CN107971194A - A kind of method for lifting woodwork anti-pollution characteristic - Google Patents

A kind of method for lifting woodwork anti-pollution characteristic Download PDF

Info

Publication number
CN107971194A
CN107971194A CN201711393498.2A CN201711393498A CN107971194A CN 107971194 A CN107971194 A CN 107971194A CN 201711393498 A CN201711393498 A CN 201711393498A CN 107971194 A CN107971194 A CN 107971194A
Authority
CN
China
Prior art keywords
woodwork
parts
lifting
mentioned steps
pollution characteristic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711393498.2A
Other languages
Chinese (zh)
Inventor
殷四明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Ming Hao Solid Wood Furniture Co Ltd
Original Assignee
Anhui Ming Hao Solid Wood Furniture Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Ming Hao Solid Wood Furniture Co Ltd filed Critical Anhui Ming Hao Solid Wood Furniture Co Ltd
Priority to CN201711393498.2A priority Critical patent/CN107971194A/en
Publication of CN107971194A publication Critical patent/CN107971194A/en
Pending legal-status Critical Current

Abstract

The present invention discloses a kind of method of woodwork anti-pollution characteristic, including following operating procedure：（1）The spraying modified liquid of molding wood product surface will be prepared, be then placed in baking oven, when drying and processing 23 is small after, fully polished using 600# sand paper；（2）Wood product surface brushing resistant is painted again；（3）After being brushed on resistant paint, woodwork is put into baking oven, after drying and processing, finished product.A kind of method for lifting woodwork anti-pollution characteristic provided by the invention, it is easy to operate, it is of low cost, obtained woodwork, surface has excellent wear-resisting, corrosion resistance, especially with excellent anti-pollution characteristic, can effectively reduce the scouring number of wood product surface.

Description

A kind of method for lifting woodwork anti-pollution characteristic
Technical field
The invention belongs to woodwork preparing technical field, and in particular to a kind of method for lifting woodwork anti-pollution characteristic.
Background technology
It is with wood raw material, by processing and fabricating, the product formed, woodwork is broadly divided into following a few major classes： Furniture woodwork, office woodwork, technique woodwork, gardening woodwork, life woodwork.Woodwork during use, It should not be wiped with the towel with water, if often taking wet rag to wipe, moisture can be made to be deep into woodwork, will gradually damaged Woodwork.Therefore need woodwork that there is extremely excellent anti-pollution characteristic.
The content of the invention
The object of the present invention is to provide a kind of method for lifting woodwork anti-pollution characteristic.
The present invention is achieved by the following technical solutions.
A kind of method for lifting woodwork anti-pollution characteristic, including following operating procedure：
（1）The spraying modified liquid of molding wood product surface will be prepared, be then placed in baking oven, when drying and processing 2-3 is small after, use 600# sand paper is fully polished, and wherein modification liquid is made of the component of following parts by weight：3-5 parts of ethylenediamine base propanesulfonate, isopropyl 3-6 parts of alcohol pinacol borate, 22-26 parts of shellac, 250-300 parts of ethanol；
（2）Wood product surface brushing resistant is painted again, wherein resistant paint is made of the component of following parts by weight：Water-based poly- ammonia 36-45 parts of ester resin emulsion, 4-8 parts of ten difluoro enanthol, 1-3 parts of butyl borate, 2-5 parts of defoamer, kojic dipalmitate 2-6 parts；
（3）After being brushed on resistant paint, woodwork is put into baking oven, after drying and processing, finished product.
Specifically, above-mentioned steps（1）In, the mass fraction of ethanol is 75-80%.
Specifically, above-mentioned steps（1）In, modification liquid is made of following methods：Shellac is added into ethanol, it is completely molten Xie Hou, adds ethylenediamine base propanesulfonate, isopropanol pinacol borate thereto successively, after being mixed evenly, is made and changes Property liquid.
Specifically, above-mentioned steps with（1）In, the temperature of baking oven is 65-70 DEG C.
Specifically, above-mentioned steps（2）In, aqueous polyurethane resin emulsion active ingredient is 60%.
Specifically, above-mentioned steps（2）In, defoamer is organic silicon defoamer.
Specifically, above-mentioned steps（2）In, the temperature of oven for drying is 60-65 DEG C, when the time of drying is 3-4 small.
From the above technical scheme, it can be seen that the beneficial effects of the invention are as follows：
A kind of method for lifting woodwork anti-pollution characteristic provided by the invention, easy to operate, of low cost, obtained woodwork, Surface has excellent wear-resisting, corrosion resistance, especially with excellent anti-pollution characteristic, can effectively reduce wood product surface Scouring number.Wherein, step（1）In modification liquid, can effectively be lifted sand paper polishing effect, wood product surface pass through After the polishing of 600# sand paper, the use of priming paint can be avoided, reduces cost, while also effectively improve resistant paint in woodwork The adhesive force on surface, resistant paint provided by the invention, has relatively low surface energy, can effectively lift the soil resistance of woodwork Energy.
Embodiment
Below by specific embodiment, the present invention is described in detail, but the purposes of these illustrative embodiments and Purpose is only used for enumerating the present invention, not forms any type of any restriction to the real protection scope of the present invention, more non-to incite somebody to action Protection scope of the present invention is confined to this.
Embodiment 1
A kind of method for lifting woodwork anti-pollution characteristic, including following operating procedure：
（1）The spraying modified liquid of molding wood product surface will be prepared, be then placed in baking oven, when drying and processing 2 is small after, use 600# sand paper is fully polished, and wherein modification liquid is made of the component of following parts by weight：3 parts of ethylenediamine base propanesulfonate, isopropanol 3 parts of pinacol borate, 22 parts of shellac, 250 parts of ethanol；
（2）Wood product surface brushing resistant is painted again, wherein resistant paint is made of the component of following parts by weight：Water-based poly- ammonia 36 parts of ester resin emulsion, 4 parts of ten difluoro enanthol, 1 part of butyl borate, 2 parts of defoamer, 2 parts of kojic dipalmitate；
（3）After being brushed on resistant paint, woodwork is put into baking oven, after drying and processing, finished product.
Specifically, above-mentioned steps（1）In, the mass fraction of ethanol is 75%.
Specifically, above-mentioned steps（1）In, modification liquid is made of following methods：Shellac is added into ethanol, it is completely molten Xie Hou, adds ethylenediamine base propanesulfonate, isopropanol pinacol borate thereto successively, after being mixed evenly, is made and changes Property liquid.
Specifically, above-mentioned steps with（1）In, the temperature of baking oven is 65 DEG C.
Specifically, above-mentioned steps（2）In, aqueous polyurethane resin emulsion active ingredient is 60%.
Specifically, above-mentioned steps（2）In, defoamer is organic silicon defoamer.
Specifically, above-mentioned steps（2）In, the temperature of oven for drying is 60 DEG C, when the time of drying is 3 small.
Embodiment 2
A kind of method for lifting woodwork anti-pollution characteristic, including following operating procedure：
（1）The spraying modified liquid of molding wood product surface will be prepared, be then placed in baking oven, when drying and processing 2.5 is small after, use 600# sand paper is fully polished, and wherein modification liquid is made of the component of following parts by weight：4 parts of ethylenediamine base propanesulfonate, isopropanol 5 parts of pinacol borate, 24 parts of shellac, 280 parts of ethanol；
（2）Wood product surface brushing resistant is painted again, wherein resistant paint is made of the component of following parts by weight：Water-based poly- ammonia 42 parts of ester resin emulsion, 6 parts of ten difluoro enanthol, 2 parts of butyl borate, 3 parts of defoamer, 4 parts of kojic dipalmitate；
（3）After being brushed on resistant paint, woodwork is put into baking oven, after drying and processing, finished product.
Specifically, above-mentioned steps（1）In, the mass fraction of ethanol is 78%.
Specifically, above-mentioned steps（1）In, modification liquid is made of following methods：Shellac is added into ethanol, it is completely molten Xie Hou, adds ethylenediamine base propanesulfonate, isopropanol pinacol borate thereto successively, after being mixed evenly, is made and changes Property liquid.
Specifically, above-mentioned steps with（1）In, the temperature of baking oven is 68 DEG C.
Specifically, above-mentioned steps（2）In, aqueous polyurethane resin emulsion active ingredient is 60%.
Specifically, above-mentioned steps（2）In, defoamer is organic silicon defoamer.
Specifically, above-mentioned steps（2）In, the temperature of oven for drying is 63 DEG C, when the time of drying is 3.5 small.
Embodiment 3
A kind of method for lifting woodwork anti-pollution characteristic, including following operating procedure：
（1）The spraying modified liquid of molding wood product surface will be prepared, be then placed in baking oven, when drying and processing 3 is small after, use 600# sand paper is fully polished, and wherein modification liquid is made of the component of following parts by weight：5 parts of ethylenediamine base propanesulfonate, isopropanol 6 parts of pinacol borate, 26 parts of shellac, 300 parts of ethanol；
（2）Wood product surface brushing resistant is painted again, wherein resistant paint is made of the component of following parts by weight：Water-based poly- ammonia 45 parts of ester resin emulsion, 8 parts of ten difluoro enanthol, 3 parts of butyl borate, 5 parts of defoamer, 6 parts of kojic dipalmitate；
（3）After being brushed on resistant paint, woodwork is put into baking oven, after drying and processing, finished product.
Specifically, above-mentioned steps（1）In, the mass fraction of ethanol is 80%.
Specifically, above-mentioned steps（1）In, modification liquid is made of following methods：Shellac is added into ethanol, it is completely molten Xie Hou, adds ethylenediamine base propanesulfonate, isopropanol pinacol borate thereto successively, after being mixed evenly, is made and changes Property liquid.
Specifically, above-mentioned steps with（1）In, the temperature of baking oven is 70 DEG C.
Specifically, above-mentioned steps（2）In, aqueous polyurethane resin emulsion active ingredient is 60%.
Specifically, above-mentioned steps（2）In, defoamer is organic silicon defoamer.
Specifically, above-mentioned steps（2）In, the temperature of oven for drying is 65 DEG C, when the time of drying is 4 small.
Finally illustrate, the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted, although with reference to compared with The present invention is described in detail in good embodiment, it will be understood by those of ordinary skill in the art that, can be to the skill of the present invention Art scheme technical scheme is modified or replaced equivalently, without departing from the objective and scope of technical solution of the present invention, it should all cover at this Among the right of invention.

Claims (7)

  1. A kind of 1. method for lifting woodwork anti-pollution characteristic, it is characterised in that including following operating procedure：
    （1）The spraying modified liquid of molding wood product surface will be prepared, be then placed in baking oven, when drying and processing 2-3 is small after, use 600# sand paper is fully polished, and wherein modification liquid is made of the component of following parts by weight：3-5 parts of ethylenediamine base propanesulfonate, isopropyl 3-6 parts of alcohol pinacol borate, 22-26 parts of shellac, 250-300 parts of ethanol；
    （2）Wood product surface brushing resistant is painted again, wherein resistant paint is made of the component of following parts by weight：Water-based poly- ammonia 36-45 parts of ester resin emulsion, 4-8 parts of ten difluoro enanthol, 1-3 parts of butyl borate, 2-5 parts of defoamer, kojic dipalmitate 2-6 parts；
    （3）After being brushed on resistant paint, woodwork is put into baking oven, after drying and processing, finished product.
  2. A kind of 2. method for lifting woodwork anti-pollution characteristic according to claim 1, it is characterised in that above-mentioned steps（1） In, the mass fraction of ethanol is 75-80%.
  3. A kind of 3. method for lifting woodwork anti-pollution characteristic according to claim 1, it is characterised in that above-mentioned steps（1） In, modification liquid is made of following methods：Shellac is added into ethanol, after being completely dissolved, adds ethylenediamine thereto successively Base propanesulfonate, isopropanol pinacol borate, after being mixed evenly, are made modification liquid.
  4. 4. it is according to claim 1 it is a kind of lifted woodwork anti-pollution characteristic method, it is characterised in that above-mentioned steps with （1）In, the temperature of baking oven is 65-70 DEG C.
  5. A kind of 5. method for lifting woodwork anti-pollution characteristic according to claim 1, it is characterised in that above-mentioned steps（2） In, aqueous polyurethane resin emulsion active ingredient is 60%.
  6. A kind of 6. method for lifting woodwork anti-pollution characteristic according to claim 1, it is characterised in that above-mentioned steps（2） In, defoamer is organic silicon defoamer.
  7. A kind of 7. method for lifting woodwork anti-pollution characteristic according to claim 1, it is characterised in that above-mentioned steps（2） In, the temperature of oven for drying is 60-65 DEG C, when the time of drying is 3-4 small.
CN201711393498.2A 2017-12-21 2017-12-21 A kind of method for lifting woodwork anti-pollution characteristic Pending CN107971194A (en)