CN107954602A - Unglazed argentine crystal glaze and preparation method thereof - Google Patents
Unglazed argentine crystal glaze and preparation method thereof Download PDFInfo
- Publication number
- CN107954602A CN107954602A CN201711304378.0A CN201711304378A CN107954602A CN 107954602 A CN107954602 A CN 107954602A CN 201711304378 A CN201711304378 A CN 201711304378A CN 107954602 A CN107954602 A CN 107954602A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- component
- unglazed
- crystal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of unglazed argentine crystal glaze and preparation method thereof, the quality of unglazed metal crystal glaze each component and each component is as follows：35 parts~40 parts of potassium feldspar；8 parts~12 parts of calcite；8 parts~11 parts of wollastonite；8 parts~11 parts of zinc oxide；12 parts~15 parts of iron oxide；5 parts~8 parts of manganese carbonate；10 parts~15 parts of rutile；Light glaze each component and each component quality are as follows：35 parts~38 parts of potassium feldspar；15 parts~18 parts of albite；8 parts~12 parts of calcite；6 parts~8 parts of dolomite；10 parts~12 parts of zinc oxide；1 part~2 parts of lithium carbonate；4 parts~5 parts of strontium carbonate；Suitable toner is added according to required color and makes color for light glaze；Metal crystal glaze that this is unglazed is using black as background color, crystal is into silver color, light glaze is according to the demand colour matching of client, the characteristic of the decoration is that black background color is mutually echoed with the crystal silver color generated, huge contrast is formed in the light tone by light glaze, the decoration is had a distinctive style, extensively liked by consumer.
Description
Technical field
The present invention relates to a kind of unglazed argentine crystal glaze and preparation method thereof, belong to glaze preparing technical field.
Background technology
At present, the crystal glaze being rapidly fired at a temperature of 1200 DEG C, using husky brilliant glaze as main representative.Our company passes through to height
The numerous studies data of danger microcrystalline glaze, start to make a search to 1200 DEG C of microcrystalline glazes being rapidly fired to, finally in the research and development of 2017 years
The unglazed metal crystal glaze that can be matched in excellence or beauty with husky brilliant glaze is gone out, has then been sought by interspersing for light glaze than the husky brilliant more resistance to people of glaze
Taste, makes the only selection of consumers in general.
The content of the invention
The technical problems to be solved by the invention are the defects of overcoming the prior art, improve the control to crystal effect, make
It is more beautiful, and the quality of this is unglazed metal crystal glaze each component and each component is as follows：35 parts~40 parts of potassium feldspar；Calcite 8
Part~12 parts；8 parts~11 parts of wollastonite；8 parts~11 parts of zinc oxide；12 parts~15 parts of iron oxide；5 parts~8 parts of manganese carbonate；Golden red
10 parts~15 parts of stone；Light glaze each component and each component quality are as follows：35 parts~38 parts of potassium feldspar；15 parts~18 parts of albite；
8 parts~12 parts of calcite；6 parts~8 parts of dolomite；10 parts~12 parts of zinc oxide；1 part~2 parts of lithium carbonate；Strontium carbonate 4 parts~5
Part；
In order to solve the above-mentioned technical problem, the technical scheme is that：A kind of unglazed argentine crystal glaze, its group
Part and each component quality are as follows：
A) stock up according to each component and each component mass parts：
B) by material：Glaze:Ball:Water=1:1.6:0.6, when wet ball grinding 14~16 is small, the glaze after ball milling crosses 200 mesh sieves
Afterwards, it is stand-by that 51~53 Baume concentration are modulated into；
C) stock up according to each component and each component mass parts；
D) by material：Glaze:Ball:Water=1:1.6:0.8, when wet ball grinding 13~15 is small, the glaze after ball milling crosses 200 mesh sieves
Afterwards, it is stand-by that 51~53 Baume concentration are modulated into；
E) clean base substrate is taken, latex is accomplished fluently on mouth side, upper panchromatic unglazed metal crystal glaze, after first-class, beats on internal orifice side
Upper waterproofing agent, light glaze is stamped on mouth side again after drying；
F) base that above-mentioned decoration is completed is burnt till in 1200 DEG C of roller kilns.
Embodiment
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, the present invention is made into
One step is described in detail.
Embodiment one：
The quality of this is unglazed metal crystal glaze each component and each component is as follows：35 parts~40 parts of potassium feldspar；8 parts of calcite~
12 parts；8 parts~11 parts of wollastonite；8 parts~11 parts of zinc oxide；12 parts~15 parts of iron oxide；5 parts~8 parts of manganese carbonate；Rutile 5
Part~8 parts；Light glaze each component and each component quality are as follows：35 parts~38 parts of potassium feldspar；15 parts~18 parts of albite；Calcite
8 parts~12 parts；6 parts~8 parts of dolomite；10 parts~12 parts of zinc oxide；1 part~2 parts of lithium carbonate；4 parts~5 parts of strontium carbonate；
A kind of the step of unglazed argentine crystal glaze and preparation method thereof, this method, is as follows：
A) stock up according to each component and each component mass parts；
B) glaze:Ball:Water=1:1.6:0.6, when wet ball grinding 14~16 is small, after the glaze after ball milling crosses 200 mesh sieves, adjust
It is stand-by that 51~53 Baume concentration are made；
C) stock up according to each component and each component mass parts；
D) glaze:Ball:Water=1:1.6:0.8, when wet ball grinding 13~15 is small, after the glaze after ball milling crosses 200 mesh sieves, adjust
It is stand-by that 51~53 Baume concentration are made；
E) clean base substrate is taken, latex is accomplished fluently on mouth side, upper panchromatic unglazed metal crystal glaze, after first-class, beats on internal orifice side
Upper waterproofing agent, light glaze is stamped on mouth side again after drying；
F) base that above-mentioned decoration is completed is burnt till in 1200 DEG C of roller kilns.
Embodiment two：
The quality of this is unglazed metal crystal glaze each component and each component is as follows：35 parts~40 parts of potassium feldspar；8 parts of calcite~
12 parts；8 parts~11 parts of wollastonite；8 parts~11 parts of zinc oxide；12 parts~15 parts of iron oxide；5 parts~8 parts of manganese carbonate；Rutile 10
Part~15 parts；Light glaze each component and each component quality are as follows：35 parts~38 parts of potassium feldspar；15 parts~18 parts of albite；Fang Xie
8 parts~12 parts of stone；6 parts~8 parts of dolomite；10 parts~12 parts of zinc oxide；1 part~2 parts of lithium carbonate；4 parts~5 parts of strontium carbonate；
The step of production method of the unglazed argentine crystal glaze decoration, this method, is as follows：
A) unglazed metal crystal glaze is stocked up according to each component and each component mass parts；
B) glaze:Ball:Water=1:1.6:0.6, when wet ball grinding 14~16 is small, after the glaze after ball milling crosses 200 mesh sieves, adjust
It is stand-by that 51~53 Baume concentration are made；
C) unglazed metal crystal glaze is stocked up according to each component and each component mass parts；
D) glaze:Ball:Water=1:1.6:0.8, when wet ball grinding 13~15 is small, after the glaze after ball milling crosses 200 mesh sieves, adjust
It is stand-by that 51~53 Baume concentration are made；
E) clean base substrate is taken, latex is accomplished fluently on mouth side, upper panchromatic unglazed metal crystal glaze, after first-class, beats on internal orifice side
Upper waterproofing agent, light glaze is stamped on mouth side again after drying；
F) base that above-mentioned decoration is completed is burnt till in 1200 DEG C of roller kilns.
Embodiment three：
A kind of quality of unglazed metal crystal glaze each component and each component is as follows：35 parts~40 parts of potassium feldspar；8 parts of calcite
~12 parts；8 parts~11 parts of wollastonite；8 parts~11 parts of zinc oxide；12 parts~15 parts of iron oxide；5 parts~8 parts of manganese carbonate；Rutile
10 parts~15 parts；Light glaze each component and each component quality are as follows：35 parts~38 parts of potassium feldspar；15 parts~18 parts of albite；Side
Solve 8 parts~12 parts of stone；6 parts~8 parts of dolomite；10 parts~12 parts of zinc oxide；5 parts~6 parts of lithium carbonate；4 parts~5 parts of strontium carbonate；
The step of production method of the unglazed argentine crystal glaze decoration, this method, is as follows：
A) unglazed metal crystal glaze is stocked up according to each component and each component mass parts；；
B) glaze:Ball:Water=1:1.6:0.6, when wet ball grinding 14~16 is small, after the glaze after ball milling crosses 200 mesh sieves, adjust
It is stand-by that 51~53 Baume concentration are made；
C) unglazed metal crystal glaze is stocked up according to each component and each component mass parts；
D) glaze:Ball:Water=1:1.6:0.8, when wet ball grinding 13~15 is small, after the glaze after ball milling crosses 200 mesh sieves, adjust
It is stand-by that 51~53 Baume concentration are made；
E) clean base substrate is taken, latex is accomplished fluently on mouth side, upper panchromatic unglazed metal crystal glaze, after first-class, beats on internal orifice side
Upper waterproofing agent, light glaze is stamped on mouth side again after drying；
F) base that above-mentioned decoration is completed is burnt till in 1200 DEG C of roller kilns.
In summary 3 points to test two as ideal developmental achievement.Experiment one：Crystal effect is undesirable, crystal compared with
The contrast of black and silver color cannot be formed less.Experiment two：Meet the research and development original intention of company, the desired product of company's research and development.Experiment
Three：The mobile performance of light glaze is too strong, influences the overall effect of the decoration.
Particular embodiments described above, pair present invention solves the technical problem that, technical solution and beneficial effect carry out
It is further described, it should be understood that the foregoing is merely the specific embodiment of the present invention, is not limited to this
Invention, within the spirit and principles of the invention, any modification, equivalent substitution, improvement and etc. done, should be included in this hair
Within bright protection domain.
Claims (2)
1. a kind of unglazed argentine crystal glaze, it is characterised in that its each component and the quality of each component are as follows：Potassium feldspar 35
Part~40 parts；8 parts~12 parts of calcite；8 parts~11 parts of wollastonite；8 parts~11 parts of zinc oxide；12 parts~15 parts of iron oxide；Carbon
Sour 5 parts~8 parts of manganese；10 parts~15 parts of rutile；Light glaze each component and each component quality are as follows：35 parts~38 parts of potassium feldspar；
15 parts~18 parts of albite；8 parts~12 parts of calcite；6 parts~8 parts of dolomite；10 parts~12 parts of zinc oxide；Lithium carbonate 1 part~2
Part；4 parts~5 parts of strontium carbonate.
2. unglazed argentine crystal glaze according to claim 1, it is characterised in that its each component and each component party
The step of method, is as follows：
A) stock up according to each component and each component mass parts；
B) by material：Glaze:Ball:Water=1:1.6:0.6, when wet ball grinding 14~16 is small, after the glaze after ball milling crosses 200 mesh sieves,
It is stand-by to be modulated into 51~53 Baume concentration；
C) stock up according to each component and each component mass parts；
D) by material：Glaze:Ball:Water=1:1.6:0.8, when wet ball grinding 13~15 is small, after the glaze after ball milling crosses 200 mesh sieves,
It is stand-by to be modulated into 51~53 Baume concentration；
E) clean base substrate is taken, latex is accomplished fluently on mouth side, upper panchromatic unglazed metal crystal glaze, after first-class, resistance is stamped on internal orifice side
Aqua, light glaze is stamped on mouth side again after drying；
F) base that above-mentioned decoration is completed is burnt till in 1200 DEG C of roller kilns.