinctive performance will be accepted constantly, and the application prospect of water-permeable brick will be paid close attention to be subject to more and more people, more next More researchers starts to study toward this respect.
The content of the invention
Goal of the invention:The purpose of the present invention is to solve deficiency of the prior art, there is provided one kind can mitigate environment and bear Lotus, plays the beautifying and decorating effect to environment, can improve the permeance property of brick body and improve the processing performance of raw material, work Skill is simple and environmentally-friendly, and easy to the sponge city water-permeable brick of industrialized production.
Technical solution:A kind of sponge city water-permeable brick of the present invention, raw material by percentage to the quality, by gold tail Ore deposit 80% one 90%, gangue 2%~13%, bentonite 5%~9%, high molecular polymer 0%~0.2% form;
Bentonite includes montmorillonite, galapectite, quartz, and the content of montmorillonite is 75%-80%, and bentonitic cation exchange is held Measure as 69.7mmol/g;
The compression strength of water-permeable brick is 40MPa~55MPa, and porosity is 27%~35%, coefficient of permeability 0.042cm/s~ 0.051cm/s。
Further, high molecular polymer is organic high molecular polymer, including carboxymethylcellulose sodium, polyacrylamide Amine.
Further, the chemical composition of gold tailings includes aluminium oxide 17wt%, silica 63wt%, a small amount of oxidation Iron, magnesia and other impurities.
Further, the particle diameter of gold tailings is less than 0.025mm.
Further, the preparation method of water-permeable brick is after raw material is weighed by mass percentage plus water is uniformly mixed, It is compressing with different pressures on sampling machine after 20 h of batch mixing, shaping idiosome is obtained, then molding blank is put into drying box, Respectively successively at 110 DEG C, 115 DEG C, 120 DEG C respectively drying 2h, dried molding blank is put into resistance furnace, with 2 DEG C/ The speed of min is warming up to 850 DEG C~950 DEG C, and 1070 DEG C~1120 DEG C are warming up to the speed of 3 DEG C/min, after then keeping the temperature 1h Natural cooling.
Further optimize, the mass ratio of water and raw material mixture is 0.85:1.
Further optimize, be molded idiosome it is compressing in, first time briquetting pressure is 15-35MPa, and molding time is 2-3h;Second of molding pressure is 65-85MPa, molding time 2-3h.
Beneficial effect:The present invention improves resource utilization, reduces tailing and takes up an area, can mitigate carrying capacity of environment, play to environment Beautifying and decorating effect, the permeance property of brick body can be improved and improve the processing performance of raw material, technique is simple and environmentally-friendly, and Easy to industrialized production, and manufactured water-permeable brick has the advantages that water permeability is good, intensity is high, cost is low etc., has well Economic benefit and social benefit.
Embodiment
Embodiments of the present invention are illustrated by particular specific embodiment below, those skilled in the art can be by this explanation Content disclosed by book understands other advantages and effect of the present invention easily.
A kind of sponge city water-permeable brick of the present invention, raw material by percentage to the quality, by gold tailings 80% one 90%, Gangue 2%~13%, bentonite 5%~9%, high molecular polymer 0%~0.2% form.
Bentonite includes montmorillonite, galapectite, quartz, and the content of montmorillonite is 75%-80%, and bentonitic cation is handed over It is 69.7mmol/g to change capacity.
The compression strength of water-permeable brick is 40MPa~55MPa, and porosity is 27%~35%, coefficient of permeability 0.042cm/s~ 0.051cm/s。
As the further optimization to the present invention, high molecular polymer is organic high molecular polymer, including carboxymethyl is fine Dimension element is received, polyacrylamide.The chemical composition of gold tailings includes aluminium oxide 17wt%, silica 63wt%, a small amount of oxygen Change iron, magnesia and other impurities.The particle diameter of gold tailings is less than 0.025mm.The preparation method of water-permeable brick is that raw material is pressed matter After amount percentage weighs plus water is uniformly mixed, compressing with different pressures on sampling machine after 20 h of batch mixing, is obtained into Type idiosome, then molding blank is put into drying box, 2h is respectively dried at 110 DEG C, 115 DEG C, 120 DEG C successively respectively, after drying Molding blank be put into resistance furnace, be warming up to 850 DEG C~950 DEG C with the speed of 2 DEG C/min, heated up with the speed of 3 DEG C/min To 1070 DEG C~1120 DEG C, natural cooling after 1h is then kept the temperature.The mass ratio of water and raw material mixture is 0.85:1.It is molded idiosome It is compressing in, first time briquetting pressure is 15-35MPa, molding time 2-3h;Second of molding pressure is 65- 85MPa, molding time 2-3h.
Embodiment one
A kind of sponge city water-permeable brick, first by mass percentage by gold tailings 80%, gangue 13%, bentonite 6.8%, after carboxymethylcellulose sodium 0.2% weighs plus water is uniformly mixed, and bentonite includes montmorillonite, galapectite, quartz, The content of montmorillonite is 75%, and the chemical composition of gold tailings includes aluminium oxide 17wt%, silica 63wt%, a small amount of oxygen Change iron, magnesia and other impurities.The particle diameter of gold tailings is 0.024mm.Bentonitic cation exchange capacity is 69.7mmol/g.It is compressing with different pressures on sampling machine after batch mixing 20h, shaping idiosome is obtained, then molding blank is put Enter drying box, respectively dry 2h at 110 DEG C, 115 DEG C, 120 DEG C successively respectively, dried molding blank is put into resistance furnace In, 850 DEG C are warming up to the speed of 2 DEG C/min, 1070 DEG C are warming up to the speed of 3 DEG C/min, it is then naturally cold after insulation 1h But.The mass ratio of water and raw material mixture is 0.85:1.Be molded idiosome it is compressing in, first time briquetting pressure is 15MPa, Molding time is 2h;Second of molding pressure is 65MPa, molding time 2h.Obtained water-permeable brick compression strength is 40MPa, porosity 27%, coefficient of permeability 0.042cm/s.
Embodiment two
A kind of sponge city water-permeable brick, first by mass percentage by gold tailings 90%, gangue 4.9%, bentonite 5%, after polyacrylamide 0.1% weighs plus water is uniformly mixed, and bentonite includes montmorillonite, galapectite, quartz, montmorillonite Content be 77%, the chemical compositions of gold tailings includes aluminium oxide 17wt%, silica 63wt%, a small amount of iron oxide, oxygen Change magnesium and other impurities.The particle diameter of gold tailings is 0.022mm.Bentonitic cation exchange capacity is 69.7mmol/g.It is mixed It is compressing with different pressures on sampling machine after expecting 20h, shaping idiosome is obtained, then molding blank is put into drying box, respectively 2h is respectively dried at 110 DEG C, 115 DEG C, 120 DEG C successively, dried molding blank is put into resistance furnace, with 2 DEG C/min's Speed is warming up to 900 DEG C, and 1100 DEG C are warming up to the speed of 3 DEG C/min, then keeps the temperature natural cooling after 1h.Water and raw material mixing The mass ratio of material is 0.85:1.Be molded idiosome it is compressing in, first time briquetting pressure is 25MPa, molding time 2.5h; Second of molding pressure is 75MPa, molding time 2.5h.Obtained water-permeable brick compression strength is 47MPa, and porosity is 30%, coefficient of permeability 0.048cm/s.
Embodiment three
A kind of sponge city water-permeable brick, first by mass percentage by gold tailings 85%, gangue 5.85%, bentonite 9%, after carboxymethylcellulose sodium 0.15% weighs plus water is uniformly mixed, and bentonite includes montmorillonite, galapectite, quartz, The content of montmorillonite is 80%, and the chemical composition of gold tailings includes aluminium oxide 17wt%, silica 63wt%, a small amount of oxygen Change iron, magnesia and other impurities.The particle diameter of gold tailings is less than 0.02mm.Bentonitic cation exchange capacity is 69.7mmol/g.It is compressing with different pressures on sampling machine after batch mixing 20h, shaping idiosome is obtained, then molding blank is put Enter drying box, respectively dry 2h at 110 DEG C, 115 DEG C, 120 DEG C successively respectively, dried molding blank is put into resistance furnace In, 950 DEG C are warming up to the speed of 2 DEG C/min, 1120 DEG C are warming up to the speed of 3 DEG C/min, it is then naturally cold after insulation 1h But.The mass ratio of water and raw material mixture is 0.85:1.Be molded idiosome it is compressing in, first time briquetting pressure is 35MPa, Molding time is 3h;Second of molding pressure is 85MPa, molding time 3h.Obtained water-permeable brick compression strength is 55MPa, porosity 35%, coefficient of permeability 0.051cm/s.
The water-permeable brick of the present invention can improve resource utilization, reduce tailing and take up an area, can mitigate carrying capacity of environment, play to environment Beautifying and decorating effect, the permeance property of brick body can be improved and improve the processing performance of raw material, technique is simple and environmentally-friendly, and Easy to industrialized production, and manufactured water-permeable brick has the advantages that water permeability is good, intensity is high, cost is low etc., has well Economic benefit and social benefit.
Above-mentioned embodiment, technical concept and architectural feature only to illustrate the invention, it is therefore intended that allow and be familiar with this The stakeholder of item technology can implement according to this, but above content is not intended to limit protection scope of the present invention, every according to this hair Any equivalent change or modification that bright Spirit Essence is made, should all fall under the scope of the present invention.

Claims (7)

  1. A kind of 1. sponge city water-permeable brick, it is characterised in that:Raw material by percentage to the quality, by gold tailings 80% 1 90%, gangue 2%~13%, bentonite 5%~9%, the composition of high molecular polymer 0%~0.2%;
    The bentonite includes montmorillonite, galapectite, quartz, and the content of the montmorillonite is 75%-80%, described bentonitic Cation exchange capacity is 69.7mmol/g;
    The compression strength of the water-permeable brick is 40MPa~55MPa, and porosity is 27%~35%, coefficient of permeability 0.042cm/s~ 0.051cm/s。
  2. A kind of 2. sponge city water-permeable brick according to claim 1, it is characterised in that:The high molecular polymer is to have Machine high molecular polymer, including carboxymethylcellulose sodium, polyacrylamide.
  3. A kind of 3. sponge city water-permeable brick according to claim 1, it is characterised in that:The gold tailings chemistry into Dividing includes aluminium oxide 17wt%, silica 63wt%, a small amount of iron oxide, magnesia and other impurities.
  4. A kind of 4. sponge city water-permeable brick according to claim 1, it is characterised in that:The particle diameter of the gold tailings is small In 0.025mm.
  5. A kind of 5. sponge city water-permeable brick according to claim 1, it is characterised in that:The preparation method of the water-permeable brick For after raw material is weighed by mass percentage plus water is uniformly mixed, after 20 h of batch mixing, with different pressures pressure on sampling machine Shape is made, obtains shaping idiosome, then molding blank is put into drying box, is respectively dried at 110 DEG C, 115 DEG C, 120 DEG C successively respectively Dry 2h, dried molding blank is put into resistance furnace, 850 DEG C~950 DEG C are warming up to the speed of 2 DEG C/min, with 3 DEG C/ The speed of min is warming up to 1070 DEG C~1120 DEG C, then keeps the temperature natural cooling after 1h.
  6. A kind of 6. sponge city water-permeable brick according to claim 5, it is characterised in that:Water and the raw material mixture Mass ratio is 0.85:1.
  7. A kind of 7. sponge city water-permeable brick according to claim 5, it is characterised in that:The shaping idiosome is pressed into In shape, first time briquetting pressure is 15-35MPa, molding time 2-3h;Second of molding pressure is 65-85MPa, shaping Time is 2-3h.
CN201711294130.0A 2017-12-08 2017-12-08 A kind of sponge city water-permeable brick Pending CN107973589A (en)